CN110885567A - Preparation method of wall surface heat insulation material with strong adsorption function - Google Patents
Preparation method of wall surface heat insulation material with strong adsorption function Download PDFInfo
- Publication number
- CN110885567A CN110885567A CN201911284859.9A CN201911284859A CN110885567A CN 110885567 A CN110885567 A CN 110885567A CN 201911284859 A CN201911284859 A CN 201911284859A CN 110885567 A CN110885567 A CN 110885567A
- Authority
- CN
- China
- Prior art keywords
- parts
- adsorption function
- strong adsorption
- wall surface
- insulation material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a wall surface heat-insulating material with a strong adsorption function, which is implemented according to the following steps: step 1, weighing the following raw materials in parts by weight: 31-41 parts of plant fiber, 21-29 parts of ammonium chloride, 3-5 parts of glycerol, 3-5 parts of a flame retardant, 0.5-1.5 parts of lauryl sodium sulfate, 10-21 parts of corn starch, 10-21 parts of quartz sand, 0.8-1.4 parts of barium carbonate, 17-23 parts of deionized water and 5-9 parts of a compound antioxidant; step 2, uniformly stirring and heating the raw materials; and 3, mixing the mixture obtained in the step 2, and cooling to obtain the wall surface heat insulation material with the strong adsorption function. The invention solves the problem that the heat-insulating material is easy to fall off in the prior art.
Description
Technical Field
The invention belongs to the technical field of energy conservation and environmental protection, and particularly relates to a preparation method of a wall surface heat-insulating material with a strong adsorption function.
Background
Common thermal insulation materials, wherein inorganic materials mainly adopt porous materials such as open-cell expanded perlite, aerated concrete, rock wool, glass wool and the like, organic materials mainly adopt a polymer foaming mode to improve the thermal insulation performance of the materials, but the thermal insulation materials have the characteristics of light weight, looseness, porosity and the like, the thermal insulation performance of the conventional thermal insulation materials is poor, the compressive and flexural strength is also poor, in addition, certain fire phenomena frequently occur in the environment, the conventional thermal insulation materials cannot play a role in restraining fire, and the fire combustion can be promoted, so that greater harm is caused. Therefore, the heat insulation material is greatly limited in the using process, and meanwhile, the existing heat insulation material is easy to fall off and is a problem difficult to solve.
Disclosure of Invention
The invention aims to provide a preparation method of a wall surface heat-insulating material with a strong adsorption function, and solves the problem that the heat-insulating material is easy to fall off in the prior art.
The invention adopts the technical scheme that the preparation method of the wall surface heat-insulating material with the strong adsorption function is implemented according to the following steps:
step 1, weighing the following raw materials in parts by weight: 31-41 parts of plant fiber, 21-29 parts of ammonium chloride, 3-5 parts of glycerol, 3-5 parts of a flame retardant, 0.5-1.5 parts of lauryl sodium sulfate, 10-21 parts of corn starch, 10-21 parts of quartz sand, 0.8-1.4 parts of barium carbonate, 17-23 parts of deionized water and 5-9 parts of a compound antioxidant;
step 2, uniformly stirring and heating the raw materials;
and 3, mixing the mixture obtained in the step 2, and cooling to obtain the wall surface heat insulation material with the strong adsorption function.
The present invention is also characterized in that,
in the step 2, the stirring speed is 200-300 r/min.
And in the step 2, the stirring time is 3-5 h.
Heating to 80-120 ℃ in the step 2.
The mixing time in the step 3 is 30-50 min.
The preparation method of the wall surface heat insulation material with the strong adsorption function has the advantages of simple process, low cost and good application prospect.
Detailed Description
The present invention will be described in detail with reference to the following embodiments.
The invention relates to a preparation method of a wall surface heat insulation material with a strong adsorption function, which is implemented according to the following steps:
step 1, weighing the following raw materials in parts by weight: 31-41 parts of plant fiber, 21-29 parts of ammonium chloride, 3-5 parts of glycerol, 3-5 parts of a flame retardant, 0.5-1.5 parts of lauryl sodium sulfate, 10-21 parts of corn starch, 10-21 parts of quartz sand, 0.8-1.4 parts of barium carbonate, 17-23 parts of deionized water and 5-9 parts of a compound antioxidant;
step 2, uniformly stirring the raw materials, wherein the stirring speed is 200-300 r/min, the stirring time is 3-5 h, and heating to 80-120 ℃;
and 3, mixing the mixture obtained in the step 2 for 30-50 min, and cooling to obtain the wall surface heat insulation material with the strong adsorption function.
Example 1
The invention relates to a preparation method of a wall surface heat insulation material with a strong adsorption function, which is implemented according to the following steps:
step 1, weighing the following raw materials in parts by weight: 41 parts of plant fiber, 29 parts of ammonium chloride, 5 parts of glycerol, 5 parts of a flame retardant, 1.5 parts of lauryl sodium sulfate, 21 parts of corn starch, 21 parts of quartz sand, 1.4 parts of barium carbonate, 23 parts of deionized water and 9 parts of a compound antioxidant;
step 2, uniformly stirring the raw materials, wherein the stirring speed is 300r/min, the stirring time is 5 hours, and heating to 120 ℃;
and 3, mixing the mixture obtained in the step 2 for 50min, and cooling to obtain the wall surface heat insulation material with the strong adsorption function.
Example 2
The invention relates to a preparation method of a wall surface heat insulation material with a strong adsorption function, which is implemented according to the following steps:
step 1, weighing the following raw materials in parts by weight: 31 parts of plant fiber, 21 parts of ammonium chloride, 3 parts of glycerol, 3 parts of a flame retardant, 0.5 part of lauryl sodium sulfate, 10 parts of corn starch, 10 parts of quartz sand, 0.8 part of barium carbonate, 17 parts of deionized water and 5 parts of a compound antioxidant;
step 2, uniformly stirring the raw materials, wherein the stirring speed is 200r/min, the stirring time is 3 hours, and heating to 80 ℃;
and 3, mixing the mixture obtained in the step 2 for 30min, and cooling to obtain the wall surface heat insulation material with the strong adsorption function.
Example 3
The invention relates to a preparation method of a wall surface heat insulation material with a strong adsorption function, which is implemented according to the following steps:
step 1, weighing the following raw materials in parts by weight: 35 parts of plant fiber, 23 parts of ammonium chloride, 4 parts of glycerol, 4 parts of flame retardant, 0.9 part of lauryl sodium sulfate, 15 parts of corn starch, 19 parts of quartz sand, 0.9 part of barium carbonate, 19 parts of deionized water and 7 parts of compound antioxidant;
step 2, uniformly stirring the raw materials, wherein the stirring speed is 250r/min, the stirring time is 4 hours, and heating to 90 ℃;
and 3, mixing the mixture obtained in the step 2 for 40min, and cooling to obtain the wall surface heat insulation material with the strong adsorption function.
Example 4
The invention relates to a preparation method of a wall surface heat insulation material with a strong adsorption function, which is implemented according to the following steps:
step 1, weighing the following raw materials in parts by weight: 38 parts of plant fiber, 26 parts of ammonium chloride, 3 parts of glycerol, 4 parts of flame retardant, 1.2 parts of lauryl sodium sulfate, 18 parts of corn starch, 16 parts of quartz sand, 1.3 parts of barium carbonate, 19 parts of deionized water and 7 parts of compound antioxidant;
step 2, uniformly stirring the raw materials, wherein the stirring speed is 280r/min, the stirring time is 4 hours, heating, and heating to 110 ℃;
and 3, mixing the mixture obtained in the step 2 for 35min, and cooling to obtain the wall surface heat insulation material with the strong adsorption function.
Claims (5)
1. A preparation method of a wall surface heat insulation material with a strong adsorption function is characterized by comprising the following steps:
step 1, weighing the following raw materials in parts by weight: 31-41 parts of plant fiber, 21-29 parts of ammonium chloride, 3-5 parts of glycerol, 3-5 parts of a flame retardant, 0.5-1.5 parts of lauryl sodium sulfate, 10-21 parts of corn starch, 10-21 parts of quartz sand, 0.8-1.4 parts of barium carbonate, 17-23 parts of deionized water and 5-9 parts of a compound antioxidant;
step 2, uniformly stirring and heating the raw materials;
and 3, mixing the mixture obtained in the step 2, and cooling to obtain the wall surface heat insulation material with the strong adsorption function.
2. The preparation method of the wall surface thermal insulation material with the strong adsorption function according to claim 1, wherein the stirring speed in the step 2 is 200-300 r/min.
3. The preparation method of the wall surface heat-insulating material with the strong adsorption function according to claim 1, wherein the stirring time in the step 2 is 3-5 hours.
4. The method for preparing a wall insulation material with a strong adsorption function according to claim 1, wherein the heating in the step 2 is carried out to 80-120 ℃.
5. The method for preparing a wall insulation material with a strong adsorption function according to claim 1, wherein the mixing time in the step 3 is 30-50 min.