CN1210826A - Method for producing wire blended glass cup handle - Google Patents
Method for producing wire blended glass cup handle Download PDFInfo
- Publication number
- CN1210826A CN1210826A CN 98117436 CN98117436A CN1210826A CN 1210826 A CN1210826 A CN 1210826A CN 98117436 CN98117436 CN 98117436 CN 98117436 A CN98117436 A CN 98117436A CN 1210826 A CN1210826 A CN 1210826A
- Authority
- CN
- China
- Prior art keywords
- glass
- cup handle
- glass cup
- mould
- vitreum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
By adding 1-4 pieces of colored glass wires into molten glass and through subsequent heating and rotary drawing, glass cup handle with various colored glass wire is produced. The present invention makes glass cup unique and elegant.
Description
The present invention relates to a kind of making method of glass cup handle, especially relate to a kind of making method of wire blended glass cup handle.The glass cup handle of making of this method makes the beverage cup exotic shape with after cup combines, and is elegant and graceful.
At present, make the making of industry, especially beverage cup at glass cylinder, in beer mug making processes, the employing plastics that are manufactured with of its glass handle are material, and the employing transparent glass that has is made the cup handle, owing to be flooded with such beverage cup everywhere on the market, just show stiff and lack variation.
The objective of the invention is at the deficiencies in the prior art, a kind of making method of brand-new glass cup handle is provided,, produce exotic shape, the glass cup handle that the typical case is generous by in the making processes of glass cup handle, mixing versicolor glass yarn.
The object of the present invention is achieved like this, pour the glass metal that dissolves into mould, mix versicolor glass yarn, be cooled to vitreum slightly, to mix vitreum and mould separating behind the glass yarn while hot, the heating glass body by stretch, rotation or do not rotate the remollescent vitreum, make the stained glass silk that includes form various moulding, adhere to while hot on the cup, make the cup handle.
The making method of a kind of wire blended glass cup handle of the present invention has been broken the circle of existing making glass cup handle technology, has introduced a kind of making method of brand-new glass cup handle, the glass cup handle that adopts this method to make, and exotic shape, elegant and graceful.
Fig. 1 is a wire blended glass cup handle manufacture craft schema
Embodiment 1
From the glass kiln, get the glass metal that dissolves the in right amount mould of packing into, one of insertion is long 5 centimetres in the glass metal that dissolves of the mould of packing into, the stained glass silk that diameter is 4 millimeters, cut and be exposed at the outer glass yarn of metal level, while hot the vitreum that slightly solidifies is glued, calcined about 1 minute for 1300 ℃ with blowing bar, by calcining, glass yarn and vitreum are together softening, and the vitreum lower end of remollescent being mixed glass yarn is bonded at while hot on the glass cup of preheating, and do by design requirements the upper end that stretches
Embodiment 2
From the glass kiln, get the glass metal that dissolves the in right amount mould of packing into, 2 of insertions are long 6 centimetres in the glass metal that dissolves of the mould of packing into, the stained glass silk that diameter is 3 millimeters, cut and be exposed at the outer glass yarn of metal level, while hot the vitreum that slightly solidifies in the mould is glued with blowing bar, calcined about 1 minute for 1400 ℃, by calcining, glass yarn and vitreum are together softening, the vitreum lower end that remollescent is mixed with 2 glass yarn is bonded at while hot on the glass cup of preheating, the rotation upper end stretches, along with Vitrea rotation, in two glass yarn mixing also be rotated into the hank knotting pattern thereupon, by design requirements the glass cup is made definite shape again after, while hot the upper end is bonded on the glass cup, mixes the glass cup handle of 2 root dyeing glass yarn hank knotting patterns in making.
Embodiment 3
From the glass kiln, get the glass metal that dissolves the in right amount mould of packing into, 4 of insertions are long 7 centimetres in the glass metal that dissolves of the mould of packing into, the stained glass silk that diameter is 2 millimeters, cut and be exposed at the outer glass yarn of metal level, while hot the vitreum that slightly solidifies in the mould is glued with blowing bar, about 1 minute of 1500 ℃ of calcinings, treat that vitreum and glass yarn together soften after, move apart flame.The vitreum lower end that is mixed with 4 glass yarn is bonded on the glass cup of preheating, and definite shape is made by design requirements in the upper end that stretches, and while hot the upper end is bonded on the glass cup, mixes the glass cup handle of 4 root dyeing glass yarn in making.
Claims (1)
1, a kind of method of making wire blended glass cup handle is characterized in that:
A. pour the glass metal that dissolves into mould, 1-4 root dyeing glass yarn is inserted mould, cooling slightly makes the glass metal in the mould become vitreum;
B. take out vitreum from mould, 1300 ℃-1500 ℃ calcinings are softening;
C. the vitreum lower end with soft China is bonded on the glass cup, and the glass handle modeling on rotating or not rotating, is made in the upper end that stretches, and the upper end is bonded on the glass cup.