CN1177581A - Fuli colour-plate of inorganic glass fiber reinforced plastics, and production process thereof - Google Patents
Fuli colour-plate of inorganic glass fiber reinforced plastics, and production process thereof Download PDFInfo
- Publication number
- CN1177581A CN1177581A CN96117730A CN96117730A CN1177581A CN 1177581 A CN1177581 A CN 1177581A CN 96117730 A CN96117730 A CN 96117730A CN 96117730 A CN96117730 A CN 96117730A CN 1177581 A CN1177581 A CN 1177581A
- Authority
- CN
- China
- Prior art keywords
- layer
- mentioned
- colloidal substance
- substance thing
- glass fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to an inorganic glass fibre reinforced plastic colour decorative veneer and its production process. Saind invented product is made up by using magnesium chloride and magnesium oxide as main raw material, adding proper auxiliary material and adopting a special production process. Said invented product has no need of surface-spraying treatment, is smooth in surface, acid-resisting and alkali-resisting, strong in moisture resistance and refratoriness, and its surface is fadeless after used for a long period, so that it is an ideal building and decorative material as substitute for shaving board and fiberboard.
Description
The present invention relates to a kind of decorative sheet and production technique thereof that is used for building wall and indoor separation.
Inorganic Fuli plate is with its lightweight, fire-retardant and good decorating effect and be used widely in building decoration.It is major ingredient that this Fuli plate adopts magnesium oxide and magnesium chloride, adds auxiliary material stearic acid, laking agent etc. and produces.But above-mentioned Fuli plate is only limited to monochrome, can not produce various color and lusters, if need produce distinct colors, then needs to carry out spray treatment on the surface of plate.And surface peeling can appear in the shades of colour of spray treatment in use for some time, phenomenon such as fade, and presents former true qualities, has had a strong impact on quality product and decorative effect.
At the problem of above-mentioned existence, the objective of the invention is to propose a kind of color and luster and select arbitrarily, need not carry out surperficial spray treatment, do not fade and any surface finish, the simple Fuli colour-plate of inorganic glass fiber reinforced plastics of production technique and production technique thereof.
Technical scheme of the present invention is achieved in that
Starting material and weight proportion thereof that the present invention is selected are as follows:
Major ingredient:
Magnesium oxide 55--60
Magnesium chloride 15--20
Sawdust 5--10
Auxiliary material:
Stearic acid 0.03--0.2
Peregal 0.02--0.15
Laking agent 0.02--0.2
Machine oil 0.0--2.5
Vaseline 0.05--0.6
Pigment 0.5--10
Production technique of the present invention is:
To heat behind stearic acid, peregal, laking agent, Vaseline and the machine oil uniform mixing in the above-mentioned auxiliary material earlier to boiling point and melt, add above-mentioned melt total amount 50% and temperature be 50C--70C hot water, make solvent;
The major ingredient magnesium chloride is added its total amount 1-2 water-soluble liquid that changes into doubly, add the above-mentioned auxiliary material solvent 2%--10% for preparing therein again, cold is put after 12 hours and is used;
The above-mentioned magnesium chloride liquid for preparing is added magnesium oxide be mixed into the colloidal substance thing, add machine oil and needed pigment again, thorough mixing evenly back is stand-by;
Selecting a good flat sheet of smooth finish for use is substrate, the above-mentioned colloidal substance thing for preparing of even thereon coated one deck, layer of glass fiber fabric tiles on this colloidal substance thing layer, coated second layer colloidal substance thing on this fiberglass layer again, second layer glass cloth then tiles on above-mentioned second layer colloidal substance thing layer, the uniform mixture of coated again one deck sawdust and above-mentioned colloidal substance thing on this layer glass cloth covers the 3rd layer of glass cloth then thereon;
Last tiling covers one deck mylar on the 3rd layer of above-mentioned glass cloth, and steam bubble is caught up with to the greatest extent;
Take off from substrate after leaving standstill the above-mentioned sheet material of making more than 4 hours, be put in and handle in the pond that is added with sodium hydroxide more than 4 hours, taking-up airing and pressing from the pond, finishing corner get final product then.
In above-mentioned production technique, should note strict controlled temperature and magnesia reaction, the excessive temperature in preventing to react, and can adopt multi-platform production, to improve work efficiency, can increase and decrease the add-on of auxiliary material according to the conversion of weather.
Adopt the Fuli plate of prescription of the present invention and explained hereafter, can adjust color arbitrarily, the color and luster nature, the plate face is bright and clean, and the decolouring and the phenomenon of fading can not take place in life-time service, and the plate surface does not need to carry out spray treatment, good decorating effect yet again.Owing to can adopt multi-platform production, thereby improve work efficiency greatly.Simultaneously, the good flame retardation effect of this plate can reach the requirement of the not flammable type PLASTIC LAMINATED of A level, and have acid and alkali-resistance, advantage such as do not make moist, do not ftracture, be a kind of ideal architecture and decorative boards that substitutes existing shaving board, fiberboard etc.
Further specified below in conjunction with embodiment:
Claim with stearic acid 5g, peregal 8g, laking agent 9g, Vaseline 10g and machine oil 110g, will heat behind the above-mentioned raw materials uniform mixing that add the 71g water of above-mentioned melt total amount, water temperature is 50C--70C, makes solvent to the boiling point fusing.Take by weighing the adding of 1.5Kg magnesium chloride and put into container, add the water-soluble liquid that changes into of 3kg, add the above-mentioned auxiliary material solvent 8% for preparing therein again, cold is put after 12 hours and is used.The above-mentioned magnesium chloride liquid for preparing is added 5.8Kg magnesium oxide be mixed into the colloidal substance thing, add 100g machine oil and 100g pink pigment again, thorough mixing evenly back is stand-by.Select for use a 1.2m * 2.4m layered board (other sheet material that also optional smooth finish is good) as substrate, the above-mentioned colloidal substance thing for preparing of even thereon coated one deck, layer of glass fiber fabric tiles on this colloidal substance thing layer, coated second layer colloidal substance thing on this fiberglass layer again, second layer glass cloth then tiles on above-mentioned second layer colloidal substance thing layer, invest on the second layer glass cloth being coated with again behind 0.8kg sawdust and the above-mentioned residue colloidal substance thing uniform mixing, cover the 3rd layer of glass cloth then thereon.Last tiling covers one deck mylar on the 3rd layer of above-mentioned glass cloth, and steam bubble is caught up with to the greatest extent.Take off from substrate after leaving standstill the above-mentioned sheet material of making more than 4 hours, be put in and handle in the pond that is added with sodium hydroxide more than 4 hours, from the pond, take out airing then and flatten, repair the corner and can dispatch from the factory.
Claims (2)
1, a kind of Fuli colour-plate of inorganic glass fiber reinforced plastics is characterized in that selected starting material and weight proportion thereof are as follows:
Major ingredient:
Magnesium oxide 55--60
Magnesium chloride 15--20
Sawdust 5--10
Auxiliary material:
Stearic acid 0.03--0.2
Peregal 0.02--0.15
Laking agent 0.02--0.2
Machine oil 0.0--2.5
Vaseline 0.05--0.6
Pigment 0.5--10
2, a kind of production technique of Fuli colour-plate of inorganic glass fiber reinforced plastics is characterized in that:
A. will heat behind stearic acid, peregal, laking agent, Vaseline and the machine oil uniform mixing in the above-mentioned auxiliary material earlier to boiling point and melt, add above-mentioned melt total amount 50% and temperature be 50C--70C hot water, make solvent;
B. the major ingredient magnesium chloride is added its total amount 1-2 water-soluble liquid that changes into doubly, add the above-mentioned auxiliary material solvent 2%--10% for preparing therein again, cold is put after 12 hours and is used;
C. the above-mentioned magnesium chloride liquid for preparing is added magnesium oxide and be mixed into the colloidal substance thing, add machine oil and needed pigment again, thorough mixing evenly back is stand-by;
D. selecting a good flat sheet of smooth finish for use is substrate, the above-mentioned colloidal substance thing for preparing of even thereon coated one deck, layer of glass fiber fabric tiles on this colloidal substance thing layer, coated second layer colloidal substance thing on this fiberglass layer again, second layer glass cloth then tiles on above-mentioned second layer colloidal substance thing layer, the uniform mixture of coated again one deck sawdust and above-mentioned colloidal substance thing on this layer glass cloth covers the 3rd layer of glass cloth then thereon;
E. last tiling covers one deck mylar on the 3rd layer of above-mentioned glass cloth, and steam bubble is caught up with to the greatest extent;
F. take off from substrate after the above-mentioned sheet material of making being left standstill more than 4 hours, be put in and handle in the pond that is added with sodium hydroxide more than 4 hours, from the pond, take out airing then and flatten, repair the corner.