CN1171453A - 稀土代替铝－镁－硅变形铝合金的均匀化处理 - Google Patents
稀土代替铝－镁－硅变形铝合金的均匀化处理 Download PDFInfo
- Publication number
- CN1171453A CN1171453A CN 96110564 CN96110564A CN1171453A CN 1171453 A CN1171453 A CN 1171453A CN 96110564 CN96110564 CN 96110564 CN 96110564 A CN96110564 A CN 96110564A CN 1171453 A CN1171453 A CN 1171453A
- Authority
- CN
- China
- Prior art keywords
- alloy
- rare earth
- aluminum
- magnesium
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于用稀土代替铝—镁—硅变型铝合金的均匀化处理工艺。本发明首先在电解槽中加入稀土,电解成稀土铝合金,之后在混合炉中配制稀土变型铝合金的铸态合金,在460℃±10℃下,压力200～170巴进行挤压成型材之后,在12小时内,180℃±10℃进行时效处理2—4小时,得到铝—镁—硅变型合金,机械性能优于已有合金。本发明由于加入稀土Ce,使生产工艺简化,节省了高温下进行均匀化处理的生产环节,从而不仅节约能源、设备和占地,而且提高了产品的性能指标。
Description
本发明属于用稀土代替铝-镁-硅变形铝合金的均匀化处理工艺。
铝-镁-硅变形铝合金具有重量轻、挤压性能好的特点，因此铝及其合金制品早已进入人们的家庭生活之中，特别是铝-镁-硅变形铝合金易加工成形状复杂的型材，表面光洁度好，有金属光泽，还可以氧化着色，近年在建筑、装璜及交通运输等行业中普遍受到欢迎。
目前铝-镁-硅变形铝合金的生产，一般采用镁≤0.9％，硅≤0.6％，Fe≤0.35％，其它微量元素≤0.1％，其工艺为将φ190mm的铸态铝合金经450℃±10℃高温处理，以达到其各组分的均匀分布，在460℃±10℃，压力200-170巴进行挤压，挤压速度为4-5mm/s，成型材之后在12小时内180±10℃处理2-4小时，得到的铝-镁-硅变形合金机械性能：
状态 RCS
强度σb MPa 157
延伸率δ％ 8
硬度HV 58
本发明的目的是在铝-镁-硅变形铝合金中添加少量稀土，以代替铝-镁-硅变形铝合金的均匀化处理工艺，而且可以提高合金的机械性能。
本发明采用(wt％)Mg0.5～0.6，Si0.25～0.32，Fe0.20～0.25稀土是Al-Ce中间合金，Ce的含量～10％，合金中稀土加入量0.05-0.30，其余为Al。工艺过程，首先在电解槽中加入稀土，电解成稀土铝合金，之后在混合炉中配制成稀土变形铝合金的铸态合金其φ190×700mm，在460℃±10℃下，压力为200～170巴进行挤压，挤压速度为4～5mm/s，成型材之后在12小时内，180℃±10℃进行时效处理2-4小时，得到的铝-镁-硅变形合金机械性能为：
状态 RCS
抗拉强度σb MPa 200～219
延伸率δ％ 9.0～9.4
硬度HV 70.2～78.6
本发明由于加入稀土Ce，使生产工艺简化，节省了高温下进行均匀化处理的生产环节，从而不仅节约能源、设备和占地，而且提高了产品的性能指标。
本发明提供的实施例如下：
实施例1：
铝-镁-硅合金，添加Mg0.60％、Si0.29％、Fe0.24％、Ce0.05％，在60KA电解槽中电解成稀土铝合金，然后在混合炉中配制成铸态稀土铝-镁-硅合金，铸棒尺寸为φ190×700mm，在压力200巴，挤压速度4mm/s下，挤压成型材，在12小时内180℃进行时效处理2小时，得稀土铝合金抗拉强度200MPa，硬度70.5HV，延伸率9.3％。
实施例2：
除Al之外，Mg0.5％、Si0.25％、Fe0.22％、Ce0.30％，铸棒190×700mm，压力170巴，挤压速度4mm/s，在12小时内185℃进行时效处理3.5小时，得稀土铝合金，抗拉强度220MPa，硬度73HV，延伸率9.4％。
Claims (1)
1.一种稀土代替铝-镁-硅变型铝合金的均匀化处理工艺，其特征在于采用(wt％)Mg0.5～0.6，Si0.25～0.32，Fe0.20～0.25稀土是Al-Ce中间合金，Ce的含量～10％，合金中稀土加入量0.05-0.30，其余为Al。工艺过程，首先在电解槽中加入稀土，电解成稀土铝合金，之后在混合炉中配制成稀土变形铝合金的铸态合金其φ190×700mm，在460℃±10℃下，压力为200～170巴进行挤压，挤压速度为4～5mm/s，成型材之后在12小时内，180℃±10℃进行时效处理2-4小时，得到的铝-镁-硅变形合金机械性能为：
状态 RCS
抗拉强度σb MPa 200～219
延伸率δ％ 9.0～9.4
硬度HV 70.2～78.6。