CN117098672A - 用于形成一个或多个卡片的片材组件 - Google Patents
用于形成一个或多个卡片的片材组件 Download PDFInfo
- Publication number
- CN117098672A CN117098672A CN202280026511.3A CN202280026511A CN117098672A CN 117098672 A CN117098672 A CN 117098672A CN 202280026511 A CN202280026511 A CN 202280026511A CN 117098672 A CN117098672 A CN 117098672A
- Authority
- CN
- China
- Prior art keywords
- layer
- edge
- resin
- bio
- sheet assembly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
片材组件(100)可被切割成卡片(102),包括:上层(124),该上层被配置成接受第一印刷(122);芯层(126),该芯层与上层和下层(128)联接,下层被配置成接受第二印刷(130)并与芯层联接,其中芯层被设置在上片材和下片材之间。上层、芯层或下层中的一者或多者形成自用树脂浸渍的纸,该树脂包括基于生物的树脂。基于生物的树脂可包括以下一者或多者:植物、基于石油的或不基于石油的、纤维素、木质纤维素、天然纤维、淀粉、多糖、脂肪和油、蛋白质和/或藻朊酸盐、洋麻、剑麻、黄麻、大麻和亚麻、玉米淀粉、马铃薯淀粉、木薯淀粉、果胶、几丁质、果聚糖、支链淀粉、大豆、雷斯克懒勒、菜籽、酪蛋白、玉米蛋白、大豆蛋白、PLA、PHA、PBAT、PBS、PE、PP、PET、PUR、EPDM、PVC、PMMA、PEF、PTF、PTT、SBR、PBT、ABS、PA、APC、CA。
Description
关联申请的交叉引用
本申请要求2021年2月10日提交的美国申请63/147,898的优先权,其全部内容援引包含于此。
背景技术
技术领域
本文描述的主题涉及可被切割成较小的卡片的多层片材组件,所述较小的卡片例如是身份卡、金融交易卡(信用卡、借记卡、礼品卡等)或其它类型的卡片。
背景技术
卡片可用于多种用途,例如识别或安保、金融交易等。随着朝向越来越多的环境考虑和“绿色”产品的趋势,一些制造商转而生产生物可降解卡片。这些卡片由多个纸层形成,所述多个纸层通过生物可降解聚合物保持在一起。但这些已知的可降解卡片不耐久并且可能无法经受反复使用、潮湿环境等。例如,一些这样的卡片经受剥落,这使得卡片不可使用。一些较高端的金融交易卡片由金属制成或包括金属以提供较重的卡片,这对于消费者来说可能是理想的。但是引入这些类型的材料可能使得卡片的再循环利用变得更难或更高成本。
发明内容
在一个实施例中,提供了一种能够被切割成一个或多个卡片的片材组件。片材组件包括上层,该上层被配置成接受一个或多个卡片的第一印记的第一印刷。片材组件也可包括芯层,该芯层与上层和下层联接,该下层被配置成接受一个或多个卡片的第二印记的第二印刷。下层可与芯层联接,芯层设置在上片材和下片材之间。上层、芯层或下层中的一者或多者可由浸渍有树脂的纸形成,该树脂包括基于生物的树脂。
在一个实施例中,一种用于生产片材组件的方法可包括:形成芯层并将上层联接至芯层,上层被配置成接受一个或多个卡片的第一印记的第一印刷。该方法可包括将下层联接至芯层以形成包括上层、芯层和下层的片材组件。下层可与芯层联接,芯层设置在上层和下层之间。下层可被配置成接受一个或多个卡片的第二印记的第二印刷。片材组件可被配置成切割成一个或多个卡片。上层、芯层或下层中的一者或多者可由浸渍有树脂的纸形成,该树脂包括基于生物的树脂。
附图简述
本发明主题可通过参照附图阅读对非限定性实施例的以下描述来理解,附图如下:
图1示出多层片材组件的一个实施例的立体图;
图2示出根据一个实施例的图1所示的卡片沿图1中的剖切线2-2得到的横截面图;
图3示出根据一个实施例的图1所示的卡片沿图1中的剖切线2-2得到的横截面图;
图4示出根据一个实施例的图1所示的卡片沿图1中的剖切线2-2得到的横截面图;
图5示出根据一个实施例的图1所示的卡片沿图1中的剖切线2-2得到的横截面图;
图6示出根据一个实施例的卡片的分解图;以及
图7示出根据一个实施例的用于形成片材组件的方法的流程图,该片材组件可被切割成较小卡片。
具体实施方式
本文描述的本发明的主题提供了多层片材组件,可从中切割出若干卡片。卡片可被成形以用作身份卡、安保卡、金融交易卡等等。片材组件可由包括浸渍有树脂的纸的材料形成。树脂可以是基于石油的树脂或基于生物的树脂。基于生物的树脂可包括由可再生或生物资源(例如植物)构成的树脂。基于生物的树脂可包括非基于石油的树脂。该树脂可以是热塑或热固的。
卡片可包括高密度颗粒以提高卡片的特性并为卡片提供金属的重量和金属的质感或重冲击的卡片。可提供高密度颗粒以使卡片非导电,由此卡片不会经历静电放电。卡片可以使用用于生产塑料卡片的当前设备来制造。卡片可以比当前塑料卡片更耐久并可使用多达五年或更多年。卡片可以是例如金融交易卡、身份卡、密钥卡、门禁卡或安保卡。
片材组件也可用于形成其它产品。例如,片材组件可用于形成柜面、台面、家具表面和地板上的装饰薄板。
图1示出多层片材组件100的一个实施例的立体图。片材组件100可以足够大以从片材组件切割出若干卡片102。这些卡102可以是身份卡(例如驾驶员的驾照、工作身份卡等)、金融交易卡(例如信用卡、借记卡、礼品卡等)等等。在一个实施例中,每个卡片102具有由ISO/IEC 7810ID-1标准定义的形状和尺寸。替代地,卡片102可具有不同的形状和/或尺寸。片材组件100可以足够大以从片材组件100切割出若干个(例如63个或其它数量)卡片102。例如,片材组件100在片材组件100的每一侧上可具有一定表面积,该表面积为至少2911平方厘米。
图2示出根据一个实施例的图1所示的卡片沿图1中的剖切线2-2得到的横截面图。卡片包括上透明覆盖层120和下透明覆盖层132。上透明覆盖层和下透明覆盖层可由聚合物形成。在另一实施例中,上透明覆盖层和下透明覆盖层可由浸渍有树脂的纸形成。浸渍有树脂的纸可用树脂浸透。浸渍有树脂的纸可具有纸纤维和树脂聚合物的中间渗透网。纸浸渍的树脂可具有散布在整个纸上或嵌入到纸中的树脂。浸渍有树脂的纸可具有与纸混合的树脂。树脂可均匀地或同质地提供在树脂浸渍的纸中。
树脂可包括基于生物的树脂。基于生物的树脂可以是由生物资源(例如植物)形成的树脂。基于生物的树脂可以是非基于石油的树脂。树脂也可包括基于石油的树脂。例如,浸渍有树脂的纸可浸渍有树脂,该树脂是40%基于生物的树脂,剩下的是基于石油的树脂。根据其它示例,该树脂可包括多达50%、多达60%、多达70%、多达80%、多达90%或多达100%的基于生物的材料,剩下的是基于石油的树脂。根据另一示例,浸渍有树脂的纸可包括树脂,该树脂是40%-70%基于生物的树脂。
可以在浸渍有树脂的纸中的基于生物的树脂可包括用纤维素、木质纤维素、天然纤维、淀粉、多糖、脂肪和油、蛋白质和/或藻朊酸盐形成的基于生物的聚合物。天然纤维的示例可包括洋麻、剑麻、黄麻、大麻和亚麻。木质纤维素的示例可包括玉米淀粉、马铃薯淀粉或木薯淀粉。多糖的示例可包括果胶、几丁质、果聚糖或支链淀粉。油脂的例子可包括大豆、雷斯克懒勒(lesquerella)和菜籽。蛋白质的例子可包括酪蛋白、玉米蛋白或大豆蛋白。
可用于树脂浸渍纸的基于生物的聚合物可包括聚乳酸(PLA)、聚羟基烷酸酯(PHA)、聚己二酸丁二醇酯(PBAT)、聚丁二酸丁二醇酯(PBS)、聚乙烯(PE)、聚丙烯(PP)、聚对苯二甲酸乙二酯(PET)、聚氨基甲酸乙酯(PUR)、乙烯丙烯二烯单体(EPDM)、聚氯乙烯(PVC);聚丙烯(PP)、聚对苯二甲酸乙二醇酯(PET)、聚氨酯(PUR)、三元乙丙橡胶(EPDM)、聚氯乙烯(PVC)、聚甲基丙烯酸甲酯(PMMA)、聚呋喃乙烯酯(PEF)、聚三亚甲基呋喃二甲酸酯(PTF)、聚对苯二甲酸三甲酯(PTT)、丁苯橡胶(SBR)、聚对苯二甲酸丁二醇酯(PBT)、丙烯腈-丁二烯-苯乙烯(ABS)、聚酰胺(PA)、脂肪族聚碳酸酯(APC)和醋酸纤维素(CA)。
可用于片材组件的基于生物的薄膜可由上述基于生物的聚合物形成。例如,可用于片材组件的基于生物的薄膜可以是由基于生物的聚碳酸酯(如三菱化学公司的DURABIOTM或德国科思创公司的EC)形成的基于生物的聚碳酸酯薄膜。例如,可用于片材组件的基于生物的薄膜可以是基于纤维素的聚合物,如TREVATM或基于生物的共聚聚酯,如伊士曼化学公司生产的TRITANTM。
纸可以是酚醛纸。纸最多可浸渍约50%的树脂。纸可用少于50%的树脂(包括基于石油的树脂)浸渍。其他可用于浸渍纸的树脂包括三聚氰胺、甲醛和酚醛树脂。
卡片可进一步包括上印刷层122和下印刷层130。上印刷层122和下印刷层130可由一种材料形成,该材料能够通过油墨印刷在其上以在卡片102的上印刷层122的可见表面(例如顶表面或前表面)和卡片102的下印刷层130的可见表面(例如底表面或后表面)上形成印记。该印记可包括识别信息(例如人名、公司名、账号、照片、图像等)或其它信息。上印刷层和下印刷层可由聚对苯二甲酸乙二醇(PET)形成。上印刷层和下印刷层可由基于生物的聚碳酸酯薄膜形成。上印刷层122和下印刷层130可由预先浸渍的印刷底层纸形成。
上印刷层和下印刷层可包括卡片的一个或多个光学特征。例如,一个或多个金属片材本体或类似物可被包含在和/或添加到上印刷层或下印刷层中的一者或多者以形成卡片的反射特征、衍射特征、安全和/或不透明特征。
卡片也可包括上部树脂浸渍可印刷纸层124和下部树脂浸渍可印刷层128。基于生物的上部和下部树脂浸渍可印刷纸层可以是不透明的、半透明的或透明的。树脂可包括基于生物的树脂。树脂可包括基于石油的树脂。例如,树脂可以是这样的树脂:其中具有40%-70%的基于生物的树脂,其余是基于石油的树脂。
卡片也可包括芯层126。芯层可以由树脂浸渍的纸形成。树脂可包括基于生物的树脂。树脂也可以包括基于石油的树脂。例如,树脂可以是这样的树脂:其具有40%-70%的基于生物的树脂,其余部分的树脂是基于石油的树脂。通过将芯层提供为多个薄层或片材,芯层可以被形成为分裂的芯层。芯层的纸和/或浸渍的树脂可包括高密度颗粒134以增加卡片的重量,这对于较高端的或豪华交易卡来说可能是理想的,而不必在片材组件100或卡片102内引入金属层。这可防止片材组件100和每个卡片102形成、具有或包括导电层,该导电层将ESD或其它电流传导通过片材组件100或卡片102。选择地,卡片的其它层可具有设置在纸或树脂的一者或多者内的高密度颗粒。选择地,卡片没有任何一个层可具有高密度颗粒。
高密度颗粒可以是无机物颗粒。无机物颗粒208可包括钒酸铋、一种或多种金属氧化物颜料、或一种或多种导电颗粒(例如铜颗粒、青铜颗粒等)中的一者或多者。尽管无机物颗粒可包括金属、金属氧化物或其它导电颗粒,但无机物颗粒可通过纸和/或基于生物的树脂彼此隔开,使得不存在经由无机物颗粒从一个边缘或任意另一边缘穿过片材组件100和/或卡片102的任何导电路径。
片材组件100可从第一边缘104连续地延伸至相对的第二边缘106,并且可从第三边缘108(其与第一边缘104和第二边缘106相交)连续地延伸至相对的第四边缘110(其与第一边缘104和第二边缘106相交)。每个卡片102类似地可从第一边缘112连续地延伸至相对的第二边缘114,并且可从第三边缘116(其与第一边缘112和第二边缘114相交)连续地延伸至相对的第四边缘118(其与第一边缘112和第二边缘114相交)。在片材组件100和每个卡片102中没有导电的层、片材、芯层或本体可防止片材组件100将ESD或其它电流从一个片材边缘104、106、108、110传导至任意其它的片材边缘104、106、108、110并且可以防止每个卡片102将ESD或其它电流从一个卡片边缘112、114、116、118传导到任意其它卡片边缘112、114、116、118。
参照图3,根据一个实施例的卡片103可包括上透明覆盖层120、下透明覆盖层132、上印刷层122、下印刷层130、上部树脂浸渍可印刷纸层124、下部树脂浸渍可印刷纸层128、芯层126,如前面针对图2所描述的。卡片103也可包括在上部树脂浸渍可印刷纸层和上印刷层122之间的基于生物的上薄膜123。上薄膜123可以是非基于生物的薄膜。基于生物的上薄膜可以是基于生物的聚碳酸酯。卡片103也可包括在下部树脂浸渍可印刷纸层128与下印刷层131之间的基于生物的下薄膜130。基于生物的下薄膜可以是基于生物的聚碳酸酯。下薄膜130可以是非基于生物的薄膜。
基于生物的上薄膜和基于生物的下薄膜中的一者或多者可包括金属化、全息、衍射、折射、色移和/或安全特征。
参照图4,根据一个实施例的卡片102可包括上透明覆盖层220和下透明覆盖层232。上透明覆盖层和下透明覆盖层可由聚合物形成。在另一实施例中,上透明覆盖层和下透明覆盖层可由用树脂浸渍的纸形成。树脂可包括基于生物的树脂。树脂也可包括基于石油的树脂。例如,树脂可以是这样的树脂:其具有40%-70%的基于生物的树脂,其余树脂是基于石油的树脂。树脂可以是热固型树脂。树脂可以是热塑性树脂。纸可以是酚醛纸。纸可以用基于生物的树脂浸渍到大约50%。纸可以用小于约50%的包括基于石油的树脂的树脂来浸渍。可用于浸渍纸的其它树脂包括三聚氰胺、甲醛和酚醛树脂。
卡片可进一步包括上印刷层222和下印刷层230。上印刷层和下印刷层可由一种材料形成,该材料能够通过油墨印刷在上面以在卡片的上印刷层的可见表面(例如顶表面或前表面)和卡片的下印刷层的可见表面(例如底表面或后表面)上形成印记。印记可包括识别信息(例如人名、公司名、账号、照片、图像等)或其它信息。上印刷层和下印刷层可由PET形成。上印刷层和下印刷层可由基于生物的聚碳酸酯薄膜形成。上印刷层和下印刷层可由预先浸渍的印刷底层纸形成。上印刷层和下印刷层可以是不透明的、半透明的或透明的。
上印刷层和下印刷层可分别通过上粘合层221和下粘合层227附连至上透明覆盖层和下透明覆盖层。可选地,卡片可以不包括上粘合层和下粘合层,并且透明覆层可以通过在制造工艺期间向卡片层施加热和压力而附连至印刷层。
卡片可进一步包括芯层226。芯层可由树脂浸渍的纸形成。树脂可包括基于生物的树脂。树脂也可包括基于石油的树脂。例如,树脂可以是这样的树脂:其具有40%-70%的基于生物的树脂,其余部分的树脂是基于石油的树脂。通过将芯层提供为多个薄层或片材,芯层可以被形成为分裂的芯层。芯层的纸和/或浸渍的树脂可包括高密度颗粒229以增加卡片的重量,这对于较高端的或豪华交易卡来说可能是理想的,而不必在片材组件或卡片内引入金属层。这可防止片材组件和每个卡片形成、具有或包括导电层,该导电层将ESD或其它电流传导通过片材组件或卡片。可选地,卡片的其它层可具有设置在纸或树脂的一者或多者内的高密度颗粒。可选地,卡片没有任何一个层可具有高密度颗粒。
参照图5,根据一个实施例的卡片203可包括上透明覆盖层220和下透明覆盖层232。上透明覆盖层和下透明覆盖层可由聚合物形成。在另一实施例中,上透明覆盖层和下透明覆盖层可由用树脂浸渍的纸形成。树脂可包括基于生物的树脂。树脂也可包括基于石油的树脂。例如,树脂可以是这样的树脂:其具有40%-70%的基于生物的树脂,其余树脂是基于石油的树脂。树脂可以是热固型树脂。树脂可以是热塑性树脂。纸可以是酚醛纸。纸可以用基于生物的树脂浸渍到大约50%。纸可以用小于约50%的包括基于石油的树脂的树脂来浸渍。可用于浸渍纸的其它树脂包括三聚氰胺、甲醛和酚醛树脂。卡片可进一步包括上薄膜228,其可以是基于生物的薄膜。基于生物的上薄膜可通过粘合剂221附连至上透明覆盖层。基于生物的上薄膜可以是基于生物的聚碳酸酯。基于生物的上薄膜也可包括金属化、全息、衍射、折射、色移和/或安全特征。上薄膜可以是非基于生物的薄膜。
卡片可进一步包括下薄膜233,该下薄膜可以是基于生物的薄膜。基于生物的下薄膜可通过粘合层227附连至下透明覆盖层。基于生物的下薄膜可以是基于生物的聚碳酸酯。基于生物的下薄膜也可包括金属化、全息、衍射、折射、色移和/或安全特征。
卡片可进一步包括在上薄膜228或下薄膜233的一者或多者上形成印刷层的油墨。上印刷层和下印刷层可由一种材料形成,该材料能够通过油墨被印刷在其上以在卡片的上印刷层的可见表面(例如顶表面或前表面)和卡片的下印刷层的可见表面(例如底表面或后表面)上形成印记。该印记可包括识别信息(例如人名、公司名、账号、照片、图像等)或其它信息。
卡片可进一步包括芯层226。芯层可有树脂浸渍的纸形成。树脂可包括基于生物的树脂。树脂也可包括基于石油的树脂。例如,树脂可以是这样的树脂:其具有40%-70%的基于生物的树脂,其余部分的树脂是基于石油的树脂。通过将芯层提供为多个薄层或片材,芯层可以被形成为分裂的芯层。芯层的纸和/或浸渍的树脂可包括高密度颗粒229以增加卡片的重量,这对于较高端的或豪华交易卡来说可能是理想的,而不必在片材组件或卡片内引入金属层。这可防止片材组件和每个卡片形成、具有或包括导电层,该导电层将ESD或其它电流传导通过片材组件或卡片。可选地,卡片的其它层可具有设置在纸或树脂的一者或多者内的高密度颗粒。可选地,卡片没有任何一个层可具有高密度颗粒。上薄膜228可通过粘合层223附连至芯层226,而下薄膜233可通过粘合层225附连至芯层226。
参照图6,根据一个实施例的卡片302可包括上透明覆盖层320和下透明覆盖层332。上透明覆盖层和下透明覆盖层可由用树脂浸渍的纸形成。树脂可包括基于生物的树脂。树脂也可包括基于石油的树脂。例如,树脂可以是这样的树脂:其具有40%-70%的基于生物的树脂,其余树脂是基于石油的树脂。树脂可以是热固型树脂。树脂可以是热塑性树脂。纸可以是酚醛纸。纸可以用基于生物的树脂浸渍到大约50%。纸可以用小于约50%的包括基于石油的树脂的树脂来浸渍。可用于浸渍纸的其它树脂包括三聚氰胺、甲醛和酚醛树脂。
卡片可进一步包括上印刷层322和下印刷层330。上印刷层和下印刷层可由一种材料形成,该材料能够通过油墨印刷在上面以在卡片的上印刷层的可见表面(例如顶表面或前表面)和卡片的下印刷层的可见表面(例如底表面或后表面)上形成印记。印记可包括识别信息(例如人名、公司名、账号、照片、图像等)或其它信息。上印刷层和下印刷层可由PET形成。上印刷层和下印刷层可由基于生物的聚碳酸酯薄膜形成。上印刷层和下印刷层可由预先浸渍的印刷底层纸形成。
上印刷层和下印刷层可附连至上透明覆盖层和下透明覆盖层。在一个实施例中,上透明覆盖层和下透明覆盖层可通过在制造工艺期间向卡片层施加热和压力而附连至上印刷层和下印刷层。
卡片可进一步包括芯层326。芯层可包括上芯层325、中间芯层327、下芯层329。芯层可包括卡片的一个或多个光学特征。例如,一个或多个金属片材本体或类似物可被包含在和/或添加到上芯层、中间芯层和/或下芯层中的一者或多者以形成卡片的反射特征、衍射特征和/或全息特征。如前所述,芯层可由树脂浸渍的纸形成。一个或多个芯层的纸和/或浸渍的树脂可包括高密度颗粒以增加卡片的重量,这对于较高端的或豪华交易卡来说可能是理想的,而不必在片材组件或卡片内引入金属层。这可防止片材组件和每个卡片形成、具有或包括导电层,该导电层将ESD或其它电流传导通过片材组件或卡片。可选地,卡片的其它层可具有设置在纸或树脂的一者或多者内的高密度颗粒。可选地,卡片没有任何一个层可具有高密度颗粒。
芯层可包括一个或多个内嵌物331,例如电路或天线,它们在一个或多个芯层中、在两个芯层之间和/或在一个或多个芯层和印刷层之间。在所示实施例中,内嵌物被设置在中间芯层内。内嵌物可以射频识别(RFID)天线为代表,RFID天线可用于响应于通过RFID读取器对电磁信号的数据获取(interrogated)经由电磁波接收和/或发送电磁信号。例如,电路内嵌物可用于涉及卡片的无接触或无线交互。
如下文所描述的,在从片材组件切割卡片以结束卡片制造之前或之后,一个或多个附加的层、片材或器件可被包括在片材组件内和/或布置在片材上。卡片和片材组件的芯层可以提供重量加大的卡片(这对于较高端的或豪华交易卡来说可能是理想的),而不必在片材组件或卡片内引入金属层。这可防止片材组件和每个卡片形成、具有或包括导电层,该导电层将ESD或其它电流传导通过片材组件或卡片。
在从片材组件切割卡片之后,可将一种或多种油墨印刷、转移或以其他方式沉积到上印刷层和/或下印刷层上。这些油墨可形成文字、数字、图像等,用于识别卡片的持卡人、识别金融机构、识别账户等。可选地,油墨可形成图形等。尽管油墨在附图中被展示为在印刷层上延伸地连续层,但替代地,油墨可仅覆盖上印刷层和/或下印刷层的一部分,而不是全部。
可在油墨上印刷或沉积上透明覆盖层和/或下透明覆盖层,以保护油墨免于从上印刷层和/或下印刷层移除。例如,在上印刷层和/或下印刷层之上和上方可设置透明覆盖层。这种透明覆盖层可通过热和压力或通过透明覆盖层与印刷层之间的粘合剂提供在印刷层上和上方。
图7示出根据一个实施例的用于形成片材组件的方法500的流程图,该片材组件可被切割成较小卡片。该方法500可代表一些操作,这些操作被执行以形成被切割成卡片102、202、302的片材组件100。在502处,芯层由用树脂浸渍的纸形成。树脂可以是基于生物的树脂。基于生物的树脂可以是由可再生或生物资源构成的树脂。基于生物的树脂可包括非基于石油的树脂。可选地,纸和/或树脂可包括可以是无机物颗粒的高密度颗粒。无机物颗粒可包括钒酸铋、一种或多种金属氧化物颜料、或一种或多种导电颗粒(例如铜颗粒、青铜颗粒等)中的一者或多者。芯层也可设有内嵌物,例如RFID天线。芯层也可包括用树脂浸渍的一个或多个纸层。
在504处,上层联接至芯层。上层可以是用树脂浸渍的纸。树脂可以包括基于生物的树脂。树脂也可包括基于石油的树脂。上层可通过热和压力联接至芯层。上层和芯层中的树脂可对热和压力作出反应以将各个层自胶合在一起。上层可由PET、基于生物的聚碳酸酯或预先浸渍的印刷底层纸形成。上层可接受用于一个或多个卡片的第一印记的第一印刷,如前所述。例如,油墨可通过卡片制造商或生产商印刷在上片材上。上层也可设有卡片的反射特征、衍射特征、安全和/或不透明的特征。
在506处,下层联接至芯层以形成上层、芯层和下层的片材组件。下层可与芯层联接,其中芯层被设置在上层和下层之间。下层可由与上层相同的材料形成并类似于上层,下层可接受一个或多个卡的第二印记的第二印刷。下层也可设有卡片的反射特征、衍射特征、安全和/或不透明特征。
片材组件可设有上透明覆盖层和下透明覆盖层以形成卡片,所述卡片可从片材组件切割出。这些透明覆盖层可以是用树脂浸渍的聚合物或纸。树脂可以是基于石油的树脂或非生物降解的树脂。透明的上透明覆盖层和下透明覆盖层可通过热和压力或通过粘合剂联接至相应的上层和下层。
在一个实施例中,提供一种片材组件,该片材组件可被切割成一个或多个卡片。片材组件包括上层,该上层被配置成接受一个或多个卡片的第一印记的第一印刷。片材组件也可包括与上层和下层联接的芯层,该下层被配置成接受一个或多个卡片的第二印记的第二印刷。下层可与芯层联接,其中芯层设置在上片材和下片材之间。上层、芯层或下层中的一者或多者可由用树脂浸渍的纸形成,该树脂包括基于生物的树脂。
树脂可进一步包括基于石油的树脂。
树脂可以是具有40%-70%的基于生物的树脂。
一个或多个上层、芯层或下层的纸或树脂中的一者或多者可包括无机物颗粒。无机物颗粒可包括钒酸铋、一种或多种金属氧化物颜料、或一种或多种导电颗粒中的一者或多者。无机物颗粒可包括一种或多种导电颗粒,该导电颗粒包括铜颗粒或青铜颗粒中的一者或多者。
上层、芯层和下层可从片材组件的第一边缘连续地延伸至片材组件的相对的第二边缘,并且上层、芯层和下层可从片材组件的第三边缘连续地延伸至片材组件的相对的第四边缘,其中第三边缘和第四边缘中的每一个从第一边缘连续地延伸至第二边缘。片材组件可以不将电流从第一边缘、第二边缘、第三边缘或第四边缘中的任意一个传导至第一边缘、第二边缘、第三边缘或第四边缘中的任意一个。
芯层可包括射频识别天线。
芯层可由至少上芯层、中间芯层和下芯层形成,其中上芯层位于中间芯层和上层之间,而下芯层位于中间芯层和下层之间。
上芯层或下芯层中的一者或两者可包括反射特征、衍射特征或全息特征中的一者或多者。
片材组件可进一步包括设置在中间芯层上的内嵌物,该中间芯层位于上芯层和下芯层之间,内嵌物包括射频识别天线。
片材组件进一步包括基于生物的上薄膜和基于生物的下薄膜。基于生物的上薄膜和基于生物的下薄膜可以是基于生物的聚碳酸酯薄膜。基于生物的上薄膜和基于生物的下薄膜中的一者或多者可包括金属化、全息、衍射、折射、色移或安全特征中的一者或多者。
片材组件可以不传导电流。
卡片可有片材组件形成。卡片可以是金融交易卡、身份卡、门禁卡、密钥卡或安保卡中的一者或多者。
薄片可以由片材组件制成。薄片可形成台面、桌面、家具覆层或地板中的一者或多者。
在一个实施例中,一种用于生产片材组件的方法可包括:形成芯层并将上层联接至芯层,上层被配置成接受一个或多个卡片的第一印记的第一印刷。该方法可包括将下层联接至芯层以形成由上层、芯层和下层构成的片材组件。下层可联接至芯层,其中芯层设置在上层和下层之间。下层可被配置成接受一个或多个卡片的第二印记的第二印刷。片材组件可被配置成切割成一个或多个卡片。上层、芯层或下层中的一者或多者可由用树脂浸渍的纸形成,该树脂包括基于生物的树脂。
树脂可进一步包括基于石油的树脂。
树脂可以是具有40%-70%的基于生物的树脂。
一个或多个上层、芯层或下层的纸或树脂中的一者或多者可包括无机物颗粒。该无机物颗粒可包括钒酸铋、一种或多种金属氧化物颜料、或一种或多种导电颗粒中的一者或多者。无机物颗粒可包括一种或多种导电颗粒,该导电颗粒包括铜颗粒或青铜颗粒中的一者或多者。
上层、芯层和下层可从片材组件的第一边缘连续地延伸到片材组件的相对的第二边缘,并且上层、芯层和下层可从片材组件的第三边缘连续地延伸至片材组件的相对的第四边缘,其中第三边缘和第四边缘中的每个边缘从第一边缘连续地延伸至第二边缘。片材组件可以不将电流从第一边缘、第二边缘、第三边缘或第四边缘中的任何一者传导至第一边缘、第二边缘、第三边缘或第四边缘中的任何一者。
该方法可包括将射频识别天线布置在芯层中。
形成芯层可包括形成至少上芯层和下芯层,其中上芯层位于下芯层和上层之间,而底部芯层位于上芯层和下层之间。上芯层或下芯层中的一者或两者可包括反射特征、衍射特征或全息特征中的一者或多者。
形成芯层可包括形成上芯层、下芯层和设置在上芯层和下芯层之间的内嵌物。内嵌物可包括射频识别天线。
该方法可包括提供基于生物的上薄膜和基于生物的下薄膜。基于生物的上薄膜和基于生物的下薄膜可以是基于生物的聚碳酸酯薄膜。基于生物的上薄膜和基于生物的下薄膜中的一者或多者可包括金属化、全息、衍射、折射、色移或安全特征中的一者或多者。
片材组件可以不传导电流。
该方法可包括切割片材组件以形成卡片。卡片可以是金融交易卡、身份卡、门禁卡、密钥卡或安保卡中的一者或多者。
该方法可包括从片材组件形成薄片。薄片可以是柜面、台面、家具覆盖层和地板中的一者或多者。
在一个实施例中,提供一种可被切割成一个或多个卡片的片材组件。片材组件可包括上层和芯层,其中上层被配置成接受一个或多个卡片的第一印记的第一印刷,而芯层与上片材联接。片材组件可包括下层,该下层被配置成接受一个或多个卡片的第二印记的第二印刷。下层可与芯层联接,芯层被设置在上层和下层之间。片材组件可包括设置在上层之上的上透明覆盖层以及设置在下层之上的下透明覆盖层。上层、芯层或下层中的一者或多者可由用树脂浸渍的纸形成,该树脂包括基于生物的树脂,并且上透明覆盖层和下透明覆盖层由用树脂浸渍的聚合物或纸形成,该树脂包括基于生物的树脂。
树脂也可包括基于石油的树脂。
树脂可以是具有40%-70%的基于生物的树脂。
一个或多个上层、芯层或下层的纸或树脂中的一者或多者可包括无机物颗粒。无机物颗粒可包括钒酸铋、一种或多种金属氧化物颜料、或一种或多种导电颗粒中的一者或多者,该导电颗粒可包括铜颗粒或青铜颗粒中的一者或多者。
上层、芯层和下层可从片材组件的第一边缘连续地延伸至片材组件的相对的第二边缘,并且上层、芯层和下层可从片材的第三边缘连续地延伸至片材的相对的第四边缘,其中第三边缘和第四边缘中的每个边缘从第一边缘连续地延伸至第二边缘。片材组件可以不将电流从第一边缘、第二边缘、第三边缘或第四边缘中的任意一个传导至第一边缘、第二边缘、第三边缘或第四边缘中的任意一个。
芯层可包括射频识别天线。
芯层可由至少上芯层和下芯层形成,其中上芯层位于下芯层和上层之间,而下芯层位于上芯层和下层之间。上芯层或下芯层中的一者或两者可包括反射特征、衍射特征或全息特征中的一者或多者。
片材组件可包括设置在上芯层和下芯层之间的内嵌物。内嵌物可包括射频识别天线。
上层可包括基于生物的上薄膜并且下层可包括基于生物的下薄膜。基于生物的上薄膜和/或基于生物的下薄膜可以是基于生物的聚碳酸酯薄膜。
基于生物的上薄膜或基于生物的下薄膜中的一者或多者包括金属化、全息、衍射、折射、色移或安全特征中的一者或多者。
片材组件可以不传导电流。
该方法可包括切割片材组件以形成卡片。卡片可以是金融交易卡、身份卡、门禁卡、密钥卡或安保卡中的一者或多者。
该方法可包括从片材组件形成薄片。薄片可以是柜面、台面、家具覆盖层或地板中的一者或多者。
单数形式“一”、“一个”和“该”包括复数项,除非上下文清楚地规定相反情形。“可选的”或“可选地”表示接下来描述的事件或情况可以发生或可以不发生,并且表示说明书可包括事件发生的实例和事件不发生的实例。近似的表达,如本文中贯穿说明书和权利要求书中使用的,可用来修饰可允许变化而不会导致与其相关的基本功能改变的任何定量表达。因此,由一个或多个术语,比如“大约”、“基本上”和“近似”等修饰的值可以不局限于所指定的精确值。在至少一些实例中,近似的表达可对应于测量该值的仪器的精度。在这里并且贯穿说明书和权利要求书,范围限定可以被组合和/或互换,这样的范围可被确定并包括包含在其中的所有子范围,除非上下文或表达指示相反情形。
所写的说明书使用示例来公开实施例,包括最佳模式,并使得本领域内技术人员能够实践这些实施例,包括制造和使用任何装置或系统和执行任何所包含的方法。权利要求书限定本公开的可授予专利的范围,并且包括对本领域技术人员显而易见的其他示例。如果一些其他示例具有与权利要求书的文字表达没有区别的构成要素或者包括与权利要求书的文字表达具有非实质区别的等效结构要素,这些其他示例旨在落在权利要求书的范围内。
Claims (22)
1.一种被配置成切割成一个或多个卡片的片材组件,所述片材组件包括:
上层,所述上层被配置成接受一个或多个卡片的第一印记的第一印刷;
芯层,所述芯层与所述上层联接;以及
下层,所述下层被配置成接受一个或多个卡片的第二印记的第二印刷,所述下层与芯层联接,所述芯层设置在所述上层和所述下层之间,
其中所述上层、所述芯层或所述下层中的一者或多者由浸渍有树脂的纸形成,所述树脂包括基于生物的树脂。
2.如权利要求1所述的片材组件,其中所述树脂还包括基于石油的树脂。
3.如权利要求1或2所述的片材组件,其中所述树脂是具有40%-70%的基于生物的树脂。
4.如权利要求1-3中任一项所述的片材组件,其中所述上层、所述芯层或所述下层中的一个或多个层的纸或树脂中的一者或多者包括无机物颗粒,所述无机物颗粒包括钒酸铋、一种或多种金属氧化物颜料、或一种或多种导电颗粒中的一者或多者,所述导电颗粒包括铜颗粒或青铜颗粒中的一者或多者。
5.如权利要求1-4中任一项所述的片材组件,其中所述上层、所述芯层和所述下层从片材组件的第一边缘连续地延伸至所述片材组件的相对的第二边缘,并且所述上层、所述芯层和所述下层从所述片材组件的第三边缘连续地延伸至所述片材组件的相对的第四边缘,其中所述第三边缘和所述第四边缘中的每一个从所述第一边缘连续地延伸至所述第二边缘,
其中所述片材组件不将电流从所述第一边缘、所述第二边缘、所述第三边缘或所述第四边缘中的任意一个传导至所述第一边缘、所述第二边缘、所述第三边缘或所述第四边缘中的任意一个。
6.如权利要求1-5中任一项所述的片材组件,其中所述芯层形成自至少上芯层、中间芯层和下芯层,其中所述上芯层位于所述中间芯层和所述上层之间,而所述下芯层位于所述中间芯层和所述下层之间,并且所述上芯层或所述下芯层中的一者或两者包括反射特征、衍射特征或全息特征中的一者或多者。
7.如权利要求6所述的片材组件,还包括设置在所述上芯层与所述下芯层之间的中间芯层上的内嵌物,所述内嵌物包括射频识别天线。
8.如权利要求1-7中任一项所述的片材组件,还包括基于生物的上薄膜和基于生物的下薄膜,例如基于生物的聚碳酸酯薄膜,并且基于生物的上薄膜和基于生物的下薄膜中的一者或多者包括金属化、全息、衍射、折射、色移或安全特征中的一者或多者。
9.如权利要求1-8中任一项所述的片材组件,还包括:
设置在所述上层之上的上透明覆盖层;以及
设置在所述下层之上的下透明覆盖层,其中所述上透明覆盖层或所述下透明覆盖层中的一者或多者由用树脂浸渍的基于生物的聚合物或纸形成,所述树脂包括基于生物的树脂。
10.如权利要求1-9中任一项所述的片材组件,其中所述卡是金融交易卡、身份卡、门禁卡、密钥卡或安保卡中的一者或多者。
11.一种包括如权利要求1-9中任一项所述的片材组件的薄片,其中所述薄片形成柜面、台面、家具覆盖物或地板中的一者或多者。
12.一种方法,包括:
形成芯层;
将上层联接至所述芯层,所述上层被配置成接受一个或多个卡片的第一印记的第一印刷;以及
将下层联接至所述芯层以形成由所述上层、所述芯层和所述下层组成的片材组件,所述下层与所述芯层联接,其中所述芯层设置在所述上层和所述下层之间,所述下层被配置成接受所述一个或多个卡片的第二印记的第二印刷,
其中所述片材组件被配置成切割成一个或多个卡片,
其中所述上层、所述芯层或所述下层中的一者或多者由用树脂浸渍的纸形成,所述树脂包括基于生物的树脂。
13.如权利要求12所述的方法,其中所述树脂还包括基于石油的树脂。
14.如权利要求12或13所述的方法,其中所述树脂是40%-70%的基于生物的树脂。
15.如权利要求12-15中任一项所述的方法,其中所述上层、所述芯层或所述下层中的一个或多个层的所述纸或树脂中的一者或多者包括无机物颗粒,所述无机物颗粒包括钒酸铋、一种或多种金属氧化物颜料或一种或多种导电颗粒中的一者或多者,所述导电颗粒包括铜颗粒或青铜颗粒中的一者或多者。
16.如权利要求12-15中任一项所述的方法,其中所述上层、所述芯层和所述下层从所述片材组件的第一边缘连续地延伸至所述片材组件的相对的第二边缘,并且所述上层、所述芯层和所述下层从所述片材组件的第三边缘连续地延伸至所述片材组件的相对的第四边缘,其中所述第三边缘和所述第四边缘中的每一者从所述第一边缘连续地延伸至所述第二边缘,
其中所述片材组件不将电流从所述第一边缘、所述第二边缘、所述第三边缘或所述第四边缘中的任意一个传导至所述第一边缘、所述第二边缘、所述第三边缘或所述第四边缘中的任意一个。
17.如权利要求12-16中任一项所述的方法,其中形成芯层包括形成至少上芯层和下芯层,其中所述上芯层位于所述下芯层和所述上层之间,并且所述下芯层位于所述上芯层和所述下层之间,其中所述上芯层或所述下芯层中的一者或两者包括反射特征、衍射特征或全息特征中的一者或多者。
18.如权利要求17所述的方法,其中形成所述芯层包括形成上芯层、下芯层以及设置在所述上芯层和所述下芯层之间的内嵌物,所述内嵌物包括射频识别天线。
19.如权利要求18所述的方法,还包括在所述上层和所述芯层之间设置基于生物的上薄膜并在所述芯层和所述下层之间设置基于生物的下薄膜,其中所述基于生物的上薄膜和所述基于生物的下薄膜是基于生物的聚碳酸酯薄膜,并且所述基于生物的上薄膜和基于生物的下薄膜中的一者或多者包括金属化、全息、衍射、折射、色移或安全特征中的一者或多者。
20.如权利要求12-19中任一项所述的方法,还包括:
在所述上层之上提供上透明覆盖层;以及
在所述下层之上提供下透明覆盖层,其中所述上透明覆盖层或所述下透明覆盖层中的一者或多者由用树脂浸渍的基于生物的聚合物或纸形成,所述树脂包括基于生物的树脂。
21.如权利要求12-20中任一项所述的方法,还包括切割所述片材组件以形成卡片,其中所述卡片是金融交易卡、身份卡、门禁卡、密钥卡或安保卡中的一者或多者。
22.如权利要求12-20中任一项所述的方法,还包括从所述片材组件形成薄片,其中所述薄片包括柜面、台面、家具覆盖面或地板中的一者或多者。