CN116751481A - 一种双组分复合型甜味油墨及其制备方法 - Google Patents
一种双组分复合型甜味油墨及其制备方法 Download PDFInfo
- Publication number
- CN116751481A CN116751481A CN202310754829.XA CN202310754829A CN116751481A CN 116751481 A CN116751481 A CN 116751481A CN 202310754829 A CN202310754829 A CN 202310754829A CN 116751481 A CN116751481 A CN 116751481A
- Authority
- CN
- China
- Prior art keywords
- ink
- component
- parts
- sweetener
- sweet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及印刷油墨领域，尤其涉及一种双组分复合型甜味油墨及其制备方法。双组分复合型甜味油墨，以质量份计，包括组分A：丙烯酸乳液2～10份，溶剂50～100份，甜味剂3～15份；包括组分B：树脂基体5～20份，改性树脂2～5份，增塑剂0.5～2份，助剂0.1～5份，溶剂50～90份。本发明提供的甜味油墨，能够在保持良好的油墨印刷效果的基础上，明显地提高油墨本身的甜味的梯次感觉，并且能够有效保存甜味，使得油墨在长期的印刷保存期中能够最大程度保留其自身甜味，抑制甜味的衰减现象。
Description
技术领域
本发明涉及印刷油墨领域，尤其涉及一种双组分复合型甜味油墨及其制备方法。
背景技术
作为卷接香烟的重要辅助材料，水松纸因为直接与人的口腔接触，其功能性和安全性也备受消费者们的重视。因此，对于水松纸的安全性以及其功能性的研发，成为了企业愈发重视的课题。
而水松纸的功能性方面，其甜味的研发也是重要的研究方向，当水松纸有了甜味的加持后，抑制了吸烟时的苦、辣、涩等不良口感，提高了卷烟的口感和舒适性，使得消费者能够有良好的使用体验。但是，目前水松纸的甜味主要来自于印刷在水松纸上的甜味剂，这种方法会使得甜味无法在水松纸上长期的保留，随着抽吸时间或者储存时间的延长，会导致甜味逐渐的变淡或者消失。
现有技术，中国专利CN106280705A提供了一种可食用性印刷油墨，其以蜡基脂肪油墨作为油墨基体，加入了甜味剂等辅助助剂，声称制备了一种电导率高，粘度低的可食用油墨，但是其并未解决上述所述的油墨甜味的消散和流失问题。
因此，为了解决上述问题，本申请提供了一种双组分复合型甜味油墨及其制备方法，所制备出的油墨的甜度可调，并且具有长期的甜味保持效果。
发明内容
为了解决上述问题，本发明第一方面提供了一种双组分复合型甜味油墨，以质量份计，包括组分A：丙烯酸乳液2～10份，溶剂50～100份，甜味剂3～15份；包括组分B：树脂基体5～20份，改性树脂2～5份，增塑剂0.5～2份，助剂0.1～5份，溶剂50～90份。
作为一种优选的方案，所述组分A和组分B的质量比为1～10：1～10。
作为一种优选的方案，所述组分A和组分B的质量比为1～5：1～5。
作为一种优选的方案，所述组分A和组分B的质量比为1.5～2：2～4。
作为一种优选的方案，所述组分A和组分B的质量比为1.5：4。
作为一种优选的方案，所述丙烯酸乳液为苯乙烯/丙烯酸聚合物乳液。
作为一种优选的方案，所述丙烯酸乳液为2800型苯乙烯/丙烯酸聚合物乳液，购买自广州骏骅公司。
在本发明中，丙烯酸乳液的固含为25～35％，密度25℃为1.04，PH为7.5-8.5，粘度＜100CPS，玻璃转化温度17℃。
作为一种优选的方案，所述溶剂为脂溶性溶剂、去离子水中的至少一种。
作为一种优选的方案，所述组分A中的溶剂为乙醇和去离子水混合物。
作为一种优选的方案，所述组分A中乙醇和去离子水的质量比为1～2:6～7。
作为一种优选的方案，所述组分B中的溶剂为乙醇。
作为一种优选的方案，所述甜味剂为Taline糖、爱德万甜、阿斯巴甜、木糖醇、纽甜、糖精钠、葡糖剂、果糖、红糖、乳糖中的至少一种。
作为一种优选的方案，所述甜味剂为Taline糖，爱德万甜，纽甜和糖精钠的混合物。
作为一种优选的方案，所述Taline糖，爱德万甜，纽甜和糖精钠的质量比为5～8：1～2：1～2：3～5。
作为一种优选的方案，所述Taline糖，爱德万甜，纽甜和糖精钠的质量比为6：1：1.5：4。
作为一种优选的方案，所述树脂基体为聚乙烯醇缩丁醛。
作为一种优选的方案，所述树脂基体的平均分子量为1500～200000。
作为一种优选的方案，所述树脂基体的平均分子量为15000～25000。
在本发明中，通过采用特定分子量选择下的聚乙烯醇缩丁醛能够有效提高油墨的甜味保持性，避免甜味在长期储存过程中的失散现象，并且还进一步地提高了油墨体系的均一稳定性。本申请人认为：当采用特定分子量的聚乙烯醇缩丁醛作为组分B的树脂基体时，其除了能够有效配合本发明中选用的丙烯酸乳液形成交叉稳定的网络缠结体系从而提高油墨自身以及印刷稳定性，还能够在体系中形成良好的分子迁移阻力，从而不管是在储存还是使用的过程中都能有效抑制甜味剂分子源源不断的向外迁移分散现象，从而大幅抑制甜味的衰减。当聚乙烯醇缩丁醛的平均分子量小于15000时，过小的聚乙烯醇缩丁醛的粒子粒径减弱了油墨在水松纸上的附着力大小，从而会减弱油墨整体对于甜味剂的固定效果，而当平均分子量大于25000时，过大的分子量会抑制油墨本身的流动性，从而影响油墨的印刷效果，同样无法实现良好的油墨性能。
作为一种优选的方案，所述改性树脂为改性松香树脂；所述改性松香树脂为氢化松香、歧化松香、聚合松香中的至少一种。
作为一种优选的方案，所述改性松香树脂为非饱和氢化松香。
在本发明中，通过选用非饱和氢化松香能够进一步地提高油墨的各项性能，并且保留油墨甜味。本申请人认为：采用的非饱和氢化松香中的对应双键能够在油墨中起到良好的交联作用，并且起到部分的扩链效果，从而提高油墨分子间的紧密程度，进而抑制甜味剂分子在油墨体系中的分子迁移速率。
另一方面，本申请人发现，本申请中采用的特定分子量的聚乙烯醇缩丁醛虽然能够有效的提高甜味的保持度，但是相对应的对于水松纸的附着粘度以及附着持久力会有不同程度的下降，而松香树脂的加入能够有效地避免这一现象，从而在保证良好的甜味保持度的基础上，保留有优异的印刷性能。
作为一种优选的方案，所述增塑剂为乙酰柠檬酸三丁酯。
作为一种优选的方案，所述助剂为增稠剂、耐磨剂、抗划伤剂、防水剂、防腐剂、阻燃剂、抗氧剂中的至少一种。
作为一种优选的方案，所述助剂为耐磨剂和抗划伤剂。
作为一种优选的方案，所述耐磨剂为聚乙烯蜡。
作为一种优选的方案，所述抗划伤剂为聚二甲基硅氧烷。
本发明第二方面提供了一种上述双组分复合型甜味油墨的制备方法，步骤包括以下几步：(1)将组分A中的丙烯酸乳液和溶剂加入至配料罐中搅拌5～10min，之后加入甜味剂搅拌10～30min直至完全溶解，备用；(2)将组分B中的树脂基体，改性树脂以及溶剂加入至反应釜中，在500～800r/min下搅拌5～15min，升温至60～70℃后搅拌溶解100～200min；(3)待反应釜中温度下降至20～30℃后，将上述乳液加入至高速分散机，在1000～1500r/min转速下搅拌，并且依次加入剩余组分B原料，分散30～60min，备用；(4)将组分A和组分B按比例混合搅拌，即得。
有益效果：
1、本发明提供的一种甜味油墨，具有甜味可调配，甜感梯次好，甜味储存性高，不易衰减的优点，十分适合与水松纸的共同使用并应用于卷烟行业，能够有效避免现有行业中水松纸甜感差，甜味衰减快的问题。
2、本发明提供的一种甜味油墨，能够在保持良好的油墨印刷效果的基础上，明显地提高油墨本身的甜味的梯次感觉，并且能够有效保存甜味，使得油墨在长期的印刷保存期中能够最大程度保留其自身甜味，抑制甜味的衰减现象。
3、本发明提供的一种甜味油墨，通过采用特定分子量选择下的聚乙烯醇缩丁醛能够有效提高油墨的甜味保持性，避免甜味在长期储存过程中的失散现象，当聚乙烯醇缩丁醛的平均分子量为15000～25000时，能够在体系中形成良好的分子迁移阻力，从而不管是在储存还是使用的过程中都能有效抑制甜味剂分子源源不断的向外迁移分散现象，从而大幅抑制甜味的衰减。
4、本发明提供的一种甜味油墨，通过选用非饱和氢化松香能够进一步地提高油墨的各项性能，并且保留油墨甜味，其双键能够在油墨中起到良好的交联作用，并且起到部分的扩链效果，从而提高油墨分子间的紧密程度，进而抑制甜味剂分子在油墨体系中的分子迁移速率。
5、本发明提供的一种甜味油墨，采用聚乙烯醇缩丁醛和改性松香的复配，能够有效避免油墨对于水松纸的附着粘度以及附着持久力会有不同程度的下降的现象，从而在保持良好甜味的基础上，留有良好的油墨印刷性能。
具体实施方式
实施例1
实施例1第一方面提供了一种双组分复合型甜味油墨，包括组分A，以质量份计：丙烯酸乳液6份，溶剂75份，甜味剂12.5份；包括组分B，以质量份计：树脂基体15份，改性树脂3份，增塑剂1份，助剂0.7份，溶剂60份。
组分A和组分B的质量比为1.5：4。
丙烯酸乳液为2800型苯乙烯/丙烯酸聚合物乳液，购买自广州骏骅公司。
丙烯酸乳液的固含为30％，密度25℃为1.04，PH为8，粘度＜100CPS，玻璃转化温度17℃。
组分A中的溶剂为乙醇和去离子水混合物，质量比为10:6.5。
组分B中的溶剂为乙醇。
甜味剂为Taline糖，爱德万甜，纽甜和糖精钠的混合物，质量比为6：1：1.5：4。
树脂基体为聚乙烯醇缩丁醛，平均分子量为18000，购买自济宁三石生物科技有限公司出售的相应分子量工业级聚乙烯醇缩丁醛产品。
改性树脂为非饱和氢化松香树脂，购买自三井化学(山东)有限公司出售的氢化松香树脂产品。
增塑剂为乙酰柠檬酸三丁酯；助剂为耐磨剂和抗划伤剂，耐磨剂为德国DA806聚乙烯蜡(0.4份)，购买自翁开尔(上海)国际贸易有限公司；抗划伤剂为道康宁聚DC51二甲基硅氧烷(0.3分)，购买自南京利东化工有限公司。
本实施例第二方面提供了一种上述油墨的制备方法，步骤包括以下几步：(1)将组分A中的丙烯酸乳液和溶剂加入至配料罐中搅拌6min，之后加入甜味剂搅拌15min直至完全溶解，备用；(2)将组分B中的树脂基体，改性树脂以及溶剂加入至反应釜中，在600r/min下搅拌10min，升温至65℃后搅拌溶解120min；(3)待反应釜中温度下降至30℃后，将上述乳液加入至高速分散机，在1200r/min转速下搅拌，并且依次加入剩余组分B原料，分散40min，备用；(4)将组分A和组分B按比例混合搅拌，即得。
实施例2
本实施例的具体实施方式同实施例1，不同之处在于：组分A和组分B的质量比为2：3。
对比例1
本对比例的具体实施方式同实施例1，不同之处在于：聚乙烯醇缩丁醛的平均分子量为8000，购买自济宁三石生物科技有限公司出售的相应分子量工业级聚乙烯醇缩丁醛产品。
对比例2
本对比例的具体实施方式同实施例1，不同之处在于：改性松香树脂为歧化松香，购买自江苏润丰合成科技有限公司出售的工业级歧化松香树脂。
对比例3
本对比例的具体实施方式同实施例1，不同之处在于：丙烯酸乳液MT-2600广州骏骅，固含量45％，密度(25℃)1.04，PH8.3，粘度4000CPS，玻璃转化温度(Tg)70℃。
性能评价
甜感：前甜，中甜和后甜的梯次搭配测试，由10人组成的甜味评价小组，对印刷后的样品进行感官测试，通过综合评价得出结果，测得的结果记入表1。
油墨储存性：对实施例和对比例制得的油墨进行储存性测试，在恒温保湿箱中测试保存，保存温度为40℃，储存6个月，之后取出进行油墨的剩余质量测试，计算质量的下降百分比，测得的结果取10次平均值记入表1。
表1
Claims (10)
1.一种双组分复合型甜味油墨，其特征在于：以质量份计，包括组分A：丙烯酸乳液2～10份，溶剂50～100份，甜味剂3～15份；包括组分B：树脂基体5～20份，改性树脂2～5份，增塑剂0.5～2份，助剂0.1～5份，溶剂50～90份。
2.根据权利要求1所述的双组分复合型甜味油墨，其特征在于：所述组分A和组分B的质量比为1～10：1～10。
3.根据权利要求1～2任一项所述的双组分复合型甜味油墨，其特征在于：所述丙烯酸乳液为苯乙烯/丙烯酸聚合物乳液。
4.根据权利要求1～3任一项所述的双组分复合型甜味油墨，其特征在于：所述溶剂为脂溶性溶剂、去离子水中的至少一种。
5.根据权利要求1～4任一项所述的双组分复合型甜味油墨，其特征在于：所述甜味剂为Taline糖、爱德万甜、阿斯巴甜、木糖醇、纽甜、糖精钠、葡糖剂、果糖、红糖、乳糖中的至少一种。
6.根据权利要求1～5任一项所述的双组分复合型甜味油墨，其特征在于：所述树脂基体为聚乙烯醇缩丁醛。
7.根据权利要求1～6任一项所述的双组分复合型甜味油墨，其特征在于：所述树脂基体的平均分子量为1500～200000。
8.根据权利要求1～7任一项所述的双组分复合型甜味油墨，其特征在于：所述改性树脂为改性松香树脂；所述改性松香树脂为氢化松香、歧化松香、聚合松香中的至少一种。
9.根据权利要求1～8任一项所述的双组分复合型甜味油墨，其特征在于：所述助剂为增稠剂、耐磨剂、抗划伤剂、防水剂、防腐剂、阻燃剂、抗氧剂中的至少一种。
10.一种根据权利要求1～9任一项所述的双组分复合型甜味油墨的制备方法，其特征在于：步骤包括以下几步：(1)将组分A中的丙烯酸乳液和溶剂加入至配料罐中搅拌5～10min，之后加入甜味剂搅拌10～30min直至完全溶解，备用；(2)将组分B中的树脂基体，改性树脂以及溶剂加入至反应釜中，在500～800r/min下搅拌5～15min，升温至60～70℃后搅拌溶解100～200min；(3)待反应釜中温度下降至20～30℃后，将上述乳液加入至高速分散机，在1000～1500r/min转速下搅拌，并且依次加入剩余组分B原料，分散30～60min，备用；(4)将组分A和组分B按比例混合搅拌，即得。