CN116544350A - 二次电池和电子装置 - Google Patents
二次电池和电子装置 Download PDFInfo
- Publication number
- CN116544350A CN116544350A CN202310637473.1A CN202310637473A CN116544350A CN 116544350 A CN116544350 A CN 116544350A CN 202310637473 A CN202310637473 A CN 202310637473A CN 116544350 A CN116544350 A CN 116544350A
- Authority
- CN
- China
- Prior art keywords
- active material
- negative electrode
- electrode active
- material layer
- secondary battery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请提供了一种二次电池和电子装置。本申请的二次电池包括负极,负极包括集流体和设置于集流体表面的负极活性材料层,负极活性材料层包括第一负极活性材料层和第二负极活性材料层,第一负极活性材料层设置于集流体和第二负极活性材料层之间,第一负极活性材料层包括第一负极活性材料,第一负极活性材料的最大反弹率为Ra,第二负极活性材料层包括第二负极活性材料,第二负极活性材料的最大反弹率为Rb,其中,5%≤Ra≤13%,10%≤Rb≤17%,Ra<Rb。本申请的二次电池兼具高的能量密度和优异的快充能力。
Description
技术领域
本申请涉及储能领域。具体地,本申请涉及一种二次电池和电子装置。
背景技术
随着二次电池市场不断扩大,对其性能要求也在不断提升,其中能量密度和快充性能就是较为重要的指标。现有二次电池中常规极片设计通常为单层,所用活性材料难以兼具高能量密度和和快充能力,往往需要通过降低涂布重量来提高二次电池的快充能力,或增加涂布重量来提高锂二次电池的能量密度。但是在降低涂布重量来提高二次电池快充能力的同时,由于活性材料较少导致能量密度损失严重;同理,在增加涂布重量来提高二次电池能量密度的同时,由于极片厚度较大,活性离子传输路径过长,会导致其快充能力较差。
发明内容
鉴于现有技术存在的上述问题,本申请提供一种二次电池。本申请的二次电池通过采用特定的多层极片设计,在显著提升二次电池快充性能的同时,又尽可能减少了对二次电池体积能量密度的影响,使得二次电池兼具高的能量密度和优异的快充能力。
本申请的第一方面提供了一种二次电池,其包括负极,该负极包括集流体和设置于集流体表面的负极活性材料层,负极活性材料层包括第一负极活性材料层和第二负极活性材料层,料第一负极活性材料层设置于集流体和第二负极活性材料层之间,第一负极活性材料层第一负极活性材料第一负极活性材料,第一负极活性材料的最大反弹率为Ra,第二负极活性材料层包括第二负极活性材料,第二负极活性材料的最大反弹率为Rb,其中,5%≤Ra≤13%,10%≤Rb≤17%,Ra<Rb。对于负极活性材料例如石墨材料而言,最大反弹率可以反映其被制成极片后的耐压性能。最大反弹率较低时,对应极片冷压后的反弹较小,有利于极片保持高的压实密度,意味着颗粒之间的堆积比较密实,会使得极片的孔隙减少,不利于电解液的渗透和活性离子的扩散,进而影响二次电池的快充能力。最大反弹率较高时,极片具有丰富的孔隙结构,有利于电解液的渗透和活性离子的扩散,但压实密度较低,会损失二次电池的体积能量密度。本申请的二次电池采用多层活性材料层设计,在上层(第二负极活性材料层)选用最大反弹率较高的第二负极活性材料,下层(第一负极活性材料层)选用最大反弹率较低的第一负极活性材料,并同时控制上下层活性材料的最大反弹率在上述范内,使得极片既有较高的压实密度,又能保持较高的表层孔隙率,从而使二次电池兼顾高能量密度和优异的快充能力。
在一些实施方式中,5%≤Ra≤10%,10%≤Rb≤14%。在一些实施方式中,8%≤Ra≤10%,12%≤Rb≤14%。第一负极活性材料的最大反弹率过低时,堆积越过于密实,会使得极片的孔隙减少,不利于电解液的渗透和活性离子的扩散,进而影响二次电池的快充能力。第二负极活性材料的最大反弹率过高时,虽然有利于快充能力的提升,但会使得压实密度较过低,损失二次电池的体积能量密度。
在一些实施方式中,5%≤Ra≤10%。在一些实施方式中,8%≤Ra≤10%。
在一些实施方式中,10%≤Rb≤14%。在一些实施方式中,12%≤Rb≤14%。
在一些实施方式中,0<Rb-Ra≤10%。Rb-Ra的差值在上述范围内时,能够在保证体积能量密度的基础上,进一步提升二次电池的快充性能。在一些实施方式中,2%≤Rb-Ra≤6%。
在一些实施方式中,第一负极活性材料达到最大反弹率时的粉末压实密度为PDa其中,1.95g/cm3≤PDa≤2.20g/cm3。在一些实施方式中,2.00g/cm3≤PDa≤2.20g/cm3。第一负极活性材料的PDa在上述范围内时,第一负极活性材料满足较高的极片压实密度设计并能够保持颗粒结构完整。
在一些实施方式中,第二负极活性材料达到最大反弹率时的粉末压实密度为PDb,其中,1.75g/cm3≤PDb≤2.00g/cm3。在一些实施方式中,1.80g/cm3≤PDb≤2.00g/cm3。第二负极活性材料的PDb在上述范围内时,第二负极活性材料在保持一定压实密度的基础上具有较高的反弹率。
在一些实施方式中,第一负极活性材料选自人造石墨,第二负极活性材料选自人造石墨。
在一些实施方式中,基于负极活性材料层的质量,第一负极活性材料层的质量含量为60%至80%。在一些实施方式中,基于负极活性材料层的质量,第二负极活性材料层的质量含量为20%至40%。第一负极活性材料层和第二负极活性材料层的含量在上述范围内时,二次电池兼顾高能量密度和优异的电化学性能。当第二负极活性材料层的质量含量大于40%,第一负极活性材料层的质量含量小于60%时,二次电池的能量密度损失较多。当第二负极活性材料层的质量含量小于20%,第一负极活性材料层的质量含量大于80%时,二次电池的快充能力显著降低。
在一些实施方式中,以N-甲基吡咯烷酮为测试油进行测试,第一负极活性材料的吸油值小于或等于65mL/100g,第二负极活性材料的吸油值小于或等于65mL/100g。活性材料的吸油值反应了颗粒的亲油性质,吸油值过高,则活性材料颗粒在浆料分散时需要更多的分散剂才能均匀分散,使得浆料中活性物材料的占比降低,进而影响二次电池的能量密度和动力学性能。
在一些实施方式中,负极活性材料层与集流体之间的粘结力大于或等于8N/m。粘结力过低,极片在加工和循环过程中易发生掉粉和脱膜,因此限定粘结力大于等于8N/m,以保证极片具有较稳定的结构。
在一些实施方式中,负极的压实密度为1.70g/cm3至1.85g/cm3。负极的压实密度过大时,易导致极片过压,恶影响极片加工和电性能,负极的压实密度过小时,无法有效改善二次电池的能量密度。
在一些实施方式中,负极在50%SOC时的极片反弹率为T,其中,15%≤T≤20%。
本申请的第二方面提供了一种电子装置,其包括第一方面的二次电池。
本申请的二次电池通过采用多层极片设计,靠近集流体的下层选用最大反弹率较低的负极活性材料,使极片拥有较高的压实密度;上层选用最大反弹率较高的负极活性材料,使极片表层具有较多的孔隙,便于电解液的浸润和渗透,以及促进锂离子的扩散,使得极片既有较高的压实密度,又能保持较高的表层孔隙率,从而使二次电池兼顾高能量密度和优异的快充能力。
本申请的第三方面提供了一种负极的制备方法,负极制备方法包括:第一活性材料的制备和第二活性材料的制备;第一活性材料由天然石墨和/或人造石墨经过包覆后,再进行两次不同的热处理制得,第二活性材料由人造石墨经过包覆后,再进行一次热处理制得。
具体地,第一活性材料制备:将人造石墨和/或天然石墨与包覆剂进行混合,得到第一混合物,基于第一混合物的质量,包覆剂的质量含量为1%至5%;在惰性气氛中,将第一混合物进行第一热处理,得到第一热处理产物;在CO2和N2的混合气中,将第一热处理产物进行第二热处理,得到第一活性材料。
第二活性材料的制备:将人造石墨与包覆剂进行混合,得到第二混合物,基于第二混合物的质量,包覆剂的质量含量为1%至5%;在惰性气氛中,将第二混合物进行第三热处理,得到第二活性材料。
第一热处理的温度为950℃至1200℃,第一热处理的时间为1h至5h;第二热处理的温度为500℃至900℃,第二热处理的时间为5h至15h;第三热处理的温度为700℃至1100℃,第三热处理的时间为4h至10h;包覆剂为沥青。
将上述第一活性材料和第二活性材料分别用做负极的第一活性材料层和第二活性材料层,且第二活性材料层在第一活性材料层的上表面(即负极厚度方向上远离集流体的方向的表面),能使得二次电池兼顾较高的能量密度和快充能力。
附图说明
图1示出了本申请实施例10的第一负极活性材料和第二负极活性材料的反弹率曲线,其中,1为第一负极活性材料,2为第二负极活性材料。
具体实施方式
在本申请的描述中,除非另有说明,“以上”、“以下”包含本数。
除非另有说明,本申请中使用的术语具有本领域技术人员通常所理解的公知含义。除非另有说明,本申请中提到的各参数的数值可以用本领域常用的各种测量方法进行测量(例如,可以按照在本申请的实施例中给出的方法进行测试)。
术语“中的至少一者”、“中的至少一个”、“中的至少一种”或其他相似术语所连接的项目的列表可意味着所列项目的任何组合。例如,如果列出项目A及B,那么短语“A及B中的至少一者”意味着仅A;仅B;或A及B。在另一实例中,如果列出项目A、B及C,那么短语“A、B及C中的至少一者”意味着仅A;或仅B;仅C;A及B(排除C);A及C(排除B);B及C(排除A);或A、B及C的全部。项目A可包含单个组分或多个组分。项目B可包含单个组分或多个组分。项目C可包含单个组分或多个组分。
下面将结合本申请实施方式中的附图,对本申请实施方式中的技术方案进行清楚、完整地描述,显然,所描述的实施方式仅仅是本申请一部分实施方式,而不是全部的实施方式。在不冲突的情况下,下述的实施方式及实施方式中的特征可以相互组合。
一、二次电池
本申请提供的二次电池包括负极,该负极包括集流体和设置于集流体表面的负极活性材料层,负极活性材料层包括第一负极活性材料第一负极活性材料层和第二负极活性材料层,第一负极活性材料层设置于集流体和第二负极活性材料层之间,第一负极活性材料层包括第一负极活性材料,第一负极活性材料的最大反弹率为Ra,第二负极活性材料层包括第二负极活性材料,第二负极活性材料的最大反弹率为Rb,其中,5%≤Ra≤13%,10%≤Rb≤17%,Ra<Rb。对于负极活性材料例如石墨材料而言,最大反弹率可以反应其被制成极片后的耐压性能。最大反弹率较低时,对应极片冷压后的反弹较小,有利于极片保持高的压实密度,意味着颗粒之间的堆积比较密实,会使得极片的孔隙减少,不利于电解液的渗透和活性离子的扩散,进而影响二次电池的快充能力。最大反弹率较高时,极片具有丰富的孔隙结构,有利于电解液的渗透和活性离子的扩散,但压实密度较低,会损失二次电池的体积能量密度。本申请的二次电池采用多层活性材料层设计,在上层(第二负极活性材料层)选用最大反弹率较高的第二负极活性材料,下层(第一负极活性材料层)选用最大反弹率较低的第一负极活性材料,并同时控制上下层活性材料的最大反弹率在上述范内,使得极片既有较高的压实密度,又能保持较高的表层孔隙率,从而使二次电池兼顾高能量密度和优异的快充能力。
本申请中,活性材料的最大反弹率代表活性材料在不同压力条件下,经历加压-卸压后材料反弹的最大程度。具体测试方式请参考下文具体实施例中的测试方法。
在一些实施方式中,Ra为5%、5.5%、6%、6.5%、7%、7.5%、8%、8.5%、9%、9.5%、10%、10.5%、11%、11.5%、12%、12.5%、13%或这种值中任意两者组成的范围。第一负极活性材料的最大反弹率过低时,堆积越过于密实,会使得极片的孔隙减少,不利于电解液的渗透和活性离子的扩散,进而影响二次电池的快充能力。在一些实施方式中,5%≤Ra≤10%。在一些实施方式中,8%≤Ra≤10%,
在一些实施方式中,Rb为10%、10.5%、11%、11.5%、12%、12.5%、13%、13.5%、14%、14.5%、15%、15.5%、16%、16.5%、17%或这种值中任意两者组成的范围。第二负极活性材料的最大反弹率过高时,虽然有利于快充能力的提升,但会使得压实密度较过低,损失二次电池的体积能量密度。在一些实施方式中,10%≤Rb≤14%。在一些实施方式中,12%≤Rb≤14%。
在一些实施方式中,5%≤Ra≤10%,10%≤Rb≤14%。在一些实施方式中,8%≤Ra≤10%,12%≤Rb≤14%。
在一些实施方式中,0<Rb-Ra≤10%。在一些实施方式中,Rb-Ra为0.5%、1%、1.5%、2%、2.5%、3%、3.5%、4%、4.5%、5%、5.5%、6%、6.5%、7%、7.5%、8%、8.5%、9%、9.5%、10%或这些值中任意两者组成的范围。Rb-Ra的差值在上述范围内时,能够在保证体积能量密度的基础上,进一步提升二次电池的快充性能。在一些实施方式中,2%≤Rb-Ra≤6%。
在一些实施方式中,第一负极活性材料达到最大反弹率时的粉末压实密度为PDa,其中,1.95g/cm3≤PDa≤2.20g/cm3。在一些实施方式中,PDa为1.95g/cm3、1.96g/cm3、1.98g/cm3、2.00g/cm3、2.01g/cm3、2.02g/cm3、2.03g/cm3、2.04g/cm3、2.05g/cm3、2.06g/cm3、2.07g/cm3、2.08g/cm3、2.09g/cm3、2.10g/cm3、2.11g/cm3、2.12g/cm3、2.13g/cm3、2.14g/cm3、2.15g/cm3、2.16g/cm3、2.17g/cm3、2.18g/cm3、2.19g/cm3、2.20g/cm3或这些值中任意两者组成的范围。第一负极活性材料的PDa在上述范围内时,第一负极活性材料满足较高的极片压实密度设计并能够保持颗粒结构完整。在一些实施方式中,2.00g/cm3≤PDa≤2.20g/cm3。
在一些实施方式中,第二负极活性材料达到最大反弹率时的粉末压实密度为PDb,其中,1.75g/cm3≤PDb≤2.00g/cm3。在一些实施方式中,PDb为1.75g/cm3、1.77g/cm3、1.79g/cm3、1.80g/cm3、1.81g/cm3、1.82g/cm3、1.83g/cm3、1.84g/cm3、1.85g/cm3、1.86g/cm3、1.87g/cm3、1.88g/cm3、1.89g/cm3、1.90g/cm3、1.91g/cm3、1.92g/cm3、1.93g/cm3、1.94g/cm3、1.95g/cm3、1.96g/cm3、1.97g/cm3、1.98g/cm3、1.99g/cm3、2.00g/cm3或这些值中任意两者组成的范围。第二负极活性材料的PDb在上述范围内时,第二负极活性材料在保持一定压实密度的基础上具有较高的反弹率。在一些实施方式中,1.80g/cm3≤PDb≤2.00g/cm3。
本申请中,活性材料达到最大反弹率时的粉末压实密度为材料的极限压实密度,再进一步施加压力时,活性材料颗粒结构遭到破坏,颗粒从弹性形变转变为非弹性形变,反弹率下降。具体测试方式请参考下文具体实施例中的测试方法。
在一些实施方式中,第一负极活性材料选自人造石墨和/或天然石墨。在一些实施方式中,第二负极活性材料选自人造石墨。
在一些实施方式中,第一负极活性材料选自人造石墨。在一些实施方式中,第二负极活性材料选自人造石墨。
在一些实施方式中,第一负极活性材料的制备方法包括以下步骤:
S1:将人造石墨和/或天然石墨与包覆剂进行混合,得到第一混合物;
S2:在惰性气氛中,将第一混合物进行第一热处理,得到第一热处理产物;
S3:在CO2和N2混合气中,将第一热处理产物进行第二热处理,得到所述第一负极活性材料。
在一些实施方式中,S1中,基于第一混合物的质量,包覆剂的质量含量为1%至5%,例如为2%、3%或4%。在一些实施方式中,包覆剂为沥青。
在一些实施方式中,S2中,第一热处理的温度为950℃至1200℃,例如为1000℃、1050℃、1100℃或1150℃。在一些实施方式中,S2中,第一热处理的时间为1h至5h,例如为2h、3h或4h。
在一些实施方式中,S3中,第二热处理的温度为500℃至900℃,例如为550℃、600℃、650℃、700℃、750℃、800℃或850℃。在一些实施方式中,S3中,第二热处理的时间为5h至15h,例如为6h、7h、8h、9h、10h、11h、12h、13h或14h。
在一些实施方式中,CO2和N2混合气中,CO2的体积百分含量为3%至7%,例如为4%、5%或6%。
在一些实施方式中,第二负极活性材料的的制备方法包括以下步骤:
M1:将人造石墨与包覆剂进行混合,得到第二混合物;
M2:在惰性气氛中,将第二混合物进行第三热处理,得到所述第二负极活性材料。
在一些实施方式中,M1中,基于第二混合物的质量,包覆剂的质量含量为1%至5%,例如为2%、3%或4%。在一些实施方式中,包覆剂为沥青。
在一些实施方式中,M2中,第三热处理的温度为700℃至1100℃,例如为750℃、800℃、850℃、900℃、950℃、1000℃或1050℃。在一些实施方式中,M2中,第二热处理的时间为4h至10h,例如为5h、6h、7h、8h或9h。
在一些实施方式中,人造石墨由针状焦、石油焦、沥青焦等碳质原料经高温石墨化得到。在一些实施方式中,天然石墨由天然鳞片石墨经酸洗球化得到。在一些实施方式中,基于负极活性材料层的质量,第一负极活性材料层的质量含量为60%至90%,例如为60%、65%、70%、75%、80%、85%或90%。在一些实施方式中,基于负极活性材料层的质量,第二负极活性材料层的质量含量为10%至40%,例如为10%、15%、20%、25%、30%或35%、40%。第一负极活性材料层和第二负极活性材料层的含量在上述范围内时,二次电池兼顾高能量密度和优异的电化学性能。当第二负极活性材料层的质量含量大于40%,第一负极活性材料层的质量含量小于60%时,二次电池的能量密度损失较多。当第二负极活性材料层的质量含量小于10%,第一负极活性材料层的质量含量大于90%时,二次电池的快充能力显著降低。
在一些实施方式中,以N-甲基吡咯烷酮为测试油进行测试,第一负极活性材料的吸油值小于或等于65mL/100g,第二负极活性材料的吸油值小于或等于65mL/100g。活性材料的吸油值反应了颗粒的亲油性质,吸油值过高,则活性材料颗粒在浆料分散时需要更多的分散剂才能均匀分散,使得浆料中活性物材料的占比降低,进而影响二次电池的能量密度和动力学性能。
在一些实施方式中,负极活性材料层与集流体之间的粘结力大于或等于8N/m。粘结力过低,极片在加工和循环过程中易发生掉粉和脱膜,因此限定粘结力大于等于8N/m,以保证极片具有较稳定的结构。
在一些实施方式中,负极的压实密度为1.70g/cm3至1.85g/cm3。在一些实施方式中,负极的压实密度为1.70g/cm3、1.73g/cm3、1.75g/cm3、1.77g/cm3、1.80g/cm3、1.83g/cm3、1.85g/cm3或这些值中任意两者组成的范围。负极的压实密度过大时,易导致极片过压,恶影响极片加工和电性能,负极的压实密度过小时,无法有效改善二次电池的能量密度。
在一些实施方式中,所述负极的极片反弹率为T,其中,15%≤T≤20%,例如为16%、17%、18%或19%。
在一些实施方式中,负极活性材料层还包括粘结剂和导电剂。在一些实施方式中,粘结剂包括丁苯橡胶、聚丙烯酸、聚丙烯酸盐、聚酰亚胺、聚酰胺酰亚胺、聚偏氟乙烯、聚二氟乙烯、聚四氟乙烯、水性丙烯酸树脂、聚乙烯醇缩甲醛或苯乙烯-丙烯酸共聚树脂中的至少一种。在一些实施方式中,可以使用任何导电的材料作为该导电材料,只要它不引起化学变化即可。在一些实施方式中,导电材料包括导电炭黑、乙炔黑、碳纳米管、科琴黑、导电石墨或石墨烯中的至少一种。
在一些实施例中,负极集流体可以为铜箔、镍箔、不锈钢箔、钛箔、泡沫镍、泡沫铜、包覆有导电金属的聚合物基板或它们的组合。
在一些实施方式中,二次电池还包括正极,正极包括正极集流体和正极活性材料层。
在一些实施方式中,正极活性材料层包括正极活性材料、粘结剂和导电剂。在一些实施方式中,正极活性材料可以包括钴酸锂、镍锰钴酸锂、镍锰铝酸锂、磷酸铁锂、磷酸钒锂、磷酸钴锂、磷酸锰锂、磷酸锰铁锂、硅酸铁锂、硅酸钒锂、硅酸钴锂、硅酸锰锂、尖晶石型锰酸锂、尖晶石型镍锰酸锂和钛酸锂中的至少一种。在一些实施方式中,粘结剂可以包括各种粘合剂聚合物,例如聚偏氟乙烯、聚四氟乙烯、聚烯烃类、羧甲基纤维素钠、羧甲基纤维素锂、改性聚偏氟乙烯、改性SBR橡胶或聚氨酯中的至少一种。在一些实施例中,可以使用任何导电的材料作为导电剂,只要它不引起化学变化即可。导电剂的示例包括:碳基材料,例如天然石墨、人造石墨、炭黑、乙炔黑、科琴黑、碳纤维等;金属基材料,例如包括铜、镍、铝、银等的金属粉或金属纤维;导电聚合物,例如聚亚苯基衍生物等;或它们的混合物。
在一些实施方式中,正极极集流体可以采用金属箔片或复合集流体。例如,可以使用铝箔。复合集流体可以通过将金属材料(铜、铜合金、镍、镍合金、钛、钛合金、银及银合金等)形成在高分子基材上而形成。
本申请的二次电池还包括隔离膜,本申请的二次电池中使用的隔离膜的材料和形状没有特别限制,其可为任何现有技术中公开的技术。在一些实施例中,隔离膜包括由对本申请的电解液稳定的材料形成的聚合物或无机物等。
例如隔离膜可包括基材层和表面处理层。基材层为具有多孔结构的无纺布、膜或复合膜,基材层的材料选自聚乙烯、聚丙烯、聚对苯二甲酸乙二醇酯和聚酰亚胺中的至少一种。具体的,可选用聚丙烯多孔膜、聚乙烯多孔膜、聚丙烯无纺布、聚乙烯无纺布或聚丙烯-聚乙烯-聚丙烯多孔复合膜。
基材层的至少一个表面上设置有表面处理层,表面处理层可以是聚合物层或无机物层,也可以是混合聚合物与无机物所形成的层。无机物层包括无机颗粒和粘结剂,无机颗粒选自氧化铝、氧化硅、氧化镁、氧化钛、二氧化铪、氧化锡、二氧化铈、氧化镍、氧化锌、氧化钙、氧化锆、氧化钇、碳化硅、勃姆石、氢氧化铝、氢氧化镁、氢氧化钙和硫酸钡中的至少一种。粘结剂选自聚偏氟乙烯、偏氟乙烯-六氟丙烯的共聚物、聚酰胺、聚丙烯腈、聚丙烯酸酯、聚丙烯酸、聚丙烯酸盐、聚乙烯呲咯烷酮、聚乙烯烷氧、聚甲基丙烯酸甲酯、聚四氟乙烯和聚六氟丙烯中的至少一种。聚合物层中包含聚合物,聚合物的材料选自聚酰胺、聚丙烯腈、丙烯酸酯聚合物、聚丙烯酸、聚丙烯酸盐、聚乙烯呲咯烷酮、聚乙烯烷氧、聚偏氟乙烯、聚(偏氟乙烯-六氟丙烯)中的至少一种。
本申请的二次电池还包括电解液。可用于本申请的电解液可以为现有技术中已知的电解液。
根据本申请的一些实施方式,电解液包括有机溶剂、锂盐和可选的添加剂。本申请的电解液中的有机溶剂可为现有技术中已知的任何可作为电解液的溶剂的有机溶剂。根据本申请的电解液中使用的电解质没有限制,其可为现有技术中已知的任何电解质。根据本申请的电解液的添加剂可为现有技术中已知的任何可作为电解液添加剂的添加剂。在一些实施例中,有机溶剂包括,但不限于:碳酸乙烯酯(EC)、碳酸丙烯酯(PC)、碳酸二乙酯(DEC)、碳酸甲乙酯(EMC)、碳酸二甲酯(DMC)、碳酸亚丙酯或丙酸乙酯。在一些实施例中,有机溶剂包括醚类溶剂,例如包括1,3-二氧五环(DOL)和乙二醇二甲醚(DME)中的至少一种。在一些实施例中,锂盐包括有机锂盐或无机锂盐中的至少一种。在一些实施例中,锂盐包括,但不限于:六氟磷酸锂(LiPF6)、四氟硼酸锂(LiBF4)、二氟磷酸锂(LiPO2F2)、双三氟甲烷磺酰亚胺锂LiN(CF3SO2)2(LiTFSI)、双(氟磺酰)亚胺锂Li(N(SO2F)2)(LiFSI)、双草酸硼酸锂LiB(C2O4)2(LiBOB)或二氟草酸硼酸锂LiBF2(C2O4)(LiDFOB)。在一些实施例中,添加剂包括氟代碳酸乙烯酯和己二腈中的至少一种。
在一些实施方式中,二次电池为卷绕式二次电池或叠片式二次电池。
根据本申请的一些实施方式,本申请的二次电池包括,但不限于:锂离子电池或钠离子电池。在一些实施例中,二次电池包括锂离子电池。
二、电子装置
本申请进一步提供了一种电子装置,其包括本申请第一方面的二次电池。
本申请的电子设备或装置没有特别限定。在一些实施例中,本申请的电子设备包括但不限于,笔记本电脑、笔输入型计算机、移动电脑、电子书播放器、便携式电话、便携式传真机、便携式复印机、便携式打印机、头戴式立体声耳机、录像机、液晶电视、手提式清洁器、便携CD机、迷你光盘、收发机、电子记事本、计算器、存储卡、便携式录音机、收音机、备用电源、电机、汽车、摩托车、助力自行车、自行车、照明器具、玩具、游戏机、钟表、电动工具、闪光灯、照相机、家庭用大型蓄电池和锂离子电容器等。
在下述实施例及对比例中,所使用到的试剂、材料以及仪器如没有特殊的说明,均可商购获得。
实施例及对比例
以下,举出实施例及对比例来对本申请的实施方式进行更具体地说明。各种的试验及评价按照下述的方法进行。另外,只要无特别说明,“份”、“%”为质量基准。
实施例1
1、负极活性材料的制备
石墨材料制备
第一负极活性材料:称取5kg人造石墨材料,以沥青为包覆剂与石墨材料混合均匀得到第一混合物,其中沥青与石墨材料的质量比为3:97。将第一混合物进行第一热处理;第一热处理条件为:在氮气气氛1000℃条件下反应2h,待反应结束并且温度降至室温后得到第一热处理产物,将第一热处理产物进行第二热处理,第二热处理条件为:反应气氛为5%CO2和95%N2混合气,900℃条件下反应6h,待反应结束冷却至室温后即可得第一负极活性材料。
第二负极活性材料:称取5kg人造石墨材料,以沥青为包覆剂与石墨材料混合均匀得到第二混合物,其中沥青与石墨材料的质量比为4:96。将第二混合物进行第三热处理,第三热处理条件:反应温度T2为700℃氮气气氛下反应时间H2为4h;待反应结束冷却至室温即可得第二负极活性材料。
通过调节实施例1中,第一负极活性材料制备条件中在5%CO2和95%N2混合气氛下的反应温度T1和反应时间H1,以及第二负极活性材料制备条件的反应温度T2和反应时间H2,即可制备其他实施例及对比例。
2、负极的制备
将第一负极活性材料、羧甲基纤维素钠(CMC)、丁苯橡胶(SBR)按质量比97.5:1.2:1.3在适量去离子水中分散均匀,得到浆料1。将第二负极活性材料、羧甲基纤维素钠(CMC)及丁苯橡胶(SBR)按质量比97.5:1.2:1.3在适量去离子水中分散均匀,得到浆料2。铜箔作集流体,以浆料1作为第一负极活性材料层,浆料2作为第二负极活性材料层并均匀涂覆在集流体上,涂布后烘干、冷压,即制得负极极片,也称负极。其中,基于第一负极活性材料层和第二负极活性材料层的总质量,第一负极活性材料层的质量含量为70%,第二负极活性材料层的质量含量为30%。
3、正极的制备
正极以钴酸锂(化学式:LiCoO2)作为活性材料,将其与导电剂乙炔黑、粘结剂聚偏二氟乙烯(简写为PVDF)按重量比96.3:2.2:1.5在适量的N-甲基吡咯烷酮(简写为NMP)溶剂中充分搅拌混合,使其形成均匀的正极浆料,将浆料涂覆于集流体Al箔上,涂布后烘干、冷压,即制得到正极极片,也称正极。
4、电解液的制备
在干燥的氩气气氛手套箱中,将碳酸乙烯酯(EC)、碳酸丙烯酯(PC)、碳酸甲乙酯(EMC)、碳酸二乙酯(DEC)按照质量比为EC:PC:EMC:DEC=1:3:3:3进行混合,接着加入氟代碳酸乙烯酯和1,3-丙烷磺内酯,溶解并充分搅拌后加入锂盐LiPF6,混合均匀后得到电解液。其中,LiPF6的质量百分含量为12.5%,氟代碳酸乙烯酯的质量百分含量为2%,1,3-丙烷磺内酯的质量百分含量为2%,各物质的质量百分含量为基于电解液的质量计算得到。
5、隔离膜的制备
以聚乙烯多孔聚合物薄膜作为隔离膜。
6、锂离子电池的制备
将正极、隔离膜、负极按顺序叠好,使隔离膜处于正极和负极之间起到隔离的作用,然后卷绕得到电极组件;焊接极耳后将电极组件置于外包装箔铝塑膜中,将上述制备好的电解液注入到干燥后的电极组件中,经过真空封装、静置、化成、整形、容量测试等工序,获得软包锂离子电池。
实施例2至实施例13、对比例1至对比例9
负极活性材料制备
不同之处在于通过调整反应温度T1和反应时间H1来制备相应的第一负极活性材料,通过调整反应温度T2和反应时间H2来制备相应的第二负极活性材料。具体制备参数如表1所示。负极、正极、隔离膜、电解液以及锂离子电池的制备同实施例1。
实施例14至实施例20
负极活性材料制备
负极活性材料的制备过程与实施例9相同。
负极制备,负极的制备过程与实施例9类似,不同之处在于通过调整浆料的涂布重量来调整第一负极活性材料层和第二负极活性材料层的质量含量,具体调整后的第一负极活性材料层和第二负极活性材料层的质量含量见表2。
正极、隔离膜、电解液以及锂离子电池的制备同实施例9。
测试方法
负极活性材料相关参数测试
取完全放电的锂离子电池,拆解后取出负极用DMC(碳酸二甲酯)浸泡20min后,再依次用DMC、丙酮各淋洗一遍,以去除电解液及表层SEI膜,之后将其置于烘箱内,80℃烘烤12h,获得处理后的负极极片。
用刮刀刮下负极极片距表层10μm厚度范围内的粉末M1克,并将刮下的粉末在500℃空气气氛下焙烧3h,获得第一负极活性材料。
用刮刀刮下负极极片距集流体10μm厚度范围内的粉末M2克,并将刮下的粉末在500℃空气气氛下焙烧3h,获得第二负极活性材料。
对所获得的第一负极活性材料和第二负极活性材料进行如下测试:
1、反弹率和最大反弹率时的粉末压实密度
采用PRCD3100粉末压实密度仪测试活性材料的反弹率和最大反弹率时的粉末压实密度,即极限压实密度。
具体地,取m克的活性材料装入粉压测试专用模具中,装填厚度约为模具深度的1/3,设定压力点分别为5MPa、25MPa、45MPa、65MPa、85MPa、105MPa、125MPa、130MPa,然后逐渐施加压力,并记录各设定压力点下所对应的活性材料厚度h1。以活性材料质量m、厚度h1和固定的装填面积s可计算该受压状态下的粉末压实密度,即该压力点的保压压密;卸掉压力后,记录活性材料反弹后的厚度h2,可计算相应的卸压压密。粉末反弹率=(保压压密/卸压压密-1)×100%。
以粉末反弹率和卸压压密作图可得材料的粉末反弹率变化曲线,当达到最大反弹率时的卸压压密即为活性材料的极限压实密度。
2、吸油值测试
采用DABS-H吸油计对活性材料的吸油值进行测定。具体地,用恒速滴定器将N-甲基吡咯烷酮加入到吸油计混合槽内的试样上,随着试样吸油量的增加,混合物料粘度不断增大,当粘度达到预定值时,吸油计和滴定器同时关闭。从滴定管直接读取加入油的体积,每单位质量试样吸收油的体积记为样品的吸油值。
3、极片反弹率
测量负极极片冷压后的厚度记为T1,拆解50%SOC电芯的负极极片并测量厚度记为T2,负极50%SOC的极片反弹率T=(T2-T1)/T1*100%。
锂离子电池相关性能测试
4、体积能量密度
将锂离子电池按如下流程进行容量测试:
1)25℃条件下搁置30min;
2)0.5C充电至4.48V,恒压至0.05C;
3)搁置5min;
4)0.2C放电至3.0V;
5)搁置5min,测试结束。
记录第4)步的放电容量为C,放电平台电压为P,测量锂离子电池厚度为G、锂离子电池长度为L,锂离子电池宽度为W,则该锂离子电池的体积能量密度E可根据如下公式进行计算
E=(C×P)/(G×L×W)。
5、快充性能测试
1)将锂离子电池在25℃条件下搁置10min;
2)0.025C放电至3.0V;
3)搁置10min;
4)3C充电至4.48V,恒压至0.025C;
5)搁置10min;
6)0.025C放电至3.0V;
7)搁置10min;
8)第5)-8)步循环10圈;
将最后一圈放电的容量记为D10,将第一圈充电的容量记为C1,不可逆Li损失率Q表示为:Q=(C1-D10)/C1×100%。
Q越小,表示不可逆Li损失越少,则锂离子电池的快充能力越好。
测试结果
表1示出了第一负极活性材料的最大反弹率Ra和第二负极活性材料的最大反弹率Rb对锂离子电池性能的影响。
表1
注:“/”表示不进行相应的热处理。
从表1的实施例1至实施例13可以看出,在Ra满足范围5%≤Ra≤13%,Rb满足范围10%≤Rb≤17%时,锂离子电池在具有较高能量密度的同时不可逆Li损失率仍维持在较低的水平,说明其可兼顾高的能量密度和较好的快充能力。
从对比例2、对比例6可以看出,当Ra大于13%时,虽然锂离子电池的快充能力优异,但极片反弹率较大,能量密度损失较多。从对比例1、对比例5可以看出,当Ra小于5%时,虽然极片反弹率较小,锂离子电池的能量密度较高,但快充能力会受到较大的影响。
从对比例4、对比例6可以看出,当Rb大于17%时,极片反弹率大,锂离子电池的快充能力优异,但其能量密度损失较多。从对比例3、对比例5可以看出,当Rb小于9%时,极片反弹率较小,锂离子电池的能量密度较高,但快充能力会受到较大的影响。
从对比例7可以看出至对比例9可以看出,当Ra大于或等于Rb时,锂离子电池的能量密度及快充能力均会受到一定影响。
表2在实施例9的基础上进一步研究了第一负极活性材料层的质量含量Wa和第二负极活性材料层的质量含量Wb对锂离子性能的影响。
表2
从表2中的数据可以看,第一负极活性材料层的质量含量Wa为60%至80%,第二负极活性材料层的质量含量Wb为20%至40%时,锂离子电池兼具高的能量密度和优异的快充性能。
虽然已经说明和描述了本申请的一些示例性实施方式,然而本申请不限于所公开的实施方式。相反,本领域普通技术人员将认识到,在不脱离如所附权利要求中描述的本申请的精神和范围的情况下,可对所描述的实施方式进行一些修饰和改变。
Claims (13)
1.一种二次电池,其包括负极,所述负极包括集流体和设置于所述集流体表面的负极活性材料层,所述负极活性材料层包括第一负极活性材料层和第二负极活性材料层,所述第一负极活性材料层设置于所述集流体和所述第二负极活性材料层之间,所述第一负极活性材料层包括第一负极活性材料,所述第一负极活性材料的最大反弹率为Ra,所述第二负极活性材料层包括第二负极活性材料,所述第二负极活性材料的最大反弹率为Rb,其中,5%≤Ra≤13%,10%≤Rb≤17%,Ra<Rb。
2.根据权利要求1所述的二次电池,其中,5%≤Ra≤10%,10%≤Rb≤14%。
3.根据权利要求1所述的二次电池,其中,8%≤Ra≤10%,12%≤Rb≤14%。
4.根据权利要求2所述的二次电池,其中,0<Rb-Ra≤10%。
5.根据权利要求3所述的二次电池,其中,2%≤Rb-Ra≤6%。
6.根据权利要求1所述的二次电池,其中,所述第一负极活性材料选自人造石墨和/或天然石墨,所述第二负极活性材料选自人造石墨。
7.根据权利要求1所述的二次电池,基于所述负极活性材料层的质量,所述第一负极活性材料层的质量含量为60%至80%,所述第二负极活性材料层的质量含量为20%至40%。
8.根据权利要求1所述的二次电池,基于所述负极活性材料层的质量,所述第一负极活性材料层的质量含量为70%至80%,所述第二负极活性材料层的质量含量为20%至30%。
9.根据权利要求1所述的二次电池,其中,所述负极满足如下条件(i)至(iii)中的至少一者:
(i)以N-甲基吡咯烷酮为测试油进行测试,所述第一负极活性材料的吸油值小于或等于65mL/100g,所述第二负极活性材料的吸油值小于或等于65mL/100g;
(ii)所述负极的压实密度为1.70g/cm3至1.85g/cm3;
(iii)所述负极极片反弹率为T,其中,15%≤T≤20%。
10.一种电子装置,包括权利要求1至9中任一项所述的二次电池。
11.一种负极的制备方法,所述负极包括集流体和设置于所述集流体表面的负极活性材料层,所述负极活性材料层包括第一负极活性材料层和第二负极活性材料层,所述第一负极活性材料层设置于所述集流体和所述第二负极活性材料层之间,所述第一负极活性材料层包括第一负极活性材料,所述第二负极活性材料层包括第二负极活性材料,其中,所述负极制备方法包括:
所述第一负极活性材料的制备:
将人造石墨和/或天然石墨与包覆剂进行混合,得到第一混合物,基于所述第一混合物的质量,所述包覆剂的质量含量为1%至5%;
在惰性气氛中,将所述第一混合物进行第一热处理,得到第一热处理产物;
在CO2和N2的混合气中,将所述第一热处理产物进行第二热处理,得到所述第一负极活性材料;
所述第二负极活性材料的制备:
将所述人造石墨与所述包覆剂进行混合,得到第二混合物;
在惰性气氛中,将所述第二混合物进行第三热处理,得到所述第二负极活性材料;
所述第一热处理的温度为950℃至1200℃,所述第一热处理的时间为1h至5h;
所述第二热处理的温度为500℃至900℃,所述第二热处理的时间为5h至15h;
所述第三热处理的温度为700℃至1100℃,所述第三热处理的时间为4h至10h;
所述包覆剂为沥青。
12.如权利要求11所述的制备方法,所述第二热处理的温度为700℃至900℃,所述第二热处理的时间为5h至7h。
13.如权利要求11所述的制备方法,所述第三热处理的温度为700℃至900℃,所述第三热处理的时间为4h至6h。