CN116535907A - 一种玩具高环保耐消毒液一次性pp喷油 - Google Patents
一种玩具高环保耐消毒液一次性pp喷油 Download PDFInfo
- Publication number
- CN116535907A CN116535907A CN202310513101.8A CN202310513101A CN116535907A CN 116535907 A CN116535907 A CN 116535907A CN 202310513101 A CN202310513101 A CN 202310513101A CN 116535907 A CN116535907 A CN 116535907A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- disposable
- disinfectant
- toy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于涂料技术领域,具体涉及一种玩具高环保耐消毒液一次性PP喷油,包括以下按照质量份数计算的组分:酯溶性氯化聚丙烯树脂30~69.3份,氯醚树脂3~6份,高Tg值丙烯酸树脂5~8份,无苯无酮型醇酸树脂4~6份,酮醛树脂3~5份,PP附着力促进剂2~4份,流平剂0.1~0.5份,消泡剂0.1~0.5份,丙二醇甲醚醋酸酯3~5份,醋酸丁酯8~15份,色粉2.5~20份。本发明提供的一次性PP喷油无需对PP底材进行前处理,可用于直接喷涂,并达到附着力优良及无苯无酮的高环保要求,喷涂后的漆膜表干时间短,光泽度更高,具有良好的流平及表观效果,对不同PP底材的附着力稳定,可耐消毒液尤其是丝洁牌免过水洗手消毒液擦拭。
Description
技术领域
本发明属于涂料技术领域,具体涉及一种玩具高环保耐消毒液一次性PP喷油。
背景技术
PP料是丙烯酸加聚反应而成的聚合物,PP料全名Polypropylene,中文名聚丙烯,它具有无臭、无味、无毒、质轻、韧性好、耐热性好、耐化学性好、可塑性好、良好的加工性能等特点,因此PP料广泛应用于玩具、机械、汽车、包装和食品工业等众多领域。为在已成型PP玩具或其他PP工件上有更好的装饰和保护等作用需涂覆一层不同色彩不同质感的涂料,然而PP料耐溶剂,表面能低、极性小、润湿性差,普通油漆极难直接附着,传统工艺采用先在PP料表面喷处理剂(俗称PP水),再喷普通油漆的方案解决。
随着玩具行业环保要求进一步提高,除了国家及国际标准规定的重金属、邻苯、多环芳烃、双酚A、甲醛等及法律法规环保要求不断提升外,各玩具行自己内部的测试要求和标准也不断更新和提高,例如:费列罗玩具行要求对所用油漆无苯无酮;麦当劳玩具行要求对所用油漆不含甲苯、二甲苯和丁酮。新冠疫情期间人们对清洁、卫生、消毒日常防护的注重和普及,威露士免过水洗手消毒液、滴露免过水消毒液及丝洁牌免过水洗手消毒液等成为日常卫生防护消毒的主要常用洗手消毒液,麦当劳玩具行在对其玩具用洗手消毒液清洗消毒测试时发现其中丝洁牌免过水洗手消毒液对普通硬胶单组分玩具漆漆膜和普通一次性玩具PP油漆膜有溶蚀和脱色现象(其他品牌如:威露士免过水洗手消毒液、滴露免过水洗手消毒液等均未发现对玩具漆膜有溶蚀和脱色现象),为此麦当劳玩具行内部测试新增加了玩具漆漆膜耐消毒液擦拭要求。
现有普通一次性PP喷油既不能满足费列罗玩具行无苯无酮高环保要求也不能满足麦当劳玩具行不含甲苯、二甲苯和丁酮的要求,更达不到麦当劳玩具行耐消毒液擦拭测试要求,因此如何提供一种在保证附着力优良的基础上发明一种玩具高环保(无苯无酮)耐消毒液一次性PP喷油已成为目前亟待解决的技术问题。
发明内容
本发明所解决的技术问题是提供一种玩具高环保耐消毒液一次性PP喷油,在不使用苯类溶剂、附着力优良的条件下实现无苯无酮高环保、耐消毒液擦拭的要求,同时漆膜干性及施工性能得到较大改善。另一方面,本发明可应用于各类PP底材玩具上的喷涂,获得耐消毒液的PP玩具漆膜,尤其耐丝洁牌免过水洗手消毒液擦拭。
本发明将通过以下技术方案解决上述问题:
本发明提供一种玩具高环保耐消毒液一次性PP喷油,包括以下组分:酯溶性氯化聚丙烯树脂,氯醚树脂,高Tg值丙烯酸树脂,无苯无酮型醇酸树脂,酮醛树脂,PP附着力促进剂,流平剂,消泡剂,丙二醇甲醚醋酸酯,醋酸丁酯,色粉。
具体的,以上组分按质量份数计算,包括:酯溶性氯化聚丙烯树脂30~69.3份,氯醚树脂3~6份,高Tg值丙烯酸树脂5~8份,无苯无酮型醇酸树脂4~6份,酮醛树脂3~5份,PP附着力促进剂2~4份,流平剂0.1~0.5份,消泡剂0.1~0.5份,丙二醇甲醚醋酸酯3~5份,醋酸丁酯8~15份,色粉2.5~20份。
具体的,所述酯溶性氯化聚丙烯树脂的固含为46±2%,该树脂摒弃常规用甲苯/二甲苯为主溶解的氯化聚丙烯树脂,以达到无苯无酮更高环保要求。由于玩具漆颜色丰富多彩及在不同PP底材上遮盖力要求不同导致所加色粉的比例不同,因此酯溶性氯化聚丙烯树脂在不同颜色和不同遮盖力油中添加的比例不同,色粉的重量份数为2.5~20份时,酯溶性氯化聚丙烯树脂的重量份数为30~69.3份。
具体的,所述氯醚树脂包括巴斯夫Laroflex MP-45固体树脂;所述高Tg值丙烯酸树脂Tg值(玻璃化转变温度)至少为90℃,固含为50±2%。氯醚树脂和高Tg值丙烯酸树脂在配方中可以增加漆膜耐化学性能,使漆膜耐消毒液测试要求,以及改善溶剂释放性使漆膜表干时间缩短。
具体的,所述无苯无酮型醇酸树脂为无苯无酮的环保型醇酸树脂,固含为70±2%;所述酮醛树脂为固体树脂。无苯无酮型醇酸树脂和酮醛树脂在配方中起到增加和平衡组分的混溶性,提高油漆光泽及进一步改善施工雾化性能的作用,同时改善漆膜在PP底材上的附着力。
具体的,所述PP附着力促进剂包括氯化聚烯烃,其固含为40±2%,在配方中增进油漆与PP底材的附着力作用。
具体的,所述流平剂包括聚醚改性聚硅氧烷流平剂,具有很好的抗水抗油和流平效果。
具体的,所述消泡剂包括聚硅氧烷消泡剂,在油漆制造和施工过程中破泡能力强,具有很好的消泡效果。
具体的,丙二醇甲醚醋酸酯可以对树脂的溶解及干性做出调整;醋酸丁酯增进对树脂的溶解;色粉由于玩具漆颜色丰富多彩及在不同PP底材上遮盖力要求不同,其比例可以按需调整,种类不作特别限制。
根据本发明的另一方面,提供上述玩具高环保耐消毒液一次性PP喷油在制造耐消毒液PP底材玩具中的应用,例如,使用本发明喷涂于具有PP底材的玩具表面。
本发明所述的耐消毒液包括耐丝洁牌免过水洗手消毒液,该消毒液组成包括正丙醇,异丙醇,水,丙三醇,羟丙基纤维素,棕榈酸异丙酯,按体积百分比计算,其主要有效成份为正丙醇44~55%,异丙醇17~23%;另外,本发明还满足耐其他消毒液的要求,例如威露士免过水洗手消毒液,其组成包括乙醇,水,按体积百分比计算,其主要有效成份为乙醇55~65%;滴露免过水洗手消毒液,其组成包括乙醇,水,按体积百分比计算,其主要有效成份为乙醇55~65%。本发明一种玩具高环保耐消毒液一次性PP喷油漆膜主要耐洗手消毒液成份中棕榈酸异丙酯及正丙醇,异丙醇,丙三醇和乙醇的擦拭。
本发明的有益效果在于:本发明提供的一次性PP喷油无需对PP底材进行前处理,可用于直接喷涂,并达到附着力优良及无苯无酮的高环保要求。喷涂后的漆膜表干时间短,光泽度更高,具有良好的流平及表观效果,对不同PP底材的附着力稳定,可耐消毒液尤其是丝洁牌免过水洗手消毒液擦拭。
具体实施方式
下面结合具体实施方式对本发明进行详细的说明,实施例仅是本发明的优选实施方式,不是对本发明的限定,本发明中未详细说明的方法为本领域常用的方法。
本发明喷涂于具有PP底材的玩具上,下表1为施工玩具所使用的3个实施例(本发明)及3个对比例(市售普通一次性PP喷油)的配方表,制备方法为本领域常规的混合搅拌和研磨。
表1:实施例及对比例的配方表
将上述实施例及对比例用开油水开稀喷版(开稀质量比为黑色油漆:开油水为1:1.1;白色油漆:开油水为1:0.8;银色油漆:开油水为1:1.3)后室温自干24小时,测试各项性能,测试方法为本领域的常规方法,在此不作特殊说明。
需作特殊说明的是,耐消毒液的测试方法采用麦当劳玩具行对玩具漆膜的测试方法,包括以下步骤:将消毒液滴落在被测试的漆膜上用手擦拭30秒,擦拭过程保持漆膜上一直有湿润的消毒液,30秒后在同一位置再次滴上消毒液用手擦拭30秒,观察漆膜是否被溶蚀或脱色,如有漆膜溶蚀或脱色被视为不耐消毒液。
测试结果如下表2所示:
表2:实施例及对比例性能测试结果
通过实施例与对比例各项相关性能的测试结果可知,本发明的油漆混合溶剂为醋酸丁酯和丙二醇甲醚醋酸酯,在保证附着力优良的前提下实现无苯无酮更高环保要求,耐丝洁牌免过水洗手消毒液,威露士免过水洗手消毒液,滴露免过水洗手消毒液,三种消毒液测试均达标(尤其是丝洁牌免过水洗手消毒液),漆膜无溶蚀无脱色,同时油漆干性得到较大改善和提升。
以上详细描述了本发明的优选实施方式,但是,本发明并不限于上述实施方式中的具体细节,在本发明的技术构思范围内,可以根据不同颜色不同遮盖力要求对本发明的技术方案进行多种简单变型,这些简单变型均属于本发明的保护范围。
Claims (10)
1.一种玩具高环保耐消毒液一次性PP喷油,其特征在于,包括以下按照质量份数计算的组分:酯溶性氯化聚丙烯树脂30~69.3份,氯醚树脂3~6份,高Tg值丙烯酸树脂5~8份,无苯无酮型醇酸树脂4~6份,酮醛树脂3~5份,PP附着力促进剂2~4份,流平剂0.1~0.5份,消泡剂0.1~0.5份,丙二醇甲醚醋酸酯3~5份,醋酸丁酯8~15份,色粉2.5~20份。
2.根据权利要求1所述的玩具高环保耐消毒液一次性PP喷油,其特征在于,所述酯溶性氯化聚丙烯树脂的固含为46±2%。
3.根据权利要求1所述的玩具高环保耐消毒液一次性PP喷油,其特征在于,所述氯醚树脂包括巴斯夫LaroflexMP-45固体树脂。
4.根据权利要求1所述的玩具高环保耐消毒液一次性PP喷油,其特征在于,所述高Tg值丙烯酸树脂的Tg值至少为90℃,固含为50±2%。
5.根据权利要求1所述的玩具高环保耐消毒液一次性PP喷油,其特征在于,所述无苯无酮型醇酸树脂的固含为70±2%。
6.根据权利要求1所述的玩具高环保耐消毒液一次性PP喷油,其特征在于,所述酮醛树脂为固体树脂。
7.根据权利要求1所述的玩具高环保耐消毒液一次性PP喷油,其特征在于,所述PP附着力促进剂包括氯化聚烯烃。
8.根据权利要求1所述的玩具高环保耐消毒液一次性PP喷油,其特征在于,所述流平剂包括聚醚改性聚硅氧烷流平剂,所述消泡剂包括聚硅氧烷消泡剂。
9.一种耐消毒液的PP玩具漆膜,其特征在于,由权利要求1-8任一项所述玩具高环保耐消毒液一次性PP喷油制备而成。
10.根据权利要求9所述的耐消毒液的PP玩具漆膜,其特征在于,所述消毒液为丝洁牌免过水洗手消毒液。