CN116515330A - Water-proof zero-formaldehyde inorganic interior wall coating - Google Patents
Water-proof zero-formaldehyde inorganic interior wall coating Download PDFInfo
- Publication number
- CN116515330A CN116515330A CN202310590942.9A CN202310590942A CN116515330A CN 116515330 A CN116515330 A CN 116515330A CN 202310590942 A CN202310590942 A CN 202310590942A CN 116515330 A CN116515330 A CN 116515330A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- formaldehyde
- interior wall
- wall coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-proof zero-formaldehyde inorganic interior wall coating, which comprises the following components in parts by weight: 1-10 parts of volcanic ash, 5-30 parts of barite powder, 1-10 parts of sodium aluminosilicate, 10-80 parts of silica sand, 5-30 parts of ore powder, 5-50 parts of ash calcium powder, 1-15 parts of calcium silicate, 1-20 parts of perlite powder and 0.1-1 part of grass tendon. The waterproof zero-formaldehyde inorganic interior wall coating fully utilizes the environment-friendly health performance of inorganic materials, is prepared by an inorganic cementing technology, is environment-friendly and healthy, has no formaldehyde and VOC emission, is good in waterproof and aging resistance, does not crack or fall off slag, is heat-insulating and energy-saving, is fireproof and incombustible, is antibacterial and mildew-proof, is breathable and is moisture-regulating, and more importantly, the pain points of cracking and falling slag and color-changing dirt of the wet or water-permeable wall coating are thoroughly solved.
Description
Technical Field
The invention belongs to the field of coatings, relates to a coating, and in particular relates to a bubble-resistant zero-formaldehyde inorganic interior wall coating.
Background
Among interior wall decorative coatings, organic emulsion paint has been mainly used so far, and the other part is a coating combining organic and inorganic materials. The use of more organic materials in the production of the coating is not friendly to the environment, and simultaneously has adverse effects on human health, especially formaldehyde has the greatest effect on human health. The inorganic paint has no influence on human health, is an environment-friendly product, but the pure inorganic paint in the market has a plurality of defects, namely the poor scratch resistance and the poor water resistance, and the organic paint emulsion paint has poor aging resistance under water environment, especially like the wall surfaces of toilets and kitchens, has aging and cracking earlier than the wall surfaces in other places under the condition of water vapor infiltration or water seepage throughout the year, and then has the problems of powder and slag falling in the interior, thereby seriously affecting the living quality.
The main defects are as follows: the existing paint has poor water resistance and aging resistance, is easy to crack and fall, contains formaldehyde and organic matters, influences health and pollutes the environment.
Disclosure of Invention
The invention provides a waterproof zero-formaldehyde inorganic interior wall coating, which is prepared by fully utilizing the environment-friendly health performance of inorganic materials and by an inorganic cementing technology, is environment-friendly and healthy, has no formaldehyde emission and VOC emission, has good waterproof and ageing resistance, and does not crack or drop slag.
In order to achieve the above purpose, the present invention adopts the following technical scheme:
the invention provides a water-proof zero-formaldehyde inorganic interior wall coating, which comprises the following components in parts by weight: 1-10 parts of volcanic ash, 5-30 parts of barite powder, 1-10 parts of sodium aluminosilicate, 10-80 parts of silica sand, 5-30 parts of ore powder, 5-50 parts of ash calcium powder, 1-15 parts of calcium silicate, 1-20 parts of perlite powder and 0.1-1 part of grass tendon.
According to the invention, the water-resistant zero-formaldehyde inorganic interior wall coating fully utilizes the environment-friendly health performance of inorganic materials, is prepared by an inorganic cementing technology, is environment-friendly and healthy, has no formaldehyde and VOC emission, is good in water resistance and aging resistance, does not crack or fall slag, is heat-insulating and energy-saving, is fireproof and incombustible, is antibacterial and mildew-proof, is breathable and is moisture-regulating, and more importantly, the pain points of cracking and slag fall and color-changing dirt of the wet or easily-permeated wall coating are thoroughly solved.
As a preferable scheme of the invention, the water-resistant zero-formaldehyde inorganic interior wall coating comprises the following components in parts by weight: 1-8 parts of volcanic ash, 10-25 parts of barite powder, 1-5 parts of sodium aluminosilicate, 30-60 parts of silica sand, 10-25 parts of ore powder, 10-40 parts of ash calcium powder, 1-10 parts of calcium silicate, 1-15 parts of perlite powder and 0.1-0.8 part of grass tendon.
As a preferable scheme of the invention, the water-resistant zero-formaldehyde inorganic interior wall coating comprises the following components in parts by weight: 1-5 parts of volcanic ash, 10-20 parts of barite powder, 1-3 parts of sodium aluminosilicate, 30-50 parts of silica sand, 10-20 parts of ore powder, 20-30 parts of ash calcium powder, 5-10 parts of calcium silicate, 1-10 parts of perlite powder and 0.1-0.3 part of grass tendon.
The invention also provides a preparation method of the bubble-resistant zero-formaldehyde inorganic interior wall coating, which comprises the following steps:
1) Preparing raw materials;
2) Stirring, namely sequentially adding volcanic ash, ore powder, gray calcium powder, calcium silicate, barite powder, sodium aluminosilicate, perlite powder, grass tendon and silica sand, and stirring;
3) And (5) discharging and packaging to obtain the bubble-resistant zero-formaldehyde inorganic interior wall coating.
As a preferred embodiment of the present invention, in the step 2), the stirring time is 10 to 50 minutes.
As a preferred embodiment of the present invention, in the step 2), the stirring time is 20 to 40 minutes.
As a preferable scheme of the invention, in the step 1), the particle sizes of volcanic ash, ore powder, ash calcium powder, calcium silicate, barite powder and sodium aluminosilicate are 600-1200 meshes, the particle sizes of perlite powder and silica sand are 40-150 meshes, and the length of grass bars is 0.5-3cm.
When the invention is used, firstly, water is added into a mixing barrel, then dry powder is added into the barrel, and the coating can be carried out by uniformly stirring, and the water addition amount is as follows: water = 1.0: preferably 0.4-0.6, the consistency is that the paint is coated on the wall and does not sag.
Compared with the prior art, the invention has the following beneficial effects:
the water-resistant zero-formaldehyde inorganic interior wall coating disclosed by the invention is healthy and environment-friendly, has no voc emission, is heat-insulating and energy-saving, is fireproof and incombustible, is antibacterial and mildew-proof, is breathable and is moisture-regulating, and more importantly, the pain points of cracking, deslagging and color-changing dirt of a wet or easily-infiltrated wall coating are thoroughly solved. The sample plate manufactured by the invention is maintained for three days (72 hours), soaked in water for two days (48 hours), taken out and still remains intact, and the powder and the slag are not removed by rubbing with cotton cloth. In practice, the original paint is only shoveled off for the emulsion paint wall surface which is cracked and deslagged due to water seepage, other protective treatment is not carried out, and the wall surface is not cracked and deslagged after the paint is scraped again.
Drawings
FIG. 1 is a graph of a test comparison after soaking of inventive example 1 with a comparative example.
FIG. 2 is a graph showing the test comparison of the invention after the air-dried test of example 1 and comparative example.
FIG. 3 is a schematic diagram of the use of example 4.
FIG. 4 is a schematic of the use of example 5.
Detailed Description
In order to facilitate understanding of the technical means, the creation characteristics, the achievement of the objects and the effects achieved by the present invention, the present invention is further described below with reference to specific examples, but the following examples are only preferred examples of the present invention, not all of which are described in detail below. Based on the examples in the embodiments, those skilled in the art can obtain other examples without making any inventive effort, which fall within the scope of the invention. The experimental methods in the following examples are conventional methods unless otherwise specified, and materials, reagents, etc. used in the following examples are commercially available unless otherwise specified.
Example 1
The embodiment provides a water-proof zero-formaldehyde inorganic interior wall coating, which comprises the following components in parts by weight: 5 parts of volcanic ash, 10 parts of barite powder, 1 part of sodium aluminosilicate, 50 parts of silica sand, 10 parts of ore powder, 20 parts of gray calcium powder, 5 parts of calcium silicate, 1 part of perlite powder and 0.1 part of grass tendon.
The preparation method of the water-resistant zero-formaldehyde inorganic interior wall coating comprises the following steps:
1) Preparing raw materials;
2) Stirring, namely sequentially adding volcanic ash, ore powder, gray calcium powder, calcium silicate, barite powder, sodium aluminosilicate, perlite powder, grass tendon and silica sand, and stirring;
3) And (5) discharging and packaging to obtain the bubble-resistant zero-formaldehyde inorganic interior wall coating.
Named as TP plastering paint.
Example 2
The embodiment provides a water-proof zero-formaldehyde inorganic interior wall coating, which comprises the following components in parts by weight: 1 part of volcanic ash, 20 parts of barite powder, 3 parts of sodium aluminosilicate, 30 parts of silica sand, 20 parts of ore powder, 25 parts of gray calcium powder, 8 parts of calcium silicate, 5 parts of perlite powder and 0.3 part of grass tendon.
The preparation method of the water-resistant zero-formaldehyde inorganic interior wall coating comprises the following steps:
1) Preparing raw materials;
2) Stirring, namely sequentially adding volcanic ash, ore powder, gray calcium powder, calcium silicate, barite powder, sodium aluminosilicate, perlite powder, grass tendon and silica sand, and stirring;
3) And (5) discharging and packaging to obtain the bubble-resistant zero-formaldehyde inorganic interior wall coating.
Named as TP plastering paint.
Example 3
The embodiment provides a water-proof zero-formaldehyde inorganic interior wall coating, which comprises the following components in parts by weight: 3 parts of volcanic ash, 15 parts of barite powder, 2 parts of sodium aluminosilicate, 40 parts of silica sand, 15 parts of ore powder, 30 parts of ash calcium powder, 10 parts of calcium silicate, 10 parts of perlite powder and 0.2 part of grass tendon.
The preparation method of the water-resistant zero-formaldehyde inorganic interior wall coating comprises the following steps:
1) Preparing raw materials;
2) Stirring, namely sequentially adding volcanic ash, ore powder, gray calcium powder, calcium silicate, barite powder, sodium aluminosilicate, perlite powder, grass tendon and silica sand, and stirring;
3) And (5) discharging and packaging to obtain the bubble-resistant zero-formaldehyde inorganic interior wall coating.
Named as TP plastering paint.
When the invention is used, a proper amount of water is added into the barrel, and then a proper amount of powder is added and stirred uniformly, so that the coating can be performed, and the consistency is determined to be that the coating does not sag on the wall.
Example 4
Referring to fig. 3, the wall surface of a toilet of a certain owner in the rest Hangzhou city is wetted for a long time due to water seepage, so that the emulsion paint newly made on the wall surface is bubbling and cracked within two years, the putty therein is continuously pulverized and falls off, the residual emulsion paint is removed by shoveling, and the phenomenon of cracking and slag falling does not occur after the plastering paint of the embodiment 2 of the invention is scraped again for five years so far.
Example 5
Referring to fig. 4, in a certain courtyard in a western lake area of Hangzhou, due to the large moisture in mountain forests and serious wall surface wetting, a newly made emulsion paint wall surface starts bubbling and cracking within one month, a plurality of stains appear, the image of the courtyard is seriously affected, and the adverse effect of a wet environment on the courtyard wall surface is thoroughly solved after the plastering coating of the embodiment 1 of the invention is coated.
Comparative example, a commercially available latex paint.
Example 1 of the present invention was compared with comparative example.
The implementation method comprises the following steps: (1) The method comprises the steps of firstly scraping common putty powder on a cement board with the size of A4 twice according to a normal wall paint construction process, airing each time, polishing and leveling, then rolling a primer, airing, rolling a finish paint, standing and airing for one week, meanwhile scraping the primer of the plastering paint of the invention on the other cement board with the size of A4 twice, scraping the top paint of the plastering paint of the invention, standing and airing for one week.
(2) Two A4 templates which are prepared with paint are soaked in a water bucket at the same time, the templates can be horizontally placed or vertically placed, vertical placement is adopted for convenient observation in the comparative example, the water level in the bucket reaches 2/3 of the height of the templates, a bucket cover is covered, and after the two templates are placed for 72 hours, the fact that a plurality of bubbling bulges are formed on the surface of the template which uses emulsion paint in the comparative example is obviously found, and the surface of the plastering paint template of the invention is good as before, and the plastering paint template is shown in fig. 1. The two templates are then dried, and the bubbling latex paint is lightly poked with fingers to break and fall off, while the plastering paint of the invention has no abnormality under the poking of fingers, see fig. 2.
The bubble-resistant zero-formaldehyde inorganic interior wall coating prepared by the invention is subjected to third party detection, and the detection party is as follows: detection center limited company of construction and research, detection item: formaldehyde content, VOC content, mold resistance, flammability class A1, alkali resistance, resistance to artificial weathering (500 h), water absorption, initial drying crack resistance.
The detection results are shown in Table 1.
TABLE 1 detection results
Through detection, items 1-2 of the detection item of the bubble-resistant zero-formaldehyde inorganic interior wall coating disclosed by the invention accord with technical index elements of 18582-2020 ' limit of harmful substances in wall coating for building ', item 3 accords with technical index requirements of HG/T3950-2007 ' antibacterial coating ' 1 level antibacterial coating ', item 4 accords with technical index requirements of GB 8624-2012 ' grade A1 of building material and product combustion performance grading ' flat plate-shaped building material, and item 5-8 accords with technical index requirements of GB/T9756-2018 ' synthetic resin emulsion interior wall coating '.
The water-resistant zero-formaldehyde inorganic interior wall coating disclosed by the invention is healthy and environment-friendly, has no voc emission, is heat-insulating and energy-saving, is fireproof and incombustible, is antibacterial and mildew-proof, is breathable and is moisture-regulating, and more importantly, the pain points of cracking, deslagging and color-changing dirt of a wet or easily-infiltrated wall coating are thoroughly solved. The sample plate manufactured by the invention is maintained for three days (72 hours), soaked in water for two days (48 hours), taken out and still remains intact, and the powder and the slag are not removed by rubbing with cotton cloth. In practice, the original paint is only shoveled off for the emulsion paint wall surface which is cracked and deslagged due to water seepage, other protective treatment is not carried out, and the wall surface is not cracked and deslagged after the paint is scraped again.
While the invention has been described with respect to preferred embodiments thereof, it will be understood by those skilled in the art that various modifications and additions may be made without departing from the scope of the invention. Equivalent embodiments of the present invention will be apparent to those skilled in the art having the benefit of the teachings disclosed herein, when considered in the light of the foregoing disclosure, and without departing from the spirit and scope of the invention; meanwhile, any equivalent changes, modifications and evolution of the above embodiments according to the essential technology of the present invention still fall within the scope of the technical solution of the present invention.
Claims (7)
1. The water-proof zero-formaldehyde inorganic interior wall coating is characterized by comprising the following components in parts by weight: 1-10 parts of volcanic ash, 5-30 parts of barite powder, 1-10 parts of sodium aluminosilicate, 10-80 parts of silica sand, 5-30 parts of ore powder, 5-50 parts of ash calcium powder, 1-15 parts of calcium silicate, 1-20 parts of perlite powder and 0.1-1 part of grass tendon.
2. The water-resistant zero-formaldehyde inorganic interior wall coating according to claim 1, wherein the water-resistant zero-formaldehyde inorganic interior wall coating comprises, in parts by weight: 1-8 parts of volcanic ash, 10-25 parts of barite powder, 1-5 parts of sodium aluminosilicate, 30-60 parts of silica sand, 10-25 parts of ore powder, 10-40 parts of ash calcium powder, 1-10 parts of calcium silicate, 1-15 parts of perlite powder and 0.1-0.8 part of grass tendon.
3. The water-resistant zero-formaldehyde inorganic interior wall coating according to claim 1, wherein the water-resistant zero-formaldehyde inorganic interior wall coating comprises, in parts by weight: 1-5 parts of volcanic ash, 10-20 parts of barite powder, 1-3 parts of sodium aluminosilicate, 30-50 parts of silica sand, 10-20 parts of ore powder, 20-30 parts of ash calcium powder, 5-10 parts of calcium silicate, 1-10 parts of perlite powder and 0.1-0.3 part of grass tendon.
4. A method for preparing the bubble-resistant zero-formaldehyde inorganic interior wall coating material according to any one of claims 1 to 3, wherein the preparation method comprises the following steps:
1) Preparing raw materials;
2) Stirring, namely sequentially adding volcanic ash, ore powder, gray calcium powder, calcium silicate, barite powder, sodium aluminosilicate, perlite powder, grass tendon and silica sand, and stirring;
3) And (5) discharging and packaging to obtain the bubble-resistant zero-formaldehyde inorganic interior wall coating.
5. The method for preparing a water-resistant formaldehyde-free inorganic interior wall coating according to claim 4, wherein in the step 2), the stirring time is 10-50 minutes.
6. The method for preparing the bubble-resistant formaldehyde-free inorganic interior wall coating according to claim 5, wherein in the step 2), the stirring time is 20-40 minutes.
7. The preparation method of the water-resistant formaldehyde-free inorganic interior wall coating according to claim 4, wherein in the step 1), the particle sizes of volcanic ash, ore powder, ash calcium powder, calcium silicate, barite powder and sodium aluminosilicate are 600-1200 meshes, the particle sizes of perlite powder and silica sand are 40-150 meshes, and the length of grass ribs is 0.5-3cm.