CN1164697C - High performance weak solvent resin outer wall surface paint - Google Patents
High performance weak solvent resin outer wall surface paint Download PDFInfo
- Publication number
- CN1164697C CN1164697C CNB011337591A CN01133759A CN1164697C CN 1164697 C CN1164697 C CN 1164697C CN B011337591 A CNB011337591 A CN B011337591A CN 01133759 A CN01133759 A CN 01133759A CN 1164697 C CN1164697 C CN 1164697C
- Authority
- CN
- China
- Prior art keywords
- resin
- present
- class
- high performance
- wall surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The present invention discloses high performance weak solvent resin surface layer paint for an outer wall for achieving the effects of an aluminium plate or glass or ceramics. The present invention is prepared by weatherability resin, filler material, a diluent, an auxiliary agent and metallic pigment according to the weight compounding ratio of 10 to 12: 2 to 5: 70 to 75: 6 to 7: 2 to 8. The present invention has very strong anti-pollution and antistatic performance, abrasion resistance, corrosion resistance, stable color, strong cohesive force, high hardness, scrub resistance and ageing resistance and has no cellulose or mold. The present invention can be compared with the aluminium plate and is the important display mode of modern chemical paint as construction paint.
Description
Affiliated technical field:
The present invention relates to a kind of surface layer slurry of adoring wall, particularly a kind of exterior wall that is applicable to need reach the fluorine modified high performance Weak solvent type resin surface layer slurry of aluminium sheet effect or glass effects or ceramic effect.
Background technology:
Existing aluminum facade material therefor energy consumption height (every square metre aluminium sheet decreases 20000 kilowatts of energy), Mineral resources consumption big (every square metre aluminium sheet will consume 10 tons of aluminium ores), and produce this material and cause very big pollution; During the aluminium sheet construction, complexity is installed, renovation dismounting difficulty is very big; Simultaneously, aluminium sheet cost height (800～1200 yuan/square metre); Aluminum facade is very easily by air corrosion, and color is single.
Summary of the invention:
The purpose of this invention is to provide a kind of the have imitative aluminium sheet of nanoscale structures or silicon, the fluorine modified high performance fluoro-resin surface layer slurry of imitative glass or imitative pottery.Its antifouling property and antistatic property are extremely strong, and be wear-resisting, corrosion resistance nature is good, and color and luster is stable, and cohesive force is strong, and cellulose is not gone mouldy, the hardness height, and superpower self-cleaning function, scrubbing resistance, ageing-resistant, can match in excellence or beauty with aluminium sheet.It is the important behaviour form that the modern chemistry material is covered with paint, lacquer, colour wash, etc. as building, has extremely strong practicality, science, economy and aesthetic effect, meets the weather and the architectural feature of China.
Technical scheme of the present invention is as follows:
The invention is characterized in: by weathering resistance resin, filler, thinner, auxiliary agent and metallic pigment by weight ratio 10～12: 2～5: 70～75: 6～7: 2～8 is formulated.
Weathering resistance resin of the present invention is an acryl resin, or silicone resin, or fluoro-resin.
Filler of the present invention is talcum powder class or lime carbonate class or swelling great soil group etc.;
Thinner of the present invention is no benzene class aliphatics innoxious solvent.
Auxiliary agent of the present invention is thixotropic agent class or flow agent class etc.
Pigment of the present invention is nanosize metal oxide class pigment.
The concrete constructional method that the present invention is sprayed at body of wall is as follows:
1, by slurry of the present invention: the construction proportioning dilution of cleaning water or tap water (thinner)=2.5: 1, to look slurry viscosity and can suitably regulate ratio, the coating after the dilution must be poured spray gun into and spray then with the filtration of 200 order filtering nets;
2, pressing (once twice) twice constructs:
The first degree construction: after treating the coatingsurface thorough drying (fine, at least 12 hours), carry out sand milling with 600# sand paper, must add water in the sand grinding process carries out, otherwise meeting scab paper, bad polishing is after sand milling is intact, wash metope with cleaning water, the flush away residual particles, treat the metope drying after, can carry out the work of following step; Require: smooth surface, no rough, spraying does not evenly have the phenomenon of growing dim.
The second degree construction: at exsiccant coatingsurface with the thorough dedusting of rag (the spray gun blowing does not reach requirements), the dust on the removing scaffolding, avoid being stained with film on, single-block area is above 20 square metres, must use nacelle construction, the place that need not spray must fully hide, in order to avoid pollute; Require: surface effect is identical with model, and film coated surface does not have granule dust, is smooth to the touch, and spraying is even, and the gloss homogeneous does not have the phenomenon of growing dim.
Antifouling property of the present invention and antistatic property are extremely strong, and be wear-resisting, corrosion resistance nature is good, and color and luster is stable, and cohesive force is strong, and cellulose is not gone mouldy, the hardness height, and superpower self-cleaning function, scrubbing resistance, ageing-resistant, can match in excellence or beauty with aluminium sheet.It is the important behaviour form that the modern chemistry slurry is covered with paint, lacquer, colour wash, etc. as building, has extremely strong practicality, science, economy and aesthetic effect, meets the weather and the architectural feature of China.
Embodiment:
Embodiment 1:
The present invention was by weathering resistance resin, filler, thinner, auxiliary agent and metallic pigment 10: 3: 75 by weight ratio: 7: 5 formulated.
Weathering resistance resin of the present invention is silicone resin or fluoro-resin, silicone resin or the fluoro-resin produced as German COLOYS factory.
Filler of the present invention is the talcum powder class, as the talcum powder of Di Gaosha factory production.
Thinner of the present invention is weak dissolubility aliphatic solvents, as the weak dissolubility aliphatic solvents of shell factory production.
Auxiliary agent of the present invention is the flow agent class, as the flow agent of Bi Ke factory production.
Metallic pigment of the present invention are the titanium dioxide that factory of Du Pont produces.
Embodiment 2:
The present invention was by weathering resistance resin, filler, thinner, auxiliary agent and metallic pigment 12: 4: 70 by weight ratio: 6: 8 formulated.
Weathering resistance resin of the present invention is the acryl acrylic resin.
Filler of the present invention is a Paris white.
Thinner of the present invention is weak dissolubility aliphatic hydrocarbon.
Auxiliary agent of the present invention is the flow agent class.
Metallic pigment of the present invention are titanium dioxide.
Inspection after construction of the present invention is reported as follows:
| Test event | Standard-required (acceptable end product) | Measured result | The individual event conclusion |
| At condition in container | Mixing the back does not have firmly soon, shows off uniform state | Meet the requirements | Qualified |
| Application property | It is accessible to brush two roads | Meet the requirements | Qualified |
| Appearance of film | Appearance of film is normal | Beige, film evenly, brush mark is not obvious, do not have pin hole not have sagging, appearance of film is normal | Qualified |
| Time of drying (h) | ≤2 | ＜1 | Qualified |
| Contrast ratio (white and light color) | ≥0.90 | 0.97 | Qualified |
| Water tolerance (96h) | No abnormal | No abnormal | Qualified |
| Alkali resistance (48h) | No abnormal | No abnormal | Qualified |
| Abrasion resistance (inferior) | ≥1000 | ＞2000 | Qualified |
| The slurry freeze-thaw resistance | Never degenerate | Never degenerate | Qualified |
| Coating temperature-change resistance (10 circulations) | No abnormal | No abnormal | Qualified |
Antifouling property of the present invention and antistatic property are extremely strong, and be wear-resisting, corrosion resistance nature is good, and color and luster is stable, and cohesive force is strong, and cellulose is not gone mouldy, the hardness height, and superpower self-cleaning function, scrubbing resistance, ageing-resistant, can match in excellence or beauty with aluminium sheet.It is the important behaviour form that the modern chemistry material is covered with paint, lacquer, colour wash, etc. as building, has extremely strong practicality, science, economy and aesthetic effect, meets the weather and the architectural feature of China.
Claims (3)
1, a kind of high performance weak solvent resin outer wall surface slurry is characterized in that: by weathering resistance resin, filler, thinner, auxiliary agent and metallic pigment by weight ratio 10～12: 2～5: 70～75: 6～7: 2～8 is formulated, wherein:
Described weathering resistance resin is an acryl resin, or silicone resin, or fluoro-resin;
Described filler is talcum powder class or lime carbonate class or swelling great soil group;
Described thinner is no benzene class aliphatics innoxious solvent;
Described auxiliary agent is thixotropic agent class or flow agent class;
Described pigment is nanosize metal oxide class pigment.
2, a kind of high performance weak solvent resin outer wall surface slurry according to claim 1 is characterized in that: by weathering resistance resin, filler, thinner, auxiliary agent and metallic pigment 10: 3: 75 by weight ratio: 7: 5 formulated.
3, a kind of high performance weak solvent resin outer wall surface slurry according to claim 1 is characterized in that: by weathering resistance resin, filler, thinner, auxiliary agent and metallic pigment 12: 4: 70 by weight ratio: 6: 8 formulated.