CN116333628A - 一种保温隔热的复合型膜 - Google Patents
一种保温隔热的复合型膜 Download PDFInfo
- Publication number
- CN116333628A CN116333628A CN202310290174.5A CN202310290174A CN116333628A CN 116333628 A CN116333628 A CN 116333628A CN 202310290174 A CN202310290174 A CN 202310290174A CN 116333628 A CN116333628 A CN 116333628A
- Authority
- CN
- China
- Prior art keywords
- layer
- substrate layer
- release
- pet substrate
- polypropylene film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种保温隔热的复合型膜，包括PET基材层和聚丙烯薄膜，PET基材层上表面镀覆有第一气凝胶薄层，第一气凝胶薄层与聚丙烯薄膜之间通过一亚克力胶粘层连接，PET基材层的下表面涂覆有一压敏胶粘层，压敏胶粘层与PET基材层相背的表面贴覆有离型材料层，离型材料层由第二气凝胶薄层、离型剂涂层和离型基材层组成，离型剂涂层和离型基材层接触的表面间隔分布有若干个凸起部。复合进第一气凝胶薄层和第二气凝胶薄层，气凝胶材料具有超强的隔热耐高温的性能，且质量轻，弹性高，则大幅度的增强了本发明中复合型膜的隔热性能。
Description
技术领域
本发明涉及薄膜技术领域，具体为一种保温隔热的复合型膜。
背景技术
薄膜是一种薄而软的透明薄片。用塑料、胶粘剂、橡胶或其他材料制成。隔热膜的使用可以大大提升室内的保温效果，降低空调等制冷设备的能耗，隔热膜主要是通过阻隔热能的传递来实现上述目的，并广泛地应用于交通工具和建筑物上，如公交车、阳台、玻璃幕墙等等。目前常用的隔热膜一般为通过溅射或蒸发镀膜等方式形成具有防红外层的隔热膜，以减弱热辐射，从而达到隔热降温的目的。然而，上述隔热膜不能实现较高的隔热效果。
发明内容
本发明的目的在于提供一种保温隔热的复合型膜，以解决上述背景技术中提出的问题。
为了解决上述技术问题，本发明提供如下技术方案：一种保温隔热的复合型膜，包括PET基材层和聚丙烯薄膜，所述PET基材层上表面镀覆有第一气凝胶薄层，所述第一气凝胶薄层与聚丙烯薄膜之间通过一亚克力胶粘层连接；
所述PET基材层的下表面涂覆有一压敏胶粘层，所述压敏胶粘层与PET基材层相背的表面贴覆有离型材料层，所述离型材料层由第二气凝胶薄层、离型剂涂层和离型基材层组成；所述离型剂涂层和离型基材层接触的表面间隔分布有若干个凸起部。
所述聚丙烯薄膜厚度为70μm-90μm。
所述PET基材层的厚度为100-300μ。
所述聚丙烯薄膜的上部表面设有防刮伤表层。
所述离型材料层的表面设有吸附粘接层。
与现有技术相比，本发明所达到的有益效果是：其PET层透光率高，金属层会选择性的将阳光中的各种热能源，包括红外线、紫外线及可见光热能反射回去，再配合PET层对太阳热辐射的吸收后，再二次向外释放，随着室外的空气流动带走一部份热量，从而有效起到隔热的作用，而本发明的复合型膜在PET层的基础上，复合进第一气凝胶薄层和第二气凝胶薄层，气凝胶材料具有超强的隔热爱高温的性能，且质量轻，弹性高，则大幅度的增强了本发明中复合型膜的隔热性能。
附图说明
附图用来提供对本发明的进一步理解，并且构成说明书的一部分，并不构成对本发明的限制。在附图中：
图1是本发明实施例1的结构示意图；
图2是本发明实施例2的结构示意图；
图中：1PET基材层；2聚丙烯薄膜；3第一气凝胶薄层；4亚克力胶粘层；5压敏胶粘层；6离型材料层；61第二气凝胶薄层；62离型剂涂层；63离型基材层；7凸起部；8防刮伤表层；9吸附粘接层。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
请参阅图1，本发明提供技术方案：一种保温隔热的复合型膜，包括PET基材层1和聚丙烯薄膜2，PET基材层1上表面镀覆有第一气凝胶薄层3，第一气凝胶薄层3与聚丙烯薄膜2之间通过一亚克力胶粘层4连接；
PET基材层1的下表面涂覆有一压敏胶粘层5，压敏胶粘层5与PET基材层1相背的表面贴覆有离型材料层6，离型材料层6由第二气凝胶薄层61、离型剂涂层62和离型基材层63组成；离型剂涂层62和离型基材层63接触的表面间隔分布有若干个凸起部7。
其离型材料层6除了第二气凝胶薄层61外，还包括离型剂涂层62和离型基材层63组成，离型剂涂层62和离型基材层63组成接触的表面间隔分布有若干个凸起部7，提高了离型剂涂层62和离型基材层63的结合力，结合更加牢固、可靠，从而使得镜面防爆膜贴合的更加牢固
聚丙烯薄膜2厚度为70μm-90μm。
PET基材层1的厚度为100-300μ。
本发明的保温隔热的复合型膜与现有技术常规隔热保温膜的性能比较如下表：
| 项次 | 常规值 | 本实施例值 |
| 导热系数(w/m·K) | ≤0.1 | 0.031 |
| 热阻值(M2/K·W) | ≥0.08 | 0.132 |
| 反射率％ | ≥85％ | 95％ |
| 拉伸强度/Kpa | ≥15.5 | 711 |
| 断裂伸长率 | ≤140％ | 72％ |
实施例2
请参阅图2，聚丙烯薄膜2的上部表面设有防刮伤表层8；
离型材料层6的表面设有吸附粘接层9。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (5)
1.一种保温隔热的复合型膜，其特征在于：包括PET基材层(1)和聚丙烯薄膜(2)，所述PET基材层(1)上表面镀覆有第一气凝胶薄层(3)，所述第一气凝胶薄层(3)与聚丙烯薄膜(2)之间通过一亚克力胶粘层(4)连接；
所述PET基材层(1)的下表面涂覆有一压敏胶粘层(5)，所述压敏胶粘层(5)与PET基材层(1)相背的表面贴覆有离型材料层(6)，所述离型材料层(6)由第二气凝胶薄层(61)、离型剂涂层(62)和离型基材层(63)组成，所述离型剂涂层(62)和离型基材层(63)接触的表面间隔分布有若干个凸起部(7)。
2.根据权利要求1所述的一种保温隔热的复合型膜，其特征在于：所述聚丙烯薄膜(2)厚度为70μm-90μm。
3.根据权利要求1所述的一种保温隔热的复合型膜，其特征在于：所述PET基材层(1)的厚度为100-300μ。
4.根据权利要求1所述的一种保温隔热的复合型膜，其特征在于：所述聚丙烯薄膜(2)的上部表面设有防刮伤表层(8)。
5.根据权利要求1所述的一种保温隔热的复合型膜，其特征在于：所述离型材料层(6)的表面设有吸附粘接层(9)。