CN116239959A - 一种水印全息防伪标识膜 - Google Patents
一种水印全息防伪标识膜 Download PDFInfo
- Publication number
- CN116239959A CN116239959A CN202211718580.9A CN202211718580A CN116239959A CN 116239959 A CN116239959 A CN 116239959A CN 202211718580 A CN202211718580 A CN 202211718580A CN 116239959 A CN116239959 A CN 116239959A
- Authority
- CN
- China
- Prior art keywords
- layer
- watermark
- holographic
- color
- counterfeiting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水印全息防伪标识膜，属于防伪标识领域，包括依次层叠设置的基膜层、全息色层、镀层、不干胶层，还包括设置在所述基膜层和所述全息色层之间的水印层，所述水印层由丙烯酸树脂和固化剂经过涂布烘干交联固化而成，用于吸收经镀层反射穿过所述全息色层中的冷色光，使全息色层产生色偏现象。本发明水印层通过特殊的丙烯酸树脂交联固化而成，其交联固化程度和厚度会影响水印层对色层中冷色光的吸收程度。通过控制配方比例、涂布克重、烘干工艺调节水印层的交联固化程度和厚度，达到对色层中冷色光的特定吸收量，干扰翻版和调色，增大仿制难度，产生更强的防伪效果。
Description
技术领域
本发明属于防伪标识领域，具体涉及一种水印全息防伪标识膜。
背景技术
为了保护消费者及商家合法权益，商家采用多种防伪手段对商品进行防伪标示，目前多采用在商品表面粘贴防伪标签的方式，防伪标签是不干胶产品的一类，能粘贴、印刷、转移在标的物表面，或标的物包装上，或标的物附属物(如商品挂牌、名片以及防伪证卡)上，发挥防伪作用。
全息防伪标签即是防伪标签的一种类型，图1是常用的全息防伪标签的组成示意图，参见图1，全息防伪标签一般由基膜层1、全息色层3、镀层4、不干胶层5组成，当撕下基膜层1后显现出防伪图案。
目前全息防伪标识膜的颜色由全息色层添加的染料颜色决定，易于观察；导致全息防伪标识易于被仿制，容易调色和翻版，造成防伪标识不能防伪的局面，无法发挥真正的防伪效果。
发明内容
针对现有技术的以上缺陷或改进需求中的一种或者多种，本发明提供了一种水印全息防伪标识膜，解决现有全息防伪标识膜容易调色和翻版的问题。
为实现上述目的，本发明提供一种水印全息防伪标识膜，其包括依次层叠设置的基膜层、全息色层、镀层、不干胶层，还包括设置在所述基膜层和所述全息色层之间的水印层，所述水印层可以吸收所述全息色层中的冷色光。
进一步的，所述水印层经过丙烯酸树脂和固化剂交联固化而成。
进一步的，所述水印层中丙烯酸树脂和固化剂组分配比为3:1至1:1。
进一步的，所述水印层厚度为1～2μm。
进一步的，所述基膜层为PET膜。
进一步的，所述全息色层厚度为1～4μm，成分为复合涂料。
进一步的，所述镀层为金属铝层或介质层，厚度为20～60nm。
进一步的，所述不干胶层厚度为2～6μm。
上述改进技术特征只要彼此之间未构成冲突就可以相互组合。
总体而言，通过本发明所构思的以上技术方案与现有技术相比，具有的有益效果包括：
（1）本发明的水印全息防伪标识膜，其通过增加水印层，当光照经镀层反射后穿过全息色层时，其中冷色光被吸收，产生偏色现象，增加水印装饰效果。
（2）本发明的水印全息防伪标识膜，其水印层通过特殊的丙烯酸树脂交联固化而成，其交联固化程度和厚度会影响水印层对色层中冷色光的吸收程度。通过控制配方比例、涂布克重、烘干工艺调节水印层的交联固化程度和厚度，达到对色层中冷色光的特定吸收量，干扰翻版和调色，增大仿制难度，产生更强的防伪效果。
附图说明
为了更清楚地说明本发明实施例中的技术方案，下面将对实施例中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1是常用的全息防伪标识膜整体结构示意图；
图2是本发明实施例中一种水印全息防伪标识膜的整体结构示意图；
在所有附图中，同样的附图标记表示相同的技术特征，具体为：
1、基膜层；2、水印层；3、全息色层；4、镀层；5、不干胶层。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合附图及实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅用以解释本发明，并不用于限定本发明。此外，下面所描述的本发明各个实施方式中所涉及到的技术特征只要彼此之间未构成冲突就可以相互组合。
在本发明的描述中，需要理解的是，术语“中心”、“纵向”、“横向”、“长度”、“宽度”、“厚度”、“上”、“下”、“前”、“后”、“左”、“右”、“竖直”、“水平”、“顶”、“底”、“内”、“外”、“顺时针”、“逆时针”、“轴向”、“径向”、“周向”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
此外，术语“第一”、“第二”仅用于描述目的，而不能理解为指示或暗示相对重要性或者隐含指明所指示的技术特征的数量。由此，限定有“第一”、“第二”的特征可以明示或者隐含地包括至少一个该特征。在本发明的描述中，“多个”的含义是至少两个，例如两个，三个等，除非另有明确具体的限定。
实施例：
请参阅图2，本发明优选实施例中的一种水印全息防伪标识膜包括依次层叠设置的基膜层1、全息色层3、镀层4、不干胶层5，还包括设置在所述基膜层1和所述全息色层3之间的水印层2，用于吸收经由所述镀层4反射穿过所述全息色层3中的冷色光。
本实施例中，在制造水印全息防伪标识膜时，在基膜层1上用局部图文型网纹辊涂布水印层2，再在水印层2上用满幅面的网纹辊涂布全息色层3，在全息色层3上模压全息防伪信息后，真空蒸镀形成镀层4，最后在镀层4上涂布不干胶层5。
在本实施例中，核心主要在水印层2上，水印层2采用丙烯酸树脂和固化剂经过涂布烘干交联固化而成，丙烯酸树脂和固化剂组分配比为3:1，涂布后该层呈无色或淡黄色透明，在其上继续涂布全息色层3时，透过水印层2会吸收全息色层3中的冷色光，导致从基膜层1一侧观察全息色层3的防伪信息会出现色偏，对于无论是翻版还是调色，水印层的存在都会产生强干扰，导致翻版和调色失败，起到更强的防伪功能。
水印层2中丙烯酸树脂和固化剂交联固化程度和厚度会影响水印层2对全息色层3中冷色光的吸收程度。通过控制配方比例、涂布克重、烘干工艺调节水印层的交联固化程度和厚度，达到对色层中冷色光的特定吸收量。
本实施例中，所述水印层2厚度为1～2μm。
在具体实施例中，层叠设置的基膜层1、全息色层3、镀层4、不干胶层5，还包括设置在所述基膜层1和所述全息色层3之间的水印层2。其中，
基膜层1可以采用各种常规适于加工激光全息图案的薄膜材料，譬如PET双向拉伸膜等，是整个水印全息防伪标识膜的支撑结构，对整个水印全息防伪标识膜起到覆盖和 保护的作用。一般来说，基膜层1为透明有色结构，以便透过该层结构获取水印全息防伪标识膜其他层结构中的信息内容。
本实施例中，基膜层1采用PET膜，所述基膜层1本体呈现第一颜色且透明，该第一颜色具体种类不做限定。
水印层2是水印全息防伪标识膜的核心结构。所述水印层2经过在基膜层1上用局部图文型网纹辊涂布烘干而成，在使用涂布机涂布烘干时，涂布材料成分为丙烯酸树脂和固化剂；丙烯酸树脂和固化剂组分配比为3:1至1:1，5节烘箱时涂布烘干温度分别设置为80-100-150-150-100℃至80-130-170-170-130℃，车速60至100米/分钟。水印层2由于特殊分子结构，对冷色光具有吸收作用。
本实施例中，水印层2厚度1～2μm，采用组分配比3:1的丙烯酸树脂和固化剂经过涂布烘烤交联固化而成，丙烯酸树脂可以采用市面上的成熟产品，如武汉金和成化工的L-60A；固化剂也可以采用市面上的成熟产品，如武汉金和成化工的L-60B，5节烘箱时涂布烘干温度分别设置为80-100-150-150-100℃，车速60/分钟，得到的水印层2呈现无色或淡黄色透明。
全息色层3上设置有一种或多种能够形成起防伪作用的全息图案的微结构，该微结构可以仅设置在全息色层3靠近镀层4的一侧表面，也可以贯穿整个全息色层3，甚至在全息色层3与水印层2接触的一侧表面上形成微结构。在镀层4的作用下，该微结构可以呈现基于衍射的单色、动态、同位异像、深度、全息透镜、紫光和基于反射的猫眼、铂金浮雕及零级衍射、纳米光学等视觉效果的全息图案，并形成一定的信息表达。该微结构本体呈现第二颜色，第二颜色不做具体限制。在本实施例水印全息防伪标识膜的制备过程中，全息图案可以用于提供包括生产厂家、品牌标志等在内的基本信息，也可以用于制作提示消费者揭开验证标识物商品真伪的信息等，不作具体限制。全息色层3厚度为1～4μm，成分采用复合涂料，可以采用市面上的成熟材料，如邦固化学的PET-308-40。
本实施例中，全息色层3上模压有全息防伪信息，厚度为4μm，成分为丙烯酸树脂。
镀层4主要作用在于防止光线完全穿过，水印全息防伪标识膜在使用时，光线入射后，在镀层4与全息色层3的微结构之间的界面形成反射，使得全息图案可以呈现出来。镀层4可以采用金属铝层或介质层，金属铝层、介质层均可以通过真空蒸镀的方式制备。当采用金属铝层时，铝层厚度为300～500AI。介质层选自硫化锌、氟化镁、 二氧化硅、二氧化钛中的任意一种或多种，介质层的透光率为60～80％。
本实施例中，镀层4采用硫化锌介质层，厚度为20～60nm。
不干胶层5的表面复合有硅油纸，在使用时，撕除硅油纸，将水印全息防伪标识膜的不干胶层5面向需要粘贴的包装表面贴好，用户揭开基膜层1时即可产生水印全息防伪效果。
本实施例中，不干胶层5的厚度为2～6μm。
本实施例中，基膜层1、水印层2、全息色层3处于叠加状态。全息色层3的第二颜色在水印层2的作用下，冷色光被吸收，产生偏色现象，呈现出第三颜色；当基膜层1未撕下时，水印全息防伪标识膜呈现第一颜色和第三颜色的叠加色，当基膜层1撕下时，呈现第三颜色。所以无论是否撕下基膜层1，都无法判定所述第二颜色具体为何种颜色，对于他人的调色和翻版，水印层的存在都会产生强干扰，导致翻版和调色失败，起到更强的防伪功能。
本领域的技术人员容易理解，以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种水印全息防伪标识膜，包括依次层叠设置的基膜层（1）、全息色层（3）、镀层（4）、不干胶层（5），其特征在于，
还包括设置在所述基膜层（1）和所述全息色层（3）之间的水印层（2），用于吸收经所述镀层（4）反射穿过所述全息色层（3）中的冷色光。
2.根据权利要求1所述的水印全息防伪标识膜，其特征在于，所述水印层（2）由丙烯酸树脂和固化剂交联固化而成。
3.根据权利要求2所述的水印全息防伪标识膜，其特征在于，所述水印层（2）中丙烯酸树脂和固化剂组分配比为3:1至1:1。
4.根据权利要求3所述的水印全息防伪标识膜，其特征在于，所述水印层（2）厚度为1～2μm。
5.根据权利要求1所述的水印全息防伪标识膜，其特征在于，所述基膜层（1）为PET膜。
6.根据权利要求1所述的水印全息防伪标识膜，其特征在于，所述全息色层（3）厚度为1～4μm，成分为复合涂料。
7.根据权利要求1所述的水印全息防伪标识膜，其特征在于，所述镀层（4）为金属铝层或介质层，厚度为20～60nm。
8.根据权利要求1所述的水印全息防伪标识膜，其特征在于，所述不干胶层（5）厚度为2～6μm。