CN116239911B - 一种零甲醛、不含可溶性重金属腻子及其生产工艺 - Google Patents
一种零甲醛、不含可溶性重金属腻子及其生产工艺 Download PDFInfo
- Publication number
- CN116239911B CN116239911B CN202310427950.1A CN202310427950A CN116239911B CN 116239911 B CN116239911 B CN 116239911B CN 202310427950 A CN202310427950 A CN 202310427950A CN 116239911 B CN116239911 B CN 116239911B
- Authority
- CN
- China
- Prior art keywords
- parts
- putty
- powder
- free
- ruyi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于墙面装饰材料技术领域，具体涉及一种零甲醛、不含可溶性重金属腻子及其生产工艺。所述腻子包括以下重量份的组分：50‑60份滑石粉；20‑25份重质碳酸钙粉；10‑15份电气石负离子粉；5‑10份硅藻土；5‑8份如意草提取物；2‑5份可再分散型乳胶粉；1‑3份阳离子聚丙烯酰胺衍生物；腻子的生产工艺为：按照选定重量配比，依次将滑石粉、重质碳酸钙粉、电气石负离子粉、硅藻土、如意草提取物、可再分散型乳胶粉、阳离子聚丙烯酰胺衍生物放入混合装置的内部，搅拌均匀得到腻子。本发明的腻子环保、无毒无害，不含甲醛及可溶性重金属，具有良好耐水性能、抗菌防霉性能及抗裂性能，更能满足市场需求。
Description
技术领域
本发明属于墙面装饰材料技术领域，具体涉及一种零甲醛、不含可溶性重金属腻子及其生产工艺。
背景技术
腻子是用来墙面修补找平的一种基材，主要目的是填充施工面的空隙及矫正施工面的空隙和矫正施工面的曲线偏差，为获得均匀、平滑的漆面打好基础。现有腻子大多采用滑石粉、双飞粉、羧甲基纤维素和聚乙烯醇缩甲醛胶黏剂等材料制备而成，虽然原料成本低，但是工艺复杂，特别是含有甲醛等有害物质，对人的神经系统有很大的影响，尤其是婴幼儿以及年老体弱者危害更大，甚至引起严重的疾病。
申请号为201310358531.3的专利公开了一种天然植物胶腻子，其配方的组成为：瓜尔豆胶0.2-0.4，改性天然淀粉0.4-0.6，腻子专用胶粉0.05-0.15，羟乙基纤维素0.15-0.3，防腐防霉剂0.05-0.1，悬浮触变改性剂0.3-1.5，灰钙粉33-36，滑石粉4-6，重质碳酸钙32-35，水25.5-27，该腻子具有环保、不含甲醛等有害物质的优点，但所使用的植物胶存在胶接强度较低，耐水性和耐霉性较差的缺点。申请号为202210006170.5的专利公开了一种环保型净味抗菌内墙腻子，包括以下重量份的原料：碳酸钙35-40份、灰钙粉20-28份、硅藻土8-14份、钛白粉5-13份、白水泥50-67份、方解石3-6份、电气石负离子粉12-24份、防腐剂8-10份、防霉剂5-7份；该腻子可以散发负氧离子净化除尘，改善室内空气环境，通过添加防腐剂和防霉剂，可以起到抗菌的作用，但所添加的防腐剂(溴代乙酸苄酯)和防霉剂(对氯间二甲基苯酚)为有机试剂，尤其对氯间二甲基苯酚具有毒性，会随水蒸气一起挥发，导致该腻子粉使用一段时间后，防霉效果差，同时该专利并未涉及到腻子抗裂性能等方面的改进。
因此，开发出一种既环保、无毒无害，又具有良好耐水性、抗菌防霉性及抗裂性能的高品质腻子，对于保证内墙涂料装修质量及安全至关重要。
发明内容
本发明的目的在于针对现有技术的不足，提供一种零甲醛、不含可溶性重金属腻子及其生产工艺，该腻子环保、无毒无害，不含甲醛及可溶性重金属，具有良好耐水性能、抗菌防霉性能及抗裂性能，更能满足市场需求。
本发明为实现上述目的所采取的技术方案为：
一种零甲醛、不含可溶性重金属腻子，包括以下重量份的组分：50-60份滑石粉；20-25份重质碳酸钙粉；10-15份电气石负离子粉；5-10份硅藻土；5-8份如意草提取物；2-5份可再分散型乳胶粉；1-3份阳离子聚丙烯酰胺衍生物；所述滑石粉的粒度为400-600目；所述电气石负离子粉粒度为300-400目；所述硅藻土粒度为400-500目；所述重质碳酸钙粒度为400-500目，白度为95，碳酸钙的含量为98-99％。
所述阳离子聚丙烯酰胺衍生物的制备方法为：
S1、将聚丙烯酰胺、三乙胺依次加入到乙二醇中，搅拌下滴加环氧氯丙烷，升温至40-50℃，反应4-6h，然后降温至30℃，滴加对羟基苯甲酰氯，继续反应2-3h后得到聚丙烯酰胺衍生物；所述聚丙烯酰胺衍生物的反应过程如下：
S2、将聚丙烯酰胺衍生物、四丁基溴化铵、十二烷基二甲基叔胺加入到80％的异丙醇中，升温至83℃，回流反应8-10h，得到阳离子聚丙烯酰胺衍生物；所述阳离子聚丙烯酰胺衍生物的反应过程如下：
进一步地，步骤S1中所述聚丙烯酰胺、环氧氯丙烷、三乙胺、对羟基苯甲酰氯的质量比为1:0.1-0.2:0.3-0.4:0.1-0.2；步骤S2中所述聚丙烯酰胺衍生物、十二烷基二甲基叔胺、四丁基溴化铵的质量比为1:0.2-0.4:0.4-0.5。
进一步地，所述如意草提取物的制备方法为：
(1)将如意草清洗去杂后，置于烘箱内45-50℃下烘干至恒重，粉碎成粉末，过300目筛得到如意草粉；
(2)将如意草粉加入到75％乙醇溶液中，升温至40-50℃，超声提取2-4h，然后加入0.1％的阳离子聚丙烯酰胺衍生物溶液进行后处理，继续超声20-30min，离心分离后，上清液经浓缩、喷雾干燥后得到如意草提取物；其中如意草提取物与阳离子聚丙烯酰胺衍生物的质量比为1:0.1-0.15。
本发明提供了一种零甲醛、不含可溶性重金属腻子的生产工艺，按照选定重量配比，依次将滑石粉、重质碳酸钙粉、电气石负离子粉、硅藻土、如意草提取物、可再分散型乳胶粉、阳离子聚丙烯酰胺衍生物放入混合装置的内部，搅拌均匀得到腻子；其中搅拌速度为800-1000r/min，搅拌时间为20-30min。
本发明具有如下有益效果：
本发明以聚丙烯酰胺为原料进行改性，引入含有刚性苯环的对羟基苯甲酸酯侧链、疏水作用的长链烷烃及阳离子季铵盐结构，得到阳离子聚丙烯酰胺衍生物，阳离子聚丙烯酰胺衍生物的加入能够明显提高腻子的抗裂性能、耐水性及抗菌防腐性能；同时阳离子季铵盐中带正电荷的氮原子通过静电作用吸引电气石负离子粉所携带的负电荷，能够提高电气石负离子粉的分散性，进而充分发挥其抗菌杀菌作用；将阳离子聚丙烯酰胺衍生物用于如意草提取的后处理中，得到了总生物碱含量较高的如意草提取物，如意草提取物的加入，进一步增强腻子的抗菌性能。本发明提供的一种零甲醛、不含可溶性重金属腻子，该腻子环保、无毒无害，不含甲醛及可溶性重金属，具有良好耐水性能、抗菌防霉性能及抗裂性能，更能满足市场需求。
具体实施方式
下面将结合本申请实施例，对本申请实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本申请一部分实施例，而不是全部的实施例。基于本申请中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本申请保护的范围。
下述实施例、对比例中所用原料均为普通市售产品。聚丙烯酰胺CAS号9003-05-8；环氧氯丙烷CAS号106-89-8；对羟基苯甲酰氯CAS号28141-24-4；三乙胺CAS号121-44-8；四丁基溴化铵CAS号1643-19-2；十二烷基二甲基叔胺CAS号112-18-5；高锰酸钾CAS号7722-64-7；丙酮CAS号67-64-1；乙二醇CAS号107-21-1；异丙醇CAS号67-63-0。
实施例1
本实施例提供了一种零甲醛、不含可溶性重金属腻子及其生产工艺。
一种零甲醛、不含可溶性重金属腻子，包括以下重量份的组分：60份滑石粉；25份重质碳酸钙粉；15份电气石负离子粉；10份硅藻土；8份如意草提取物；5份可再分散型乳胶粉；3份阳离子聚丙烯酰胺衍生物；其中滑石粉的粒度为600目，电气石负离子粉粒度为400目；硅藻土粒度为500目；所述重质碳酸钙粒度为500目，白度为95，碳酸钙的含量为99％。
阳离子聚丙烯酰胺衍生物的制备方法为：
S1、将聚丙烯酰胺(分子量600万)、三乙胺依次加入到乙二醇中，搅拌下滴加环氧氯丙烷，升温至50℃，反应5h，然后降温至30℃，滴加对羟基苯甲酰氯，继续反应2h，反应完成后，自然降至室温，使用丙酮(与乙二醇相同体积)进行沉淀提纯，沉淀物在45℃的真空干燥箱中干燥10h，得到聚丙烯酰胺衍生物，通过元素分析法测定环氧氯丙烷的取代度为30.5％；所制得的聚丙烯酰胺衍生物在紫外灯(254nm)下，有荧光吸收，并且能够使酸性高锰酸钾溶液褪色；其中聚丙烯酰胺、环氧氯丙烷、三乙胺、对羟基苯甲酰氯的质量比为1:0.2:0.4:0.2；聚丙烯酰胺与乙二醇的质量比为1:15；所述聚丙烯酰胺衍生物的反应过程如下：
S2、将聚丙烯酰胺衍生物、四丁基溴化铵、十二烷基二甲基叔胺加入到80％的异丙醇中，升温至83℃，回流反应10h，反应完成后，自然降至室温，使用丙酮(与80％的异丙醇相同体积)进行沉淀提纯，沉淀物在45℃的真空干燥箱中干燥10h，得到阳离子聚丙烯酰胺衍生物；所制得的阳离子聚丙烯酰胺衍生物在紫外灯(254nm)下，有荧光吸收，能使酸性高锰酸钾溶液褪色；其中聚丙烯酰胺衍生物、十二烷基二甲基叔胺、四丁基溴化铵的质量比为1:0.3:0.5；聚丙烯酰胺衍生物与80％的异丙醇的质量比为1:15；阳离子聚丙烯酰胺衍生物的反应过程如下：
如意草提取物的制备方法为：
(1)将如意草清洗去杂后，置于烘箱内50℃下烘干至恒重，粉碎成粉末，过300目筛得到如意草粉；
(2)将如意草粉加入到75％乙醇溶液中，升温至50℃，超声提取4h，然后加入0.1％的阳离子聚丙烯酰胺衍生物溶液进行后处理，继续超声30min，离心分离后，上清液经浓缩、喷雾干燥后得到如意草提取物；其中如意草提取物与75％乙醇的固液比为1g/15mL；如意草提取物与阳离子聚丙烯酰胺衍生物的质量比为1:0.1；如意草中含有的生物碱为乙酸紫堇灵、消旋紫堇灵、必枯枯灵、左旋紫堇灵、紫堇文碱、原阿片碱及刻叶紫堇胺盐酸盐，采用药典中的高效液相法测定如意草提取物中总生物碱含量为58.2％；如果超声提取后不使用0.1％的阳离子聚丙烯酰胺衍生物溶液进行后处理，二次离心分离后，上清液经浓缩、喷雾干燥后所得到的如意草提取物中总生物碱含量为34.5％。
腻子的生产工艺为：按照选定重量配比，依次将滑石粉、重质碳酸钙粉、电气石负离子粉、硅藻土、如意草提取物、可再分散型乳胶粉、阳离子聚丙烯酰胺衍生物放入混合装置的内部，搅拌均匀得到腻子；其中搅拌速度为1000r/min，搅拌时间为20min。
实施例2
本实施例提供了一种零甲醛、不含可溶性重金属腻子及其生产工艺，与实施例1相比腻子的原料配比不同。
一种零甲醛、不含可溶性重金属腻子，包括以下重量份的组分：55份滑石粉；23份重质碳酸钙粉；13份电气石负离子粉；8份硅藻土；6份如意草提取物；3份可再分散型乳胶粉；2份阳离子聚丙烯酰胺衍生物；其中滑石粉的粒度为500目，电气石负离子粉粒度为300目；硅藻土粒度为400目；所述重质碳酸钙粒度为400目，白度为95，碳酸钙的含量为99％。
其中阳离子聚丙烯酰胺衍生物的制备方法、如意草提取物的制备方法、腻子的生产工艺均与实施例1相同。
实施例3
本实施例提供了一种零甲醛、不含可溶性重金属腻子及其生产工艺，与实施例1相比腻子的原料配比及制备方法不同。
一种零甲醛、不含可溶性重金属腻子，包括以下重量份的组分：50份滑石粉；20份重质碳酸钙粉；10份电气石负离子粉；5份硅藻土；5份如意草提取物；2份可再分散型乳胶粉；1份阳离子聚丙烯酰胺衍生物；其中滑石粉的粒度为600目，电气石负离子粉粒度为400目；硅藻土粒度为500目；所述重质碳酸钙粒度为500目，白度为95，碳酸钙的含量为99％。
其中阳离子聚丙烯酰胺衍生物的制备方法、如意草提取物的制备方法均与实施例1相同。
腻子的生产工艺为：按照选定重量配比，依次将滑石粉、重质碳酸钙粉、电气石负离子粉、硅藻土、如意草提取物、可再分散型乳胶粉、阳离子聚丙烯酰胺衍生物放入混合装置的内部，搅拌均匀得到腻子；其中搅拌速度为800r/min，搅拌时间为30min。
对比例1
本对比例提供一种零甲醛、不含可溶性重金属腻子及其生产工艺，与实施例1相比腻子原料组成不同。
一种零甲醛、不含可溶性重金属腻子，包括以下重量份的组分：60份滑石粉；25份重质碳酸钙粉；15份电气石负离子粉；10份硅藻土；8份如意草提取物；5份可再分散型乳胶粉；3份聚丙烯酰胺衍生物；其中滑石粉的粒度为600目，电气石负离子粉粒度为400目；硅藻土粒度为500目；所述重质碳酸钙粒度为500目，白度为95，碳酸钙的含量为99％。
其中聚丙烯酰胺衍生物的制备方法、如意草提取物的制备方法、腻子的生产工艺均与实施例1相同。
对比例2
本对比例提供一种零甲醛、不含可溶性重金属腻子及其生产工艺，与实施例1相比腻子原料组成不同。
一种零甲醛、不含可溶性重金属腻子，包括以下重量份的组分：60份滑石粉；25份重质碳酸钙粉；15份电气石负离子粉；10份硅藻土；8份如意草提取物；5份可再分散型乳胶粉；3份聚丙烯酰胺；其中滑石粉的粒度为600目，电气石负离子粉粒度为400目；硅藻土粒度为500目；所述重质碳酸钙粒度为500目，白度为95，碳酸钙的含量为99％。
其中如意草提取物的制备方法、腻子的生产工艺均与实施例1相同。
对比例3
本对比例提供一种零甲醛、不含可溶性重金属腻子及其生产工艺，与实施例1相比腻子原料组成不同。
一种零甲醛、不含可溶性重金属腻子，包括以下重量份的组分：60份滑石粉；25份重质碳酸钙粉；15份电气石负离子粉；10份硅藻土；5份可再分散型乳胶粉；3份阳离子聚丙烯酰胺衍生物；其中滑石粉的粒度为600目，电气石负离子粉粒度为400目；硅藻土粒度为500目；所述重质碳酸钙粒度为500目，白度为95，碳酸钙的含量为99％。
其中阳离子聚丙烯酰胺衍生物的制备方法、腻子的生产工艺均与实施例1相同。
相关测试
1.有害物质检测
按照GB18582-2008标准测试实施例1-3中有害物质VOC、游离甲醛、可溶性重金属(Pb、Cd、Cr、Hg)的含量，其中VOC限度为≤15g/kg，游离甲醛限度为≤100mg/kg，可溶性重金属Pb限度为≤90mg/kg，可溶性重金属Cd限度为≤75mg/kg，可溶性重金属Cr、Hg限度均为≤60mg/kg；结果如表1所示。
表1有害物质测试结果
由表1结果可知，实施例1-3所制得的腻子中均未检出VOC、游离甲醛及可溶性重金属(Pb、Cd、Cr、Hg)，说明本发明能够制备得到一种零甲醛、不含可溶性重金属的环保腻子。
2.相关性能测试
根据建材行业标准JC/T298-2010规定的方法测试上述实施例1-3、对比例1-3所制得的腻子及普通腻子粉(购自沈阳丽饰家新型建材有限公司：不含甲醛的环保内墙腻子粉)的表干时间，粘结、抗折、抗压强度相关性能进行测试，结果如表2所示。
表2腻子相关性能测试结果
| 组别 | 表干时间/min | 粘结强度/MPa | 抗折强度/MPa | 抗压强度/MPa |
| 实施例1 | 28 | 1.4 | 7.8 | 9.8 |
| 实施例2 | 30 | 1.3 | 8.0 | 9.6 |
| 实施例3 | 32 | 1.2 | 7.9 | 9.7 |
| 对比例1 | 46 | 0.72 | 3.4 | 3.9 |
| 对比例2 | 49 | 0.64 | 3.0 | 3.7 |
| 对比例3 | 47 | 0.57 | 2.9 | 3.6 |
| 普通腻子粉 | 54 | 0.32 | 1.5 | 1.9 |
由表2结果可知，实施例1-3所制得的腻子的表干时间，粘结、抗折、抗压强度要优于对比例1-3制得的腻子及普通腻子粉，其中实施例1制得的腻子表干时间最短，粘结、抗折、抗压强度最好；与对比例1(使用聚丙烯酰胺衍生物)、对比例2(使用聚丙烯酰胺)、对比例3(不含如意草提取物)、普通腻子粉相比，实施例1-3中所使用的阳离子聚丙酰胺衍生物及如意草提取物，其中阳离子聚丙酰胺衍生物结构中引入的刚性苯环结构、疏水作用的长链烷烃及阳离子季铵盐结构，具有更好的分散性，不仅能够提高腻子的机械性能，还能够使各组分在水中混合更加充分，进而制得粘结、抗折、抗压强度较好的腻子；如意草提取物中的总生物碱为含有多个苯环的小分子有机物，能够被吸附于多孔硅藻土中，有助于提高腻子的强度。
3.抗菌、防霉性能测试
按照GBT1741-2007标准测试实施例1-3、对比例1-3所制得的腻子及普通腻子粉的抗菌、防腐性能；其中防霉性能试验：将黑曲霉、土曲霉、绳状青霉、出芽短梗霉、球毛壳的混合孢子悬液喷在待测样品和培养基上，在温度28摄氏度，相对湿度90％RH以上的条件下培养28天，通过直接观测长霉程度来评价样品的防霉性能；结果如表3所示。
表3抗菌、防霉性能测试结果
由表3结果可知，实施例1-3所制得的腻子的抗菌、防霉性能均优于对比例1-3制得的腻子及普通腻子粉，其中实施例1制得的腻子的抗菌、防霉性能最好；与对比例1(使用聚丙烯酰胺衍生物)、对比例2(使用聚丙烯酰胺)、对比例3(不含如意草提取物)、普通腻子粉相比，实施例1-3中所使用的阳离子聚丙酰胺衍生物，其结构中的季铵盐结构能够明显提高腻子的抗菌作用，也能够通过静电作用吸引电气石负离子粉所携带的负电荷，提高电气石负离子粉的分散性，进而充分发挥其抗菌杀菌作用；同时结构中含有的对羟基苯甲酸酯的侧链，具有良好的防腐作用，能够提高腻子的防腐性能；如意草提取物中的总生物碱也具有良好的抗菌作用，能够进一步提高腻子的抗菌性能。
4.耐水性测试
其中实施例1-3、对比例1-3所制得的腻子及普通腻子粉的耐水性测试方法为：将腻子粉刮涂后浸泡在水中48小时观察是否出现起皮、开裂、起鼓现象，结果如表4所示。
表4腻子耐水性测试结果
由表4结果可知，实施例1-3所制得的腻子的耐水性均优于对比例1-3制得的腻子及普通腻子粉，其中实施例1制得的腻子的耐水性能最好；与对比例1(使用聚丙烯酰胺衍生物)、对比例2(使用聚丙烯酰胺)、对比例3(不含如意草提取物)、普通腻子粉相比，实施例1-3中所使用的阳离子聚丙酰胺衍生物和如意草提取物，将聚丙酰胺中亲水基团(羟基、氨基)通过改性，引入了较多数量的疏水基团(苯环、长链烷烃)，添加了如意草提取物(强脂溶性的总生物碱)，从而制得了具有良好耐水性能的腻子。
聚丙烯酰胺具有絮凝、粘合、增稠的作用，可以增强腻子抗裂性能；本发明以聚丙烯酰胺为原料进行改性，引入含有刚性苯环的对羟基苯甲酸酯侧链、疏水作用的长链烷烃及阳离子季铵盐结构，得到阳离子聚丙烯酰胺衍生物，刚性的苯环结构能够增强腻子的机械性能，进一步提升腻子强度及抗裂能力；疏水作用的长链烷烃能够增加腻子的疏水性，提高腻子的耐水性能；阳离子季铵盐结构的存在一方面具有抗菌作用，能增强腻子的抗菌性能，另一方面也能够通过静电作用吸引电气石负离子粉所携带的负电荷，提高电气石负离子粉的分散性，进而充分发挥其抗菌杀菌作用；同时结构中含有的对羟基苯甲酸酯的侧链，具有突出的抑制真菌、霉毒、细菌和藻类等微生物在有机介质中滋生的作用，能有效避免微生物污染后易发生变酸、变黑、变臭和粘度下降等腐败现象，提高了腻子的防腐性能。
如意草是罂粟科紫堇属植物，别名大理紫堇、断肠草、水黄连、水如意、五味草，主要分布于四川、贵州、云南等地，目前，如意草中已被鉴定有出含有七个生物碱，包括乙酸紫堇灵、消旋紫堇灵、必枯枯灵、左旋紫堇灵、紫堇文碱、原阿片碱及刻叶紫堇胺盐酸盐，如意草提取物中的总生物碱被证实具有良好的抗菌作用；本发明以如意草为原料，使用75％乙醇对其生物碱进行提取，后处理利用阳离子聚丙烯酰胺衍生物的絮凝作用，能够吸附如意草粉渣及大分子杂质，加快其聚沉，以便较好地实现固液分离，提高如意草提取物中总生物碱的含量。
需要说明的是，在本文中，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
尽管已经示出和描述了本申请的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本申请的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本申请的范围由所附权利要求及其等同物限定。
Claims (7)
1.一种零甲醛、不含可溶性重金属腻子，其特征在于，包括以下重量份的组分：50-60份滑石粉；20-25份重质碳酸钙粉；10-15份电气石负离子粉；5-10份硅藻土；5-8份如意草提取物；2-5份可再分散型乳胶粉；1-3份阳离子聚丙烯酰胺衍生物；
所述阳离子聚丙烯酰胺衍生物的制备方法为：
S1、将聚丙烯酰胺、三乙胺依次加入到乙二醇中，搅拌下滴加环氧氯丙烷，升温至40-50℃，反应4-6h，然后降温至30℃，滴加对羟基苯甲酰氯，继续反应2-3h后得到聚丙烯酰胺衍生物；
S2、将聚丙烯酰胺衍生物、四丁基溴化铵、十二烷基二甲基叔胺加入到80%的异丙醇中，升温至83℃，回流反应8-10h，得到阳离子聚丙烯酰胺衍生物；
所述如意草提取物的制备方法为：
（1）将如意草清洗去杂后，置于烘箱内45-50℃下烘干至恒重，粉碎成粉末，过300目筛得到如意草粉；
（2）将如意草粉加入到75%乙醇溶液中，升温至40-50℃，超声提取2-4h，然后加入0.1%的阳离子聚丙烯酰胺衍生物溶液进行后处理，继续超声20-30min，离心分离后，上清液经浓缩、喷雾干燥后得到如意草提取物。
2.根据权利要求1所述的一种零甲醛、不含可溶性重金属腻子，其特征在于，步骤S1中所述聚丙烯酰胺、环氧氯丙烷、三乙胺、对羟基苯甲酰氯的质量比为1:0.1-0.2:0.3-0.4:0.1-0.2。
3.根据权利要求1所述的一种零甲醛、不含可溶性重金属腻子，其特征在于，步骤S2中所述聚丙烯酰胺衍生物、十二烷基二甲基叔胺、四丁基溴化铵的质量比为1:0.2-0.4:0.4-0.5。
4.根据权利要求1所述的一种零甲醛、不含可溶性重金属腻子，其特征在于，所述滑石粉的粒度为400-600目；所述电气石负离子粉粒度为300-400目；所述硅藻土粒度为400-500目。
5.根据权利要求1所述的一种零甲醛、不含可溶性重金属腻子，其特征在于，所述重质碳酸钙粒度为400-500目，白度为95，碳酸钙的含量为98-99％。
6.根据权利要求1-5任一项所述的一种零甲醛、不含可溶性重金属腻子的生产工艺，其特征在于，按照选定重量配比，依次将滑石粉、重质碳酸钙粉、电气石负离子粉、硅藻土、如意草提取物、可再分散型乳胶粉、阳离子聚丙烯酰胺衍生物放入混合装置的内部，搅拌均匀得到腻子。
7.根据权利要求6所述的一种零甲醛、不含可溶性重金属腻子的生产工艺，其特征在于，搅拌速度为800-1000r/min，搅拌时间为20-30min。