CN1159397A - Imitating crystal agate black jade decoration board - Google Patents
Imitating crystal agate black jade decoration board Download PDFInfo
- Publication number
- CN1159397A CN1159397A CN 96103262 CN96103262A CN1159397A CN 1159397 A CN1159397 A CN 1159397A CN 96103262 CN96103262 CN 96103262 CN 96103262 A CN96103262 A CN 96103262A CN 1159397 A CN1159397 A CN 1159397A
- Authority
- CN
- China
- Prior art keywords
- alumina cement
- parts
- agate
- modifier solution
- bed material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to an imitation cyrstal agate blackish jasper decorative board, belonging to the field of decorative artificial stone material technology. Said inventions elects and uses a set of novel formula compositions and production process to produce the invented imitation crystal agate blackish jasper decorative board. Said decorative board possesses glossy and bright face layer, natural smooth figure and pattern, high strength and hardness, does not decolour and can resist acid and alkali, resist wear, resist heat, and can be cut into various shapes, and can be used as decorative material for internal wall and external wall, also can be used as indoor floor material.
Description
The present invention relates to a kind of imitating crystal agate black jade decoration board, belong to decorating and use artificial stone's technical field.
In the market popular granolith, marble, terrazzo, floor tile etc., though various types of products are more, but all owing to the various defectives of its selected crystallizing agent formula combination and production technology, cause not bright-coloured, the intensely dark pool of superficial layer color and luster, decorative pattern nature, low, the fugitive color of intensity, come off, wear out, be out of shape, chap thus decorative effect poor, the operating period lacks.
The present invention is for solving a kind of imitating crystal agate black jade decoration board that above-mentioned deficiency provides.This decorative panel has that smooth surface is shinny, floral designs are natural and tripping, will never fade, anti-skid wearable, freeze proof heatproof, acid and alkali-resistance, hardness height, folding, withstand voltage and can cut into arbitrary shape, and good decorating effect is durable in use.
The present invention is achieved in that at first and gets edible alum 0.5-2 part by formula ratio (weight ratio), water reducer or plasticiser 40-150 part, early strength agent 15-60 part, according to the humiture situation, add in 1000 parts of water in good time, it is standby to be mixed with modifier solution, use alumina cement as cementing agent then, add inorganic mineral powders such as pigment, silica flour, aluminite quarrel, river sand in proportion, hierarchical modulation becomes cement mortar, stir, the imitating crystal agate black jade decoration board of all styles of specification, pattern is made in the continuous injection molding of layering and one-shot forming successively.
Give an actual example by formula combination and technical process below the present invention is described in further detail.
Example 1, imitative quartzy: be mixed with a certain proportion of modifier solution with edible alum, water reducer, early strength agent and water by formula ratio and add 0.15 part of pigment in right amount, 1 part of alumina cement, 0.8 part of 140 order white sand, 200 order white sands are mixed with the finish coat sizing material for 0.4 part; Get above-mentioned same solution and add 1 part of alumina cement in right amount, river sand is mixed with topped balance layer bed material for 3 parts; Get above-mentioned same solution and add 1 part of alumina cement in right amount, river sand is mixed with antagonism layer bed material for 1.4 parts.At first the finish coat sizing material is cast on the washed glass template and also vibrates several times gently, make slip smooth evenly, begin to pour into a mould topped balance layer bed material immediately, vibration a little again, floating with hawk, the layer of cast antagonism at last bed material, drain moisture content repeatedly with hawk, floating four jiaos and integral body make its average thickness 3-8mm, and all Production Time must not be above 30 minutes, go up nursing frame then, it is once moistening to treat to add water in 10-18 hour according to temperature conditions, crosses the demoulding in 30-90 hour, is the imitative quartzy stone material of finished product again in maintenance 5-10 days.
Example 2, imitative agate: use edible alum, water reducer, early strength agent and water are mixed with a certain proportion of modifier solution by formula ratio and add 0.15 part of pigment in right amount, and alumina cement is mixed with the dyeing sizing material for 1 part; Get 1 part of dyeing sizing material then, 10-14 number all stone 8-9 parts are mixed with colored stone; Get above-mentioned same solution and add 0.13 part of pigment in right amount, 1 part of alumina cement, 0.8 part of 70-140 order white sand, 200 order white sands are mixed with the finish coat sizing material for 0.4 part; Get above-mentioned same solution and add 1 part of alumina cement in right amount, river sand is mixed with the balance layer bed material for 3 parts; Get above-mentioned same solution and add 1 part of alumina cement in right amount, 2.1 parts of river sands, 10-14 number all stone is mixed with antagonism floor bed material for 1.9 parts.At first colored stone is sprinkling upon on the washed glass template equably by rule, pouring into a mould the finish coat sizing material immediately also vibrates several times gently, make slip smooth evenly, pour into a mould the balance layer bed material again, vibration a little, floating with hawk, the layer of cast antagonism at last bed material drains moisture content repeatedly with hawk, floating four jiaos and integral body, make its average thickness 6-12mm, all Production Time must not surpass 30 minutes, goes up nursing frame then, and it is once moistening to treat to add water in 10-18 hour according to temperature conditions, cross the demoulding in 30-90 hour, be the imitative agate stone material of finished product again in maintenance 5-10 days.
Example 3, imitative black jade: be mixed with a certain proportion of modifier solution with edible alum, water reducer, early strength agent and water by formula ratio and add 0.13 part of black pigment in right amount, 1 part of alumina cement, 0.6 part of 140 order white sand, 200 order white sands are mixed with the finish coat sizing material for 0.3 part; Get above-mentioned same solution and add 1 part of alumina cement in right amount, river sand is mixed with the balance layer bed material for 2.8 parts; Get above-mentioned same solution and add 1 part of alumina cement in right amount, river sand is mixed with antagonism layer bed material for 2 parts.At first the finish coat sizing material is cast on the washed glass template and vibration gently, the clean sand grains that to get ready subsequently is sprinkling upon on the slurry surface layer, treated the dried substantially solid moulding of colloid layer in the quiet 2-4 of stopping hour, pour into a mould the balance layer bed material again, vibration a little, floating with hawk, the layer of cast antagonism at last bed material, drain moisture content repeatedly with hawk, floating four jiaos and integral body make its average thickness 3-8mm, go up nursing frame then, it is once moistening to treat to add water in 8-16 hour according to temperature conditions, crosses the demoulding in 30-90 hour, is the imitative black jade stone material of finished product again in maintenance 5-10 days.
According to detection, glossiness of the present invention is up to 120 degree, and compression strength can reach more than the 80MPa, and rupture strength can reach 10-14MPa, and is low 1-2 times with other like product comparative costs.Can produce all styles of specification according to the present invention, the product of floral designs.
Claims (5)
1, a kind of imitating crystal agate black jade decoration board is characterized in that: formula combination is edible alum 0.5-2 part, water reducer or plasticiser 40-150 part, early strength agent 15-60 part, according to the humiture situation, add in 1000 parts of water in good time, it is standby to be mixed with modifier solution, use alumina cement as cementing agent then, add pigment in proportion, silica flour, the aluminite quarrel, inorganic mineral powders such as river sand, hierarchical modulation becomes colored stone, the finish coat sizing material, overcoat, balance layer and antagonism layer bed material, stir, the continuous injection molding of layering and one-shot forming successively is again through the demoulding, it is imitative quartzy that maintenance is finished product, agate, the black jade decorative panel.
2, imitating crystal agate black jade decoration board according to claim 1 is characterized in that: imitative quartzy finish coat sizing material is 0.15 part of a pigment, 1 part of alumina cement, and 0.8 part of 140 order white sand, 200 order white sands add appropriate modifier solution for 0.4 part; Topped balance layer bed material is 1 part of an alumina cement, and river sand adds appropriate modifier solution for 3 parts; Antagonism layer bed material is 1 part of alumina cement, and river sand adds appropriate modifier solution for 1.4 parts.
3, imitating crystal agate black jade decoration board according to claim 1 is characterized in that: the colored stone of imitative agate is 0.15 part of a pigment, 1 part of alumina cement, and 10-14 number all stone 8-9 parts add appropriate modifier solution; The finish coat sizing material is 0.13 part of a pigment, 1 part of alumina cement, and 0.8 part of 70-140 order white sand, 200 order white sands add appropriate modifier solution for 0.4 part; The balance layer bed material is 1 part of an alumina cement, and river sand adds appropriate modifier solution for 3 parts; Antagonism layer bed material is 1 part of alumina cement, 2.1 parts in river sand, and 10-14 number all stone adds appropriate modifier solution for 1.9 parts.
4, imitating crystal agate black jade decoration board according to claim 1 is characterized in that: the finish coat sizing material of imitative black jade is 0.13 part of a black pigment, 1 part of alumina cement, and 0.6 part of 140 order white sand, 200 order white sands add appropriate modifier solution for 0.3 part; The balance layer bed material is 1 part of an alumina cement, and river sand adds appropriate modifier solution for 2.8 parts; Antagonism layer bed material is 1 part of alumina cement, and river sand adds appropriate modifier solution for 2 parts.
5, imitating crystal agate black jade decoration board according to claim 1 is characterized in that: early strength agent is 2000 parts in water, salt 200-280 part triethanolamine 20-30 part.