CN115813023A - 一种减害香烟过滤嘴及其制备方法及应用 - Google Patents
一种减害香烟过滤嘴及其制备方法及应用 Download PDFInfo
- Publication number
- CN115813023A CN115813023A CN202211569862.7A CN202211569862A CN115813023A CN 115813023 A CN115813023 A CN 115813023A CN 202211569862 A CN202211569862 A CN 202211569862A CN 115813023 A CN115813023 A CN 115813023A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- filter
- smoldering
- monazite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及香烟过滤嘴技术领域，更具体的说涉及一种减害香烟过滤嘴及其制备方法及应用；该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；用采用PC或PMMA塑胶注塑成型；试验研究表明，本发明的香烟过滤嘴，对焦油和尼古丁碱具有很好的吸附作用，降低吸烟人群吸收有害物质的目的。
Description
技术领域
本发明涉及香烟过滤嘴技术领域，更具体的涉及一种减害香烟过滤嘴及其制备方法及应用。
技术背景
吸烟有害健康是世界公认的，为了减少吸烟对身体健康的危害，众多科学家都在努力寻找方法，设计了数千总香烟添加剂、过滤棉、过滤嘴等产品，通过过滤、吸附等干预手段，确实可以起到减少部分焦油、尼古丁等有害物质的作用，美中不足的是，无法完全过滤掉香烟中严重的致癌物质，另辟蹊径，在现有技术的基础上研发一种既可以过滤大部分焦油、尼古丁、苯酚、巴豆醛，又可以分解、转换苯并芘、亚硝胺、一氧化碳、氰化氢、氨等致癌物质和气体，同时具备空间抗菌抑菌、灭活病毒，预防感冒、咽炎、肺炎、鼻炎、口腔炎症、净化空气等功效，减少吸烟对人体的伤害，减少二手烟对其他人的伤害的香烟添加剂及香烟过滤嘴，有着广阔的市场空间和创造巨大的经济价值。
发明内容
基于上述原因，申请人经过若干次创造性的劳动，获得了得到一种新的香烟过滤嘴，该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；用采用无毒的PC或PMMA塑胶注塑成型。试验研究表明，本发明的香烟过滤嘴，对焦油和尼古丁碱具有很好的吸附作用，降低吸烟人群吸收有害物质的目的。
本发明所述的PC就是聚碳酸酯材料，这是一种强韧的热塑性树脂，它具有无色透明，耐热，抗冲击，阻燃，折射率高，加工性能好等特点。
本发明所述的PMMA指聚甲基丙烯酸甲酯；聚甲基丙烯酸甲酯(polymethylmethacrylate)，简称PMMA，是一种高分子聚合物，又称作亚克力或有机玻璃，具有高透明度，低价格，易于机械加工等优点，是平常经常使用的玻璃替代材料。
本发明通过下述技术方案实现的。
一种香烟过滤嘴，该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；用采用无毒的PC或PMMA塑胶注塑成型。在使用时将硅胶盖去掉，插入烟上即可。
所述的一种香烟过滤嘴，其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土60-70重量份、尿素5-15重量份、柠檬粉5-15重量份、碘值为1100的活性炭3-7重量份、纳米气凝胶2-4重量份、纳米二氧化钛1-3重量份、维生素c1-5重量份、壳聚糖0.5-1.5重量份、冰糖粉1-5重量份、活性纳米氧化锌1-5重量份、闷烧蒸馏独居石晶粉1-3重量份、玉米淀粉1-5重量份。
本发明所述的纳米气凝胶：纳米气凝胶作为一种新型的工业隔热保温材料,具有密度低、导热率低、高孔隙率等特点。导热系数的高低决定着保温材料的保温隔热效果的好坏,导热系数越低其保温隔热效果越好,纳米气凝胶具有很低的导热系数小于等于0.020W/m·K(常温下),因此具有很好的隔热效果。具有稳定的化学性能,在高温下不分解,不释放有害气体,是一种绿色环保型材料。市售。
所述的一种香烟过滤嘴，其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土65重量份、尿素10重量份、柠檬粉10重量份、碘值为1100的活性炭5重量份、纳米气凝胶3重量份、纳米二氧化钛2重量份、维生素c3重量份、壳聚糖1重量份、冰糖粉3重量份、活性纳米氧化锌3重量份、闷烧蒸馏独居石晶粉2重量份、玉米淀粉3重量份。
所述的一种香烟过滤嘴，其中第五层过滤液由下述原料制备而成：柠檬酸60-70重量份、尿素5-15重量份、维生素c 5-15重量份、壳聚糖2-4重量份、闷烧活性纳米氧化锌蒸馏溶液4-6重量份、闷烧独居石蒸馏溶液2-4重量份、氨基酸1-3重量份、纳米气凝胶1-3重量份，纯化水80-120重量份。
本发明所述的氨基酸：是含有碱性氨基和酸性羧基的有机化合物。羧酸碳原子上的氢原子被氨基取代后形成的化合物。市售。
所述的一种香烟过滤嘴，其中第五层过滤液由下述原料制备而成：柠檬酸65重量份、尿素10重量份、维生素c10份、壳聚糖3重量份、闷烧活性纳米氧化锌蒸馏溶液5重量份、闷烧独居石蒸馏溶液3重量份、氨基酸2重量份、纳米气凝胶2重量份，纯化水100重量份。
所述的一种香烟过滤嘴，其中闷烧活性纳米氧化锌蒸馏溶液的制备方法为：将纳米氧化锌置于1800-2200度高温炉中，烧制75-105分钟；冷却后，将烧制的粉置于800-1200目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液。
所述的一种香烟过滤嘴，其中闷烧独居石蒸馏溶液的制备方法为：将独居石粉碎后，置于1800-2200度高温炉中，烧制75-105分钟；冷却后，将烧制的粉置于800-1200目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液；蒸馏后的独居石，粉碎，得到闷烧蒸馏独居石晶粉。
所述的一种香烟过滤嘴，其中第四层过滤颗粒是将所述原料混合完全，置于造粒机中制粒，粒径为0.1-3mm，将颗粒30-100粒置于第四层。
所述的一种香烟过滤嘴，其中第五层是含有过滤液是将所述原料混合完全均匀后，使用自动计量滴胶机滴在做好的过滤嘴底部的过滤棉中，滴0.1ml-3ml。或者适量。该剂量可以适度剂量
本发明所述原料均由隆誉翼尧(北京)科技有限公司免费提供。
本发明有益的技术效果在于“过滤颗粒”、“过滤液”在香烟过滤嘴的应用，其中过滤颗粒和过滤液的组成成分，均可以由市售所得，原料易得，适合工业化生产。
本发明的香烟过滤嘴，对于香烟中的焦油和尼古丁碱等有害物质，具有很好的吸附作用，从而降低香烟对人体的损伤。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明了，下面结合具体实施方式，对本发明进一步详细说明。应该理解，这些描述只是示例性的，而并非要限制本发明的范围。此外，在以下说明中，省略了对公知结构和技术的描述，以避免不必要地混淆本发明的概念。
实施例1
一种香烟过滤嘴，该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；用采用无毒的PC或PMMA塑胶注塑成型。在使用时将硅胶盖去掉，插入烟上即可。
其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土60g、尿素5g、柠檬粉5g、碘值为1100的活性炭3g、纳米气凝胶2g、纳米二氧化钛1g、维生素c1g、壳聚糖0.5g、冰糖粉1g、活性纳米氧化锌1g、闷烧蒸馏独居石晶粉1g、玉米淀粉1g。
其中第五层过滤液由下述原料制备而成：柠檬酸60g、尿素5g、维生素c 5g、壳聚糖2g、闷烧活性纳米氧化锌蒸馏溶液4g、闷烧独居石蒸馏溶液2g、氨基酸1g、纳米气凝胶1g，纯化水80g。
其中闷烧活性纳米氧化锌蒸馏溶液的制备方法为：将纳米氧化锌置于1800度高温炉中，烧制105分钟；冷却后，将烧制的粉置于800目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液。
其中闷烧独居石蒸馏溶液的制备方法为：将独居石粉碎后，置于1800度高温炉中，烧制105分钟；冷却后，将烧制的粉置于800目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液；蒸馏后的独居石，粉碎，得到闷烧蒸馏独居石晶粉。
所述的一种香烟过滤嘴，其中第四层过滤颗粒是将所述原料混合完全，置于造粒机中制粒，粒径为0.1-3mm，将颗粒30粒置于第四层。
所述的一种香烟过滤嘴，其中第五层是含有过滤液是将所述原料混合完全均匀后，使用自动计量滴胶机滴在做好的过滤嘴底部的过滤棉中，滴3ml。
实施例2
一种香烟过滤嘴，该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；用采用无毒的PC或PMMA塑胶注塑成型。在使用时将硅胶盖去掉，插入烟上即可。
其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土70g、尿素15g、柠檬粉15g、碘值为1100的活性炭7g、纳米气凝胶4g、纳米二氧化钛3g、维生素c5g、壳聚糖1.5g、冰糖粉5g、活性纳米氧化锌5g、闷烧蒸馏独居石晶粉3g、玉米淀粉5g。
其中第五层过滤液由下述原料制备而成：柠檬酸70g、尿素15g、维生素c 15g、壳聚糖4g、闷烧活性纳米氧化锌蒸馏溶液6g、闷烧独居石蒸馏溶液4g、氨基酸3g、纳米气凝胶3g，纯化水120g。
其中闷烧活性纳米氧化锌蒸馏溶液的制备方法为：将纳米氧化锌置于2000度高温炉中，烧制75分钟；冷却后，将烧制的粉置于1200目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液。
其中闷烧独居石蒸馏溶液的制备方法为：将独居石粉碎后，置于2200度高温炉中，烧制75分钟；冷却后，将烧制的粉置于1200目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液；蒸馏后的独居石，粉碎，得到闷烧蒸馏独居石晶粉。
其中第四层过滤颗粒是将所述原料混合完全，置于造粒机中制粒，粒径为0.1-3mm，将颗粒100粒置于第四层。
其中第五层是含有过滤液是将所述原料混合完全均匀后，使用自动计量滴胶机滴在做好的过滤嘴底部的过滤棉中，滴0.1ml。
实施例3
一种香烟过滤嘴，该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；用采用无毒的PC或PMMA塑胶注塑成型。在使用时将硅胶盖去掉，插入烟上即可。
其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土65g、尿素10g、柠檬粉10g、碘值为1100的活性炭5g、纳米气凝胶3g、纳米二氧化钛2g、维生素c3g、壳聚糖1g、冰糖粉3g、活性纳米氧化锌3g、闷烧蒸馏独居石晶粉2g、玉米淀粉3g。
其中第五层过滤液由下述原料制备而成：柠檬酸65g、尿素10g、维生素c10g、壳聚糖3g、闷烧活性纳米氧化锌蒸馏溶液5g、闷烧独居石蒸馏溶液3g、氨基酸2g、纳米气凝胶2g，纯化水100g。
其中闷烧活性纳米氧化锌蒸馏溶液的制备方法为：将纳米氧化锌置于2000度高温炉中，烧制90分钟；冷却后，将烧制的粉置于1000目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液。
其中闷烧独居石蒸馏溶液的制备方法为：将独居石粉碎后，置于2000度高温炉中，烧制95分钟；冷却后，将烧制的粉置于1000目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液；蒸馏后的独居石，粉碎，得到闷烧蒸馏独居石晶粉。
其中第四层过滤颗粒是将所述原料混合完全，置于造粒机中制粒，粒径为0.1-3mm，将颗粒65粒置于第四层。
其中第五层是含有过滤液是将所述原料混合完全均匀后，使用自动计量滴胶机滴在做好的过滤嘴底部的过滤棉中，滴1.5ml。
实施例4
一种香烟过滤嘴，该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；用采用无毒的PC或PMMA塑胶注塑成型。在使用时将硅胶盖去掉，插入烟上即可。
其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土62g、尿素7g、柠檬粉8g、碘值为1100的活性炭4g、纳米气凝胶2.5g、纳米二氧化钛1.5g、维生素c2g、壳聚糖0.8g、冰糖粉2g、活性纳米氧化锌2g、闷烧蒸馏独居石晶粉1.5g、玉米淀粉1.5g。
其中第五层过滤液由下述原料制备而成：柠檬酸63g、尿素6g、维生素c 7g、壳聚糖2.5g、闷烧活性纳米氧化锌蒸馏溶液4.5g、闷烧独居石蒸馏溶液2.5g、氨基酸1.5g、纳米气凝胶1.5g，纯化水90g。
其中闷烧活性纳米氧化锌蒸馏溶液的制备方法为：将纳米氧化锌置于1900度高温炉中，烧制100分钟；冷却后，将烧制的粉置于900目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液。
其中闷烧独居石蒸馏溶液的制备方法为：将独居石粉碎后，置于1900度高温炉中，烧制100分钟；冷却后，将烧制的粉置于900目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液；蒸馏后的独居石，粉碎，得到闷烧蒸馏独居石晶粉。
其中第四层过滤颗粒是将所述原料混合完全，置于造粒机中制粒，粒径为0.1-3mm，将颗粒45粒置于第四层。
其中第五层是含有过滤液是将所述原料混合完全均匀后，使用自动计量滴胶机滴在做好的过滤嘴底部的过滤棉中，滴2.5ml。
实施例5
一种香烟过滤嘴，该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；用采用无毒的PC或PMMA塑胶注塑成型。在使用时将硅胶盖去掉，插入烟上即可。
其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土68g、尿素14g、柠檬粉14g、碘值为1100的活性炭6g、纳米气凝胶3.5g、纳米二氧化钛2.5g、维生素c4g、壳聚糖1.3g、冰糖粉4g、活性纳米氧化锌4g、闷烧蒸馏独居石晶粉2.5g、玉米淀粉4.5g。
其中第五层过滤液由下述原料制备而成：柠檬酸68g、尿素13g、维生素c 13g、壳聚糖3.5g、闷烧活性纳米氧化锌蒸馏溶液5.5g、闷烧独居石蒸馏溶液3.5g、氨基酸2.5g、纳米气凝胶2.5g，纯化水110g。
其中闷烧活性纳米氧化锌蒸馏溶液的制备方法为：将纳米氧化锌置于2100度高温炉中，烧制80分钟；冷却后，将烧制的粉置于1100目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液。
其中闷烧独居石蒸馏溶液的制备方法为：将独居石粉碎后，置于2100度高温炉中，烧制85分钟；冷却后，将烧制的粉置于1100目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液；蒸馏后的独居石，粉碎，得到闷烧蒸馏独居石晶粉。
其中第四层过滤颗粒是将所述原料混合完全，置于造粒机中制粒，粒径为0.1-3mm，将颗粒90粒置于第四层。
其中第五层是含有过滤液是将所述原料混合完全均匀后，使用自动计量滴胶机滴在做好的过滤嘴底部的过滤棉中，滴1.5ml。
对比例1
一种香烟过滤嘴，该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；用采用无毒的PC或PMMA塑胶注塑成型。在使用时将硅胶盖去掉，插入烟上即可。
其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土65g、尿素10g、柠檬粉10g、纳米二氧化钛2g、维生素c3g、壳聚糖1g、冰糖粉3g、活性纳米氧化锌3g、玉米淀粉3g。
其中第五层过滤液由下述原料制备而成：柠檬酸65g、尿素10g、维生素c10g、壳聚糖3g、闷烧活性纳米氧化锌蒸馏溶液5g、闷烧独居石蒸馏溶液3g、氨基酸2g、纳米气凝胶2g，纯化水100g。
其中闷烧活性纳米氧化锌蒸馏溶液的制备方法为：将纳米氧化锌置于2000度高温炉中，烧制90分钟；冷却后，将烧制的粉置于1000目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液。
其中闷烧独居石蒸馏溶液的制备方法为：将独居石粉碎后，置于2000度高温炉中，烧制95分钟；冷却后，将烧制的粉置于1000目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液；蒸馏后的独居石，粉碎，得到闷烧蒸馏独居石晶粉。
其中第四层过滤颗粒是将所述原料混合完全，置于造粒机中制粒，粒径为0.1-3mm，将颗粒65粒置于第四层。
其中第五层是含有过滤液是将所述原料混合完全均匀后，使用自动计量滴胶机滴在做好的过滤嘴底部的过滤棉中，滴1.5ml。
对比例2
一种香烟过滤嘴，该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；用采用无毒的PC或PMMA塑胶注塑成型。在使用时将硅胶盖去掉，插入烟上即可。
其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土65g、尿素10g、柠檬粉10g、碘值为1100的活性炭5g、纳米气凝胶3g、纳米二氧化钛2g、维生素c3g、壳聚糖1g、冰糖粉3g、活性纳米氧化锌3g、闷烧蒸馏独居石晶粉2g、玉米淀粉3g。
其中第五层过滤液由下述原料制备而成：柠檬酸65g、尿素10g、壳聚糖3g、闷烧独居石蒸馏溶液3g、氨基酸2g、纳米气凝胶2g，纯化水80g。
其中闷烧活性纳米氧化锌蒸馏溶液的制备方法为：将纳米氧化锌置于2000度高温炉中，烧制90分钟；冷却后，将烧制的粉置于1000目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液。
其中闷烧独居石蒸馏溶液的制备方法为：将独居石粉碎后，置于2000度高温炉中，烧制95分钟；冷却后，将烧制的粉置于1000目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液；蒸馏后的独居石，粉碎，得到闷烧蒸馏独居石晶粉。
其中第四层过滤颗粒是将所述原料混合完全，置于造粒机中制粒，粒径为0.1-3mm，将颗粒65粒置于第四层。
其中第五层是含有过滤液是将所述原料混合完全均匀后，使用自动计量滴胶机滴在做好的过滤嘴底部的过滤棉中，滴1.5ml。
试验例
过滤嘴对香烟中焦油和尼古丁的吸附作用
试验方法：购买市售中南海(软精品)香烟(焦油含量10mg/支，尼古丁碱含量0.9mg/支)，分为不同试验组：
对照组：市售绿伞一次性过滤烟嘴抛弃型用于20支香烟(一支香烟一个过滤嘴)。
试验1组：实施例3组过滤嘴用于20支香烟(一支香烟一个过滤嘴)。
试验2组：实施例4组过滤嘴用于20支香烟(一支香烟一个过滤嘴)。
试验3组：对比例1组过滤嘴用于20支香烟(一支香烟一个过滤嘴)。
试验4组：对比例2组过滤组用于20支香烟(一支香烟一个过滤嘴)。
将不同组的带有过滤嘴的香烟依次放入博瓦特—凯希RM200A吸烟机中燃烧完毕后，检测每支香烟过滤嘴中焦油含量和尼古丁碱含量，计算平均值，试验结果见表1。
表1不同烟嘴对焦油和尼古丁碱的吸附对比
试验结论：上述试验表明，本发明的过滤嘴对香烟中焦油和尼古丁碱具有很好的吸附作用，与市售的过滤嘴和对比例的过滤嘴比较，能够显著提高进入吸烟人群口腔中的焦油含量和尼古丁含量，本申请的过滤嘴可以将香烟中80％以上的焦油和尼古丁碱进行吸附；充分说明本发明的过滤嘴具有科学意义。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (9)
1.一种香烟过滤嘴，其特征在于该过滤嘴由六层组成，从外至里依次为：第一层为添加活性炭的过滤棉，第二层为五孔胶，第三层是过滤棉，第四层是过滤颗粒，第五层是含有过滤液的过滤棉，第六层为硅胶盖；采用PC或PMMA塑胶注塑成型。
2.根据权利要求1所述的一种香烟过滤嘴，其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土60-70重量份、尿素5-15重量份、柠檬粉5-15重量份、碘值为1100的活性炭3-7重量份、纳米气凝胶2-4重量份、纳米二氧化钛1-3重量份、维生素c1-5重量份、壳聚糖0.5-1.5重量份、冰糖粉1-5重量份、活性纳米氧化锌1-5重量份、闷烧蒸馏独居石晶粉1-3重量份、玉米淀粉1-5重量份。
3.根据权利要求1所述的一种香烟过滤嘴，其中第四层过滤颗粒由下述原料制备而成：纳米级硅藻土65重量份、尿素10重量份、柠檬粉10重量份、碘值为1100的活性炭5重量份、纳米气凝胶3重量份、纳米二氧化钛2重量份、维生素c3重量份、壳聚糖1重量份、冰糖粉3重量份、活性纳米氧化锌3重量份、闷烧蒸馏独居石晶粉2重量份、玉米淀粉3重量份。
4.根据权利要求1所述的一种香烟过滤嘴，其中第五层过滤液由下述原料制备而成：柠檬酸60-70重量份、尿素5-15重量份、维生素c 5-15重量份、壳聚糖2-4重量份、闷烧活性纳米氧化锌蒸馏溶液4-6重量份、闷烧独居石蒸馏溶液2-4重量份、氨基酸1-3重量份、纳米气凝胶1-3重量份，纯化水80-120重量份。
5.根据权利要求1所述的一种香烟过滤嘴，其中第五层过滤液由下述原料制备而成：柠檬酸65重量份、尿素10重量份、维生素c10份、壳聚糖3重量份、闷烧活性纳米氧化锌蒸馏溶液5重量份、闷烧独居石蒸馏溶液3重量份、氨基酸2重量份、纳米气凝胶2重量份，纯化水100重量份。
6.根据权利要求2-5任一项所述的一种香烟过滤嘴，其中闷烧活性纳米氧化锌蒸馏溶液的制备方法为：将纳米氧化锌置于1800-2200度高温炉中，烧制75-105分钟；冷却后，将烧制的粉置于800-1200目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液。
7.根据权利要求2-5任一项所述的一种香烟过滤嘴，其中闷烧独居石蒸馏溶液的制备方法为：将独居石粉碎后，置于1800-2200度高温炉中，烧制75-105分钟；冷却后，将烧制的粉置于800-1200目的布袋中，用蒸炉进行蒸溜，得到蒸馏溶液；蒸馏后的独居石，粉碎，得到闷烧蒸馏独居石晶粉。
8.根据权利要求2或3所述的一种香烟过滤嘴，其中第四层过滤颗粒是将所述原料混合完全，置于造粒机中制粒，粒径为0.1-3mm，将颗粒30-100粒置于第四层。
9.根据权利要求4或5所述的一种香烟过滤嘴，其中第五层是含有过滤液是将所述原料混合完全均匀后，使用自动计量滴胶机滴在做好的过滤嘴底部的过滤棉中，滴0.1ml-3ml。