CN115745537B - 一种轻质抹灰砂浆及制备方法 - Google Patents
一种轻质抹灰砂浆及制备方法 Download PDFInfo
- Publication number
- CN115745537B CN115745537B CN202211644234.0A CN202211644234A CN115745537B CN 115745537 B CN115745537 B CN 115745537B CN 202211644234 A CN202211644234 A CN 202211644234A CN 115745537 B CN115745537 B CN 115745537B
- Authority
- CN
- China
- Prior art keywords
- parts
- plastering mortar
- mortar according
- water
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及建筑材料技术领域，提出了一种轻质抹灰砂浆及制备方法，包括以下重量份组分：硅酸盐水泥25‑45份、快硬硫铝酸盐水泥0‑4份、砂40‑65份、粉煤灰5‑10份、玻化微珠6‑10份、可再分散乳胶粉0.2‑0.6份、萘系减水剂0.1‑0.3份、引气剂0.005‑0.01份、塑性膨胀剂0.02‑0.04份、纤维素醚0.1‑0.3份、憎水剂0.5‑0.7份、淀粉醚0.5‑1.0份、聚丙烯纤维0.1‑0.3份、N‑苄基十六烷酰胺4‑6份、4‑碘苯乙炔基三甲基硅烷2‑4份、水15‑23份。通过上述技术方案，解决了现有技术中轻质抹灰砂浆抗压强度、拉伸粘结强度低的问题。
Description
技术领域
本发明涉及建筑材料技术领域，具体的，涉及一种轻质抹灰砂浆及制备方法。
背景技术
随着经济发展和人们生活改善，能源大量消耗，气候变暖加剧，人类生存受到严重威胁。因此，国家大力提倡节能减排，而建筑节能减排是最主要节能形式之一，薄抹灰外墙外保温系统因保温效果显著，一度成为最主要的建筑保温形式。但在使用过程中由于保温板粘结性能差、保温系统结构处理存在缺陷、防火不达标等原因，薄抹灰保温系统空鼓、开裂、脱落、着火等现象频频发生，造成严重的人身和财产损失。
国内山东、重庆、浙江、上海、河北等省规定限制和禁止采用薄抹灰外墙外保温系统和仅通过粘结锚固方式固定的外墙保温装饰一体化系统，进一步提升与承重主体结构一体成型的保温结构墙体应用规模。建筑结构保温一体化是保温层与建筑结构同步施工完成的构造技术，建筑主体围护结构通过钢筋混凝土构件与保温层及外保护层实现刚性连接。保温免拆模板由内防护层(内嵌玻璃纤维网格布)、保温板、粘结层、水泥聚苯颗粒保温过度层，外防护层(内嵌玻璃纤维网格布)组成。建筑结构保温一体化技术是实现建筑保温功能与墙体围护功能为一体，具有较长的耐久性且满足消防要求的技术，其能有效解决保温体系与建筑主体同寿命的问题，而且在抗震安全等性能方面也得到了加强，能同时满足建筑安全、防火、节能等要求，是替代外墙外保温系统的建筑保温形式。
在建筑结构保温一体化的施工中，复合建筑保温板作为外摸板，施工后不再拆除，作为墙面使用，进行外墙饰面即可。但由于现有施工技术限制，施工后模板的平整度差，存在模板变形、错位、跑浆等情况，必须对复合保温板表层进行修复和找平，为饰面层施工创造条件。目前找平材料为轻质抹灰砂浆，但施工后易出现空鼓、开裂、脱落情况，工程耐久性差。
发明内容
本发明提出一种轻质抹灰砂浆及制备方法，解决了相关技术中轻质抹灰砂浆抗压强度、拉伸粘结强度低的问题。
本发明的技术方案如下：
一种轻质抹灰砂浆，包括以下重量份组分：硅酸盐水泥25-45份、快硬硫铝酸盐水泥0-4份、砂40-65份、粉煤灰5-10份、玻化微珠6-10份、可再分散乳胶粉0.2-0.6份、萘系减水剂0.1-0.3份、引气剂0.005-0.01份、塑性膨胀剂0.02-0.04份、纤维素醚0.1-0.3份、憎水剂0.5-0.7份、淀粉醚0.5-1.0份、聚丙烯纤维0.1-0.3份、N-苄基十六烷酰胺4-6份、4-碘苯乙炔基三甲基硅烷2-4份、水15-23份。
作为进一步技术方案，所述可在分散乳胶粉为乙烯-醋酸乙烯酯共聚物，乙烯-醋酸乙烯酯共聚物中乙烯质量含量≥30％。
作为进一步技术方案，所述粉煤灰为II级粉煤灰。
作为进一步技术方案，所述砂的细度模数为1.0-3.1。
作为进一步技术方案，所述减水剂为萘系减水剂。
作为进一步技术方案，所述引气剂包括十二烷基磺酸钠、木质素磺酸钠的一种或多种。
作为进一步技术方案，所述玻化微珠的粒径为50-80目，堆积密度≤110kg/m3，体积吸水率≤45％。
作为进一步技术方案，所述增水剂为有机硅增水剂。
一种轻质抹灰砂浆的制备方法，包括以下步骤：称取如权利要求1所述的各组分重量份混合后，得到抹灰砂浆。
作为进一步技术方案，所述混合为搅拌40-60s。
本发明的工作原理及有益效果为：
1、本发明制备得到的轻质抹灰砂浆具有较高的抗压强度和抗拉粘结强度，适用范围广，可应用于复合保温板表层进行修复和找平，为饰面层施工创造条件，并且生产工艺简单便捷，品质稳定，能提高工程质量。
2、本发明轻质抹灰砂浆组分中采用N-苄基十六烷酰胺、4-碘苯乙炔基三甲基硅烷，N-苄基十六烷酰胺一方面可以增加抹灰砂浆的抗拉粘结强度，另一方面还能提高抹灰砂浆的抗压强度；4-碘苯乙炔基三甲基硅烷的加入不仅可以提高抹灰砂浆的和易性，还可以提高抹灰砂浆的力学强度。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都涉及本发明保护的范围。
下述实施例及对比例中ZM-1B萘系减水剂购自安徽鑫固环保股份有限公司、FDN-A萘系高效减水剂购自莱芜市延辉建材有限公司、EP-2塑性膨胀剂购自南京新义合成科技有限公司。
实施例1
称取硅酸盐水泥25份、砂40份、粉煤灰5份、玻化微珠6份、乙烯-醋酸乙烯酯共聚物0.2份、ZM-1B萘系减水剂0.1份、十二烷基磺酸钠0.005份、EP-2塑性膨胀剂0.02份、羟丙基纤维素醚0.1份、甲基硅酸钠0.5份、淀粉醚0.5份、聚丙烯纤维0.1份、N-苄基十六烷酰胺4份、4-碘苯乙炔基三甲基硅烷2份、水15份，搅拌60s后，得到抹灰砂浆。其中，玻化微珠的粒径为50-60目，堆积密度为110kg/m3，体积吸水率为45％；砂的细度模数为1.0-1.5；乙烯-醋酸乙烯酯共聚物中乙烯质量含量为30％。
实施例2
称取硅酸盐水泥45份、快硬硫铝酸盐水泥4份、砂65份、粉煤灰10份、玻化微珠10份、乙烯-醋酸乙烯酯共聚物0.6份、FDN-A萘系减水剂0.3份、十二烷基磺酸钠0.01份、EP-2塑性膨胀剂0.04份、羟丙基纤维素醚0.3份、甲基硅酸钠0.7份、淀粉醚1.0份、聚丙烯纤维0.3份、N-苄基十六烷酰胺6份、4-碘苯乙炔基三甲基硅烷4份、水23份，搅拌40s后，得到抹灰砂浆。其中，玻化微珠的粒径为60-70目，堆积密度为105kg/m3，体积吸水率为43％；砂的细度模数为1.5-1.9；乙烯-醋酸乙烯酯共聚物中乙烯质量含量为32％。
实施例3
称取硅酸盐水泥35份、快硬硫铝酸盐水泥2份、砂50份、粉煤灰8份、玻化微珠8份、乙烯-醋酸乙烯酯共聚物0.4份、萘系减水剂0.2份、十二烷基磺酸钠0.008份、EP-2塑性膨胀剂0.03份、羟丙基纤维素醚0.2份、甲基硅酸钠0.6份、淀粉醚0.7份、聚丙烯纤维0.2份、N-苄基十六烷酰胺5份、4-碘苯乙炔基三甲基硅烷3份、水20份，搅拌50s后，得到抹灰砂浆。其中，玻化微珠的粒径为70-80目，堆积密度102kg/m3，体积吸水率为41％；砂的细度模数为2.5-3.1；乙烯-醋酸乙烯酯共聚物中乙烯质量含量为35％。
对比例1
与实施例1相比，对比例1不添加N-苄基十六烷酰胺，其他与实施例1相同。
对比例2
与实施例1相比，对比例2不添加4-碘苯乙炔基三甲基硅烷，其他与实施例相同。
对比例3
与实施例1相比，对比例3将4-碘苯乙炔基三甲基硅烷替换成等量的KH550，其他与实施例相同。
测定实施例1-3和对比例1-3制备得到的抹灰砂浆的抗压强度和28d拉伸粘结强度，测定结果见表1。
抗压强度、28d拉伸粘结强度：依据JGJ/T70-2009《建筑砂浆基本性能试验方法标准》进行测定。
表1测定结果
| 抗压强度MPa | 28d拉伸粘结强度MPa | |
| 实施例1 | 3.5 | 0.52 |
| 实施例2 | 3.4 | 0.59 |
| 实施例3 | 3.2 | 0.54 |
| 对比例1 | 2.7 | 0.45 |
| 对比例2 | 2.9 | 0.48 |
| 对比例3 | 3.0 | 0.50 |
与实施例1相比，对比例1不添加N-苄基十六烷酰胺，对比例2不添加4-碘苯乙炔基三甲基硅烷，对比例3 4-碘苯乙炔基三甲基硅烷替换成等量的KH550，结果对比例1-3得到的抹灰砂浆的抗压强度和28d拉伸粘结强度均低于实施例1，说明添加N-苄基十六烷酰胺、4-碘苯乙炔基三甲基硅烷既能提高抹灰砂浆的抗压强度也能提高28d拉伸粘结强度。
以上仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种轻质抹灰砂浆，其特征在于，包括以下重量份组分：硅酸盐水泥25-45份、快硬硫铝酸盐水泥0-4份、砂40-65份、粉煤灰5-10份、玻化微珠6-10份、可再分散乳胶粉0.2-0.6份、萘系减水剂0.1-0.3份、引气剂0.005-0.01份、塑性膨胀剂0.02-0.04份、纤维素醚0.1-0.3份、憎水剂0.5-0.7份、淀粉醚0.5-1.0份、聚丙烯纤维0.1-0.3份、N-苄基十六烷酰胺4-6份、4-碘苯乙炔基三甲基硅烷2-4份、水15-23份；
所述可再分散乳胶粉为乙烯-醋酸乙烯酯共聚物，乙烯-醋酸乙烯酯共聚物中乙烯质量含量≥30%。
2.根据权利要求1所述的一种轻质抹灰砂浆，其特征在于，所述粉煤灰为II级粉煤灰。
3.根据权利要求1所述的一种轻质抹灰砂浆，其特征在于，所述砂的细度模数为1.0-3.1。
4.根据权利要求1所述的一种轻质抹灰砂浆，其特征在于，所述引气剂包括十二烷基磺酸钠、木质素磺酸钠的一种或多种。
5.根据权利要求1所述的一种轻质抹灰砂浆，其特征在于，所述玻化微珠的粒径为50-80目，堆积密度≤110kg/m³，体积吸水率≤45%。
6.根据权利要求1所述的一种轻质抹灰砂浆，其特征在于，所述憎水剂为有机硅憎水剂。
7.根据权利要求1所述的一种轻质抹灰砂浆的制备方法，其特征在于，包括以下步骤：称取如权利要求1所述的各组分重量份混合后，得到抹灰砂浆。
8.根据权利要求7所述的一种轻质抹灰砂浆的制备方法，其特征在于，所述混合为搅拌40-60s。