CN115323557A - Preparation method of functional sock yarn - Google Patents
Preparation method of functional sock yarn Download PDFInfo
- Publication number
- CN115323557A CN115323557A CN202110508791.9A CN202110508791A CN115323557A CN 115323557 A CN115323557 A CN 115323557A CN 202110508791 A CN202110508791 A CN 202110508791A CN 115323557 A CN115323557 A CN 115323557A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- weight
- stirring
- preparing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of yarn production, and particularly relates to a preparation method of functional sock yarns, which comprises the following steps: preparing the following raw materials in parts by weight: 300 parts of water, 60-110 parts of softwood pulp, 5-9 parts of a waterproof agent, 4-11 parts of a softening agent, 8-16 parts of a water-absorbing resin, 6-11 parts of waterborne polyurethane, 22-34 parts of polyacrylamide, 12-32 parts of nano zinc oxide, 4-9 parts of hydrogen peroxide, 5-13 parts of deacetylated chitin, 7-16 parts of silver nitrate, 4-9 parts of ammonium pyrrolidone carboxylate and 2-13 parts of fatty acid polyoxyethylene ether; the sock material manufactured by the invention has good sweat absorption performance, improves the use comfort level, does not make feet wet and slippery, plays a good anti-skidding role, has good deodorization and odor removal performance, effectively inhibits the breeding of bacteria, plays a role in moisturizing the feet, solves the problem of dry and cracked feet, and improves the use quality.
Description
Technical Field
The invention relates to the technical field of yarn production, in particular to a preparation method of functional sock yarns.
Background
The socks are one of important daily clothes and play a role in protecting and beautifying feet. With the continuous improvement of the pursuit of people for healthy life, the performance of the socks is not limited to warm keeping and beauty. The existing sock yarn is single in function, after the existing sock is manufactured, the sweat absorption effect is poor, the odor resistance is not good, meanwhile, moisture is not preserved, the sole is prone to cracking, the comfort level of product use is poor, and therefore a preparation method of the functional sock yarn is provided.
Disclosure of Invention
The invention aims to provide a preparation method of functional sock yarns, which aims to solve the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: a preparation method of functional sock yarns comprises the following steps:
s1, preparing the following raw materials in parts by weight: 300 parts of water, 60-110 parts of softwood pulp, 5-9 parts of a waterproof agent, 4-11 parts of a softening agent, 8-16 parts of water-absorbent resin, 6-11 parts of waterborne polyurethane, 22-34 parts of polyacrylamide, 12-32 parts of nano zinc oxide, 4-9 parts of hydrogen peroxide, 5-13 parts of deacetylated chitin, 7-16 parts of silver nitrate, 4-9 parts of ammonium pyrrolidone carboxylate, 2-13 parts of fatty acid polyoxyethylene ether and 12-28 parts of natural color resin;
s2, weighing the waterborne polyurethane, the polyacrylamide, the nano zinc oxide and the hydrogen peroxide in parts by weight, and stirring and mixing to prepare a deodorant;
s3, mixing the deacetylated chitin and the silver nitrate in parts by weight, reacting for 30-60 minutes, adding the pyrrolidone ammonium carboxylate, reacting for 60 minutes, adding the fatty acid polyoxyethylene ether, continuously stirring for 15 minutes, and adding water to dilute to obtain the humectant;
s4, pulping water and softwood pulp to obtain pulping liquid, and adding a waterproof agent, a softening agent, a deodorant and a humectant into the pulping liquid to obtain papermaking pulping liquid;
and S5, making 15g of roll paper by the papermaking slurry through a paper machine, and spinning the roll paper into yarns with the specification of 24-36S by a short-process fine spinning assembly line to obtain the woven sock yarns.
Preferably, in S4, the beater is stirred and beaten, the rotating speed of the beater is 720-780 rpm, and the beating time is 25-45 minutes.
Preferably, the stirring of the S3 is carried out by mixing and stirring the mixture in a reaction kettle, the rotating speed of a stirrer is 300-350r/min, and the temperature is controlled at 60-90 ℃ during stirring.
Preferably, in the step S1, the following raw materials in parts by weight are prepared: 300 parts of water, 70-110 parts of softwood pulp, 6-9 parts of a waterproof agent, 5-11 parts of a softening agent, 9-16 parts of water-absorbing resin, 7-11 parts of waterborne polyurethane, 26-34 parts of polyacrylamide, 18-32 parts of nano zinc oxide, 6-9 parts of hydrogen peroxide, 7-13 parts of deacetylated chitin, 9-16 parts of silver nitrate, 6-9 parts of pyrrolidone carboxylic acid ammonium, 6-13 parts of fatty acid polyoxyethylene ether and 15-28 parts of natural color resin.
Preferably, in the step S1, the following raw materials in parts by weight are prepared: 300 parts of water, 60-100 parts of softwood pulp, 5-8 parts of a waterproof agent, 4-10 parts of a softening agent, 8-14 parts of water-absorbing resin, 6-10 parts of waterborne polyurethane, 22-30 parts of polyacrylamide, 12-28 parts of nano zinc oxide by weight, 4-8 parts of hydrogen peroxide, 5-11 parts of deacetylated chitin, 7-14 parts of silver nitrate, 4-8 parts of ammonium pyrrolidone carboxylate, 2-11 parts of fatty acid polyoxyethylene ether and 12-23 parts of natural color resin.
Preferably, the water repellent is fluorine-containing acrylic resin, and the softening agent is any one of trialkyl phosphate, dialkyl phosphate and monoalkyl phosphate.
Preferably, in the step S2, the mixture is mixed by a stirrer, and the rotating speed of the stirrer is 220-300r/min.
The invention has the beneficial effects that:
the softwood pulp is used as a main manufacturing material of the sock yarn, and the water-absorbent resin is added in the manufacturing process, so that the manufactured sock material has good sweat absorption performance, the use comfort is improved, the feet cannot slip due to dampness, and a good anti-slip effect is achieved.
Through aqueous polyurethane, polyacrylamide, nanometer zinc oxide and hydrogen peroxide stirring mixture, make the smell removal agent, mix and prepare the socks yarn in the socks material for this material has fine deodorant performance of removing the smell, has fine antibiotic effect of disinfecting simultaneously, and effectual suppression bacterial growing promotes the whole performance of socks.
According to the invention, the chitosan and the silver nitrate are mixed and reacted, the pyrrolidone carboxylic acid ammonium and the fatty acid polyoxyethylene ether are added, the prepared humectant is injected into the manufactured paper pulp, so that the manufactured material has a good moisturizing effect, the manufactured socks play a moisturizing effect on feet, the problem of dry and cracked feet is solved, and the use quality is improved.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments.
Example one
A preparation method of functional sock yarns comprises the following steps:
s1, preparing the following raw materials in parts by weight: 300 parts of water, 60 parts of softwood pulp, 5 parts of a waterproof agent, 4 parts of a softening agent, 8 parts of water-absorbing resin, 6 parts of waterborne polyurethane, 22-34 parts of polyacrylamide, 12 parts of nano zinc oxide, 4 parts of hydrogen peroxide, 5 parts of deacetylated chitin, 7 parts of silver nitrate, 4 parts of ammonium pyrrolidone carboxylate, 2 parts of fatty acid polyoxyethylene ether and 12 parts of natural color resin;
s2, weighing the waterborne polyurethane, the polyacrylamide, the nano zinc oxide and the hydrogen peroxide in parts by weight, and stirring and mixing to prepare a deodorant;
s3, mixing the deacetylated chitin and the silver nitrate in parts by weight, reacting for 30 minutes, adding the ammonium pyrrolidone carboxylate, reacting for 60 minutes, adding the fatty acid polyoxyethylene ether, continuously stirring for 15 minutes, and adding water to dilute to obtain the humectant;
s4, pulping water and softwood pulp to obtain pulping liquid, adding a waterproof agent, a softening agent, a deodorant and a humectant into the pulping liquid, and uniformly stirring to obtain papermaking pulp;
and S5, making the papermaking slurry into 15g of roll paper by a paper machine, and spinning the roll paper into yarns with the specification of 24-36S by a short-process fine spinning assembly line to obtain the woven sock yarns.
In this embodiment, in S4, the beater is stirred and beaten, the rotation speed of the beater is 720 rpm, the beating time is 25 minutes, the stirring in S3 is performed by mixing and stirring in the reaction kettle, the rotation speed of the stirrer is 300r/min, and the temperature is controlled at 60 ℃ during stirring. The waterproof agent is fluorine-containing acrylic resin, and the softening agent is any one of trialkyl phosphate, dialkyl phosphate and monoalkyl phosphate.
Example two
A preparation method of functional sock yarns comprises the following steps:
s1, preparing the following raw materials in parts by weight: 300 parts of water, 135 parts of softwood pulp, 7 parts of a waterproof agent, 8 parts of a softening agent, 12 parts of water-absorbing resin, 9 parts of waterborne polyurethane, 28 parts of polyacrylamide, 22 parts of nano zinc oxide, 7 parts of hydrogen peroxide, 9 parts of deacetylated chitin, 12 parts of silver nitrate, 7 parts of ammonium pyrrolidone carboxylate, 8 parts of fatty acid polyoxyethylene ether and 20 parts of natural color resin;
s2, weighing the waterborne polyurethane, the polyacrylamide, the nano zinc oxide and the hydrogen peroxide in parts by weight, and stirring and mixing to prepare a deodorant;
s3, mixing the deacetylated chitin and the silver nitrate in parts by weight for reaction for 45 minutes, adding the ammonium pyrrolidone carboxylate, reacting for 60 minutes, adding the fatty acid polyoxyethylene ether, continuously stirring for 15 minutes, and adding water for dilution to obtain the humectant;
s4, pulping water and softwood pulp to obtain pulping liquid, adding a waterproof agent, a softening agent, a deodorant and a humectant into the pulping liquid, and uniformly stirring to obtain papermaking pulp;
and S5, papermaking slurry is made into 15g of roll paper through a papermaking machine, and the 15g of roll paper is spun into yarn with the specification of 30S through a short-process fine spinning assembly line to obtain the woven sock yarn.
In the embodiment, in S4, the beater is used for stirring and beating, the rotating speed of the beater is 750 rpm, the beating time is 25-45 minutes, the stirring in S3 is carried out through the reaction kettle, the rotating speed of the stirrer is 325r/min, and the temperature is controlled at 75 ℃ during stirring. The waterproof agent is fluorine-containing acrylic resin, and the softening agent is any one of trialkyl phosphate, dialkyl phosphate and monoalkyl phosphate. And in the step S2, mixing by using a stirrer, wherein the rotating speed of the stirrer is 260r/min.
EXAMPLE III
A preparation method of functional sock yarns comprises the following steps:
s1, preparing the following raw materials in parts by weight: 300 parts of water, 110 parts of softwood pulp, 9 parts of a waterproof agent, 11 parts of a softening agent, 16 parts of water-absorbing resin, 11 parts of waterborne polyurethane, 34 parts of polyacrylamide, 32 parts of nano zinc oxide, 9 parts of hydrogen peroxide, 13 parts of deacetylated chitin, 16 parts of silver nitrate, 9 parts of ammonium pyrrolidone carboxylate, 13 parts of fatty acid polyoxyethylene ether and 28 parts of natural color resin;
s2, weighing the waterborne polyurethane, the polyacrylamide, the nano zinc oxide and the hydrogen peroxide in parts by weight, and stirring and mixing to prepare a deodorant;
s3, mixing the deacetylated chitin and the silver nitrate in parts by weight, reacting for 60 minutes, adding the ammonium pyrrolidone carboxylate, reacting for 60 minutes, adding the fatty acid polyoxyethylene ether, continuously stirring for 15 minutes, and adding water to dilute to obtain the humectant;
s4, pulping water and softwood pulp to obtain pulping liquid, adding a waterproof agent, a softening agent, a deodorant and a humectant into the pulping liquid, and uniformly stirring to obtain papermaking pulp;
and S5, making the papermaking slurry into 15g of roll paper by a paper machine, and spinning the roll paper into 36S-sized yarns by a short-process fine spinning assembly line to obtain the woven sock yarns.
In the embodiment, in S4, the beater is used for stirring and beating, the rotating speed of the beater is 780 rpm, the beating time is 45 minutes, the stirring in S3 is carried out through the reaction kettle, the rotating speed of the stirrer is 350r/min, and the temperature is controlled at 90 ℃ during stirring. The waterproof agent is fluorine-containing acrylic resin, and the softening agent is any one of trialkyl phosphate, dialkyl phosphate and monoalkyl phosphate. And in the step S2, mixing by using a stirrer, wherein the rotating speed of the stirrer is 300r/min.
The softwood pulp is used as a main manufacturing material of the sock yarn, and the water-absorbent resin is added in the manufacturing process, so that the manufactured sock material has good sweat absorption performance, the use comfort is improved, the feet cannot be wet and slippery, and a good anti-skidding effect is achieved. Through aqueous polyurethane, polyacrylamide, nanometer zinc oxide and hydrogen peroxide stirring mixture, make the smell removal agent, mix and prepare socks yarn in the socks material for this material has the performance of fine deodorant smell removal, has fine bactericidal antibacterial effect simultaneously, and effectual suppression bacterial growing promotes the whole performance of socks. According to the invention, the chitosan and the silver nitrate are mixed and reacted, the pyrrolidone carboxylic acid ammonium and the fatty acid polyoxyethylene ether are added, the prepared humectant is injected into the manufactured paper pulp, so that the manufactured material has a good moisturizing effect, the manufactured socks play a moisturizing effect on feet, the problem of dry and cracked feet is solved, and the use quality is improved.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (7)
1. A preparation method of functional sock yarns is characterized by comprising the following steps:
s1, preparing the following raw materials in parts by weight: 300 parts of water, 60-110 parts of softwood pulp, 5-9 parts of a waterproof agent, 4-11 parts of a softening agent, 8-16 parts of water-absorbent resin, 6-11 parts of waterborne polyurethane, 22-34 parts of polyacrylamide, 12-32 parts of nano zinc oxide, 4-9 parts of hydrogen peroxide, 5-13 parts of deacetylated chitin, 7-16 parts of silver nitrate, 4-9 parts of ammonium pyrrolidone carboxylate, 2-13 parts of fatty acid polyoxyethylene ether and 12-28 parts of natural color resin;
s2, weighing the waterborne polyurethane, the polyacrylamide, the nano zinc oxide and the hydrogen peroxide in parts by weight, and stirring and mixing to prepare a deodorant;
s3, mixing the deacetylated chitin and the silver nitrate in parts by weight, reacting for 30-60 minutes, adding the ammonium pyrrolidone carboxylate, reacting for 60 minutes, adding the fatty acid polyoxyethylene ether, continuously stirring for 15 minutes, and adding water to dilute to obtain the humectant;
s4, pulping water and softwood pulp to obtain pulping liquid, and adding a waterproof agent, a softening agent, a deodorant and a humectant into the pulping liquid to obtain papermaking pulp;
and S5, making the papermaking slurry into 15g of roll paper by a paper machine, and spinning the roll paper into yarns with the specification of 24-36S by a short-process fine spinning assembly line to obtain the woven sock yarns.
2. The method as claimed in claim 1, wherein in S4, the beater is used for beating under stirring, the rotating speed of the beater is 720-780 rpm, and the beating time is 25-45 minutes.
3. The method for preparing a functional sock yarn according to claim 1, wherein the stirring of S3 is performed by mixing and stirring in a reaction kettle at a stirrer speed of 300-350r/min, and the temperature is controlled at 60-90 ℃.
4. The method for preparing functional sock yarn according to claim 1, wherein in the step S1, the following raw materials are prepared in parts by weight: 300 parts of water, 70-110 parts of softwood pulp, 6-9 parts of a waterproof agent, 5-11 parts of a softening agent, 9-16 parts of water-absorbing resin, 7-11 parts of waterborne polyurethane, 26-34 parts of polyacrylamide, 18-32 parts of nano zinc oxide, 6-9 parts of hydrogen peroxide, 7-13 parts of deacetylated chitin, 9-16 parts of silver nitrate, 6-9 parts of pyrrolidone carboxylic acid ammonium, 6-13 parts of fatty acid polyoxyethylene ether and 15-28 parts of natural color resin.
5. The method for preparing a functional sock yarn according to claim 1, wherein in S1, the following raw materials are prepared in parts by weight: 300 parts of water, 60-100 parts of softwood pulp, 5-8 parts of a waterproof agent, 4-10 parts of a softening agent, 8-14 parts of water-absorbing resin, 6-10 parts of waterborne polyurethane, 22-30 parts of polyacrylamide, 12-28 parts of nano zinc oxide by weight, 4-8 parts of hydrogen peroxide, 5-11 parts of deacetylated chitin, 7-14 parts of silver nitrate, 4-8 parts of ammonium pyrrolidone carboxylate, 2-11 parts of fatty acid polyoxyethylene ether and 12-23 parts of natural color resin.
6. The method for preparing functional sock yarns according to claim 1, wherein the water repellent agent is fluorine-containing acrylic resin, and the softening agent is any one of trialkyl phosphate, dialkyl phosphate and monoalkyl phosphate.
7. The method for preparing a functional sock yarn of claim 1, wherein in S2, the mixing is performed by a blender with a rotation speed of 220-300r/min.