CN108677249A - A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate - Google Patents
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate Download PDFInfo
- Publication number
- CN108677249A CN108677249A CN201810858474.8A CN201810858474A CN108677249A CN 108677249 A CN108677249 A CN 108677249A CN 201810858474 A CN201810858474 A CN 201810858474A CN 108677249 A CN108677249 A CN 108677249A
- Authority
- CN
- China
- Prior art keywords
- cocoon
- silk
- processing method
- production rate
- reelability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, which includes：1. by fresh silk cocoon be placed on intensity of illumination be 2700 ~ 3100lux under conditions of select, removal light defective cocoon, dupion, under rotten cocoon；2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction for 32~35 DEG C of auxiliary agent one after 0.0101~0.0102Mpa, is added, water inlet is higher by 6 ~ 8cm of cocoon, and the time of osmotic absorbent is 6~10min；3. step silk cocoon 2. is carried out cocoon cooking, the temperature of control cocoon cooking water is 55~65 DEG C when cocoon cooking, the time is 6~8min, PH is controlled 4.9~5.7；4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., the auxiliary agent two of the warm water quality 0.6%~0.9% is then added, is impregnated 30 minutes~60 minutes；5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.Method using the present invention promotes sericulture, the development of Silk Industry improves.
Description
Technical field
The present invention relates to agriculture fields, more particularly to a kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate.
Background technology
Silk cocoon refers to the cocoon of silkworm.The scrotiform protective layer in silkworm pupa time, includes pupal cell.Cocoon layer can be with filature, husks and reel silk from cocoons
Waste silk after system can make silk flosssilk wadding and silk spinning raw material.
Silk cocoon is slightly hung contracting in the different shapes such as oblong, elliptical beam kidney-shaped, spherical shape or spindle or middle part, cocoon have it is white,
The colors such as Huang, pale green, flesh-coloured are about 3~4 centimetres, and 1.7~2.1 centimetres of diameter, superficial white has irregular wrinkle, and has attached
The silk is in villiform.The silking of its inner wall is very regular.It is light and tough, it is not easy to tear.Silk cocoon without emergence, inside has
The integument of the light brown, shrinkage taken off before 1 piece of the silkworm chrysalis of yellowish-brown and pupa.
Since reform and opening-up, new technology high-tech research achievement is constantly converted into productivity, has pushed economic development acquirement
Huge benefit.New and high technology also begins to be applied in Silk Industry.But traditional backwardness technical method still accounts for importantly
Position, the development for hindering industry improve.
The complexity of the unwinding dissociation of silk when referring to filature, reelability percentage are exactly the percentage of length of non broken filament and silk length.
Reelability percentage is also the index for weighing silk dissociation complexity, and reelability percentage is high, indicates that silk is easy dissociation, is conducive to Silk Mill's filature,
It is on the contrary then indicate that cocoon quality is poor.Silk production rate：The silk amount that reel silk from cocoons obtains to the percentage of cocoon commercial weight, get on the bus cocoon silk production rate and hair cocoon by silk production rate point
Silk production rate, reelability percentage, silk production rate are an important indicators for weighing cocoon quality, and cocoon cooking process is mainly to improve reelability percentage, go out
Silk rate centered on, reelability percentage, silk production rate height directly affect the yield and quality of raw silk and the economic benefit of Silk Mill.It is existing
Silk cocoon processing method reelability percentage, silk production rate are relatively low, and in practical operation, often centered on improving reelability percentage, in order to carry
High reelability rate cannot meet the requirement of Industry Quick Development often suitably to sacrifice silk production rate level as cost, present invention one kind
Improve silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate.
Invention content
The present invention solves the technical problem of existing silk cocoon processing method reelability percentage, silk production rate are relatively low, and in reality
In the operation of border, often centered on improving reelability percentage, in order to improve reelability percentage often suitably to sacrifice silk production rate level as cost,
The requirement of Industry Quick Development cannot be met.
In order to solve the above technical problems, a technical solution of this use is：A kind of raising silkworm cocoon reelability rate, wire vent are provided
The silk cocoon processing method of rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, 32~35 DEG C of auxiliary agent one is added, water inlet is higher by 6~8cm of cocoon, and the time of osmotic absorbent is 6~10min；；
3. step silk cocoon 2. is subjected to cocoon cooking, when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 4.9~5.7；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., then add the warm water quality 0.6%~
0.9% auxiliary agent two impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Further, the auxiliary agent one is selected from dodecyl sodium sulfate, fatty glyceride, cocoyl glucoside, fluorination
One or more mixtures in alkyl phosphoric acid sodium.
Further, the auxiliary agent one is the aqueous solution of cocoyl glucoside.
The cocoyl glucoside is at least chemical rank.
Further, the cocoyl glucoside concentration of aqueous solution is 4.9~7.8wt%.
Further, the cocoyl glucoside concentration of aqueous solution is 6.1wt%.
Further, 3. middle PH is controlled 5.2 the step.
Further, the auxiliary agent two is the aqueous solution containing lactic acid bacteria, saccharomycete, bacteria cellulose.
Further, the auxiliary agent two is 1.1~3.3wt% saccharomycete containing 0.5~1.3wt% lactic acid bacterias, 0.9~
The mixed aqueous solution of 3.6wt% bacteria celluloses.
Further, the auxiliary agent two is lactic acid bacteria containing 0.9wt%, 2.3wt% saccharomycete, 1.9wt% bacteria celluloses
Mixed aqueous solution.
Further, the step 4. in the addition warm water quality 0.72% auxiliary agent two.
The beneficial effects of the invention are as follows：Silk is mainly made of fibroin with the silk gum for being attached to fibroin periphery, is still contained a small amount of
The substances such as grease type, pigment, inorganic matter.When matured silkworm spins, makes fibroin fiber by means of the adhesive action of silk gum and synthesize silk, and
It is mutually deadlocked to constitute close not random cocoon layer, keep the shape of silk cocoon.Cocoon cooking is exactly to keep silk peripheral using the effect of water, heat
The appropriate swelling of silk gum, softening and dissolving weaken the interparticle combination of silk gum, its deadlocked power is made to reduce, and make in cocoon layer between cocoon layer
It is deadlocked to tend to uniform, so that silk when filature is continuously sequentially dissociated, and boundling obvolvent is at the process of synnema.But according to current practice
From the point of view of, it relies solely on and changes steaming, infiltration, cocoon cooking and silk reeling technology to adjust the cooked state of silkworm cocoon, although can be in certain journey
Improve cocoon cooking effect on degree, promote the raising of Silk Reeling, but the needs of filature production far can not be met sometimes, the present invention
Auxiliary agent is added during cocoon cooking, promotes sericin within cocoon layer in water under the collective effect of heat using their physicochemical property
Appropriate swelling, dissolving and softening, to achieve the purpose that improve reelability percentage, silk production rate.
Specific implementation mode
Embodiment 1
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, the cocoyl glucoside aqueous solution of 32~35 DEG C of a concentration of 6.1wt% is added, water inlet is higher by 6~8cm of cocoon, oozes
The time to absorb water thoroughly is 6~10min；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 5.2；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., helping for the warm water quality 0.72% is then added
Agent two, wherein auxiliary agent two be 0.9wt% lactic acid bacterias, 2.3wt% saccharomycete, the mixed aqueous solution of 1.9wt% bacteria celluloses,
It impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 2
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, the sodium dodecyl sulfate aqueous solution of 32~35 DEG C of a concentration of 4.9~7.8wt% is added, water inlet is higher by cocoon 6
The time of~8cm, osmotic absorbent are 6~10min；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 5.2；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., helping for the warm water quality 0.72% is then added
Agent two, wherein auxiliary agent two be 0.9wt% lactic acid bacterias, 2.3wt% saccharomycete, the mixed aqueous solution of 1.9wt% bacteria celluloses,
It impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 3
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, be added 32~35 DEG C of a concentration of 4.9~7.8wt% fatty acid glycerine aqueous solution of ester, water inlet be higher by cocoon 6~
The time of 8cm, osmotic absorbent are 6~10min；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 5.2；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., helping for the warm water quality 0.72% is then added
Agent two, wherein auxiliary agent two be 0.9wt% lactic acid bacterias, 2.3wt% saccharomycete, the mixed aqueous solution of 1.9wt% bacteria celluloses,
It impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 4
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, the fluorinated alkyl sodium phosphate aqueous solution of 32~35 DEG C of a concentration of 4.9~7.8wt% is added, water inlet is higher by cocoon 6
The time of~8cm, osmotic absorbent are 6~10min；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 5.2；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., helping for the warm water quality 0.72% is then added
Agent two, wherein auxiliary agent two be 0.9wt% lactic acid bacterias, 2.3wt% saccharomycete, the mixed aqueous solution of 1.9wt% bacteria celluloses,
It impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 5
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, the cocoyl glucoside aqueous solution of 32~35 DEG C of a concentration of 6.1wt% is added, water inlet is higher by 6~8cm of cocoon, oozes
The time to absorb water thoroughly is 6~10min；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 4.9~5.7；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., helping for the warm water quality 0.72% is then added
Agent two, wherein auxiliary agent two be 0.9wt% lactic acid bacterias, 2.3wt% saccharomycete, the mixed aqueous solution of 1.9wt% bacteria celluloses,
It impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 6
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, the cocoyl glucoside aqueous solution of 32~35 DEG C of a concentration of 6.1wt% is added, water inlet is higher by 6~8cm of cocoon, oozes
The time to absorb water thoroughly is 6~10min；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 4.9~5.7；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., helping for the warm water quality 0.72% is then added
Agent two, wherein auxiliary agent two be 0.5wt% lactic acid bacterias, 3.3wt% saccharomycete, the mixed aqueous solution of 0.9wt% bacteria celluloses,
It impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 7
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, the cocoyl glucoside aqueous solution of 32~35 DEG C of a concentration of 6.1wt% is added, water inlet is higher by 6~8cm of cocoon, oozes
The time to absorb water thoroughly is 6~10min；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 4.9~5.7；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., helping for the warm water quality 0.72% is then added
Agent two, wherein auxiliary agent two be 1.3wt% lactic acid bacterias, 1.1wt% saccharomycete, the mixed aqueous solution of 3.6wt% bacteria celluloses,
It impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 8
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, the cocoyl glucoside aqueous solution of 32~35 DEG C of a concentration of 6.1wt% is added, water inlet is higher by 6~8cm of cocoon, oozes
The time to absorb water thoroughly is 6~10min；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 5.2；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., helping for the warm water quality 0.6% is then added
Agent two, wherein auxiliary agent two be 0.9wt% lactic acid bacterias, 2.3wt% saccharomycete, the mixed aqueous solution of 1.9wt% bacteria celluloses,
It impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 9
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, the cocoyl glucoside aqueous solution of 32~35 DEG C of a concentration of 6.1wt% is added, water inlet is higher by 6~8cm of cocoon, oozes
The time to absorb water thoroughly is 6~10min；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 5.2；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., helping for the warm water quality 0.9% is then added
Agent two, wherein auxiliary agent two be 0.9wt% lactic acid bacterias, 2.3wt% saccharomycete, the mixed aqueous solution of 1.9wt% bacteria celluloses,
It impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 10
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, 32~35 DEG C of water are added, water inlet is higher by 6~8cm of cocoon, and the time of osmotic absorbent is 6~10min；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 5.2；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., helping for the warm water quality 0.72% is then added
Agent two, wherein auxiliary agent two be 0.9wt% lactic acid bacterias, 2.3wt% saccharomycete, the mixed aqueous solution of 1.9wt% bacteria celluloses,
It impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 11
A kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, the processing method include：
1. by fresh silk cocoon be placed on intensity of illumination be 2700~3100lux under conditions of select, removal light defective cocoon, dupion,
Under rotten cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~
After 0.0102Mpa, the cocoyl glucoside aqueous solution of 32~35 DEG C of a concentration of 6.1wt% is added, water inlet is higher by 6~8cm of cocoon, oozes
The time to absorb water thoroughly is 6~10min；；
3. by cocoon cooking is carried out through step silk cocoon 2., when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~
8min, PH are controlled 5.2；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., impregnate 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
Embodiment 12
Using the silk cocoon processing method of embodiment 1~11, hereinafter referred to as embodiment 1~11, the unwinding of processing method is measured
Rate, silk production rate are as follows：
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair
Equivalent structure or equivalent flow shift made by bright description is applied directly or indirectly in other relevant technology necks
Domain is included within the scope of the present invention.
Claims (10)
1. a kind of raising silkworm cocoon reelability rate, the silk cocoon processing method of silk production rate, which is characterized in that the processing method includes：
1. by fresh silk cocoon be placed on intensity of illumination be 2700 ~ 3100lux under conditions of select, removal light defective cocoon, dupion, under it is rotten
Cocoon；
2. will be first put into vacuum pump through the silk cocoon of step 1., then vacuum pump suction be 0.0101~0.0102Mpa
Afterwards, 32~35 DEG C of auxiliary agent one is added, water inlet is higher by 6 ~ 8cm of cocoon, and the time of osmotic absorbent is 6~10min；
3. step silk cocoon 2. is subjected to cocoon cooking, when cocoon cooking the temperature of control cocoon cooking water be 55~65 DEG C, the time be 6~8min,
PH is controlled 4.9~5.7；
4. by being put into 25 DEG C~30 DEG C warm water through the silk cocoon of step 3., the warm water quality 0.6%~0.9% is then added
Auxiliary agent two impregnates 30 minutes~60 minutes；
5. by through step 4. in obtained silk cocoon be water-cooled to room temperature by 30~40 DEG C, then carry out filature.
2. a kind of raising silkworm cocoon reelability rate according to claim 1, the silk cocoon processing method of silk production rate, which is characterized in that
The one kind of the auxiliary agent one in dodecyl sodium sulfate, fatty glyceride, cocoyl glucoside, fluorinated alkyl sodium phosphate
Or a variety of mixture.
3. a kind of raising silkworm cocoon reelability rate according to claim 2, the silk cocoon processing method of silk production rate, which is characterized in that
The auxiliary agent one is the aqueous solution of cocoyl glucoside.
4. a kind of raising silkworm cocoon reelability rate according to claim 3, the silk cocoon processing method of silk production rate, which is characterized in that
The cocoyl glucoside concentration of aqueous solution is 4.9 ~ 7.8wt%.
5. a kind of raising silkworm cocoon reelability rate according to claim 4, the silk cocoon processing method of silk production rate, which is characterized in that
The cocoyl glucoside concentration of aqueous solution is 6.1wt%.
6. a kind of raising silkworm cocoon reelability rate according to claim 1, the silk cocoon processing method of silk production rate, which is characterized in that
3. middle PH is controlled 5.2 the step.
7. a kind of raising silkworm cocoon reelability rate according to claim 1, the silk cocoon processing method of silk production rate, which is characterized in that
The auxiliary agent two is the aqueous solution containing lactic acid bacteria, saccharomycete, bacteria cellulose.
8. a kind of raising silkworm cocoon reelability rate according to claim 7, the silk cocoon processing method of silk production rate, which is characterized in that
The auxiliary agent two is containing 0.5 ~ 1.3wt% lactic acid bacterias, 1.1 ~ 3.3wt% saccharomycete, the mixing water of 0.9 ~ 3.6wt% bacteria celluloses
Solution.
9. a kind of raising silkworm cocoon reelability rate according to claim 8, the silk cocoon processing method of silk production rate, which is characterized in that
The auxiliary agent two is lactic acid bacteria containing 0.9wt%, 2.3wt% saccharomycete, the mixed aqueous solution of 1.9wt% bacteria celluloses.
10. a kind of raising silkworm cocoon reelability rate according to claim 1, the silk cocoon processing method of silk production rate, which is characterized in that
The step 4. in the addition warm water quality 0.72% auxiliary agent two.