CN115259820A - 一种超高强度混凝土 - Google Patents
一种超高强度混凝土 Download PDFInfo
- Publication number
- CN115259820A CN115259820A CN202210759541.7A CN202210759541A CN115259820A CN 115259820 A CN115259820 A CN 115259820A CN 202210759541 A CN202210759541 A CN 202210759541A CN 115259820 A CN115259820 A CN 115259820A
- Authority
- CN
- China
- Prior art keywords
- agent
- concrete
- strength concrete
- ultra
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种超高强度混凝土，涉及混凝土技术领域，为解决现有混凝土受外力易损坏，导致混凝土强度差的问题。包括以下重量百分数配比的原料制成：水泥30‑40％；粗骨料5‑15％；细骨料1‑10％；轻骨料1‑10％；水20‑35％；火山灰1‑8％；粘土1‑10％；石膏1‑5％；外加剂1‑10％；改善剂1‑7％；耐腐蚀料1‑5％；耐高温纤维1‑5％；龙虾壳1‑5％；所述外加剂为混凝土加强剂、减水剂、引气剂和泵送剂中的一种或多种，所述改善剂为凝结剂、膨胀剂、着色剂、防冻剂和防水剂中的一种或多种，所述凝结剂为缓凝剂、早强剂和速凝剂中的一种或多种。
Description
技术领域
本发明涉及混凝土技术领域，具体为一种超高强度混凝土。
背景技术
混凝土是指由胶凝材料将集料胶结成整体的工程复合材料的统称。通常讲的混凝土一词是指用水泥作胶凝材料，砂、石作集料，与水按一定比例配合，经搅拌而得的水泥混凝土，也称普通混凝土，它广泛应用于土木工程；
例如公告号为CN108164284B的中国授权专利(透水混凝土)：包括水泥470～520kg，粗骨料1300～1600kg，水100～140kg，矿粉30～80kg，硅灰40～110kg，减水剂4～5kg，疏水剂3～5kg，有机纤维20～60kg，疏水性二氧化硅气凝胶150～230kg；其中所述疏水性二氧化硅气凝胶为硅烷改性二氧化硅气凝胶和酚醛树脂-二氧化硅气凝胶按照质量比为(1 -3)：(1-3)混合而成。本发明所述透水混凝土，具有良好的透水性能，并且还可以防止因雨水长期积留于透水混凝土内部而导致混凝土发生冻融破坏，改善透水混凝土的抗冻融性能。
但是，现有混凝土受外力易损坏，导致混凝土强度差；因此，不满足现有的需求，对此我们提出了一种超高强度混凝土。
发明内容
本发明的目的在于提供一种超高强度混凝土，以解决上述背景技术中提出的现有混凝土受外力易损坏，导致混凝土强度差的问题。
为实现上述目的，本发明提供如下技术方案：一种超高强度混凝土，包括以下重量百分数配比的原料制成：
水泥30-40％；
粗骨料5-15％；
细骨料1-10％；
轻骨料1-10％；
水20-35％；
火山灰1-8％；
粘土1-10％；
石膏1-5％；
外加剂1-10％；
改善剂1-7％；
耐腐蚀料1-5％；
耐高温纤维1-5％；
龙虾壳1-5％。
优选的，所述外加剂为混凝土加强剂、减水剂、引气剂和泵送剂中的一种或多种。
优选的，所述改善剂为凝结剂、膨胀剂、着色剂、防冻剂和防水剂中的一种或多种。
优选的，所述凝结剂为缓凝剂、早强剂和速凝剂中的一种或多种。
优选的，所述耐腐蚀料为石墨烯、硫黄和聚合物中的一种或多种。
优选的，所述聚合物为聚甲醛、聚碳酸酯、聚砜、聚酰亚胺和聚芳醚中的一种或多种。
优选的，所述耐高温纤维为石棉纤维、玻璃纤维、金属纤维、氮佬硼纤维和陶瓷纤维中的一种或多种。
优选的，所述粗骨料为碎石、卵石、碎砖和重矿渣中的一种或多种。
优选的，所述轻骨料为浮石、火山渣、陶粒、膨胀珍珠岩和膨胀矿渣中的一种或多种。
优选的，所述龙虾壳需要经过洗净、去油和烘干之后再集中进行研磨成粉。
与现有技术相比，本发明的有益效果是：
1、本发明通过在混凝土混合内部添加了改善剂，改善剂为凝结剂、膨胀剂、着色剂、防冻剂和防水剂中的一种或多种，其中凝结剂为缓凝剂、早强剂和速凝剂中的一种或多种，缓凝剂、早强剂和速凝剂可以调节混凝土凝结时间，使其快速凝结，从而可以提前起到坚硬的效果，这样就不易受到外力破坏，并且通过防冻剂和防水剂可以提高混凝土长期在室外的使用寿命，尤其是在天气寒冷和暴雨天气，不易受冻开裂损坏，也不易在暴雨天气长期积水造成内部腐蚀损坏，从而提高混凝土整体的强度。
2、通过在混凝土混合内部添加了耐腐蚀料，耐腐蚀料为石墨烯、硫黄和聚合物中的一种或多种，并且聚合物为聚甲醛、聚碳酸酯、聚砜、聚酰亚胺和聚芳醚中的一种或多种，石墨烯的结构非常稳定，石墨烯内部的碳原子之间的连接很柔韧，当施加外力于石墨烯时，碳原子面会弯曲变形，使得碳原子不必重新排列来适应外力，从而保持结构稳定，这种稳定的晶格结构使石墨烯具有优秀的导热性，从而使混凝土具有高稳定和高导热性能，不易开裂，同时石墨烯还具有高强度性能，硫黄可耐浓度为1％的NaOH 溶液腐蚀，聚合物可耐浓度不超过50％的NaOH溶液腐蚀，提高混凝土的耐腐蚀性和使用寿命，从而石墨烯与硫黄和聚合物配合使用，可进一步提高混凝土的强度。
3、通过在混凝土混合内部添加了耐高温纤维，耐高温纤维为石棉纤维、玻璃纤维、金属纤维、氮佬硼纤维和陶瓷纤维中的一种或多种，提高混凝土耐高温性能，保障其在室外并且车辆不停行驶的时候不易软化变形，提高强度和使用寿命。
4、通过在混凝土混合内部添加了经过洗净、去油和烘干之后再集中进行研磨成粉的龙虾壳，龙虾壳具有耐高温性能，在高温环境中可以保持高硬度，放入混凝土中可以提高混凝土的硬度和耐高温性能，车辆长期形式不易出现底面凹陷现象，并且还实现了垃圾回收再利用的效果，提高环境保护。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
实施例1
一种超高强度混凝土，包括以下重量百分数配比的原料制成：
水泥30％；
粗骨料5％；
细骨料10％；
轻骨料5％；
水20％；
火山灰3％；
粘土5％；
石膏2％；
外加剂5％；
改善剂4％；
耐腐蚀料5％；
耐高温纤维3％；
龙虾壳3％。
进一步，外加剂为混凝土加强剂和减水剂。
进一步，改善剂为凝结剂、防冻剂和防水剂。
进一步，凝结剂为速凝剂。
进一步，耐腐蚀料为石墨烯和聚合物。
进一步，聚合物为聚甲醛和聚芳醚。
进一步，耐高温纤维为玻璃纤维、金属纤维和陶瓷纤维。
进一步，粗骨料为碎石、卵石、碎砖和重矿渣。
进一步，轻骨料为陶粒和膨胀珍珠岩。
进一步，龙虾壳需要经过洗净、去油和烘干之后再集中进行研磨成粉。
实施例2
一种超高强度混凝土，包括以下重量百分数配比的原料制成：
水泥35％；
粗骨料5％；
细骨料5％；
轻骨料5％；
水25％；
火山灰3％；
粘土3％；
石膏3％；
外加剂5％；
改善剂3％；
耐腐蚀料2％；
耐高温纤维2％；
龙虾壳4％。
进一步，外加剂为混凝土加强剂和引气剂。
进一步，改善剂为凝结剂和防冻剂。
进一步，凝结剂为缓凝剂和速凝剂。
进一步，耐腐蚀料为硫黄和聚合物。
进一步，聚合物为聚甲醛和聚碳酸酯。
进一步，耐高温纤维为石棉纤维和玻璃纤维。
进一步，粗骨料为碎石、卵石和碎砖。
进一步，轻骨料为火山渣、陶粒和膨胀珍珠岩。
进一步，龙虾壳需要经过洗净、去油和烘干之后再集中进行研磨成粉。
实施例3
一种超高强度混凝土，包括以下重量百分数配比的原料制成：
水泥33％；
粗骨料10％；
细骨料3％；
轻骨料5％；
水25％；
火山灰6％；
粘土5％；
石膏1％；
外加剂2％；
改善剂2％；
耐腐蚀料3％；
耐高温纤维2％；
龙虾壳3％。
进一步，外加剂为混凝土加强剂和减水剂。
进一步，改善剂为凝结剂和防水剂。
进一步，凝结剂为缓凝剂。
进一步，耐腐蚀料为硫黄和聚合物。
进一步，聚合物为聚碳酸酯、聚酰亚胺和聚芳醚。
进一步，耐高温纤维为石棉纤维、氮佬硼纤维和陶瓷纤维。
进一步，粗骨料为碎石、碎砖和重矿渣。
进一步，轻骨料为浮石、陶粒、和膨胀矿渣。
进一步，龙虾壳需要经过洗净、去油和烘干之后再集中进行研磨成粉。
实施例4
一种超高强度混凝土，包括以下重量百分数配比的原料制成：
水泥40％；
粗骨料5％；
细骨料1％；
轻骨料1％；
水30％；
火山灰1％；
粘土4％；
石膏1％；
外加剂5％；
改善剂1％；
耐腐蚀料2％；
耐高温纤维4％；
龙虾壳5％。
进一步，外加剂为混凝土加强剂、减水剂和引气剂。
进一步，改善剂为凝结剂。
进一步，凝结剂为缓凝剂。
进一步，耐腐蚀料为石墨烯和聚合物中的一种或多种。
进一步，聚合物为聚甲醛和聚碳酸酯。
进一步，耐高温纤维为石棉纤维、玻璃纤维、金属纤维和陶瓷纤维。
进一步，粗骨料为碎石、卵石、碎砖和重矿渣。
进一步，轻骨料为陶粒。
进一步，龙虾壳需要经过洗净、去油和烘干之后再集中进行研磨成粉。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
Claims (10)
1.一种超高强度混凝土，其特征在于：包括以下重量百分数配比的原料制成：
水泥30-40％；
粗骨料5-15％；
细骨料1-10％；
轻骨料1-10％；
水20-35％；
火山灰1-8％；
粘土1-10％；
石膏1-5％；
外加剂1-10％；
改善剂1-7％；
耐腐蚀料1-5％；
耐高温纤维1-5％；
龙虾壳1-5％。
2.根据权利要求1所述的一种超高强度混凝土，其特征在于：所述外加剂为混凝土加强剂、减水剂、引气剂和泵送剂中的一种或多种。
3.根据权利要求1所述的一种超高强度混凝土，其特征在于：所述改善剂为凝结剂、膨胀剂、着色剂、防冻剂和防水剂中的一种或多种。
4.根据权利要求3所述的一种超高强度混凝土，其特征在于：所述凝结剂为缓凝剂、早强剂和速凝剂中的一种或多种。
5.根据权利要求1所述的一种超高强度混凝土，其特征在于：所述耐腐蚀料为石墨烯、硫黄和聚合物中的一种或多种。
6.根据权利要求5所述的一种超高强度混凝土，其特征在于：所述聚合物为聚甲醛、聚碳酸酯、聚砜、聚酰亚胺和聚芳醚中的一种或多种。
7.根据权利要求1所述的一种超高强度混凝土，其特征在于：所述耐高温纤维为石棉纤维、玻璃纤维、金属纤维、氮佬硼纤维和陶瓷纤维中的一种或多种。
8.根据权利要求1所述的一种超高强度混凝土，其特征在于：所述粗骨料为碎石、卵石、碎砖和重矿渣中的一种或多种。
9.根据权利要求1所述的一种超高强度混凝土，其特征在于：所述轻骨料为浮石、火山渣、陶粒、膨胀珍珠岩和膨胀矿渣中的一种或多种。
10.根据权利要求1所述的一种超高强度混凝土，其特征在于：所述龙虾壳需要经过洗净、去油和烘干之后再集中进行研磨成粉。