CN115246727A - 一种透水混凝土 - Google Patents
一种透水混凝土 Download PDFInfo
- Publication number
- CN115246727A CN115246727A CN202210884411.6A CN202210884411A CN115246727A CN 115246727 A CN115246727 A CN 115246727A CN 202210884411 A CN202210884411 A CN 202210884411A CN 115246727 A CN115246727 A CN 115246727A
- Authority
- CN
- China
- Prior art keywords
- concrete
- additive
- adhesive
- improving
- pervious concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种透水混凝土，涉及混凝土技术领域，为解决现有的透水混凝土容易冻结开裂，且火焰容易从孔隙中穿过，从而达不到防火效果在的问题。包括以下质量百分比的组分：水泥30％‑40％；水20％‑30％；骨料10％‑20％；掺合料5％‑10％；混凝土添加剂1％‑5％；粘合剂1％‑5％；色粉1％；膨胀珍珠岩5％‑10％；碎化玻纤网格布3％‑5％；防火膨胀橡胶颗粒3％‑5％；聚氨酯橡胶颗粒3％‑5％，所述水泥为硅酸盐水泥、普通硅酸盐水泥和矿渣硅盐水泥中的一种。
Description
技术领域
本发明涉及混凝土技术领域，具体为一种透水混凝土。
背景技术
透水混凝土孔隙较多，在冬季下雨环境下，气温骤然下降，导致表面水结 冰，易使透水混凝土冻结开裂。
现有的透水混凝土容易冻结开裂，且火焰容易从孔隙中穿过，从而达不到 防火效果，为此，我们提供一种透水混凝土。
发明内容
本发明的目的在于提供一种透水混凝土，以解决上述背景技术中提出的现 有的透水混凝土容易冻结开裂，且火焰容易从孔隙中穿过，从而达不到防火效 果的问题。
为实现上述目的，本发明提供如下技术方案：一种透水混凝土，包括以下 质量百分比的组分：
水泥30％-40％；
水20％-30％；
骨料10％-20％；
掺合料5％-10％；
混凝土添加剂1％-5％；
粘合剂1％-5％；
色粉1％；
膨胀珍珠岩5％-10％；
碎化玻纤网格布3％-5％；
防火膨胀橡胶颗粒3％-5％；
聚氨酯橡胶颗粒3％-5％。
优选的，所述水泥为硅酸盐水泥、普通硅酸盐水泥和矿渣硅盐水泥中的一 种。
优选的，所述掺合料为硅灰、粉煤灰、矿渣微细粉中的一种或多种。
优选的，所述骨料为单粒级或间断粒级的粗骨料作为骨架，其中，总骨料 15％-25％占比为细骨料。
优选的，所述混凝土添加剂分为改善混凝土拌合物流变性能的外加剂、调 节混凝土凝结时间、硬化性能的外加剂、改善混凝土耐久性的外加剂以及改善 混凝土其它性能的外加剂中的一种或多种组成。
优选的，所述改善混凝土拌合物流变性能的外加剂包括减水剂、引气剂、 泵送剂，调节混凝土凝结时间、硬化性能的外加剂包括缓凝剂、早强剂、速凝 剂，改善混凝土耐久性的外加剂包括引气剂、防水剂和阻锈剂，改善混凝土其 它性能的外加剂包括膨胀剂、着色剂、防冻剂。
优选的，所述粘合剂为树脂粘合剂，包括热固性树脂胶粘剂、热塑性树脂 胶粘剂和混合型胶粘剂。
优选的，所述热固性胶粘剂为酚醛、眠醛、三聚氰胺、环氧、聚氨酯、不 饱和聚酯、有机硅树脂、杂环聚合物中的一种或多种；热塑性胶粘剂为聚醋酸 乙烯醋、乙烯-醋酸乙烯共聚物、聚乙烯醇、聚乙烯醇缩醛、聚丙烯酸酯中的一 种或多种，混合型胶粘剂为a-氰基丙烯酸酯、厌氧性丙烯酸双酷、聚氯乙烯、 聚酞胺、聚矾；酚醛-缩醛、环氧-聚酰胺、环氧-聚矾、酚醛-丁腈、环氧-丁腈、 酚醛-氯丁-和橡胶改性丙烯酸醋中的一种或多种。
优选的，所述防火膨胀橡胶颗粒为三元乙丙橡胶。
优选的，所述网格布是以中碱或无碱玻纤维纱织造，经耐碱高分子乳液涂 覆而成。
与现有技术相比，本发明的有益效果是：
1、本发明通过在透水混凝土内加入碎化玻纤网格布起到加强孔隙与孔隙 之间连接性的效果，并且其能够增强骨架，使透水混凝土更加的稳定，网格布 具有通孔结构，使其不会影响孔隙正常透水，碎化后的网格布体积减小，能够 更加方便的分布在孔隙之间，并搭配树脂粘合剂粘接孔隙，使孔隙牢固性提高， 自身具备的保温、防水、防火、抗裂等特性，能够提高透水混凝土的冬季抗开 裂效果。
2、防火膨胀橡胶颗粒为三元乙丙橡胶，其在火灾发生时，能够起到遇火膨 胀的效果，使防火膨胀橡胶颗粒体积增大，将孔隙堵塞，使透水混凝土的防火 性能得到提高，减少火焰与烟气从孔隙外泄范围。
3、聚氨酯橡胶颗粒具有良好隔音吸音效果，在透水混凝土自身降噪的前提 下，其能够进一步提高透水混凝土的降噪效果。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整 地描述，显然，所描述的实施例仅是本发明一部分实施例，而不是全部的实施 例。
实施例1
一种透水混凝土，包括以下质量百分比的组分：
水泥35％；
水25％；
骨料10％；
掺合料5％；
混凝土添加剂2％；
粘合剂2％；
色粉1％；
膨胀珍珠岩5％；
碎化玻纤网格布5％；
防火膨胀橡胶颗粒5％；
聚氨酯橡胶颗粒5％。
进一步，水泥为硅酸盐水泥、普通硅酸盐水泥和矿渣硅盐水泥中的一种， 水泥起到奠定混凝土基础的效果。
进一步，掺合料为硅灰、粉煤灰、矿渣微细粉中的一种或多种，掺合料起 到改善混凝土性能，节约用水，调节混凝土强度等级的效果。
进一步，骨料为单粒级或间断粒级的粗骨料作为骨架，其中，总骨料15％-25％ 占比为细骨料，骨料起到支撑的作用。
进一步，混凝土添加剂分为改善混凝土拌合物流变性能的外加剂、调节混 凝土凝结时间、硬化性能的外加剂、改善混凝土耐久性的外加剂以及改善混凝 土其它性能的外加剂中的一种或多种组成，不同外加剂起到提高与改善混凝土 不同性能的效果。
进一步，改善混凝土拌合物流变性能的外加剂包括减水剂、引气剂、泵送 剂，调节混凝土凝结时间、硬化性能的外加剂包括缓凝剂、早强剂、速凝剂， 改善混凝土耐久性的外加剂包括引气剂、防水剂和阻锈剂，改善混凝土其它性 能的外加剂包括膨胀剂、着色剂、防冻剂，通过上述各类添加剂，能够提高混 凝土的不同性能。
进一步，粘合剂为树脂粘合剂，包括热固性树脂胶粘剂、热塑性树脂胶粘 剂和混合型胶粘剂，树脂粘合剂能够提高粘合效果。
进一步，热固性胶粘剂为酚醛、眠醛、三聚氰胺、环氧、聚氨酯、不饱和 聚酯、有机硅树脂、杂环聚合物中的一种或多种；热塑性胶粘剂为聚醋酸乙烯 醋、乙烯-醋酸乙烯共聚物、聚乙烯醇、聚乙烯醇缩醛、聚丙烯酸酯中的一种或 多种，混合型胶粘剂为a-氰基丙烯酸酯、厌氧性丙烯酸双酷、聚氯乙烯、聚酞 胺、聚矾；酚醛-缩醛、环氧-聚酰胺、环氧-聚矾、酚醛-丁腈、环氧-丁腈、酚 醛-氯丁-和橡胶改性丙烯酸醋中的一种或多种，根据透水混凝土使用的不同环 境，可搭配使用不同的树脂粘合剂，起到保障粘合效果的目的。
进一步，防火膨胀橡胶颗粒为三元乙丙橡胶，三元乙丙橡胶起到防火膨胀 的效果。
进一步，网格布是以中碱或无碱玻纤维纱织造，经耐碱高分子乳液涂覆而 成，碱高分子乳液与中碱或无碱玻纤维能够起到加强网格布自身相对性能的效 果。
实施例2
一种透水混凝土，包括以下质量百分比的组分：
水泥40％
水25％；
骨料10％；
掺合料5％；
混凝土添加剂3％；
粘合剂2％；
色粉1％；
膨胀珍珠岩5％；
碎化玻纤网格布3％；
防火膨胀橡胶颗粒3％；
聚氨酯橡胶颗粒3％。
进一步，水泥为硅酸盐水泥、普通硅酸盐水泥和矿渣硅盐水泥中的一种， 水泥起到奠定混凝土基础的效果。
进一步，掺合料为硅灰、粉煤灰、矿渣微细粉中的一种或多种，掺合料起 到改善混凝土性能，节约用水，调节混凝土强度等级的效果。
进一步，骨料为单粒级或间断粒级的粗骨料作为骨架，其中，总骨料15％-25％ 占比为细骨料，骨料起到支撑的作用。
进一步，混凝土添加剂分为改善混凝土拌合物流变性能的外加剂、调节混 凝土凝结时间、硬化性能的外加剂、改善混凝土耐久性的外加剂以及改善混凝 土其它性能的外加剂中的一种或多种组成，不同外加剂起到提高与改善混凝土 不同性能的效果。
进一步，改善混凝土拌合物流变性能的外加剂包括减水剂、引气剂、泵送 剂，调节混凝土凝结时间、硬化性能的外加剂包括缓凝剂、早强剂、速凝剂， 改善混凝土耐久性的外加剂包括引气剂、防水剂和阻锈剂，改善混凝土其它性 能的外加剂包括膨胀剂、着色剂、防冻剂，通过上述各类添加剂，能够提高混 凝土的不同性能。
进一步，粘合剂为树脂粘合剂，包括热固性树脂胶粘剂、热塑性树脂胶粘 剂和混合型胶粘剂，树脂粘合剂能够提高粘合效果。
进一步，热固性胶粘剂为酚醛、眠醛、三聚氰胺、环氧、聚氨酯、不饱和 聚酯、有机硅树脂、杂环聚合物中的一种或多种；热塑性胶粘剂为聚醋酸乙烯 醋、乙烯-醋酸乙烯共聚物、聚乙烯醇、聚乙烯醇缩醛、聚丙烯酸酯中的一种或 多种，混合型胶粘剂为a-氰基丙烯酸酯、厌氧性丙烯酸双酷、聚氯乙烯、聚酞 胺、聚矾；酚醛-缩醛、环氧-聚酰胺、环氧-聚矾、酚醛-丁腈、环氧-丁腈、酚 醛-氯丁-和橡胶改性丙烯酸醋中的一种或多种，根据透水混凝土使用的不同环 境，可搭配使用不同的树脂粘合剂，起到保障粘合效果的目的。
进一步，防火膨胀橡胶颗粒为三元乙丙橡胶，三元乙丙橡胶起到防火膨胀 的效果。
进一步，网格布是以中碱或无碱玻纤维纱织造，经耐碱高分子乳液涂覆而 成，碱高分子乳液与中碱或无碱玻纤维能够起到加强网格布自身相对性能的效 果。
实施例3
一种透水混凝土，包括以下质量百分比的组分：
水泥30％；
水20％；
骨料15％；
掺合料10％；
混凝土添加剂3％；
粘合剂2％；
色粉1％；
膨胀珍珠岩10％；
碎化玻纤网格布3％；
防火膨胀橡胶颗粒3％；
聚氨酯橡胶颗粒3％。
进一步，水泥为硅酸盐水泥、普通硅酸盐水泥和矿渣硅盐水泥中的一种， 水泥起到奠定混凝土基础的效果。
进一步，掺合料为硅灰、粉煤灰、矿渣微细粉中的一种或多种，掺合料起 到改善混凝土性能，节约用水，调节混凝土强度等级的效果。
进一步，骨料为单粒级或间断粒级的粗骨料作为骨架，其中，总骨料15％-25％ 占比为细骨料，骨料起到支撑的作用。
进一步，混凝土添加剂分为改善混凝土拌合物流变性能的外加剂、调节混 凝土凝结时间、硬化性能的外加剂、改善混凝土耐久性的外加剂以及改善混凝 土其它性能的外加剂中的一种或多种组成，不同外加剂起到提高与改善混凝土 不同性能的效果。
进一步，改善混凝土拌合物流变性能的外加剂包括减水剂、引气剂、泵送 剂，调节混凝土凝结时间、硬化性能的外加剂包括缓凝剂、早强剂、速凝剂， 改善混凝土耐久性的外加剂包括引气剂、防水剂和阻锈剂，改善混凝土其它性 能的外加剂包括膨胀剂、着色剂、防冻剂，通过上述各类添加剂，能够提高混 凝土的不同性能。
进一步，粘合剂为树脂粘合剂，包括热固性树脂胶粘剂、热塑性树脂胶粘 剂和混合型胶粘剂，树脂粘合剂能够提高粘合效果。
进一步，热固性胶粘剂为酚醛、眠醛、三聚氰胺、环氧、聚氨酯、不饱和 聚酯、有机硅树脂、杂环聚合物中的一种或多种；热塑性胶粘剂为聚醋酸乙烯 醋、乙烯-醋酸乙烯共聚物、聚乙烯醇、聚乙烯醇缩醛、聚丙烯酸酯中的一种或 多种，混合型胶粘剂为a-氰基丙烯酸酯、厌氧性丙烯酸双酷、聚氯乙烯、聚酞 胺、聚矾；酚醛-缩醛、环氧-聚酰胺、环氧-聚矾、酚醛-丁腈、环氧-丁腈、酚 醛-氯丁-和橡胶改性丙烯酸醋中的一种或多种，根据透水混凝土使用的不同环 境，可搭配使用不同的树脂粘合剂，起到保障粘合效果的目的。
进一步，防火膨胀橡胶颗粒为三元乙丙橡胶，三元乙丙橡胶起到防火膨胀 的效果。
进一步，网格布是以中碱或无碱玻纤维纱织造，经耐碱高分子乳液涂覆而 成，碱高分子乳液与中碱或无碱玻纤维能够起到加强网格布自身相对性能的效 果。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细 节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体 形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性 的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限 定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括 在本发明内。
Claims (10)
1.一种透水混凝土，其特征在于，包括以下质量百分比的组分：
水泥30％-40％；
水20％-30％；
骨料10％-20％；
掺合料5％-10％；
混凝土添加剂1％-5％；
粘合剂1％-5％；
色粉1％；
膨胀珍珠岩5％-10％；
碎化玻纤网格布3％-5％；
防火膨胀橡胶颗粒3％-5％；
聚氨酯橡胶颗粒3％-5％。
2.根据权利要求1所述的一种透水混凝土，其特征在于：所述水泥为硅酸盐水泥、普通硅酸盐水泥和矿渣硅盐水泥中的一种。
3.根据权利要求1所述的一种透水混凝土，其特征在于：所述掺合料为硅灰、粉煤灰、矿渣微细粉中的一种或多种。
4.根据权利要求1所述的一种透水混凝土，其特征在于：所述骨料为单粒级或间断粒级的粗骨料作为骨架，其中，总骨料15％-25％占比为细骨料。
5.根据权利要求1所述的一种透水混凝土，其特征在于：所述混凝土添加剂分为改善混凝土拌合物流变性能的外加剂、调节混凝土凝结时间、硬化性能的外加剂、改善混凝土耐久性的外加剂以及改善混凝土其它性能的外加剂中的一种或多种组成。
6.根据权利要求5所述的一种透水混凝土，其特征在于：所述改善混凝土拌合物流变性能的外加剂包括减水剂、引气剂、泵送剂，调节混凝土凝结时间、硬化性能的外加剂包括缓凝剂、早强剂、速凝剂，改善混凝土耐久性的外加剂包括引气剂、防水剂和阻锈剂，改善混凝土其它性能的外加剂包括膨胀剂、着色剂、防冻剂。
7.根据权利要求1所述的一种透水混凝土，其特征在于：所述粘合剂为树脂粘合剂，包括热固性树脂胶粘剂、热塑性树脂胶粘剂和混合型胶粘剂。
8.根据权利要求7所述的一种透水混凝土，其特征在于：所述热固性胶粘剂为酚醛、眠醛、三聚氰胺、环氧、聚氨酯、不饱和聚酯、有机硅树脂、杂环聚合物中的一种或多种；热塑性胶粘剂为聚醋酸乙烯醋、乙烯-醋酸乙烯共聚物、聚乙烯醇、聚乙烯醇缩醛、聚丙烯酸酯中的一种或多种，混合型胶粘剂为a-氰基丙烯酸酯、厌氧性丙烯酸双酷、聚氯乙烯、聚酞胺、聚矾；酚醛-缩醛、环氧-聚酰胺、环氧-聚矾、酚醛-丁腈、环氧-丁腈、酚醛-氯丁-和橡胶改性丙烯酸醋中的一种或多种。
9.根据权利要求8所述的一种透水混凝土，其特征在于：所述防火膨胀橡胶颗粒为三元乙丙橡胶。
10.根据权利要求9所述的一种透水混凝土，其特征在于：所述网格布是以中碱或无碱玻纤维纱织造，经耐碱高分子乳液涂覆而成。