CN115120511A - 一种硅藻土清洁泥膜及其制备方法 - Google Patents
一种硅藻土清洁泥膜及其制备方法 Download PDFInfo
- Publication number
- CN115120511A CN115120511A CN202210989543.5A CN202210989543A CN115120511A CN 115120511 A CN115120511 A CN 115120511A CN 202210989543 A CN202210989543 A CN 202210989543A CN 115120511 A CN115120511 A CN 115120511A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- diatomite
- powder
- bentonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种硅藻土清洁泥膜，包括以下重量份的原料：硅藻土，高岭土，膨润土，混合保湿剂，松针提取液，芦荟提取液，甘油，甜菜碱，赤藓糖醇，丙二醇，泛醇，辛酸/癸酸甘油三酯，聚二甲基硅氧烷，去离子水，复合乳化剂，增稠剂。本发明可通过硅藻土吸附毛孔中的油脂、灰尘等一些脏物，利用改性壳聚糖可快速补充对毛孔补充的水分，从而使此泥膜同时具有较好的清洁和补水两种效果，同时微晶纤维素与硅藻土配合，通过二者的多孔性使得硅藻土的吸附效果较好，并且加入的青刺果提取物中含有丰富的单不饱和脂肪酸，可提高硅藻土清洁面膜的抗氧化性。
Description
技术领域
本发明涉及清洁泥膜技术领域，更具体地说，本发明涉及一种硅藻土清洁泥膜及其制备方法。
背景技术
面膜通过阻隔肌肤与空气的接触、抑制皮脂分泌和汗水蒸发使肌肤温度上升，肌肤温度上升后，便会促进血液循环，使面膜内的有效成分渗入到表皮层或更深、更广的地方，达到清洁与保养皮肤的效果。人类应用泥土美容护肤的历史悠久，一般而言，在泥土中发现的自然成分有助于防止皮肤老化，而矿物质可使皮肤更具活力、更有弹性。因此，泥有助于使皮肤更年轻、更光滑和更健康。硅藻是鱼、贝、虾类特别是其幼体的主要饵料，它与其他植物一起，构成海洋的初级生产力。硅藻还是形成海底生物性沉积物的重要组成部分。经过漫长的年代，那些在海底沉积下来的以硅藻为主要成分的沉积层，逐渐形成了经济价值极高的硅藻土。硅藻土含有丰富的营养物质，应用非常广泛。
由于硅藻土具有较强的吸附性，因此非常适合应用在清洁泥膜行业，但是其弊端也非常明显，保湿能力较弱，易造成使用后脸部干燥缺水的情况出现，对皮肤造成损坏。
发明内容
为了克服现有技术的上述缺陷，本发明的实施例提供一种硅藻土清洁泥膜及其制备方法，本发明所要解决的问题是：如何提高硅藻土清洁泥膜的保湿能力。
为实现上述目的，本发明提供如下技术方案：一种硅藻土清洁泥膜，包括以下重量份的原料：硅藻土5-20份，高岭土10-20份，膨润土5-15份，混合保湿剂1-3份，松针提取液0.1-2份，芦荟提取液0.1-2份，甘油1-9份，甜菜碱1-3份，赤藓糖醇1-3份，丙二醇0.4-3份，泛醇0.1-1份，辛酸/癸酸甘油三酯0.2-10份，聚二甲基硅氧烷0.1-1.9份，去离子水余量份，复合乳化剂0.3-3份，增稠剂0.1-2份。
进一步的，包括以下重量份的原料：硅藻土8-17份，高岭土13-17份，膨润土8-12份，混合保湿剂1.5-2.5份，松针提取液0.4-1.7份，芦荟提取液0.4-1.7份，甘油4-6份，甜菜碱1.5-2.5份，赤藓糖醇1.5-2.5份，丙二醇0.9-2.5份，泛醇0.4-0.7份，辛酸/癸酸甘油三酯3.2-7份，聚二甲基硅氧烷0.4-1.6份，去离子水余量份，复合乳化剂1.3-2.5份，增稠剂0.4-1.7份。
进一步的，包括以下重量份的原料：硅藻土10份，高岭土15份，膨润土10份，混合保湿剂2份，松针提取液0.5份，芦荟提取液0.5份，甘油4份，甜菜碱2份，赤藓糖醇2份，丙二醇2份，泛醇0.5份，辛酸/癸酸甘油三酯5份，聚二甲基硅氧烷1份，去离子水余量份，复合乳化剂2份，增稠剂0.8份。
进一步的，所述复合乳化剂是质量比为20：(32～45)的16-18醇和硬酯酸甘油酯的混合物。
进一步的，所述增稠剂为聚丙烯酰基二甲基牛磺酸钠、羟乙基纤维素中的一种或多种。
进一步的，所述混合保湿剂包括改性壳聚糖、微晶纤维素溶液和青刺果提取物，所述改性壳聚糖与微晶纤维素溶液和青刺果提取物的质量比为2：0.7：(0.2～0.4)。
本发明还提供一种硅藻土清洁泥膜的制备方法，具体制备步骤如下：
步骤一：称取改性壳聚糖，将其溶于水后得到改性壳聚糖溶液，溶液溶度为25％，将其加入搅拌器内进行搅拌，搅拌速度为200-300r/min，搅拌温度为75-85℃，搅拌时间为10-15min，加入青刺果提取物，继续搅拌，搅拌速度为300-400r/min，搅拌温度为90-105℃，搅拌时间为15-20min，最后加入微晶纤维素溶液，在搅拌速度为300-400r/min，搅拌温度为90-105℃的情况下，搅拌15-20min后，充分混合得到混合保湿剂；称取硅藻土，去除其内部杂质后进行研磨，研磨后的粒径≧100目，得到硅藻土粉末，将研磨得到的部分硅藻土粉末加入搅拌器内与混合保湿剂混合，搅拌速度为150-200r/min；温度为110-120℃，搅拌时间为20-25min，使混合保湿剂与硅藻土粉末充分混合后得到A混合料备用；
步骤二：将所述步骤一中剩余的硅藻土粉末加入新的反应容器中，60-70℃预热5-10min，加入去离子水搅拌混合，直至粘稠状，加入芦荟原汁搅拌，搅拌速度为100-120r/min，搅拌温度为85-95℃，搅拌时间为10-15min，再加入松针提取液进行搅拌，搅拌速度为100-120r/min，搅拌温度为85-95℃，搅拌时间为10-15min，得到B混合料备用；
步骤三：分别称取高岭土和膨润土，去除高岭土和膨润土内的杂质后，对其分别进行研磨，得到高岭土粉末和膨润土粉末，使研磨后的粒径≧100目，将高岭土粉末和膨润土粉末搅拌混合在一起，得到C混合料备用：
步骤四：分别称取甘油，甜菜碱，赤藓糖醇，丙二醇，泛醇，辛酸/癸酸甘油三酯，聚二甲基硅氧烷，去离子水，复合乳化剂和增稠剂，加入搅拌器中搅拌混合，得到D混合料备用；
步骤五：将所述步骤一中得到的A混合料与所述步骤2中得到的B混合料加入搅拌器中搅拌，搅拌速度为200-260r/min，搅拌温度为85-95℃，搅拌时间为10-15min，加入C混合料和D混合料，保温搅拌30-40min，得到硅藻土清洁泥膜。
进一步的，所述步骤一中改性壳聚糖的制备方法为：称取壳聚糖放入反应容器中，加入去离子水，搅拌均匀，30-35℃水浴处理120-150min后，加入一氯乙酸，搅拌5-10min，加入异丙醇，搅拌5-10min，加入甲醇，搅拌5-10min后，静置35-40℃水浴处理90-100min，而后升温至45-50℃，保温2-2.5h，加入去离子水，调节PH值为6.8-7.2，将反应物过滤，得到固体产物，用适量蒸馏水溶解完全后，离心分离得到黏稠液，用冰醋酸中和再用适量无水乙醇使完全沉淀出来，抽滤，同时用无水乙醇洗涤，至产物不结块，60-65℃恒温干燥，得到改性壳聚糖。
进一步的，所述壳聚糖与一氯乙酸与异丙醇与甲醇的质量比为4：5：(25～30)。
进一步的，所述步骤三中的搅拌速度为100-120r/min，搅拌温度为90-105℃，搅拌时间为15-20min。
本发明的技术效果和优点：
1、本发明的原料配方所制备出的硅藻土清洁泥膜，可通过硅藻土吸附毛孔中的油脂、灰尘等一些脏物，吸附完成后，利用改性壳聚糖可快速补充对毛孔补充的水分，使得刚被清洁的毛孔内充满水分子，由于改性壳聚糖中的壳聚糖分子在C和C位上有-NH和-OH活性基团，因此在强碱条件下，壳聚糖会与一氯乙酸作用合成6-0-羧甲基壳聚糖，而6-0-羧甲基壳聚糖具有良好的水溶性能和优良的保湿性能，因此会大大提高硅藻土清洁面膜的保湿性，从而使得硅藻土清洁面膜同时具有较好的清洁和补水两种效果，同时微晶纤维素与硅藻土配合，通过二者的多孔性使得硅藻土的吸附效果较好，进而使得清洁效果好，并且加入的青刺果提取物中含有丰富的单不饱和脂肪酸，而单不饱和脂肪酸具有不易被氧化的特性，因此可提高硅藻土清洁面膜的抗氧化性，且青刺果的组成与人体皮脂类接近，具有极强的皮肤渗透能力，与硅藻土配合使用，可对皮肤深层进行清洁，提高本泥膜的清洁性。
2、本发明的原料配方所制备出的硅藻土清洁泥膜，通过硅藻土与松针提取液将和芦荟原液的协同使用，可增强此清洁泥膜的抗氧化性，从而可让使用者的皮肤光洁柔嫩，始终保持最好的状态，并且使用的松针提取物中含有丰富的黄酮类物质和维生素，其不但具有强抗氧化性，并且还具有抗菌、活血、抗炎、抗过敏等作用，而芦荟原液的蒽酮类化合物也具有杀菌、抑菌、消炎等作用，两者协同使用，可大大增强本清洁面膜的抗菌效果，并且芦荟含有的超氧化物歧化酶成分，可与松针提取物中含有的黄酮类物质协同使用，消除超氧化物自由基，从而加强抗氧化性，使皮肤细嫩、有弹性，具有延缓衰老的作用。
具体实施方式
下面将结合本发明中的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：
本发明提供了一种硅藻土清洁泥膜，包括以下重量份的原料：硅藻土5份，高岭土10份，膨润土5份，混合保湿剂1份，松针提取液0.1份，芦荟提取液0.1份，甘油1份，甜菜碱1份，赤藓糖醇1份，丙二醇0.4份，泛醇0.1份，辛酸/癸酸甘油三酯0.2份，聚二甲基硅氧烷0.1份，去离子水余量份，复合乳化剂0.3份，增稠剂0.1份。
优选的，所述复合乳化剂是质量比为20：37的16-18醇和硬酯酸甘油酯的混合物。
优选的，所述增稠剂为羟乙基纤维素。
优选的，所述混合保湿剂包括改性壳聚糖、微晶纤维素溶液和青刺果提取物，所述改性壳聚糖与微晶纤维素溶液和青刺果提取物的质量比为2：0.7：0.3。
本发明还提供一种硅藻土清洁泥膜的制备方法，具体制备步骤如下：
步骤一：称取改性壳聚糖，将其溶于水后得到改性壳聚糖溶液，溶液溶度为25％，将其加入搅拌器内进行搅拌，搅拌速度为220r/min，搅拌温度为80℃，搅拌时间为12min，加入青刺果提取物，继续搅拌，搅拌速度为350r/min，搅拌温度为98℃，搅拌时间为18min，最后加入微晶纤维素溶液，在搅拌速度为350r/min，搅拌温度为98℃的情况下，搅拌18min后，充分混合得到混合保湿剂；称取硅藻土，去除其内部杂质后进行研磨，研磨后的粒径≧100目，得到硅藻土粉末，将研磨得到的部分硅藻土粉末加入搅拌器内与混合保湿剂混合，搅拌速度为180r/min；温度为115℃，搅拌时间为22min，使混合保湿剂与硅藻土粉末充分混合后得到A混合料备用；
步骤二：将所述步骤一中剩余的硅藻土粉末加入新的反应容器中，65℃预热8min，加入去离子水搅拌混合，直至粘稠状，加入芦荟原汁搅拌，搅拌速度为110r/min，搅拌温度为90℃，搅拌时间为12min，再加入松针提取液进行搅拌，搅拌速度为110r/min，搅拌温度为90℃，搅拌时间为12min，得到B混合料备用；
步骤三：分别称取高岭土和膨润土，去除高岭土和膨润土内的杂质后，对其分别进行研磨，得到高岭土粉末和膨润土粉末，使研磨后的粒径≧100目，将高岭土粉末和膨润土粉末搅拌混合在一起，得到C混合料备用：
步骤四：分别称取甘油，甜菜碱，赤藓糖醇，丙二醇，泛醇，辛酸/癸酸甘油三酯，聚二甲基硅氧烷，去离子水，复合乳化剂和增稠剂，加入搅拌器中搅拌混合，得到D混合料备用；
步骤五：将所述步骤一中得到的A混合料与所述步骤2中得到的B混合料加入搅拌器中搅拌，搅拌速度为230r/min，搅拌温度为90℃，搅拌时间为12min，加入C混合料和D混合料，保温搅拌35min，得到硅藻土清洁泥膜。
优选的，所述步骤一中改性壳聚糖的制备方法为：称取壳聚糖放入反应容器中，加入去离子水，搅拌均匀，30℃水浴处理135min后，加入一氯乙酸，搅拌8min，加入异丙醇，搅拌8min，加入甲醇，搅拌8min后，静置35℃水浴处理95min，而后升温至45℃，保温2h，加入去离子水，调节PH值为7，将反应物过滤，得到固体产物，用适量蒸馏水溶解完全后，离心分离得到黏稠液，用冰醋酸中和再用适量无水乙醇使完全沉淀出来，抽滤，同时用无水乙醇洗涤，至产物不结块，60℃恒温干燥，得到改性壳聚糖。
优选的，所述壳聚糖与一氯乙酸与异丙醇与甲醇的质量比为4：5：28。
优选的，所述步骤三中的搅拌速度为110r/min，搅拌温度为95℃，搅拌时间为18min。
实施例2：
与实施例1不同的是，本发明提供了一种硅藻土清洁泥膜及其制备方法，包括以下重量份的原料：硅藻土10份，高岭土15份，膨润土10份，混合保湿剂2份，松针提取液0.5份，芦荟提取液0.5份，甘油4份，甜菜碱2份，赤藓糖醇2份，丙二醇2份，泛醇0.5份，辛酸/癸酸甘油三酯5份，聚二甲基硅氧烷1份，去离子水余量份，复合乳化剂2份，增稠剂0.8份。
实施例3：
与实施例1-2均不同的是，本发明提供了一种硅藻土清洁泥膜，包括以下重量份的原料：硅藻土20份，高岭土20份，膨润土15份，混合保湿剂3份，松针提取液2份，芦荟提取液2份，甘油9份，甜菜碱3份，赤藓糖醇3份，丙二醇3份，泛醇1份，辛酸/癸酸甘油三酯10份，聚二甲基硅氧烷1.9份，去离子水余量份，复合乳化剂3份，增稠剂2份。
实施例4：
本发明提供了一种硅藻土清洁泥膜，包括以下重量份的原料：硅藻土5份，高岭土10份，膨润土5份，混合保湿剂1份，松针提取液0.1份，芦荟提取液0.1份，甘油1份，甜菜碱1份，赤藓糖醇1份，丙二醇0.4份，泛醇0.1份，辛酸/癸酸甘油三酯0.2份，聚二甲基硅氧烷0.1份，去离子水余量份，复合乳化剂0.3份，增稠剂0.1份。
优选的，所述复合乳化剂是质量比为20：37的16-18醇和硬酯酸甘油酯的混合物。
优选的，所述增稠剂为羟乙基纤维素。
优选的，所述混合保湿剂包括改性壳聚糖、微晶纤维素溶液和青刺果提取物，所述改性壳聚糖与微晶纤维素溶液和青刺果提取物的质量比为2：0.7：0.3。
本发明还提供一种硅藻土清洁泥膜的制备方法，具体制备步骤如下：
步骤一：称取改性壳聚糖，将其溶于水后得到改性壳聚糖溶液，溶液溶度为25％，将其加入搅拌器内进行搅拌，搅拌速度为220r/min，搅拌温度为80℃，搅拌时间为12min，加入青刺果提取物，继续搅拌，搅拌速度为350r/min，搅拌温度为98℃，搅拌时间为18min，最后加入微晶纤维素溶液，在搅拌速度为350r/min，搅拌温度为98℃的情况下，搅拌18min后，充分混合得到混合保湿剂；称取硅藻土，去除其内部杂质后进行研磨，研磨后的粒径≧100目，得到硅藻土粉末，将研磨得到的部分硅藻土粉末加入搅拌器内与混合保湿剂混合，搅拌速度为180r/min；温度为115℃，搅拌时间为22min，使混合保湿剂与硅藻土粉末充分混合后得到A混合料备用；
步骤二：分别称取高岭土和膨润土，去除高岭土和膨润土内的杂质后，对其分别进行研磨，得到高岭土粉末和膨润土粉末，使研磨后的粒径≧100目，将高岭土粉末和膨润土粉末搅拌混合在一起，得到C混合料备用：
步骤三：分别称取甘油，甜菜碱，赤藓糖醇，丙二醇，泛醇，辛酸/癸酸甘油三酯，聚二甲基硅氧烷，去离子水，复合乳化剂和增稠剂，加入搅拌器中搅拌混合，得到D混合料备用；
步骤四：将所述步骤一中得到的A混合料加入搅拌器中搅拌，搅拌速度为230r/min，搅拌温度为90℃，搅拌时间为12min，加入C混合料和D混合料，保温搅拌35min，得到硅藻土清洁泥膜。
优选的，所述步骤一中改性壳聚糖的制备方法为：称取壳聚糖放入反应容器中，加入去离子水，搅拌均匀，30℃水浴处理135min后，加入一氯乙酸，搅拌8min，加入异丙醇，搅拌8min，加入甲醇，搅拌8min后，静置35℃水浴处理95min，而后升温至45℃，保温2h，加入去离子水，调节PH值为7，将反应物过滤，得到固体产物，用适量蒸馏水溶解完全后，离心分离得到黏稠液，用冰醋酸中和再用适量无水乙醇使完全沉淀出来，抽滤，同时用无水乙醇洗涤，至产物不结块，60℃恒温干燥，得到改性壳聚糖。
优选的，所述壳聚糖与一氯乙酸与异丙醇与甲醇的质量比为4：5：28。
优选的，所述步骤二中的搅拌速度为110r/min，搅拌温度为95℃，搅拌时间为18min。
实施例5：
本发明提供了一种硅藻土清洁泥膜，包括以下重量份的原料：硅藻土5份，高岭土10份，膨润土5份，混合保湿剂1份，松针提取液0.1份，芦荟提取液0.1份，甘油1份，甜菜碱1份，赤藓糖醇1份，丙二醇0.4份，泛醇0.1份，辛酸/癸酸甘油三酯0.2份，聚二甲基硅氧烷0.1份，去离子水余量份，复合乳化剂0.3份，增稠剂0.1份。
优选的，所述复合乳化剂是质量比为20：37的16-18醇和硬酯酸甘油酯的混合物。
优选的，所述增稠剂为羟乙基纤维素。
本发明还提供一种硅藻土清洁泥膜的制备方法，具体制备步骤如下：
步骤一：称取硅藻土，去除其内部杂质后进行研磨，研磨后的粒径≧100目，得到硅藻土粉末，将研磨得到的部分硅藻土粉末加入搅拌器内与壳聚糖混合，搅拌速度为180r/min；温度为115℃，搅拌时间为22min，使壳聚糖与硅藻土粉末充分混合后得到A混合料备用；
步骤二：将所述步骤一中剩余的硅藻土粉末加入新的反应容器中，65℃预热8min，加入去离子水搅拌混合，直至粘稠状，加入芦荟原汁搅拌，搅拌速度为110r/min，搅拌温度为90℃，搅拌时间为12min，再加入松针提取液进行搅拌，搅拌速度为110r/min，搅拌温度为90℃，搅拌时间为12min，得到B混合料备用；
步骤三：分别称取高岭土和膨润土，去除高岭土和膨润土内的杂质后，对其分别进行研磨，得到高岭土粉末和膨润土粉末，使研磨后的粒径≧100目，将高岭土粉末和膨润土粉末搅拌混合在一起，得到C混合料备用：
步骤四：分别称取甘油，甜菜碱，赤藓糖醇，丙二醇，泛醇，辛酸/癸酸甘油三酯，聚二甲基硅氧烷，去离子水，复合乳化剂和增稠剂，加入搅拌器中搅拌混合，得到D混合料备用；
步骤五：将所述步骤一中得到的A混合料与所述步骤2中得到的B混合料加入搅拌器中搅拌，搅拌速度为230r/min，搅拌温度为90℃，搅拌时间为12min，加入C混合料和D混合料，保温搅拌35min，得到硅藻土清洁泥膜。
优选的，所述步骤三中的搅拌速度为110r/min，搅拌温度为95℃，搅拌时间为18min。
对比例：
本发明提供了一种硅藻土清洁泥膜，包括以下重量份的原料：硅藻土5份，高岭土10份，膨润土5份，混合保湿剂1份，松针提取液0.1份，芦荟提取液0.1份，甘油1份，甜菜碱1份，赤藓糖醇1份，丙二醇0.4份，泛醇0.1份，辛酸/癸酸甘油三酯0.2份，聚二甲基硅氧烷0.1份，去离子水余量份，复合乳化剂0.3份，增稠剂0.1份。
优选的，所述复合乳化剂是质量比为20：37的16-18醇和硬酯酸甘油酯的混合物。
优选的，所述增稠剂为羟乙基纤维素。
本发明还提供一种硅藻土清洁泥膜的制备方法，具体制备步骤如下：
步骤一：分别称取硅藻土、高岭土和膨润土，去除其内部杂质后进行研磨，研磨后的粒径≧100目，得到硅藻土粉末、高岭土粉末和膨润土粉末，将其搅拌混合在一起，得到A混合料备用：
步骤二：分别称取甘油，甜菜碱，赤藓糖醇，丙二醇，泛醇，辛酸/癸酸甘油三酯，聚二甲基硅氧烷，去离子水，复合乳化剂和增稠剂，加入搅拌器中搅拌混合，得到B混合料备用；
步骤三：将所述步骤一中得到A混合料和所述步骤二中得到的B混合料加入反应容器中，保温搅拌35min，即得到硅藻土清洁泥膜。
取上述实施例1-5所制得的硅藻土清洁泥膜分别作为实验组1、实验组2、实验组3、实验组4和实验组5，选取对比例生产的一种硅藻土清洁泥膜作为对照组，对选择的硅藻土清洁泥膜进行保湿性、抗氧化性、清洁性和抗菌性测试。(采用水份含量测试仪测得本发明实施例1-5中的含水量；采用DPPH自由基清除率公式计算得到实施例1-5中的自由基清除率，其数值越大，则表示抗氧化性越好；采用抑菌实验测得实施例1-5中的抗菌率；采用皮肤检测仪测得本发明实施例1-5中的清洁性，清洁效果采取评分制，总分为10分，1分为最差，10分为最好)，测试结果如表一：
| 含水量/g | 自由基清除率/％ | 清洁性 | 抗菌率/％ | |
| 实验组1 | 6.59 | 84.5 | 9.1 | 77.6 |
| 实验组2 | 6.75 | 86.9 | 9.2 | 78.1 |
| 实验组3 | 6.94 | 90.3 | 9.3 | 79.5 |
| 实验组4 | 6.24 | 80.5 | 9.0 | 74.8 |
| 实验组5 | 5.94 | 82.4 | 8.9 | 76.1 |
| 对照组 | 5.15 | 77.1 | 8.5 | 72.5 |
表一
由表一可知，采用本发明生产的硅藻土清洁泥膜的保湿性、抗氧化性、清洁性和抗菌性效果更好，实施例4相对比实施例1未添加松针提取液和芦荟原液，其抗氧化性和抗菌性降低，实施例5相对比实施例1未添加混合保湿剂，其保湿性和清洁性效果降低，本清洁泥膜可通过硅藻土吸附毛孔中的油脂、灰尘等一些脏物，吸附完成后，利用改性壳聚糖可快速补充对毛孔补充的水分，使得刚被清洁的毛孔内充满水分子，由于改性壳聚糖中的壳聚糖分子在C和C位上有-NH和-OH活性基团，因此在强碱条件下，壳聚糖会与一氯乙酸作用合成6-0-羧甲基壳聚糖，而6-0-羧甲基壳聚糖具有良好的水溶性能和优良的保湿性能，因此会大大提高硅藻土清洁面膜的保湿性，从而使得硅藻土清洁面膜同时具有较好的清洁和补水两种效果，同时微晶纤维素与硅藻土配合，通过二者的多孔性使得硅藻土的吸附效果较好，进而使得清洁效果好，并且加入的青刺果提取物中含有丰富的单不饱和脂肪酸，而单不饱和脂肪酸具有不易被氧化的特性，因此可提高硅藻土清洁面膜的抗氧化性，且青刺果的组成与人体皮脂类接近，具有极强的皮肤渗透能力，与硅藻土配合使用，可对皮肤深层进行清洁，提高本泥膜的清洁性，并且可通过硅藻土与松针提取液将和芦荟原液的协同使用，可增强此清洁泥膜的抗氧化性，从而可让使用者的皮肤光洁柔嫩，始终保持最好的状态，并且使用的松针提取物中含有丰富的黄酮类物质和维生素，其不但具有强抗氧化性，并且还具有抗菌、活血、抗炎、抗过敏等作用，而芦荟原液的蒽酮类化合物也具有杀菌、抑菌、消炎等作用，两者协同使用，可大大增强本清洁面膜的抗菌效果，并且芦荟含有的超氧化物歧化酶成分，可与松针提取物中含有的黄酮类物质协同使用，消除超氧化物自由基，从而加强抗氧化性，使皮肤细嫩、有弹性，具有延缓衰老的作用。
最后：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种硅藻土清洁泥膜，其特征在于：包括以下重量份的原料：硅藻土5-20份，高岭土10-20份，膨润土5-15份，混合保湿剂1-3份，松针提取液0.1-2份，芦荟提取液0.1-2份，甘油1-9份，甜菜碱1-3份，赤藓糖醇1-3份，丙二醇0.4-3份，泛醇0.1-1份，辛酸/癸酸甘油三酯0.2-10份，聚二甲基硅氧烷0.1-1.9份，去离子水余量份，复合乳化剂0.3-3份，增稠剂0.1-2份。
2.根据权利要求1所述的一种硅藻土清洁泥膜，其特征在于：包括以下重量份的原料：硅藻土8-17份，高岭土13-17份，膨润土8-12份，混合保湿剂1.5-2.5份，松针提取液0.4-1.7份，芦荟提取液0.4-1.7份，甘油4-6份，甜菜碱1.5-2.5份，赤藓糖醇1.5-2.5份，丙二醇0.9-2.5份，泛醇0.4-0.7份，辛酸/癸酸甘油三酯3.2-7份，聚二甲基硅氧烷0.4-1.6份，去离子水余量份，复合乳化剂1.3-2.5份，增稠剂0.4-1.7份。
3.根据权利要求1所述的一种硅藻土清洁泥膜，其特征在于：包括以下重量份的原料：硅藻土10份，高岭土15份，膨润土10份，混合保湿剂2份，松针提取液0.5份，芦荟提取液0.5份，甘油4份，甜菜碱2份，赤藓糖醇2份，丙二醇2份，泛醇0.5份，辛酸/癸酸甘油三酯5份，聚二甲基硅氧烷1份，去离子水余量份，复合乳化剂2份，增稠剂0.8份。
4.根据权利要求1所述的一种硅藻土清洁泥膜，其特征在于：所述复合乳化剂是质量比为20：(32～45)的16-18醇和硬酯酸甘油酯的混合物。
5.根据权利要求1所述的一种硅藻土清洁泥膜，其特征在于：所述增稠剂为聚丙烯酰基二甲基牛磺酸钠、羟乙基纤维素中的一种或多种。
6.根据权利要求1所述的一种硅藻土清洁泥膜的制备方法，其特征在于：所述混合保湿剂包括改性壳聚糖、微晶纤维素溶液和青刺果提取物，所述改性壳聚糖与微晶纤维素溶液和青刺果提取物的质量比为2：0.7：(0.2～0.4)。
7.一种硅藻土清洁泥膜的制备方法，其特征在于：具体制备步骤如下：
步骤一：称取改性壳聚糖，将其溶于水后得到改性壳聚糖溶液，溶液溶度为25％，将其加入搅拌器内进行搅拌，搅拌速度为200-300r/min，搅拌温度为75-85℃，搅拌时间为10-15min，加入青刺果提取物，继续搅拌，搅拌速度为300-400r/min，搅拌温度为90-105℃，搅拌时间为15-20min，最后加入微晶纤维素溶液，在搅拌速度为300-400r/min，搅拌温度为90-105℃的情况下，搅拌15-20min后，充分混合得到混合保湿剂；称取硅藻土，去除其内部杂质后进行研磨，研磨后的粒径≧100目，得到硅藻土粉末，将研磨得到的部分硅藻土粉末加入搅拌器内与混合保湿剂混合，搅拌速度为150-200r/min；温度为110-120℃，搅拌时间为20-25min，使混合保湿剂与硅藻土粉末充分混合后得到A混合料备用；
步骤二：将所述步骤一中剩余的硅藻土粉末加入新的反应容器中，60-70℃预热5-10min，加入去离子水搅拌混合，直至粘稠状，加入芦荟原汁搅拌，搅拌速度为100-120r/min，搅拌温度为85-95℃，搅拌时间为10-15min，再加入松针提取液进行搅拌，搅拌速度为100-120r/min，搅拌温度为85-95℃，搅拌时间为10-15min，得到B混合料备用；
步骤三：分别称取高岭土和膨润土，去除高岭土和膨润土内的杂质后，对其分别进行研磨，得到高岭土粉末和膨润土粉末，使研磨后的粒径≧100目，将高岭土粉末和膨润土粉末搅拌混合在一起，得到C混合料备用：
步骤四：分别称取甘油，甜菜碱，赤藓糖醇，丙二醇，泛醇，辛酸/癸酸甘油三酯，聚二甲基硅氧烷，去离子水，复合乳化剂和增稠剂，加入搅拌器中搅拌混合，得到D混合料备用；
步骤五：将所述步骤一中得到的A混合料与所述步骤2中得到的B混合料加入搅拌器中搅拌，搅拌速度为200-260r/min，搅拌温度为85-95℃，搅拌时间为10-15min，加入C混合料和D混合料，保温搅拌30-40min，得到硅藻土清洁泥膜。
8.根据权利要求7所述的一种硅藻土清洁泥膜的制备方法，其特征在于：所述步骤一中改性壳聚糖的制备方法为：称取壳聚糖放入反应容器中，加入去离子水，搅拌均匀，30-35℃水浴处理120-150min后，加入一氯乙酸，搅拌5-10min，加入异丙醇，搅拌5-10min，加入甲醇，搅拌5-10min后，静置35-40℃水浴处理90-100min，而后升温至45-50℃，保温2-2.5h，加入去离子水，调节PH值为6.8-7.2，将反应物过滤，得到固体产物，用适量蒸馏水溶解完全后，离心分离得到黏稠液，用冰醋酸中和再用适量无水乙醇使完全沉淀出来，抽滤，同时用无水乙醇洗涤，至产物不结块，60-65℃恒温干燥，得到改性壳聚糖。
9.根据权利要求8所述的一种硅藻土清洁泥膜的制备方法，其特征在于：所述壳聚糖与一氯乙酸与异丙醇与甲醇的质量比为4：5：(25～30)。
10.根据权利要求7所述的一种硅藻土清洁泥膜的制备方法，其特征在于：所述步骤三中的搅拌速度为100-120r/min，搅拌温度为90-105℃，搅拌时间为15-20min。