CN115110346A - 一种可降解甘蔗纸浆茶具及其制备方法 - Google Patents
一种可降解甘蔗纸浆茶具及其制备方法 Download PDFInfo
- Publication number
- CN115110346A CN115110346A CN202210842673.6A CN202210842673A CN115110346A CN 115110346 A CN115110346 A CN 115110346A CN 202210842673 A CN202210842673 A CN 202210842673A CN 115110346 A CN115110346 A CN 115110346A
- Authority
- CN
- China
- Prior art keywords
- pulp
- parts
- tea set
- degradable
- sugarcane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可降解甘蔗纸浆茶具及其制备方法，属于茶具技术领域，包括甘蔗纸浆、竹纸浆、粘连剂、填料粉、植物染色剂和辅料，各原料质量组份设置为：甘蔗纸浆600‑800份、竹纸浆400‑600份、粘连剂2‑4份、凝固剂2‑4份、植物染色剂4‑6份和辅料6‑8份，所述粘连剂设置为甘油、黄原胶和瓜尔豆胶的混合物，且混合物的混合比例设置为3：1：1，所述凝固剂设置为乳酸钙、氯化钙和丙二醇的混合物，且混合物的混合比例设置为2：2：1，所述植物染色剂的制作方法为：将指定染色的植物置于破碎机内，得到破壁液，然后利用滤网进行过滤，得到植物染色剂。该可降解甘蔗纸浆茶具及其制备方法，不仅成本低，而且防渗漏能力强，且对人无害。
Description
技术领域
本发明属于茶具技术领域，具体涉及一种可降解甘蔗纸浆茶具，还涉及一种可降解甘蔗纸浆茶具的制备方法。
背景技术
现有的一次性茶具按原材料来源、生产工艺、降解方式和回收水平分为以下三大类：1、生物降解类：如纸制品(含纸浆模塑型、纸板涂膜型)、食用粉模塑型、植物纤维模塑型等；2、光/生物降解性材料类：光/生物降解塑料(非发泡)型，如光生物降解PP类；3、易于回收利用材料类：如聚丙烯类(PP)、高抗冲聚苯乙烯类(HIPS)、双向拉伸聚苯乙烯(BOPS)、天然无机矿物填充聚丙烯复合材料制品等。
当前可降解茶具是指可在自然环境微生物(细菌、霉菌、藻类)酶作用指可在自然环境微生物(细菌、霉菌、藻类)酶作用下，发生生物化学反应，引起外观霉变到内在质量变化，最终形成二氧化碳和水的茶具。成品废弃物除应符合GB18006.1-2009《塑料一次性餐饮具通用技术要求》的降解性能外，还应具有回收价值、便于再生利用，或便于卫生填埋及高温堆肥处理。可降解茶具使用材料分两种：一种是天然材料制成的，如纸制品、秸秆、淀粉等，可降解，也称之为环保产品；另一种是以塑料为主要成分，加入淀粉、光敏剂等物质制成。
目前现有的可降解茶具大多采用淀粉材质制成，防渗漏效果不好。
因此针对这一现状，迫切需要设计和生产一种可降解甘蔗纸浆茶具及其制备方法，以满足实际需要。
发明内容
本发明的目的在于提供一种可降解甘蔗纸浆茶具及其制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种可降解甘蔗纸浆茶具，包括甘蔗纸浆、竹纸浆、粘连剂、填料粉、植物染色剂和辅料，各原料质量组份设置为：甘蔗纸浆600-800份、竹纸浆400-600份、粘连剂2-4份、凝固剂2-4份、植物染色剂4-6份和辅料6-8份。
优选的，所述粘连剂设置为甘油、黄原胶和瓜尔豆胶的混合物，且混合物的混合比例设置为3：1：1，所述凝固剂设置为乳酸钙、氯化钙和丙二醇的混合物，且混合物的混合比例设置为2：2：1。
优选的，所述植物染色剂的制作方法为：将指定染色的植物置于破碎机内，得到破壁液，然后利用滤网进行过滤，得到植物染色剂。
优选的，所述辅料设置为表面活性剂和施胶剂的混合物，且混合物的混合比例设置为2：2：1。
优选的，所述表面活性剂设置为两性离子表面活性剂，所述施胶剂设置为聚氨酯。
优选的，所述甘蔗纸浆和竹纸浆的制作方法为：首先将甘蔗废料和竹子置于水力碎浆机内，在水力碎浆机下碾碎成纤维状，利用过滤网过滤出尺寸较大的粗纤维，同时加入一定的白水，碎浆浓度控制在4％，然后注入臭氧进行消毒。
优选的，所述消毒的时间设置为10-20分钟。
一种可降解甘蔗纸浆茶具的制备方法，包括以下步骤：
步骤一、混料：将各项原料置于搅拌机内，按照需要进行搅拌，得到搅拌液；
步骤二、成型：将搅拌液通过设备进行真空吸附脱水成型，脱水后产品毛坯含水量约55％；
步骤三、定型：成型后的产品毛坯，转移至热压固化定型模具中，进行脱水干燥固化定型，定型工序采用了导热油加热，定型后的产品含水率降至5％；
步骤四、切边：定型固化后的产品转至自动切边整理，切除毛坯多余的边角料，使其外形符合产品设计要求；
步骤五、包装：将产品进行消毒，完成之后包装进库。
优选的，所述搅拌的时间设置为20-30分钟，搅拌的转速设置为400-500转每分钟。
优选的，所述定型的温度设置为170-180℃，定型的时间设置为6-8分钟。
与现有技术相比，本发明的技术效果和优点：
该可降解甘蔗纸浆茶具及其制备方法，添加的甘蔗浆纸是甘蔗榨汁后的废品制成，有效的降低成本，竹浆纸作为辅助材料(相对于木制纸浆成本更低)，成本更低；
得益于粘连剂和凝固剂的设计，使得茶具的强度很高，防渗漏能力强，而且甘油、黄原胶、瓜尔豆胶、乳酸钙、氯化钙和丙二醇均为可食用的，对人体无害；
得益于植物染色剂的设计，能够对茶具进行改色，而且采用植物的颜色，对人体无害，且可食用；
该可降解甘蔗纸浆茶具及其制备方法，不仅成本低，而且防渗漏能力强，且对人无害。
具体实施方式
在下文的描述中，给出了大量具体的细节以便提供对本发明更为彻底的理解。然而，对于本领域技术人员而言显而易见的是，本发明可以无需一个或多个这些细节而得以实施。在其他的例子中，为了避免与本发明发生混淆，对于本领域公知的一些技术特征未进行描述。
实施例1
本发明提供了一种可降解甘蔗纸浆茶具，包括甘蔗纸浆、竹纸浆、粘连剂、填料粉、植物染色剂和辅料，各原料质量组份设置为：甘蔗纸浆600份、竹纸浆400份、粘连剂2份、凝固剂2份、植物染色剂4份和辅料6份。
粘连剂设置为甘油、黄原胶和瓜尔豆胶的混合物，且混合物的混合比例设置为3：1：1，凝固剂设置为乳酸钙、氯化钙和丙二醇的混合物，且混合物的混合比例设置为2：2：1，植物染色剂的制作方法为：将指定染色的植物置于破碎机内，得到破壁液，然后利用滤网进行过滤，得到植物染色剂，原料也可以换成其他的，各项原料均设置为可食用的，保证对人体无害。
辅料设置为表面活性剂和施胶剂的混合物，且混合物的混合比例设置为2：2：1，表面活性剂设置为两性离子表面活性剂，施胶剂设置为聚氨酯，原料也可以换成其他的，各项原料均设置为可食用的，保证对人体无害。
甘蔗纸浆和竹纸浆的制作方法为：首先将甘蔗废料和竹子置于水力碎浆机内，甘蔗废料为榨汁完成的甘蔗，竹子设置为竹子或者竹子的废料，在水力碎浆机下碾碎成纤维状，利用过滤网过滤出尺寸较大的粗纤维，同时加入一定的白水，碎浆浓度控制在4％，然后注入臭氧进行消毒，消毒的时间设置为10分钟。
一种可降解甘蔗纸浆茶具的制备方法，包括以下步骤：
步骤一、混料：将各项原料置于搅拌机内，按照需要进行搅拌，得到搅拌液，搅拌的时间设置为20分钟，搅拌的转速设置为400转每分钟；
步骤二、成型：将搅拌液通过设备进行真空吸附脱水成型，脱水后产品毛坯含水量约55％；
步骤三、定型：成型后的产品毛坯，转移至热压固化定型模具中，进行脱水干燥固化定型，定型工序采用了导热油加热，定型后的产品含水率降至5％，定型的温度设置为170℃，定型的时间设置为6分钟；
步骤四、切边：定型固化后的产品转至自动切边整理，切除毛坯多余的边角料，使其外形符合产品设计要求；
步骤五、包装：将产品进行消毒，完成之后包装进库。
实施例2
本发明提供了一种可降解甘蔗纸浆茶具，包括甘蔗纸浆、竹纸浆、粘连剂、填料粉、植物染色剂和辅料，各原料质量组份设置为：甘蔗纸浆6800份、竹纸浆600份、粘连剂4份、凝固剂4份、植物染色剂6份和辅料8份。
粘连剂设置为甘油、黄原胶和瓜尔豆胶的混合物，且混合物的混合比例设置为3：1：1，凝固剂设置为乳酸钙、氯化钙和丙二醇的混合物，且混合物的混合比例设置为2：2：1，植物染色剂的制作方法为：将指定染色的植物置于破碎机内，得到破壁液，然后利用滤网进行过滤，得到植物染色剂，原料也可以换成其他的，各项原料均设置为可食用的，保证对人体无害。
辅料设置为表面活性剂和施胶剂的混合物，且混合物的混合比例设置为2：2：1，表面活性剂设置为两性离子表面活性剂，施胶剂设置为聚氨酯，原料也可以换成其他的，各项原料均设置为可食用的，保证对人体无害。
甘蔗纸浆和竹纸浆的制作方法为：首先将甘蔗废料和竹子置于水力碎浆机内，甘蔗废料为榨汁完成的甘蔗，竹子设置为竹子或者竹子的废料，在水力碎浆机下碾碎成纤维状，利用过滤网过滤出尺寸较大的粗纤维，同时加入一定的白水，碎浆浓度控制在4％，然后注入臭氧进行消毒，消毒的时间设置为10-20分钟。
一种可降解甘蔗纸浆茶具的制备方法，包括以下步骤：
步骤一、混料：将各项原料置于搅拌机内，按照需要进行搅拌，得到搅拌液，搅拌的时间设置为30分钟，搅拌的转速设置为500转每分钟；
步骤二、成型：将搅拌液通过设备进行真空吸附脱水成型，脱水后产品毛坯含水量约55％；
步骤三、定型：成型后的产品毛坯，转移至热压固化定型模具中，进行脱水干燥固化定型，定型工序采用了导热油加热，定型后的产品含水率降至5％，定型的温度设置为180℃，定型的时间设置为8分钟；
步骤四、切边：定型固化后的产品转至自动切边整理，切除毛坯多余的边角料，使其外形符合产品设计要求；
步骤五、包装：将产品进行消毒，完成之后包装进库。
实施例3
本发明提供了一种可降解甘蔗纸浆茶具，包括甘蔗纸浆、竹纸浆、粘连剂、填料粉、植物染色剂和辅料，各原料质量组份设置为：甘蔗纸浆700份、竹纸浆500份、粘连剂3份、凝固剂3份、植物染色剂45份和辅料7份。
粘连剂设置为甘油、黄原胶和瓜尔豆胶的混合物，且混合物的混合比例设置为3：1：1，凝固剂设置为乳酸钙、氯化钙和丙二醇的混合物，且混合物的混合比例设置为2：2：1，植物染色剂的制作方法为：将指定染色的植物置于破碎机内，得到破壁液，然后利用滤网进行过滤，得到植物染色剂，原料也可以换成其他的，各项原料均设置为可食用的，保证对人体无害。
辅料设置为表面活性剂和施胶剂的混合物，且混合物的混合比例设置为2：2：1，表面活性剂设置为两性离子表面活性剂，施胶剂设置为聚氨酯，原料也可以换成其他的，各项原料均设置为可食用的，保证对人体无害。
甘蔗纸浆和竹纸浆的制作方法为：首先将甘蔗废料和竹子置于水力碎浆机内，甘蔗废料为榨汁完成的甘蔗，竹子设置为竹子或者竹子的废料，在水力碎浆机下碾碎成纤维状，利用过滤网过滤出尺寸较大的粗纤维，同时加入一定的白水，碎浆浓度控制在4％，然后注入臭氧进行消毒，消毒的时间设置为10-20分钟。
一种可降解甘蔗纸浆茶具的制备方法，包括以下步骤：
步骤一、混料：将各项原料置于搅拌机内，按照需要进行搅拌，得到搅拌液，搅拌的时间设置为25分钟，搅拌的转速设置为450转每分钟；
步骤二、成型：将搅拌液通过设备进行真空吸附脱水成型，脱水后产品毛坯含水量约55％；
步骤三、定型：成型后的产品毛坯，转移至热压固化定型模具中，进行脱水干燥固化定型，定型工序采用了导热油加热，定型后的产品含水率降至5％，定型的温度设置为175℃，定型的时间设置为7分钟；
步骤四、切边：定型固化后的产品转至自动切边整理，切除毛坯多余的边角料，使其外形符合产品设计要求；
步骤五、包装：将产品进行消毒，完成之后包装进库。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种可降解甘蔗纸浆茶具，其特征在于：包括甘蔗纸浆、竹纸浆、粘连剂、填料粉、植物染色剂和辅料，各原料质量组份设置为：甘蔗纸浆600-800份、竹纸浆400-600份、粘连剂2-4份、凝固剂2-4份、植物染色剂4-6份和辅料6-8份。
2.根据权利要求1所述的一种可降解甘蔗纸浆茶具，其特征在于：所述粘连剂设置为甘油、黄原胶和瓜尔豆胶的混合物，且混合物的混合比例设置为3：1：1，所述凝固剂设置为乳酸钙、氯化钙和丙二醇的混合物，且混合物的混合比例设置为2：2：1。
3.根据权利要求1所述的一种可降解甘蔗纸浆茶具，其特征在于：所述植物染色剂的制作方法为：将指定染色的植物置于破碎机内，得到破壁液，然后利用滤网进行过滤，得到植物染色剂。
4.根据权利要求1所述的一种可降解甘蔗纸浆茶具，其特征在于：所述辅料设置为表面活性剂和施胶剂的混合物，且混合物的混合比例设置为2：2：1。
5.根据权利要求4所述的一种可降解甘蔗纸浆茶具，其特征在于：所述表面活性剂设置为两性离子表面活性剂，所述施胶剂设置为聚氨酯。
6.根据权利要求1所述的一种可降解甘蔗纸浆茶具，其特征在于：所述甘蔗纸浆和竹纸浆的制作方法为：首先将甘蔗废料和竹子置于水力碎浆机内，在水力碎浆机下碾碎成纤维状，利用过滤网过滤出尺寸较大的粗纤维，同时加入一定的白水，碎浆浓度控制在4％，然后注入臭氧进行消毒。
7.根据权利要求6所述的一种可降解甘蔗纸浆茶具，其特征在于：所述消毒的时间设置为10-20分钟。
8.一种权利要求1-7任意一项所述的可降解甘蔗纸浆茶具的制备方法，其特征在于，包括以下步骤：
步骤一、混料：将各项原料置于搅拌机内，按照需要进行搅拌，得到搅拌液；
步骤二、成型：将搅拌液通过设备进行真空吸附脱水成型，脱水后产品毛坯含水量约55％；
步骤三、定型：成型后的产品毛坯，转移至热压固化定型模具中，进行脱水干燥固化定型，定型工序采用了导热油加热，定型后的产品含水率降至5％；
步骤四、切边：定型固化后的产品转至自动切边整理，切除毛坯多余的边角料，使其外形符合产品设计要求；
步骤五、包装：将产品进行消毒，完成之后包装进库。
9.根据权利要求8所述的一种可降解甘蔗纸浆茶具的制备方法，其特征在于：所述搅拌的时间设置为20-30分钟，搅拌的转速设置为400-500转每分钟。
10.根据权利要求8所述的一种可降解甘蔗纸浆茶具的制备方法，其特征在于：所述定型的温度设置为170-180℃，定型的时间设置为6-8分钟。