CN1150167A - Cleaning polish for automobile - Google Patents
Cleaning polish for automobile Download PDFInfo
- Publication number
- CN1150167A CN1150167A CN 95118909 CN95118909A CN1150167A CN 1150167 A CN1150167 A CN 1150167A CN 95118909 CN95118909 CN 95118909 CN 95118909 A CN95118909 A CN 95118909A CN 1150167 A CN1150167 A CN 1150167A
- Authority
- CN
- China
- Prior art keywords
- gram
- automobile
- emulsion
- phase solution
- cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A multifunctional quick-acting cleaning polisher for car contains triethanolamine (1-3.5%), oleic acid (2-10%), atoleine (11-19%), beeswax (0.5-3.5%), emulsified silicon oil (2-5%), deionized water (70-80%), cyclohexanol hexaphosphate (0.05-1.0%) and pH regulator (0.5-1.0%), and features multiple functions including antirust, anticorrosion, antidust, antiviolet ray and paint-protecting ones, quick cleaning and high polishing effect.
Description
The invention belongs to a kind of automobile cleaning polish.
All kinds of automobiles in use need to carry out cleaning, particularly car to vehicle body, and are attractive in appearance for keeping clean, and more will often clean, glazing.At present lustering agent that uses such as Japanese 99 board soft waxs, U.S.'s Golden Shield board lustering agent, Guangdong horse are netted green beautiful cleanly etc., all need the vehicle body water is rinsed well before application, and removing the car body surface dust and dirt could glazing, and troublesome poeration is wasted time and energy.Use solid or semisolid lustering agent, general gasoline, kerosene, the turpentine wet goods of adopting is as solvent, the smell is awful, polluted air, and certain restricted condition arranged when using, be defined under the periods of direct sunlight or the car body surface temperature all can not be used when too high as Japanese 99 board lustering agent specification sheetss, above-mentioned in addition solvent is strong to penetration powers such as paint material resin of usefulness and pigment, perviousness is big, and the oil soluble of pigment and transport property are increased, and is exposed to the top layer, to exosmosis, produce the bleeding phenomenon, automobile finish is faded easily, influence automotive service life.
In order to obtain multiple functions such as decontamination, glazing, sun-proof, moistureproof, antirust, vernix simultaneously, and reduce environmental pollution, reduce labor intensity, the invention provides a kind of economical and practical new formulation.
The present invention is the automobile-used quick-acting cleaning polish of a kind of multifunctional steam.Contain sanitising agent, optical brightener, UV light absorber, static inhibitor, rust-preventive agent etc. in this product, can play antirust, anticorrosion, dustproof, anti-plastics, protect multiple efficacies such as metal, vernix, and clean glazing and once finish.
Effective ingredient of the present invention mainly contains (weight percent content): trolamine 1-35%, oleic acid 2-10%, whiteruss 11-19%, beeswax 0.5-35%, silicone emulsion 2-5%, deionized water 70-80%, hexalin six phosphoesterase 30 .0.5-1.0%, alkaline PH circular pitch agent 0.5-1.0%.Trolamine, newborn being dissolved in than silicone oil are formed aqueous phase solution in the deionized water, oleic acid, whiteruss and beeswax under agitation are heated to molten entirely, make oil-phase solution, aqueous phase solution and oil-phase solution are in 58-62 ℃, under the high-speed stirring, mix, make the base-material emulsion, hexalin six phosphoric acid ester and pH value conditioning agent (4%NaOH) are mixed into the micro alkaline solution that pH value is 7-7.5; Base-material emulsion and micro alkaline solution are mixed into finished emulsion.Finished emulsion and butagas carry out packing by suitable proportion under certain pressure, be finished product.
Contain strong trolamine and the oleic acid of dirt effect that deoils among the present invention, adopt whiteruss and solid cera alba as lustering agent, glossiness is strengthened and improved to special-purpose emulsifying silicone oil as efficient optical brightener again, will clean, ornamental usefulness combines, dual-use function with cleaning and polishing, the product of this liquid is more easy to use than paste, pasty state car wax, does not need the water flushing in advance, directly spraying, decontamination is quick, and glazing is remarkable.Because the present invention is with the body material of solid state wax such as whiteruss replacement carnauba wax as lustering agent, and with silicone emulsion reinforcement enhanced shine, need not add gasoline, the kerosene equal solvent, so automobile finish is not had erosion action, and strengthened and suppressed to fade ability, improved the vernix performance, therefore be applicable to versicolor sedan limousine, unioresistant absorption agent hexalin six phosphoric acid ester have been added among the present invention, the high molecular material resin coating that can prevent the application of automobile top layer effectively is under the sunlight direct projection, be subjected to the influence ultraviolet and oxygen in atmosphere in the daylight and produce the photooxidation resistance effect, lacquer painting is tarnished, become fragile, be full of cracks, the new ultra-violet light absorbers also has good antistatic performance, has also just further strengthened dustproof effect.
Use for convenience; improve wiping efficient and effect, finished product of the present invention charges into butagas and penetrates agent as Throwing, pressurization; after the can; can be made into efficient foam type aerosol, the aerosol of ejection is the topped equably car body finish paint of mousse shape spumescence, forms the adhesivity foam; attract dirt; form one deck protective film at coatingsurface, strengthen antiseptic property, make the not erosion of wind-engaging, rain, snow and salt of paint film.
Embodiment:
1, takes by weighing the deionized water of 740 grams, 20 gram trolamines, the silicone emulsion of 30 grams is made aqueous phase solution, take by weighing 48 gram oleic acid again, the beeswax of 140 gram whiterusss and 15 grams, heated and stirred is to molten entirely in the time of 54-58 ℃, make oil-phase solution, is that per minute 100-150 changes with above-mentioned aqueous phase solution and oil-phase solution stirring the speed of trembling, and in the time of temperature 58-62 ℃, heating mixes and is mixed with base-material emulsion.Take by weighing hexalin six phosphoesterase 30 .5 gram and add PH conditioning agent 4% sodium hydroxide solution 6.5 grams, regulate the pH value to 7-7.5, be mixed with micro alkaline solution, above-mentioned base-material emulsion and micro alkaline solution stirred at normal temperatures is mixed with finished emulsion, and finished emulsion and propellent butagas 250 grams are distributed into canned products under the certain pressure condition.
2, take by weighing 740 gram deionized waters, 20 gram trolamines, 40 gram silicone emulsions are made aqueous phase solution, take by weighing 48 gram oleic acid again, 140 gram whiterusss and 5 gram beeswaxs, heated and stirred is to molten entirely in the time of 54-58 ℃, make oil-phase solution, above-mentioned aqueous phase solution and oil-phase solution low whipping speed are changeed for per minute 100-150, and in the time of temperature 58-62 ℃, heating mixes and is mixed with base-material emulsion.Take by weighing hexalin six phosphoric acid ester 1.0 grams, add PH conditioning agent 4% sodium hydroxide solution 6.5 grams and regulate pH value to 7-7.5, be mixed with micro alkaline solution, above-mentioned base-material emulsion and micro alkaline solution stirred at normal temperatures is mixed with finished emulsion, and finished emulsion and propellent butagas 250 grams are distributed into canned products under the certain pressure condition.
3, take by weighing 720 gram deionized waters, 15 gram trolamines, 30 gram silicone emulsions are made aqueous phase solution, take by weighing 39 gram oleic acid again, 180 gram whiterusss and 9 gram beeswaxs, heated and stirred is to molten entirely in the time of 54-58 ℃, make oil-phase solution, above-mentioned aqueous phase solution and oil-phase solution low whipping speed are changeed for per minute 100-150, and in the time of temperature 58-62 ℃, heating mixes and is mixed with base-material emulsion.Take by weighing hexalin six phosphoric acid ester 2.0 grams and add PH conditioning agent 4% sodium hydroxide solution 65 grams, regulate pH value to 7-7.5, be mixed with micro alkaline solution, above-mentioned base-material emulsion and micro alkaline solution stirred at normal temperatures is mixed with finished emulsion, and finished emulsion and propellent butagas 250 grams are distributed into canned products under the certain pressure condition.
Claims (1)
1, a kind of cleaning polish for automobile, it is characterized in that each effective ingredient and content thereof are (weight percent content): trolamine 1-35%, oleic acid 2-10%, whiteruss 11-19%, beeswax 0.5-3.5%, silicone emulsion 2-5%, deionized water 70-80%, hexalin six phosphoesterase 30 .05-1.0%, really property PH conditioning agent 0.5-1.0%.