CN115008923A - 一种易单撕纸张制本方法 - Google Patents
一种易单撕纸张制本方法 Download PDFInfo
- Publication number
- CN115008923A CN115008923A CN202210787165.2A CN202210787165A CN115008923A CN 115008923 A CN115008923 A CN 115008923A CN 202210787165 A CN202210787165 A CN 202210787165A CN 115008923 A CN115008923 A CN 115008923A
- Authority
- CN
- China
- Prior art keywords
- paper
- parts
- adhesive
- manufacturing
- tear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种易单撕纸张制本方法，涉及纸本生产技术领域，旨在解决市售稿纸本存在使用中不便于撕页的问题，撕页经常导致掉页，从而使稿纸散开破损，不再便于收纳与使用的问题，本发明通过采用胶装工艺，利用粘合剂与胶合剂涂刷多层粘接层，使纸张之间的连接更加牢固紧密，通过在纸张上加工易撕线，制得的纸本在撕掉任何一纸页时，纸张可沿易撕线脱离，其它纸页不会出现掉页问题，而且撕页平整，通过第一次上胶固定纸页和封底，让胶水渗透到纸张的纤维里面，并控制第一层胶层厚度，使得各纸页单独与第一层胶层粘接互不影响；通过第二次上胶，对粘合剂层进行保护，提高纸脊的连接强度，对纸脊的粘接处进行防护，增强纸本的粘结强度。
Description
技术领域
本发明涉及纸本生产技术领域，具体为一种易单撕纸张制本方法。
背景技术
纸，又被称为无光泽毛毡纸，由含植物纤维的原材料经过制浆、调制、抄造、加工等工艺流程制成，可用于写画、印刷书报、包装等，纸是书写、印刷的载体，也可以作为包装、卫生等其他用途，如打印纸、复写纸、卫生纸、面纸等等，由于纸的发明和推广，才使人类可以不再用泥、石、木、陶、金属等材料记录文字或图画，也使古代大量信息得到传播和保存，造纸的原料主要是植物纤维，原料中除含有纤维素、半纤维素、木素三大主要成分外，尚有其他含量较少的组分,如树脂、灰份等，此外还有硫酸钠等辅助成分。
纸张中除了植物纤维，还需要根据不同纸材添加不同的填料，比如铜系抗菌纸就是将铜离子复合在聚丙烯腈(俗称腈纶)的第一单体丙烯腈上，制得改性腈纶复合纤维，然后再将改性腈纶配加到植物纤维中，配上各种用途的纸，即可制得抗菌纸，再生纸来自于废纸，经过消毒、碎浆等处理后可以再度利用，碎浆系统的目的都是将废纸完全碎解而不损伤纤维，不打碎非纸成分。
装订，将印好的书页、书帖加工成册，或把单据、票据等整理配套，订成册本等印后加工，纸张的装订，包括订和装两大工序，订就是将纸张订成本，是本芯的加工，装是制本封面的加工，就是装帧；装订质量的优劣，会影响纸本的使用、保存，装订方式有多种，包括骑马订、铁丝平订、锁线订、胶粘订等，骑马订是用骑马订书机，将套贴配好的本芯连通封面一起，在书脊上用两个铁丝扣订牢成为书刊；铁丝平订是用铁丝订书机，将铁丝穿过书芯的订口，将纸张订在一起；锁线订将配好的书帖，按照顺序用线一帖一帖的串联起来；胶粘订是用胶粘剂将书帖或书页粘合在一起制成书芯。
CN201710396094.2公开了一种设置凸出标贴笔记本及其生产工艺，笔记本需要标示的标示页面在翻合棱边的边缘设置凸出的热熔标贴，热熔标贴对折热熔设置，热熔标贴的边缘热熔夹设在标示页面的边缘；生产工艺，包括：热熔胶带的制作：制作设置标号的热熔胶带，并置入热熔贴标设备；制作完成初装的笔记本；人工翻开初装的笔记本，依次翻开需要标贴的页码，在热熔贴标设备中进行依次设置标贴，翻合棱边凸出设置标贴。
同样作为办公经常使用到的纸类产品，稿纸时常用于书写或打印还用于打草稿，在使用过程中，经常遇到将草稿撕下的情况，市售稿纸本存在使用中不便于撕页的问题，撕页经常导致掉页，从而使稿纸散开破损，不再便于收纳与使用，不能为书写者提供提笔即写的舒适和方便。
发明内容
鉴于现有技术中所存在的问题，本发明公开了一种易单撕纸张制本方法，采用的技术方案是，包括以下步骤：
S1、首先对纸张进行预加热，然后在纸张表面均匀喷洒氯化钠溶液，之后将纸张阴干备用；
氯化钠溶液可对纸张进行消毒，室温阴干可提高纸张的含水量，增强纸张的柔软度。
S2、将S1制备的纸张堆叠，并按本芯的尺寸的两倍进行裁切，制得活页；
S3、将活页靠边贴齐，在每页活页上制作压折线，在压折线的两侧对称制作易撕线，将活页沿压折线对折，制得折帖；
在活页上预留易撕线，可在撕下单页纸张时更加方便容易，并减小对相邻纸张的影响，防止纸本拆散，增强纸本的实用性。
S4、将折帖叠放在一起并对齐，沿折帖的厚度方向进行加压；
加压使同一折帖上的单页纸张贴合更紧密，间隙更小，制本效果更好。
S5、按制本页数选用折帖，进行对齐压紧，在纸脊上涂刷粘合剂，待粘合剂凝结成粘合剂层；
粘合剂层具有一定的柔性，便于粘合折帖，并使粘合处柔软。
S6、在粘合剂层上涂刷胶合剂，胶合剂硬化后，制得纸本成品。
胶合剂层具有一定的硬度，可对纸本的粘接处进行保护，提高纸本的耐用度。
作为本发明的一种优选技术方案，所述S1中，在30-35摄氏度的条件下对纸张进行预热30-40分钟，提高纸张的活性，所述氯化钠溶液的浓度为3-7％，为低浓度氯化钠溶液，避免纸张上残留氯化钠晶体，阴干条件为在室温下通风阴干，干燥过程温和，避免纸张干燥过快产生褶皱。
作为本发明的一种优选技术方案，所述S3中，压折线位于活页的对称中线处，易撕线与压折线的距离为2-4mm，距离活页的叶脊留有空隙，便于撕下单页。
作为本发明的一种优选技术方案，所述合剂按重量组分计，包括以下组分：去离子水40-50份，聚乙烯醇10-20份，醋酸乙烯酯20-35份，丙烯酸丁酯40-50份，甲基丙烯酸甲酯30-40份，硅烷偶联剂2-5份，阴离子乳化剂3-5份，非离子乳化剂4-8份，钠盐熬合剂5-9份，消泡剂2份，防腐剂1-3份。
为了提高纸张的耐磨耐撕耐折等性能，聚乙烯醇制造的纸张表面施胶剂、颜料粘合剂和打浆机添加剂被广泛应于造纸行业，丙烯酸丁酯主要用于制作纤维、橡胶、塑料的高分子单体，有机工业用于制造黏合剂、乳化剂和用作有机合成中间体，造纸工业用于制造纸张增强剂。
作为本发明的一种优选技术方案，所述防腐剂为卡松，所述阴离子乳化剂为烷基酚聚氧乙烯醚，所述非离子乳化剂为烷基酚聚环氧乙烷，所述钠盐熬合剂为乙二胺四乙酸二钠盐、乙二胺四乙酸四钠或羟乙基乙二胺三乙酸三钠其中的一种。
烷基酚聚氧乙烯醚是一种重要的聚氧乙烯型非离子表面活性剂，它具有性质稳定、耐酸碱和成本低等特征，乙二胺四乙酸又叫做EDTA，是化学中一种良好的配合剂，它有六个配位原子，形成的配合物叫做螯合物。
作为本发明的一种优选技术方案，所述胶合剂按重量组分计，包括以下组分：无水乙醇10-12份、聚氯乙烯树脂8-11份、马来酸4-6份、石蜡3-6份、氢化松香甘油脂1-3份、苯并异噻唑酮3-5份、改性淀粉5-8份。
聚氯乙烯英文简称PVC，是氯乙烯单体在过氧化物、偶氮化合物等引发剂或在光、热作用下按自由基聚合反应机理聚合而成的聚合物。
作为本发明的一种优选技术方案，所述改性淀粉采用淀粉糊化制得，改性淀粉是在天然淀粉所具有的固有特性的基础上，为改善淀粉的性能、扩大其应用范围，利用物理、化学或酶法处理，在淀粉分子上引入新的官能团或改变淀粉分子大小和淀粉颗粒性质，从而改变淀粉的天然特性，使其更适合于一定应用的要求。
作为本发明的一种优选技术方案，所述粘合剂的涂刷厚度为0.5mm，所述粘合剂的凝结时间为1-2小时。
作为本发明的一种优选技术方案，所述胶合剂的涂刷厚度为1mm，所述胶合剂涂刷时需加热至80-90度，使胶合剂融化，有利于更好地粘接粘合剂层。
本发明的有益效果：本发明通过采用胶装工艺，利用粘合剂与胶合剂涂刷多层粘接层，使纸张之间的连接更加牢固紧密，通过在纸张上加工易撕线，制得的纸本在撕掉任何一纸页时，纸张可沿易撕线脱离，其它纸页不会出现掉页问题，而且撕页平整，通过第一次上胶固定纸页和封底，让胶水渗透到纸张的纤维里面，并控制第一层胶层厚度，使得各纸页单独与第一层胶层粘接互不影响；通过第二次上胶，对粘合剂层进行保护，提高纸脊的连接强度，对纸脊的粘接处进行防护，增强纸本的粘结强度。
具体实施方式
参选以下本发明的优选实施方法的详述以及包括的实施例可更容易地理解本发明的内容。除非另有限定，本文使用的所有技术以及科学术语具有与本发明所属领域普通技术人员通常理解的相同的含义。当存在矛盾时，以本说明书中的定义为准。
如本文所用术语“由…制备”与“包含”同义。本文中所用的术语“包含”、“包括”、“具有”、“含有”或其任何其它变形，意在覆盖非排它性的包括。例如，包含所列要素的组合物、步骤、方法、制品或装置不必仅限于那些要素，而是可以包括未明确列出的其它要素或此种组合物、步骤、方法、制品或装置所固有的要素。
连接词“由…组成”排除任何未指出的要素、步骤或组分。如果用于权利要求中，此短语将使权利要求为封闭式，使其不包含除那些描述的材料以外的材料，但与其相关的常规杂质除外。当短语“由…组成”出现在权利要求主体的子句中而不是紧接在主题之后时，其仅限定在该子句中描述的要素；其它要素并不被排除在作为整体的所述权利要求之外。
当量、浓度、或者其它值或参数以范围、优选范围、或一系列上限优选值和下限优选值限定的范围表示时，这应当被理解为具体公开了由任何范围上限或优选值与任何范围下限或优选值的任一配对所形成的所有范围，而不论该范围是否单独公开了。例如，当公开了范围“1至5”时，所描述的范围应被解释为包括范围“1至4”、“1至3”、“1至2”、“1至2和4至5”、“1至3和5”等。当数值范围在本文中被描述时，除非另外说明，否则该范围意图包括其端值和在该范围内的所有整数和分数。
单数形式包括复数讨论对象，除非上下文中另外清楚地指明。“任选的”或者“任意一种”是指其后描述的事项或事件可以发生或不发生，而且该描述包括事件发生的情形和事件不发生的情形。
说明书和权利要求书中的近似用语用来修饰数量，表示本发明并不限定于该具体数量，还包括与该数量接近的可接受的而不会导致相关基本功能的改变的修正的部分。相应的，用“大约”、“约”等修饰一个数值，意为本发明不限于该精确数值。在某些例子中，近似用语可能对应于测量数值的仪器的精度。在本申请说明书和权利要求书中，范围限定可以组合和/或互换，如果没有另外说明这些范围包括其间所含有的所有子范围。
此外，本发明要素或组分前的不定冠词“一种”和“一个”对要素或组分的数量要求(即出现次数)无限制性。因此“一个”或“一种”应被解读为包括一个或至少一个，并且单数形式的要素或组分也包括复数形式，除非所述数量明显旨指单数形式。
实施例1
本发明公开了一种易单撕纸张制本方法，采用的技术方案是，包括以下步骤：
S1、首先在30摄氏度的条件下对纸张进行预热30分钟，然后在纸张表面均匀喷洒浓度为3％的氯化钠溶液，之后将纸张在室温下通风阴干备用；
S2、将S1制备的纸张堆叠，并按本芯尺寸的两倍进行裁切，制得活页；
S3、将活页靠边贴齐，在每页活页的对称中线处制作压折线，在压折线的两侧距离为2mm处对称制作易撕线，将活页沿压折线对折，制得折帖；
S4、将折帖叠放在一起并对齐，沿折帖的厚度方向进行加压；
S5、按制本页数选用折帖，进行对齐压紧，在纸脊上涂刷厚度为0.5mm的粘合剂，待粘合剂凝结1小时成粘合剂层；
S6、将胶合剂加热至80度，在粘合剂层上涂刷厚度为1mm的胶合剂，胶合剂硬化后，制得纸本成品。
作为本发明的一种优选技术方案，按重量组分计，所述粘合剂包括以下组分：去离子水40份，聚乙烯醇10份，醋酸乙烯酯20份，丙烯酸丁酯40份，甲基丙烯酸甲酯30份，硅烷偶联剂2份，阴离子乳化剂3份，非离子乳化剂4份，钠盐熬合剂5份，消泡剂2份，防腐剂1份。
作为本发明的一种优选技术方案，所述防腐剂为卡松，所述阴离子乳化剂为烷基酚聚氧乙烯醚，所述非离子乳化剂为烷基酚聚环氧乙烷，所述钠盐熬合剂为乙二胺四乙酸二钠盐。
作为本发明的一种优选技术方案，按重量组分计，所述胶合剂包括以下组分：无水乙醇10份、聚氯乙烯树脂8份、马来酸4份、石蜡3份、氢化松香甘油脂1份、苯并异噻唑酮3份、改性淀粉5份。
作为本发明的一种优选技术方案，所述改性淀粉采用淀粉糊化制得。
实施例2
本发明公开了一种易单撕纸张制本方法，采用的技术方案是，包括以下步骤：
S1、首先在35摄氏度的条件下对纸张进行预热40分钟，然后在纸张表面均匀喷洒浓度为7％的氯化钠溶液，之后将纸张在室温下通风阴干备用；
S2、将S1制备的纸张堆叠，并按本芯尺寸的两倍进行裁切，制得活页；
S3、将活页靠边贴齐，在每页活页的对称中线处制作压折线，在压折线的两侧距离为4mm处对称制作易撕线，将活页沿压折线对折，制得折帖；
S4、将折帖叠放在一起并对齐，沿折帖的厚度方向进行加压；
S5、按制本页数选用折帖，进行对齐压紧，在纸脊上涂刷厚度为0.5mm的粘合剂，待粘合剂凝结2小时成粘合剂层；
S6、将胶合剂加热至90度，在粘合剂层上涂刷厚度为1mm的胶合剂，胶合剂硬化后，制得纸本成品。
作为本发明的一种优选技术方案，按重量组分计，所述粘合剂包括以下组分：去离子水50份，聚乙烯醇20份，醋酸乙烯酯35份，丙烯酸丁酯50份，甲基丙烯酸甲酯40份，硅烷偶联剂5份，阴离子乳化剂5份，非离子乳化剂8份，钠盐熬合剂9份，消泡剂2份，防腐剂3份。
作为本发明的一种优选技术方案，所述防腐剂为卡松，所述阴离子乳化剂为烷基酚聚氧乙烯醚，所述非离子乳化剂为烷基酚聚环氧乙烷，所述钠盐熬合剂为羟乙基乙二胺三乙酸三钠。
作为本发明的一种优选技术方案，按重量组分计，所述胶合剂包括以下组分：无水乙醇12份、聚氯乙烯树脂11份、马来酸6份、石蜡6份、氢化松香甘油脂3份、苯并异噻唑酮5份、改性淀粉8份。
作为本发明的一种优选技术方案，所述改性淀粉采用淀粉糊化制得。
实施例3
本发明公开了一种易单撕纸张制本方法，采用的技术方案是，包括以下步骤：
S1、首先在32摄氏度的条件下对纸张进行预热35分钟，然后在纸张表面均匀喷洒浓度为5％的氯化钠溶液，之后将纸张在室温下通风阴干备用；
S2、将S1制备的纸张堆叠，并按本芯尺寸的两倍进行裁切，制得活页；
S3、将活页靠边贴齐，在每页活页的对称中线处制作压折线，在压折线的两侧距离为3mm处对称制作易撕线，将活页沿压折线对折，制得折帖；
S4、将折帖叠放在一起并对齐，沿折帖的厚度方向进行加压；
S5、按制本页数选用折帖，进行对齐压紧，在纸脊上涂刷厚度为0.5mm的粘合剂，待粘合剂凝结1.5小时成粘合剂层；
S6、将胶合剂加热至85度，在粘合剂层上涂刷厚度为1mm的胶合剂，胶合剂硬化后，制得纸本成品。
作为本发明的一种优选技术方案，按重量组分计，所述粘合剂包括以下组分：去离子水45份，聚乙烯醇15份，醋酸乙烯酯30份，丙烯酸丁酯45份，甲基丙烯酸甲酯35份，硅烷偶联剂3.5份，阴离子乳化剂4份，非离子乳化剂6份，钠盐熬合剂7份，消泡剂2份，防腐剂2份。
作为本发明的一种优选技术方案，所述防腐剂为卡松，所述阴离子乳化剂为烷基酚聚氧乙烯醚，所述非离子乳化剂为烷基酚聚环氧乙烷，所述钠盐熬合剂为乙二胺四乙酸四钠。
作为本发明的一种优选技术方案，按重量组分计，所述胶合剂包括以下组分：无水乙醇11份、聚氯乙烯树脂9份、马来酸5份、石蜡4份、氢化松香甘油脂2份、苯并异噻唑酮4份、改性淀粉6份。
作为本发明的一种优选技术方案，所述改性淀粉采用淀粉糊化制得。
上述虽然对本发明的具体实施例作了详细说明，但是本发明并不限于上述实施例，在本领域普通技术人员所具备的知识范围内，还可以在不脱离本发明宗旨的前提下做出各种变化，而不具备创造性劳动的修改或变形仍在本发明的保护范围以内。
Claims (9)
1.一种易单撕纸张制本方法，其特征在于，包括以下步骤：
S1、首先对纸张进行预加热，然后在纸张表面均匀喷洒氯化钠溶液，之后将纸张阴干备用；
S2、将S1制备的纸张堆叠，并按本芯尺寸的两倍进行裁切，制得活页；
S3、将活页靠边贴齐，在每页活页上制作压折线，在压折线的两侧对称制作易撕线，将活页沿压折线对折，制得折帖；
S4、将折帖叠放在一起并对齐，沿折帖的厚度方向进行加压；
S5、按制本页数选用折帖，进行对齐压紧，在纸脊上涂刷粘合剂，待粘合剂凝结成粘合剂层；
S6、在粘合剂层上涂刷胶合剂，胶合剂硬化后，制得纸本成品。
2.根据权利要求1所述的一种易单撕纸张制本方法，其特征在于：所述S1中，在30-35摄氏度的条件下对纸张进行预热30-40分钟，所述氯化钠溶液的浓度为3-7％，阴干条件为在室温下通风阴干。
3.根据权利要求1所述的一种易单撕纸张制本方法，其特征在于：所述S3中，压折线位于活页的对称中线处，易撕线与压折线的距离为2-4mm。
4.根据权利要求1所述的一种易单撕纸张制本方法，其特征在于，按重量组分计，所述粘合剂包括以下组分：去离子水40-50份，聚乙烯醇10-20份，醋酸乙烯酯20-35份，丙烯酸丁酯40-50份，甲基丙烯酸甲酯30-40份，硅烷偶联剂2-5份，阴离子乳化剂3-5份，非离子乳化剂4-8份，钠盐熬合剂5-9份，消泡剂2份，防腐剂1-3份。
5.根据权利要求4所述的一种易单撕纸张制本方法，其特征在于：所述防腐剂为卡松，所述阴离子乳化剂为烷基酚聚氧乙烯醚，所述非离子乳化剂为烷基酚聚环氧乙烷，所述钠盐熬合剂为乙二胺四乙酸二钠盐、乙二胺四乙酸四钠或羟乙基乙二胺三乙酸三钠其中的一种。
6.根据权利要求1所述的一种易单撕纸张制本方法，其特征在于，按重量组分计，所述胶合剂包括以下组分：无水乙醇10-12份、聚氯乙烯树脂8-11份、马来酸4-6份、石蜡3-6份、氢化松香甘油脂1-3份、苯并异噻唑酮3-5份、改性淀粉5-8份。
7.根据权利要求6所述的一种易单撕纸张制本方法，其特征在于：所述改性淀粉采用淀粉糊化制得。
8.根据权利要求1所述的一种易单撕纸张制本方法，其特征在于：所述S5中，所述粘合剂的涂刷厚度为0.5mm，所述粘合剂的凝结时间为1-2小时。
9.根据权利要求1所述的一种易单撕纸张制本方法，其特征在于：所述S6中，所述胶合剂的涂刷厚度为1mm，所述胶合剂涂刷时需加热至80-90度。