CN114940802B - 一种具有良好热稳定性、低模垢的均聚pom组合物及其制备方法 - Google Patents
一种具有良好热稳定性、低模垢的均聚pom组合物及其制备方法 Download PDFInfo
- Publication number
- CN114940802B CN114940802B CN202210167196.8A CN202210167196A CN114940802B CN 114940802 B CN114940802 B CN 114940802B CN 202210167196 A CN202210167196 A CN 202210167196A CN 114940802 B CN114940802 B CN 114940802B
- Authority
- CN
- China
- Prior art keywords
- tert
- pom
- composition
- homopolymerized
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种具有良好热稳定性、低模垢的均聚POM组合物及其制备方法，包括均聚POM树脂、乙烯‑乙烯醇共聚物、酰胺类润滑剂以及抗氧剂。本发明通过配方的改进大大提高了均聚POM的热稳定性，可以降低加工过程中的异色点以及黑点的产生，并降低客户注塑加工过程中的模垢，具有良好的市场应用前景。
Description
技术领域
本发明属于工程塑料领域，特别涉及一种具有良好热稳定性、低模垢的均聚POM组合物及其制备方法。
背景技术
POM作为一种高度结晶的工程塑料，具有良好的耐磨性、抗蠕变特性和优异的机械性能，在工业机械、办公设备、家电、汽车等领域应用广泛。尤其是均聚POM，具有比共聚POM更高的强度和刚性，在很多应用场合难以被共聚POM替代。但均聚POM热稳定性更差，在加工过程中更加容易发生碳化降解，导致产品出现黑点等外观问题，注塑的时候也容易产生模垢。因此，需要对此问题进行改善。
发明内容
本发明所要解决的技术问题是提供一种具有良好热稳定性、低模垢的均聚POM组合物及其制备方法，该组合物大大提高了均聚POM的热稳定性，可以降低加工过程中的异色点以及黑点的产生，并降低客户注塑加工过程中的模垢，具有良好的市场应用前景。
本发明提供了一种具有良好热稳定性、低模垢的均聚POM组合物，按重量份数，包括如下组分：
所述均聚POM树脂在190℃、2.16kg下(测试标准：ISO 1133-1:2011)的熔融指数为2-15g/10min。
所述乙烯-乙烯醇共聚物的乙烯含量介于25mol％-50mol％之间，熔点为160-190℃之间。。
所述酰胺类润滑剂为乙撑双硬脂酰胺、芥酸酰胺、硬脂酸酰胺中的一种或几种。优选的，所述酰胺类润滑剂为乙撑双硬脂酰胺。
所述抗氧剂包括质量比为1-3：1的主抗氧剂和辅抗氧剂。
所述主抗氧剂为四(β-(3，5-二叔丁基-4-羟基苯基)丙酸)季戊四醇酯、2,2'-亚甲基-双(4-甲基-6-叔丁基苯酚)、二缩三乙二醇双[β-(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯]、三甘醇双β-(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯或己二醇双[3-(3,5-二叔丁基-4-羟基苯基)丙酸酯]中的一种或几种；所述辅抗氧剂为(2，4-二叔丁基苯基)亚磷酸酯、双(2，6-二叔丁基-4-甲基苯基)季戊四醇二磷酸酯、四(2,4-二叔丁基酚)-4,4'-联苯基二亚磷酸酯或双(2，4-二叔丁基苯基)季戊四醇二亚磷酸酯中的一种或几种。
所述组合物还包括0-25份的聚四氟乙烯、0-3份的聚乙烯、0-30份的增韧剂、0-2份的耐候剂中的一种或几种。
优选的，所述增韧剂为热塑性聚氨酯弹性体。
优选的，所述耐候剂为苯并三唑类光稳定剂、受阻胺类中的一种或几种。
所述组合物按重量份数，包括如下组分：
本发明还提供了一种具有良好热稳定性、低模垢的均聚POM组合物的制备方法，包括：
将各原料在高速混合机中混合1-2分钟得到预混料，预混料经双螺杆挤出机在160℃-230℃下熔融挤出、冷却、造粒得到均聚POM组合物。
所述双螺杆挤出机的螺杆转速为250转/分钟-350转/分钟，螺杆温度为160℃-200℃。
本发明还提供了一种具有良好热稳定性、低模垢的均聚POM组合物在家电、汽车、办公设备、电子电器组件中的应用。
有益效果
本发明中的乙烯-乙烯醇共聚物会与甲醛有一定的反应性，同时其气体阻隔性较好，有利于抑制甲醛的释放，提高热稳定性；酰胺类润滑剂可以与甲醛反应进而降低提高热稳定性，因此本发明通过配方的改进大大提高了均聚POM的热稳定性，可以降低加工过程中的异色点以及黑点的产生，并降低客户注塑加工过程中的模垢，具有良好的市场应用前景。
具体实施方式
下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的范围。
实施例及对比例所用的原材料做如下说明，但不限于这些材料：
均聚POM树脂1：190℃、2.16kg下的熔融指数为2g/10min，100P，杜邦；
均聚POM树脂2：190℃、2.16kg下的熔融指数为7g/10min，300P，杜邦；
均聚POM树脂3：190℃、2.16kg下的熔融指数为14g/10min，500P，杜邦；
共聚POM树脂：牌号M90-44，宝理，190℃、2.16kg下的熔融指数为9g/10min；
乙烯-乙烯醇共聚物1：牌号Soarnol A，聚乙烯含量44mol％，熔点164℃，日本合成化；
乙烯-乙烯醇共聚物2：牌号Soarnol D，聚乙烯含量29mol％，熔点188℃，日本合成化；
酰胺类润滑剂1：乙撑双硬脂酰胺，牌号EBS HI-LUBE，韩国信元；
酰胺类润滑剂2：芥酸酰胺，牌号Crodamide ER-BE，禾大化工；
其他润滑剂：PETS；
主抗氧剂：IRGANOX 245，市售；
辅抗氧剂：SONOX 1076，市售；
聚四氟乙烯：F-5AEX，市售。
以上实施例和对比例所用原料为同一种市售产品。
制备方法包括：
将各原料在高速混合机中混合1-2分钟得到预混料，预混料经双螺杆挤出机在160℃-230℃下熔融挤出、冷却、造粒得到POM组合物。
所述双螺杆挤出机由加料口到机头的各螺筒温度分别是：160℃-200℃、170℃-210℃、170℃-220℃、170℃-220℃、180℃-230℃、180℃-220℃、170℃-210℃、170℃-210℃、170℃-210℃、180℃-220℃，螺杆转速为250转/分钟-350转/分钟，喂料量为50kg/h-200kg/h，真空度为(-0.1)-0MPa。
性能评价方式及实行标准：
热稳定性评价方法：在样品放置于熔融指数测试仪中，于230℃下热处理25min，然后将熔体压出，观察熔体的变色情况，根据变色的程度进行打分，数值越大，代表颜色黄变越明显，热稳定性越差；数值越小，代表颜色变化越小，热稳定性越好。
模垢：将样品在230℃下于注塑机中连续注塑200模，称量所收集到的模垢重量观察模具表面的模垢情况。
表1实施例的各组分配比(重量份)
表2对比例的各组分配比(重量份)
表3实施例各性能测试结果
表4对比例各性能测试结果
由表3可以看到，实施例1-8的产品热稳定性良好，且具备低模垢的优点。由对比例1可以看出，本发明的应用于共聚POM组合物时会使得材料强度降低。由对比例3和4可以看出，乙烯-乙烯醇共聚物和酰胺类润滑剂具备一定的协同作用。由对比例5和6可以看出，主抗氧剂和辅抗氧剂均需加入。由对比例7可以看出，其他种类的润滑剂无法解决本发明的技术问题。由对比例8和9可以看出，乙烯-乙烯醇共聚物和酰胺类润滑剂并非加的越多，效果越好，同时，乙烯-乙烯醇共聚物的添加量也要达到一定要求。
Claims (5)
1.一种具有良好热稳定性、低模垢的均聚POM组合物，其特征在于：按重量份数，包括如下组分：
均聚POM树脂 100份；
乙烯-乙烯醇共聚物 0.01-0.25份；
酰胺类润滑剂 0.01-0.5份；
抗氧剂 0.1-0.8份；
其中，所述均聚POM树脂在190℃、2.16kg下的熔融指数为2-15g/10min；
所述乙烯-乙烯醇共聚物的乙烯含量介于25mol%-50mol%之间，熔点为160-190℃之间；
所述抗氧剂包括质量比为1-3：1的主抗氧剂和辅抗氧剂；所述酰胺类润滑剂为乙撑双硬脂酰胺、芥酸酰胺、硬脂酸酰胺中的一种或几种；
所述主抗氧剂为四 (β-(3，5-二叔丁基-4- 羟基苯基)丙酸)季戊四醇酯、2,2'- 亚甲基-双 (4-甲基-6-叔丁基苯酚)、二缩三乙二醇双 [β-(3-叔丁基-4-羟基-5-甲基苯基) 丙酸酯]、三甘醇双 β-(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯或己二醇双[3-(3,5-二叔丁基-4- 羟基苯基) 丙酸酯 ] 中的一种或几种；
所述辅抗氧剂为 (2，4-二叔丁基苯基) 亚磷酸酯、双(2，6-二叔丁基-4-甲基苯基)季戊四醇二磷酸酯、四 (2,4-二叔丁基酚)-4,4'- 联苯基二亚磷酸酯或双 (2，4- 二叔丁基苯基)季戊四醇二亚磷酸酯中的一种或几种。
2.根据权利要求1所述的组合物，其特征在于：所述组合物还包括0-25份的聚四氟乙烯、0-3份的聚乙烯、0-30份的增韧剂、0-2份的耐候剂中的一种或几种。
3.根据权利要求1所述的组合物，其特征在于：所述组合物按重量份数，包括如下组分：
均聚POM树脂 100份；
乙烯-乙烯醇共聚物 0.05-0.2份；
酰胺类润滑剂 0.1-0.3份；
抗氧剂 0.2-0.6份。
4.一种如权利要求1所述的具有良好热稳定性、低模垢的均聚POM组合物的制备方法，包括：
将各原料在高速混合机中混合1-2分钟得到预混料，预混料经双螺杆挤出机在160℃-230℃下熔融挤出、冷却、造粒得到均聚POM组合物。
5.一种如权利要求1所述的具有良好热稳定性、低模垢的均聚POM组合物在家电、汽车、办公设备、电子电器组件中的应用。