CN114907031A - 一种水泥生料添加剂及其应用和水泥生产工艺 - Google Patents
一种水泥生料添加剂及其应用和水泥生产工艺 Download PDFInfo
- Publication number
- CN114907031A CN114907031A CN202210589486.1A CN202210589486A CN114907031A CN 114907031 A CN114907031 A CN 114907031A CN 202210589486 A CN202210589486 A CN 202210589486A CN 114907031 A CN114907031 A CN 114907031A
- Authority
- CN
- China
- Prior art keywords
- additive
- raw material
- cement
- cement raw
- grinding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本公开涉及一种水泥生料添加剂,所述水泥生料添加剂含有丙烯酸及其酯装置产生的废水。本公开提供的水泥生料添加剂能够将丙烯酸及其酯装置产生的废水在水泥生料粉磨和水泥生产中进行回收利用,且具有良好的提高生料磨机产量、降低煤耗、改善生料易烧性和脱硫等综合效果。
Description
技术领域
本公开涉及水泥加工领域,具体地,涉及一种水泥生料添加剂及其应用和水泥生产工艺。
背景技术
水泥主流生产工艺主要分为三大工段,分别为生料粉磨工段、生料煅烧工段和熟料粉磨制水泥工段,俗称为“两磨一烧”。其中生料粉磨工段即石灰质原料、粘土质原料以及少量的校正原料经破碎或烘干后,按一定比例配合、磨细,并制备为成分合适、质量均匀的水泥生料。据统计,粉磨作业需要消耗的动力约占生产总动力的60%以上,其中生料粉磨占30%以上。
由于水泥生产能耗高,降低水泥生产能耗是重要的研究方向,人们采取了许多方法提高水泥生产能量的利用效率,降低能耗,其中,在水泥熟料粉磨工艺中大量应用水泥助磨剂,取得了广泛的社会效益及经济效益。但是,在水泥生产工艺中重要的生料粉磨和烧成过程,则研究不多。
在生产丙烯酸及其酯时由于其易聚合的性质,一般会频繁的使用低浓度碱水清洗反应装置,会产生大量的含盐清洗废水,废水中包含了较多丙烯酸钠、氢氧化钠、对甲苯磺酸钠以及其他多种化学物质。目前处理丙烯酸及其酯装置产生的工业废水的方法主要有焚烧法,湿式催化氧化法,生物法等。由于废水需要添加重油助燃,处理成本高昂;催化氧化法处理废水虽然能够有效的将污染物分解,但是关键在于催化剂,专一性强,对进水条件限制较高,目前只有少数生产厂家采用这种方法,此外催化湿式氧化法处理废水需要高温高压条件,也存在着安全隐患。
发明内容
本公开的目的是提供一种水泥生料添加剂及其应用和水泥生产工艺,并进一步实现资源的合理利用。
为了实现上述目的,本公开第一方面提供一种水泥生料添加剂,所述水泥生料添加剂含有丙烯酸及其酯装置产生的工业废水。
可选地,所述丙烯酸及其酯装置产生的工业废水含有丙烯酸钠、氢氧化钠和对甲苯磺酸钠;所述丙烯酸及其酯装置产生的工业废水的固含量为2-20重量%;以重量计并所述丙烯酸及其酯装置产生的工业废水的重量为基准,所述丙烯酸及其酯装置产生的工业废水中含有0.5-15重量%的丙烯酸钠、0.1-5重量%的氢氧化钠、0.1-2重量%的对甲苯磺酸钠和1-5重量%的其他杂质。
可选地,所述丙烯酸及其酯装置产生的工业废水为浓缩后的工业废水,所述浓缩后的工业废水的固含量为30-50重量%;以重量计并所述浓缩后的工业废水的重量为基准,所述浓缩后的工业废水中含有2-37重量%的丙烯酸钠、0.3-13重量%的氢氧化钠、0.3-5重量%的对甲苯磺酸钠和3-13重量%的其他杂质。
可选地,所述水泥生料添加剂含有醇胺类添加剂;以重量计,所述醇胺类添加剂占所述水泥生料添加剂的比例为0-20重量%;优选为5-10重量%。
可选地,所述醇胺类添加剂为选自三乙醇胺、三异丙醇胺、三环己醇胺、二乙醇单异丙醇胺、二乙醇单环己醇胺、二异丙醇单乙醇胺、二异丙醇单环己醇胺、二环己醇单乙醇胺和二环己醇单异丙醇胺中的至少一种。
可选地,所述水泥生料添加剂含有多元醇醚类添加剂;以重量计,所述多元醇醚类添加剂占所述水泥生料添加剂的比例为0-30重量%;优选为10-20重量%。
可选地,所述多元醇醚类添加剂包括选自多元醇、多元醇醚和糖类中的至少一种;所述多元醇包括选自乙二醇、丙二醇、丙三醇、聚乙二醇、三聚甘油和聚丙二醇中的至少一种;所述多元醇醚选自聚乙二醇醚和/或聚丙二醇醚,所述糖类选自蔗糖和/或糖蜜。
可选地,所述水泥生料添加剂还含有重排法制己内酰胺的废液;可选地,所述重排法制己内酰胺的废液占所述水泥生料添加剂的重量不大于20重量%,优选为5-10重量%。
可选地,所述水泥生料添加剂还含有环己烷氧化的皂化废碱液;可选地,所述环己烷氧化的皂化废碱液占所述水泥生料添加剂的重量不大于30重量%,优选为10-20重量%。
本公开第二方面提供一种水泥生料添加剂在水泥生料粉磨中的应用,该应用包括:将水泥待磨生料和水泥生料添加剂一起进行粉磨处理,得到生料粉磨产物。
可选地,以重量计,所述的水泥生料添加剂占所述水泥待磨生料重量的0.03-1重量%;所述水泥待磨生料包括石灰质原料、粘土质原料和校正原料;所述石灰质原料为选自石灰石、泥灰岩、白垩、贝壳和珊瑚中的至少一种;所述粘土质原料为选自黄土、粘土、页岩、泥岩、粉砂岩和泥沙中的至少一种;所述校正原料为选自铁矿石、铜矿渣、砂岩和河沙中的至少一种。
本公开第三方面提供一种水泥生产工艺,该工艺包括:
将所得的生料粉磨产物在回转窑中进行焙烧,得到水泥待磨熟料;将水泥待磨熟料进行粉磨处理,得到熟料粉磨产物。
通过上述技术方案,本公开将丙烯酸及其酯装置产生的工业废水作为水泥生料添加剂,可以实现丙烯酸及其酯装置产生的工业废水在水泥生料粉磨和水泥生产中进行回收利用,且具有良好的提高产量和降低煤耗等综合效果,在节省成本的同时,具有更为显著的经济效益和环保效益。
本公开的其他特征和优点将在随后的具体实施方式部分予以详细说明。
具体实施方式
以下对本公开的具体实施方式进行详细说明。应当理解的是,此处所描述的具体实施方式仅用于说明和解释本公开,并不用于限制本公开。
本公开第一方面提供一种水泥生料添加剂,所述水泥生料添加剂含有丙烯酸及其酯装置产生的工业废水。
本公开将丙烯酸及其酯装置产生的工业废水作为水泥生料添加剂,可以实现丙烯酸及其酯装置产生的工业废水在水泥生料粉磨和水泥生产中进行回收利用,且具有良好的提高产量和降低煤耗等综合效果,在节省成本的同时,具有更为显著的经济效益和环保效益。
根据本公开,所述丙烯酸及其酯装置产生的工业废水中含有丙烯酸钠、氢氧化钠和对甲苯磺酸钠;可选地,所述丙烯酸及其酯装置产生的工业废水的固含量为2-20重量%;以重量计并所述丙烯酸及其酯装置产生的工业废水的重量为基准,所述丙烯酸及其酯装置产生的工业废水中优选地含有0.5-15重量%的丙烯酸钠、0.1-5重量%的氢氧化钠、0.1-2重量%的对甲苯磺酸钠和1-5重量%的其他杂质。
本公开的丙烯酸及其酯装置产生的工业废水可以不经任何预处理即可直接作为水泥生料外加剂进行粉磨;加入调节添加剂的效果更佳。调节添加剂是指加入到助磨剂中有助于提高粉磨、增强效果的组分,其组成和添加量本发明并不进行限制,可以以单一组分加入,也可以是常规助磨剂以添加剂形式加入。
根据本公开,所述水泥生料添加剂可以含有其他任选的调节添加剂,优选地,所述调节添加剂可以包括选自醇胺类添加剂和多元醇醚添加剂中的至少一种。
根据本公开,所述水泥生料添加剂可以含有醇胺类添加剂,醇胺类添加剂有助于消除静电,提高粉磨效果;以重量计,所述醇胺类添加剂占所述水泥生料添加剂的比例可以为0-20重量%;优选为5-10重量%;所述醇胺类添加剂可以为选自三乙醇胺、三异丙醇胺、三环己醇胺、二乙醇单异丙醇胺、二乙醇单环己醇胺、二异丙醇单乙醇胺、二异丙醇单环己醇胺、二环己醇单乙醇胺和二环己醇单异丙醇胺中的至少一种。
根据本公开,所述水泥生料添加剂可以含有多元醇醚类添加剂,多元醇醚类添加剂有助于消除静电,提高粉磨效果;以重量计,所述多元醇醚类添加剂占所述水泥生料添加剂的比例可以为0-30重量%;优选为10-20重量%;所述多元醇醚类添加剂可以包括选自多元醇、多元醇醚和糖类中的至少一种,所述多元醇可以包括选自乙二醇、丙二醇、丙三醇、聚乙二醇、三聚甘油和聚丙二醇中的至少一种,所述多元醇醚可以选自聚乙二醇醚和/或聚丙二醇醚,所述糖类选自蔗糖和/或糖蜜。
作为本公开的一种优选的实施方式,所述水泥生料添加剂还含有重排法制己内酰胺的废液;其中,己内酰胺废液中扣除水外,主要有机组分如氨基己酸、己内酰胺及聚合物等占到约50-70重量%,主要无机组分为硫酸铵占约20-40重量%,还有氯化钠、硝酸钠、硫氰酸钠等总共约占5-10重量%。可选地,所述重排法制己内酰胺的废液占所述水泥生料添加剂的重量不大于20重量%,优选为5-10重量%。
作为本公开的一种优选的实施方式,所述水泥生料添加剂还含有环己烷氧化的皂化废碱液;所述环己烷氧化的皂化废碱液组分以有机酸钠为主,具有助磨等协同作用。可选地,所述环己烷氧化的皂化废碱液占所述水泥生料添加剂的重量不大于30重量%,优选为10-20重量%
本公开第二方面提供一种水泥生料添加剂在水泥生料粉磨中的应用,该应用包括:将水泥待磨生料和水泥生料添加剂一起进行粉磨处理,得到生料粉磨产物;其中,所述水泥生料添加剂为本公开所提供的水泥生料添加剂。
本公开中,工业废液可以直接进行水泥生料粉磨,也可以任选进行调配后作为水泥生料粉磨使用。
可选地,本公开提供的水泥生料添加剂可以以0.01-1重量%的内掺量用于水泥待磨生料的粉磨,达到助磨提产及节煤的效果,即,以重量计,所述的水泥生料添加剂占所述水泥待磨生料重量的0.01-1重量%;所述水泥待磨生料是本领域技术人员所熟知的,是指水泥“两磨一烧”的制备工艺中进行第一次粉磨前的水泥原材料,可以包括石灰质原料、粘土质原料和校正原料;所述石灰质原料可以为选自石灰石、泥灰岩、白垩、贝壳和珊瑚中的至少一种;所述粘土质原料可以为选自黄土、粘土、页岩、泥岩、粉砂岩和泥沙中的至少一种;所述校正原料可以为选自铁矿石、铜矿渣、砂岩和河沙中的至少一种。
本公开第三方面提供一种水泥生产工艺,该工艺包括:
将所得的生料粉磨产物在回转窑中进行焙烧,得到水泥待磨熟料;将水泥待磨熟料进行粉磨处理,得到熟料粉磨产物。
根据本公开,生料粉磨产物进行焙烧是本领域技术人员所熟知的,是指将生料粉磨产物送入水泥回转窑内焙烧至部分熔融,所得以硅酸钙为主要成分的硅酸钙水泥熟料(颗粒状或块状)。
下面通过实施例来进一步说明本公开,但是本公开并不因此而受到任何限制。
本公开实施例中所使用的丙烯酸及其酯装置产生的工业废水,记为D1,主要取自上海华谊丙烯酸有限公司。对该丙烯酸及其酯装置产生的工业废水进行检测,该丙烯酸及其酯装置产生的工业废水的固含量为18重量%;含有12重量%的丙烯酸钠、3重量%的氢氧化钠、1重量%的对甲苯磺酸钠和2重量%的其他杂质和余量的水。
本公开实施例中所使用的重排法制己内酰胺的废液和皂化废碱液,主要取自中国石化集团巴陵分公司己内酰胺事业部。
将重排法制己内酰胺的初始废液,浓度约4.5重量%,记为B1液。
环己烷氧化制环己酮工艺为无催化剂氧化法。皂化废碱液的初始废液,浓度约6重量%,记为A1液。
实施例中使用的调节添加剂:三聚甘油和三乙醇胺均为商购,对比例中丙烯酸钠溶液为使用商购的丙烯酸钠配置成与D1液等丙烯酸钠浓度的溶液。
实施例中,水泥生料添加剂掺比=水泥生料添加剂重量/水泥待磨生料重量。
应用实验的具体操作步骤如下:
(1)把水泥生料的所有原材料分别先进行预均化,然后破碎至7mm,再次进行二次均化;把二次均化后的原材料放入干燥箱内在105℃±5℃下进行不少于4h烘干备用,即为待磨水泥生料。
(2)空白实验:称取配制好的5kg待磨水泥生料,投入到φ500×500mm的实验标准球磨机中,磨至80μm方孔筛筛余16%-18%,记录粉磨时间TS,按GB/T 1345检验水泥生料粉的80μm方孔筛筛余。
(3)掺助剂的对比实验:水泥生料添加剂按实验计划掺比,均匀的加在上述备好的5kg生料原材料上,粉磨同等TS,测定水泥生料粉的80μm方孔筛筛余。通过计算空白生料样品80μm方孔筛筛余与掺生料助磨剂的80μm方孔筛筛余之差,反映外加剂的助磨效果。
(4)水泥生料外加剂的掺入,不应对水泥生料易烧性造成不利影响,具体行业采用测试同一水泥生料样品中掺入生料助磨剂前后生料易烧性的变化情况,熟料中游离氧化钙含量不应增加作为评价指标。具体按GB/T26566取样并进行煅烧试验,按GB/T 176进行游离氧化钙的测定。
具体对比例KB1和实施例SY1-6,均采用的为江西亚东水泥公司的水泥生料原料,粉磨时间9.0分钟。
对比例KB1
将待磨水泥生料单独进行生料粉磨处理,具体结果见表1。
实施例SY1
将D1液(100重量份)以0.1重量%的比例掺水泥待磨生料进行生料粉磨处理和煅烧,具体结果见表1。
实施例SY2
将D1液(100重量份)加入13重量份的二乙醇单异丙醇胺后作为水泥生料添加剂,以0.7重量%的比例掺水泥待磨生料进行生料粉磨处理和煅烧,具体结果见表1。
实施例SY3
将D1液(100重量份)加入10重量份的三聚甘油后作为水泥生料添加剂,以0.6重量%的比例掺水泥待磨生料进行生料粉磨处理和煅烧,具体结果见表1。
实施例SY4
将D1液(100重量份)加入15重量份的三聚甘油和9重量份的三乙醇胺后作为水泥生料添加剂,以0.8重量%的比例掺水泥待磨生料进行生料粉磨处理和煅烧,具体结果见表1。
实施例SY5
将D1液(100重量份)与B1液(20重量份)混合后作为水泥生料添加剂,以1重量%的比例掺水泥待磨生料进行生料粉磨处理和煅烧,具体结果见表1。
实施例SY6
将D1液(100重量份)与A1液(30重量份)混合后作为水泥生料添加剂,以1重量%的比例掺水泥待磨生料进行生料粉磨处理和煅烧,具体结果见表1。
对比例KB2
将丙烯酸钠溶液(100重量份)作为水泥生料添加剂,以0.1重量%的比例掺水泥待磨生料进行生料粉磨处理和煅烧,具体结果见表1。
表1
通过表1可以看出,随着增加及调节添加剂的加入,助磨性能优化更加明显。同时从煅烧后游离钙含量情况看,易烧性总体略有改善。
具体实施例SY7-10,用SY4中的统一配方,掺比均0.2重量%计,采用了不同地区的水泥厂的原材料进行对比,实验结果间表2。
表2
通过表2可以看出,本公开的水泥生料助磨剂对不同水泥厂原料的应用实验,在助磨和易烧性方面均体现出有益效果。但是由于每家水泥厂的矿石材料存在差异,表现的效果有所差异。
以上详细描述了本公开的优选实施方式,但是,本公开并不限于上述实施方式中的具体细节,在本公开的技术构思范围内,可以对本公开的技术方案进行多种简单变型,这些简单变型均属于本公开的保护范围。
另外需要说明的是,在上述具体实施方式中所描述的各个具体技术特征,在不矛盾的情况下,可以通过任何合适的方式进行组合,为了避免不必要的重复,本公开对各种可能的组合方式不再另行说明。
此外,本公开的各种不同的实施方式之间也可以进行任意组合,只要其不违背本公开的思想,其同样应当视为本公开所公开的内容。
Claims (10)
1.一种水泥生料添加剂,其特征在于,所述水泥生料添加剂含有丙烯酸及其酯装置产生的工业废水。
2.根据权利要求1所述的水泥生料添加剂,其中,
所述丙烯酸及其酯装置产生的工业废水含有丙烯酸钠、氢氧化钠和对甲苯磺酸钠;
所述丙烯酸及其酯装置产生的工业废水的固含量为2-20重量%;
以重量计并所述丙烯酸及其酯装置产生的工业废水的重量为基准,所述丙烯酸及其酯装置产生的工业废水中含有0.5-15重量%的丙烯酸钠、0.1-5重量%的氢氧化钠、0.1-2重量%的对甲苯磺酸钠和1-5重量%的其他杂质。
3.根据权利要求1或2所述的水泥生料添加剂,其中,所述丙烯酸及其酯装置产生的工业废水为浓缩后的工业废水,所述浓缩后的工业废水的固含量为30-50重量%;
以重量计并所述浓缩后的工业废水的重量为基准,所述浓缩后的工业废水中含有2-37重量%的丙烯酸钠、0.3-13重量%的氢氧化钠、0.3-5重量%的对甲苯磺酸钠和3-13重量%的其他杂质。
4.根据权利要求1所述的水泥生料添加剂,其中,所述水泥生料添加剂含有醇胺类添加剂;
以重量计,所述醇胺类添加剂占所述水泥生料添加剂的比例为0-20重量%;优选为5-10重量%;
可选地,所述醇胺类添加剂为选自三乙醇胺、三异丙醇胺、三环己醇胺、二乙醇单异丙醇胺、二乙醇单环己醇胺、二异丙醇单乙醇胺、二异丙醇单环己醇胺、二环己醇单乙醇胺和二环己醇单异丙醇胺中的至少一种。
5.根据权利要求1所述的水泥生料添加剂,其中,所述水泥生料添加剂含有多元醇醚类添加剂;
以重量计,所述多元醇醚类添加剂占所述水泥生料添加剂的比例为0-30重量%;优选为10-20重量%;
可选地,所述多元醇醚类添加剂包括选自多元醇、多元醇醚和糖类中的至少一种;所述多元醇包括选自乙二醇、丙二醇、丙三醇、聚乙二醇、三聚甘油和聚丙二醇中的至少一种;所述多元醇醚选自聚乙二醇醚和/或聚丙二醇醚,所述糖类选自蔗糖和/或糖蜜。
6.根据权利要求1所述的水泥生料添加剂,其中,所述水泥生料添加剂还含有重排法制己内酰胺的废液;
可选地,所述重排法制己内酰胺的废液占所述水泥生料添加剂的重量不大于20重量%,优选为5-10重量%。
7.根据权利要求1所述的水泥生料添加剂,其中,所述水泥生料添加剂还含有环己烷氧化的皂化废碱液;
可选地,所述环己烷氧化的皂化废碱液占所述水泥生料添加剂的重量不大于30重量%,优选为10-20重量%。
8.一种水泥生料添加剂在水泥生料粉磨中的应用,该应用包括:将水泥待磨生料和水泥生料添加剂一起进行粉磨处理,得到生料粉磨产物;
其中,所述水泥生料添加剂为权利要求1-7中任意一项所述的水泥生料添加剂。
9.根据权利要求8所述的应用,其中,以重量计,权利要求1-8中任意一项所述的水泥生料添加剂占所述水泥待磨生料重量的0.01-1重量%;
所述水泥待磨生料包括石灰质原料、粘土质原料和校正原料;
所述石灰质原料为选自石灰石、泥灰岩、白垩、贝壳和珊瑚中的至少一种;所述粘土质原料为选自黄土、粘土、页岩、泥岩、粉砂岩和泥沙中的至少一种;所述校正原料为选自铁矿石、铜矿渣、砂岩和河沙中的至少一种。
10.一种水泥生产工艺,该工艺包括:
将权利要求8或9中的应用所得的生料粉磨产物在回转窑中进行焙烧,得到水泥待磨熟料;将水泥待磨熟料进行粉磨处理,得到熟料粉磨产物。