CN114874680A - 一种水性漆 - Google Patents
一种水性漆 Download PDFInfo
- Publication number
- CN114874680A CN114874680A CN202210461845.5A CN202210461845A CN114874680A CN 114874680 A CN114874680 A CN 114874680A CN 202210461845 A CN202210461845 A CN 202210461845A CN 114874680 A CN114874680 A CN 114874680A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- calcium carbonate
- based paint
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及水性漆技术领域，且公开了一种水性漆，包括以下重量份数配比的原料：聚硅氧烷25‑35份，聚醚多元醇110‑115份，甲苯25‑35份，催化剂0.1‑0.3份，碳酸氢钠130‑140份，水性环氧树脂500‑550份，催化剂0.1‑0.3份，多功能助剂2‑4份，表面活性剂1‑3份，丙二醇10‑12份，二丙二醇甲醚2‑4份，钛白粉140‑150份，碳酸钙140‑150份，去离子水120‑130份，增稠剂0.2‑0.4份。该水性漆，添加钛白粉和碳酸钙等，白粉具有优越的白度、着色力、遮盖力、耐候性、耐热性、和化学稳定性，且没有毒性，使得水性漆更加环保，通添加的聚硅氧烷、聚醚多元醇、甲苯和份三氟乙酸等成分，能降低水性漆的表面张力，改善了使用时产生气泡导致涂抹面不光滑而影响涂抹质量的问题，实现了涂抹时气泡少的目的。
Description
技术领域
本发明涉及水性漆技术领域，具体为一种水性漆。
背景技术
水性漆即水性防锈漆，水性钢构漆，水性地坪漆，水性木器漆，对人体无害，不污染环境，漆膜丰满、晶莹透亮、柔韧性好并且具有耐水、耐磨、耐老化、耐黄变、干燥快、使用方便等特点。
随着环保政策的施压，消费者环保意识的不断提升，尤其全国各地省市出台了VOC排放限量标准，鼓励使用非溶剂型涂料，给水性漆等环保涂料的发展带来了机遇，但是目前市场上的水性漆在使用时会产生较多的气泡，产生的气泡导致涂抹面不光滑，影响产品质量，故而提出一种水性漆来解决上述问题。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种水性漆，具备涂抹时气泡少等优点，解决了目前市场上的水性漆在使用时会产生较多的气泡，产生的气泡导致涂抹面不光滑，影响产品质量的问题。
(二)技术方案
为实现上述涂抹时气泡少目的，本发明提供如下技术方案：一种水性漆，包括以下重量份数配比的原料：聚硅氧烷25-35份，聚醚多元醇110-115份，甲苯25-35份，催化剂0.1-0.3份，碳酸氢钠130-140份，水性环氧树脂500-550份，催化剂0.1-0.3份，多功能助剂2-4份，表面活性剂1-3份，丙二醇10-12份，二丙二醇甲醚2-4份，钛白粉140-150份，碳酸钙140-150份，去离子水120-130份，增稠剂0.2-0.4份。
优选的，所述水性环氧树脂500-550份为水性环氧树脂乳液，所述催化剂0.1-0.3份为三氟乙酸溶液。
优选的，所述碳酸钙为1000目重质碳酸钙粉，白度为94-96％，碳酸钙含量96-98％。
优选的，所述表面活性剂1-3份为脂肪酸蔗糖聚酯粉，所述增稠剂0.2-0.4份为非离子聚氨酯增稠剂。
优选的，包括以下份数的原料：聚硅氧烷25份，聚醚多元醇110份，甲苯25份，催化剂0.1份，碳酸氢钠130份，水性环氧树脂500份，催化剂0.1份，多功能助剂2份，表面活性剂1份，丙二醇10份，二丙二醇甲醚2份，钛白粉140份，碳酸钙140-150份，去离子水120份，增稠剂0.2份。
优选的，包括以下份数的原料：聚硅氧烷30份，聚醚多元醇113份，甲苯30份，催化剂0.2份，碳酸氢钠135份，水性环氧树脂525份，催化剂0.2份，多功能助剂3份，表面活性剂2份，丙二醇11份，二丙二醇甲醚3份，钛白粉145份，碳酸钙145份，去离子水125份，增稠剂0.3份。
优选的，包括以下份数的原料：聚硅氧烷35份，聚醚多元醇115份，甲苯35份，催化剂0.3份，碳酸氢钠140份，水性环氧树脂550份，催化剂0.3份，多功能助剂-4份，表面活性剂3份，丙二醇12份，二丙二醇甲醚4份，钛白粉150份，碳酸钙150份，去离子水130份，增稠剂0.4份。
(三)有益效果
与现有技术相比，本发明提供了一种水性漆，具备以下有益效果：
1、该水性漆，通过添加的聚硅氧烷、聚醚多元醇、甲苯和份三氟乙酸等成分，能降低水性漆的表面张力，改善了使用时产生气泡导致涂抹面不光滑而影响涂抹质量的问题，实现了涂抹时气泡少的目的。
2、该水性漆，添加钛白粉和碳酸钙等，其中碳酸钙使得水性漆不容易沉降，易分散，光泽好，而钛白粉具有优越的白度、着色力、遮盖力、耐候性、耐热性、和化学稳定性，且没有毒性，使得水性漆更加环保。
具体实施方式
下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一：包括以下份数的原料：聚硅氧烷25份，聚醚多元醇110份，甲苯25份，催化剂0.1份，碳酸氢钠130份，水性环氧树脂500份，催化剂0.1份，多功能助剂2份，表面活性剂1份，丙二醇10份，二丙二醇甲醚2份，钛白粉140份，碳酸钙140-150份，去离子水120份，增稠剂0.2份。
本实施例中，水性环氧树脂500份为水性环氧树脂乳液，催化剂0.1份为三氟乙酸溶液。
本实施例中，碳酸钙为1000目重质碳酸钙粉，白度为94-96％，碳酸钙含量96-98％。
本实施例中，表面活性剂1份为脂肪酸蔗糖聚酯粉，所述增稠剂0.2份为非离子聚氨酯增稠剂。
该水性漆，通过添加的聚硅氧烷、聚醚多元醇、甲苯和份三氟乙酸等成分，能降低水性漆的表面张力，改善了使用时产生气泡导致涂抹面不光滑而影响涂抹质量的问题，实现了涂抹时气泡少的目的。
实施例二：包括以下份数的原料：聚硅氧烷30份，聚醚多元醇113份，甲苯30份，催化剂0.2份，碳酸氢钠135份，水性环氧树脂525份，催化剂0.2份，多功能助剂3份，表面活性剂2份，丙二醇11份，二丙二醇甲醚3份，钛白粉145份，碳酸钙145份，去离子水125份，增稠剂0.3份。
本实施例中，水性环氧树脂525份为水性环氧树脂乳液，催化剂0.2份为三氟乙酸溶液。
本实施例中，碳酸钙为1000目重质碳酸钙粉，白度为94-96％，碳酸钙含量96-98％。
本实施例中，表面活性剂2份为脂肪酸蔗糖聚酯粉，所述增稠剂0.3份为非离子聚氨酯增稠剂。
该水性漆，通过添加的聚硅氧烷、聚醚多元醇、甲苯和份三氟乙酸等成分，能降低水性漆的表面张力，改善了使用时产生气泡导致涂抹面不光滑而影响涂抹质量的问题，实现了涂抹时气泡少的目的。
实施例三：包括以下份数的原料：聚硅氧烷35份，聚醚多元醇115份，甲苯35份，催化剂0.3份，碳酸氢钠140份，水性环氧树脂550份，催化剂0.3份，多功能助剂-4份，表面活性剂3份，丙二醇12份，二丙二醇甲醚4份，钛白粉150份，碳酸钙150份，去离子水130份，增稠剂0.4份。
本实施例中，水性环氧树脂550份为水性环氧树脂乳液，催化剂0.3份为三氟乙酸溶液。
本实施例中，碳酸钙为1000目重质碳酸钙粉，白度为94-96％，碳酸钙含量96-98％。
本实施例中，表面活性剂3份为脂肪酸蔗糖聚酯粉，所述增稠剂0.4份为非离子聚氨酯增稠剂。
该水性漆，通过添加的聚硅氧烷、聚醚多元醇、甲苯和份三氟乙酸等成分，能降低水性漆的表面张力，改善了使用时产生气泡导致涂抹面不光滑而影响涂抹质量的问题，实现了涂抹时气泡少的目的。
本发明的有益效果是：
典型案例：该水性漆，通过添加的聚硅氧烷、聚醚多元醇、甲苯和份三氟乙酸等成分，能降低水性漆的表面张力，改善了使用时产生气泡导致涂抹面不光滑而影响涂抹质量的问题，实现了涂抹时气泡少的目的；添加钛白粉和碳酸钙等，其中碳酸钙使得水性漆不容易沉降，易分散，光泽好，而钛白粉具有优越的白度、着色力、遮盖力、耐候性、耐热性、和化学稳定性，且没有毒性，使得水性漆更加环保。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (7)
1.一种水性漆，其特征在于，包括以下重量份数配比的原料：聚硅氧烷25-35份，聚醚多元醇110-115份，甲苯25-35份，催化剂0.1-0.3份，碳酸氢钠130-140份，水性环氧树脂500-550份，催化剂0.1-0.3份，多功能助剂2-4份，表面活性剂1-3份，丙二醇10-12份，二丙二醇甲醚2-4份，钛白粉140-150份，碳酸钙140-150份，去离子水120-130份，增稠剂0.2-0.4份。
2.根据权利要求1所述的一种水性漆，其特征在于，所述水性环氧树脂500-550份为水性环氧树脂乳液，所述催化剂0.1-0.3份为三氟乙酸溶液。
3.根据权利要求1所述的一种水性漆，其特征在于，所述碳酸钙为1000目重质碳酸钙粉，白度为94-96％，碳酸钙含量96-98％。
4.根据权利要求1所述的一种水性漆，其特征在于，所述表面活性剂1-3份为脂肪酸蔗糖聚酯粉，所述增稠剂0.2-0.4份为非离子聚氨酯增稠剂。
5.根据权利要求1所述的一种水性漆，其特征在于，包括以下份数的原料：聚硅氧烷25份，聚醚多元醇110份，甲苯25份，催化剂0.1份，碳酸氢钠130份，水性环氧树脂500份，催化剂0.1份，多功能助剂2份，表面活性剂1份，丙二醇10份，二丙二醇甲醚2份，钛白粉140份，碳酸钙140-150份，去离子水120份，增稠剂0.2份。
6.根据权利要求1所述的一种水性漆，其特征在于，包括以下份数的原料：聚硅氧烷30份，聚醚多元醇113份，甲苯30份，催化剂0.2份，碳酸氢钠135份，水性环氧树脂525份，催化剂0.2份，多功能助剂3份，表面活性剂2份，丙二醇11份，二丙二醇甲醚3份，钛白粉145份，碳酸钙145份，去离子水125份，增稠剂0.3份。
7.根据权利要求1所述的一种水性漆，其特征在于，包括以下份数的原料：聚硅氧烷35份，聚醚多元醇115份，甲苯35份，催化剂0.3份，碳酸氢钠140份，水性环氧树脂550份，催化剂0.3份，多功能助剂-4份，表面活性剂3份，丙二醇12份，二丙二醇甲醚4份，钛白粉150份，碳酸钙150份，去离子水130份，增稠剂0.4份。