CN114836116A - 一种水性桔纹漆及制备喷涂工艺 - Google Patents
一种水性桔纹漆及制备喷涂工艺 Download PDFInfo
- Publication number
- CN114836116A CN114836116A CN202210341783.4A CN202210341783A CN114836116A CN 114836116 A CN114836116 A CN 114836116A CN 202210341783 A CN202210341783 A CN 202210341783A CN 114836116 A CN114836116 A CN 114836116A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- aqueous
- paint
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种水性桔纹漆，包括A及B组分，其中：A组分包括如下质量份数的组分：水性羟基丙烯酸分散体15～18份、水性丙烯酸乳液30～42份、水性聚氨酯分散体60～80份、水性聚氯乙烯乳液3‑5份、钛白4～7份、滑石粉1～3份、消泡剂0.04～0.8份、成膜助剂7～10份、水性流变助剂0.01～0.06份、触变剂15～20份、催干剂2～5份；B组分包括如下质量份数的组分：水性异氰酸酯固化剂15～22份、叔十二烷基硫醇30～40份；所述A组分与B组分的‑OH/‑NCO为1：1.3，—NHCOO/‑NCO为1：2，上述组分水解后‑OH/Si‑OH为1：2.1。本发明还提供了一种水性桔纹漆的制备喷涂工艺，喷涂方法简单，桔纹漆使用牢固。
Description
技术领域
本发明涉及水性漆技术领域，特别是指一种水性桔纹漆及制备喷涂工艺。
背景技术
桔纹漆具有桔纹清晰、立体感强，装饰性能好等特点，适用于各类机械、设备、机床等保护装饰涂装，能掩饰各种金属表面粗糙不平的瑕疵起到美术装饰效果。目前，桔纹漆多以油性漆为主，随着国家对环境污染重视程度的逐步提高，桔纹漆产品水性化需求已迫在眉睫。
在CN202010120351.1中提出了一种水性聚氨酯桔纹漆，包括A组分和B组分，所述A组分包括如下质量份数的组分：羟基丙烯酸分散体45-60份；钛白粉20-25份；硫酸钡5-10份；桔纹助剂0.7-1.2份；分散剂1-1.5份；消泡剂0.08-0.3份；成膜助剂2-3份；水性流变助剂0.1-0.3份和去离子水10-20份，所述B组分包括水性异氰酸酯固化剂90-100份；所述A组分与B组分的-OH/-NCO为1：1.3，所述水性聚氨酯桔纹漆的颜料体积浓度为35～45％；所述羟基丙烯酸分散体为水性羟基丙烯酸树脂WD-551，所述桔纹助剂为桔纹助剂RZ608，所述水性流变助剂为水性流变助剂HX1080。上述成分的桔纹漆，在储存稳定性、干燥速度上及成膜稳固上效果仍然不佳。
发明内容
本发明的一目的：为了克服现有技术的缺陷，本发明提供了一种使用效果稳定的水性桔纹漆。
本发明的技术方案：一种水性桔纹漆，包括A及B组分，其中：
A组分包括如下质量份数的组分：水性羟基丙烯酸分散体15～18份、水性丙烯酸乳液30～42份、水性聚氨酯分散体60～80份、水性聚氯乙烯乳液3-5份、钛白4～7份、滑石粉1～3份、消泡剂0.04～0.8份、成膜助剂7～10份、水性流变助剂0.01～0.06份、触变剂15～20份、催干剂2～5份；
B组分包括如下质量份数的组分：水性异氰酸酯固化剂15～22份、叔十二烷基硫醇30～40份；
所述A组分与B组分的-OH/-NCO为1：1.3，—NHCOO/-NCO为1：2，上述组分水解后-OH/Si-OH为1：2.1。
所述A组分还包括：硫酸钡5～8份。
所述B组分还包括：多酚类化合物0.01～0.08份。
水性聚氨酯分散体，具有以下重量份的组分：
聚酯多元醇20～35份、聚醚多元醇20～35份、惰性乙烯基单体4～18份、交联剂0.15～0.3份和催化剂1～1.5份，其中聚酯多元醇与聚醚多元醇质量比为1:1。
水性丙烯酸乳液，具有以下重量份的组分：
纯丙烯酸乳液15-30份、苯乙烯-丙烯酸乳液0.5-3份。
水性桔纹漆的体积浓度为35～45％。
与现有技术相比，本发明的有益技术效果：
本发明提供的水性桔纹漆，水性羟基丙烯酸分散体、水性丙烯酸乳液、水性聚氨酯分散体和水性聚氯乙烯乳液为主要成膜物质，羟基丙烯酸分散体具有合适的固含量和羟基含量，与水性异氰酸酯固化剂、叔十二烷基硫醇充分交联反应，使漆膜不仅具有良好的硬度、耐化学性，还具有良好的厚涂性，有助于改善桔纹立体效果；
通过触变剂并与水性流变助剂共同使用，使漆膜单位面积内的桔纹助剂互相之间形成有效的相互牵制作用，改善桔纹立体效果，同时通过水性流变助剂可提高漆液的中低剪切粘度，进一步地改善桔纹的纹理效果。
添加水性丙烯酸乳液，加工前可使得涂料变为非牛顿流体，便于加工，还可加强漆料的耐水性和耐候性，耐碱性和抗污性，对砖石、木材和钢材表面有良好的粘附力，不易脱落；
添加水性聚氨酯分散体，可以加强漆料的粘附性；
添加水性聚氯乙烯乳液，可以加强对漆料喷涂后的粘结；
添加硫酸钡，使得漆料的粒径分布范围狭窄、分散性好、化学惰性强，稳定性好，耐酸碱，硬度适中，能吸收有害射线；
添加叔十二烷基硫醇，使得漆料耐磨、耐高冲击、还具有杀菌、防锈功能；
添加多酚类化合物，使得漆料更加健康环保，对慢性病起到预防作用。
本发明提供的水性桔纹漆纹理清晰度高、立体感强，并具有耐化学腐蚀性好、硬度高、柔韧性好、储存稳定性好、粘附性、使用适用期长和环保性能好等特点。
本发明的另一目的：为了克服现有技术的缺陷，本发明还提供了一种水性桔纹漆的制备喷涂工艺，喷涂方法简单，桔纹漆使用牢固。
所述的水性桔纹漆的制备喷涂工艺，具体包括以下步骤：
S1，配置A组分，准确称取配方量的水性羟基丙烯酸分散体、水性丙烯酸乳液、水性聚氨酯分散体、水性聚氯乙烯乳液、钛白、滑石粉、消泡剂、成膜助剂、水性流变助剂和硫酸钡，搅拌均匀，润湿过夜，用三辊机研磨至细度≤25μm,加入触变剂和催干剂，混合后得到A组分，将A组分装于A罐中储存；
S2，配置B组分，准确称取配方量的水性异氰酸酯固化剂、叔十二烷基硫醇和多酚类化合物，混合后得到B组分，将B组分装于B罐中储存；
S3,配漆，将B组分与A组分按5～8:1比例进行配漆，并用专用稀释剂稀释得到体积浓度为35～45％的水性桔纹漆；
S4,喷涂，在喷枪设定温度为30-47℃下，向喷口缓慢推出漆料，并在喷口处对漆料加压后喷涂于墙面。
相对于现有技术，本发明提供的水性桔纹漆的制备喷涂工艺，操作简单、方便，且安全环保，喷涂前对涂料先进行加热，温度为30-47℃下，漆料稠状合适，便于喷涂，通过喷枪加压喷涂出漆料，使其快速加压打散于墙面，使得漆料粘结更为牢固，且桔纹漆纹理清晰度高、立体感强、耐化学腐蚀性好、硬度高、柔韧性好。
具体实施方式
本发明的一种水性桔纹漆的制备喷涂工艺，喷涂方法简单，桔纹漆使用牢固。
所述的水性桔纹漆的制备喷涂工艺，具体包括以下步骤：
S1，配置A组分，准确称取配方量的水性羟基丙烯酸分散体、水性丙烯酸乳液、水性聚氨酯分散体、水性聚氯乙烯乳液、钛白、滑石粉、消泡剂、成膜助剂、水性流变助剂和硫酸钡，搅拌均匀，润湿过夜，用三辊机研磨至细度≤25μm,加入触变剂和催干剂，混合后得到A组分，将A组分装于A罐中储存；
S2，配置B组分，准确称取配方量的水性异氰酸酯固化剂、叔十二烷基硫醇和多酚类化合物，混合后得到B组分，将B组分装于B罐中储存；
S3,配漆，将B组分与A组分按5～8:1比例进行配漆，并用专用稀释剂稀释得到体积浓度为35～45％的水性桔纹漆；
S4,喷涂，在喷枪设定温度为30-47℃下，向喷口缓慢推出漆料，并在喷口处对漆料加压后喷涂于墙面。
实施例1：
本实施例中，一种水性桔纹漆包括A及B组分，其中：
A组分包括如下质量份数的组分：水性羟基丙烯酸分散体15份、水性丙烯酸乳液30份、水性聚氨酯分散体80份、水性聚氯乙烯乳液3份、钛白4～7份、滑石粉1～3份、消泡剂0.04～0.8份、成膜助剂7～10份、水性流变助剂0.01～0.06份、触变剂15～20份、催干剂2～5份，硫酸钡5份；
B组分包括如下质量份数的组分：水性异氰酸酯固化剂15份、叔十二烷基硫醇40份，多酚类化合物0.01份。
实施例2：
本实施例中，一种水性桔纹漆包括A及B组分，其中：
A组分包括如下质量份数的组分：水性羟基丙烯酸分散体15份、水性丙烯酸乳液42份、水性聚氨酯分散体60份、水性聚氯乙烯乳液3份、钛白4～7份、滑石粉1～3份、消泡剂0.04～0.8份、成膜助剂7～10份、水性流变助剂0.01～0.06份、触变剂15～20份、催干剂2～5份，硫酸钡5～8份；
B组分包括如下质量份数的组分：水性异氰酸酯固化剂22份、叔十二烷基硫醇40份，多酚类化合物0.08份。
实施例3：
本实施例中，一种水性桔纹漆包括A及B组分，其中：
A组分包括如下质量份数的组分：水性羟基丙烯酸分散体15份、水性丙烯酸乳液38份、水性聚氨酯分散体70份、水性聚氯乙烯乳液4份、钛白4～7份、滑石粉1～3份、消泡剂0.04～0.8份、成膜助剂7～10份、水性流变助剂0.01～0.06份、触变剂15～20份、催干剂2～5份，硫酸钡7份；
B组分包括如下质量份数的组分：水性异氰酸酯固化剂20份、叔十二烷基硫醇35份，多酚类化合物0.05份。
实施例4：
本实施例中，一种水性桔纹漆包括A及B组分，其中：
A组分包括如下质量份数的组分：水性羟基丙烯酸分散体15份、水性丙烯酸乳液30份、水性聚氨酯分散体70份、水性聚氯乙烯乳液3份、钛白4～7份、滑石粉1～3份、消泡剂0.04～0.8份、成膜助剂7～10份、水性流变助剂0.01～0.06份、触变剂15～20份、催干剂2～5份，硫酸钡5份；
B组分包括如下质量份数的组分：水性异氰酸酯固化剂20份、叔十二烷基硫醇30份，多酚类化合物0.05份。
实施例5：
本实施例中，一种水性桔纹漆包括A及B组分，其中：
A组分包括如下质量份数的组分：水性羟基丙烯酸分散体15份、水性丙烯酸乳液42份、水性聚氨酯分散体80份、水性聚氯乙烯乳液5份、钛白4～7份、滑石粉1～3份、消泡剂0.04～0.8份、成膜助剂7～10份、水性流变助剂0.01～0.06份、触变剂20份、催干剂2～5份，硫酸钡5～8份；
B组分包括如下质量份数的组分：水性异氰酸酯固化剂22份、叔十二烷基硫醇40份，多酚类化合物0.08份。
上述实施例1-5的水性桔纹漆中，水性聚氨酯分散体，具有以下重量份的组分：
聚酯多元醇20～35份、聚醚多元醇20～35份、惰性乙烯基单体4～18份、交联剂0.15～0.3份和催化剂1～1.5份，其中聚酯多元醇与聚醚多元醇质量比为1:1。
水性丙烯酸乳液，具有以下重量份的组分：
纯丙烯酸乳液15-30份、苯乙烯-丙烯酸乳液0.5-3份。
所述A组分与B组分的-OH/-NCO为1：1.3，—NHCOO/-NCO为1：2，上述组分水解后-OH/Si-OH为1：2.1，多酚类化合物0.01～0.08份。
测试上述实施例漆料与普通水性漆料的性能，
表1为水性漆料的喷涂测试结果。
由表1的测试结果可知，本发明提供的水性桔纹漆，漆膜不仅具有良好的硬度、耐化学性，还具有良好的厚涂性，桔纹立体效果好，贮存稳定性高，且以实施例5的使用效果最佳。
同时由本工艺喷涂的效果最佳，在同一组实施例5下，本工艺喷涂后的贮存稳定性为20天合格，而普通工艺喷涂则为15天合格，相应的其余性能也稍有下降。
Claims (7)
1.一种水性桔纹漆，其特征在于，包括A及B组分，其中：
A组分包括如下质量份数的组分：水性羟基丙烯酸分散体15～18份、水性丙烯酸乳液30～42份、水性聚氨酯分散体60～80份、水性聚氯乙烯乳液3-5份、钛白4～7份、滑石粉1～3份、消泡剂0.04～0.8份、成膜助剂7～10份、水性流变助剂0.01～0.06份、触变剂15～20份、催干剂2～5份；
B组分包括如下质量份数的组分：水性异氰酸酯固化剂15～22份、叔十二烷基硫醇30～40份；
所述A组分与B组分的-OH/-NCO为1：1.3，—NHCOO/-NCO为1：2，上述组分水解后-OH/Si-OH为1：2.1。
2.根据权利要求1所述的水性桔纹漆，其特征在于，所述A组分还包括：硫酸钡5～8份。
3.根据权利要求1所述的水性桔纹漆，其特征在于，所述B组分还包括：多酚类化合物0.01～0.08份。
4.根据权利要求1所述的水性桔纹漆，其特征在于，水性聚氨酯分散体，具有以下重量份的组分：
聚酯多元醇20～35份、聚醚多元醇20～35份、惰性乙烯基单体4～18份、交联剂0.15～0.3份和催化剂1～1.5份，其中聚酯多元醇与聚醚多元醇质量比为1:1。
5.根据权利要求1所述的水性桔纹漆，其特征在于，水性丙烯酸乳液，具有以下重量份的组分：
纯丙烯酸乳液15-30份、苯乙烯-丙烯酸乳液0.5-3份。
6.根据权利要求1所述的水性桔纹漆，其特征在于，水性桔纹漆的体积浓度为35～45％。
7.根据权利要求1-6中任意一项所述的水性桔纹漆的制备喷涂工艺，其特征在于，具体包括以下步骤：
S1，配置A组分，准确称取配方量的水性羟基丙烯酸分散体、水性丙烯酸乳液、水性聚氨酯分散体、水性聚氯乙烯乳液、钛白、滑石粉、消泡剂、成膜助剂、水性流变助剂和硫酸钡，搅拌均匀，润湿过夜，用三辊机研磨至细度≤25μm,加入触变剂和催干剂，混合后得到A组分，将A组分装于A罐中储存；
S2，配置B组分，准确称取配方量的水性异氰酸酯固化剂、叔十二烷基硫醇和多酚类化合物，混合后得到B组分，将B组分装于B罐中储存；
S3,配漆，将B组分与A组分按5～8:1比例进行配漆，并用专用稀释剂稀释得到体积浓度为35～45％的水性桔纹漆；
S4,喷涂，在喷枪设定温度为30-47℃下，向喷口缓慢推出漆料，并在喷口处对漆料加压后喷涂于墙面。