CN114799425B - 一种殷瓦钢中厚板焊接工艺 - Google Patents

一种殷瓦钢中厚板焊接工艺 Download PDF

Info

Publication number
CN114799425B
CN114799425B CN202210757147.XA CN202210757147A CN114799425B CN 114799425 B CN114799425 B CN 114799425B CN 202210757147 A CN202210757147 A CN 202210757147A CN 114799425 B CN114799425 B CN 114799425B
Authority
CN
China
Prior art keywords
welding
invar steel
equal
temperature
welding process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202210757147.XA
Other languages
English (en)
Other versions
CN114799425A (zh
Inventor
杨晓峰
任国柱
孙德文
李多
鲍禄强
赵宽
马东平
文燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
High Speed Aerodynamics Research Institute of China Aerodynamics Research and Development Center
Original Assignee
High Speed Aerodynamics Research Institute of China Aerodynamics Research and Development Center
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by High Speed Aerodynamics Research Institute of China Aerodynamics Research and Development Center filed Critical High Speed Aerodynamics Research Institute of China Aerodynamics Research and Development Center
Priority to CN202210757147.XA priority Critical patent/CN114799425B/zh
Publication of CN114799425A publication Critical patent/CN114799425A/zh
Application granted granted Critical
Publication of CN114799425B publication Critical patent/CN114799425B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于风洞设备技术领域，公开了一种殷瓦钢中厚板焊接工艺。本发明的殷瓦钢中厚板焊接工艺应用于板厚为16mm~40mm殷瓦钢中厚板焊接，具体步骤为：焊前清洗、钨极惰性气体保护焊、打底焊、填充焊、盖面焊；施焊过程中，最小预热温度≥5℃，最大道间温度≤100℃。本发明的殷瓦钢中厚板焊接工艺，通过严格控制各阶段工艺参数，焊缝常温和低温力学性能得到显著提高。

Description

一种殷瓦钢中厚板焊接工艺
技术领域
本发明属于风洞设备技术领域，具体涉及一种殷瓦钢中厚板焊接工艺。
背景技术
殷瓦钢是含有32%-37%镍的铁基高镍合金，从常温到超低温的膨胀系数很低。殷瓦钢主要用于LNG超低温环境，使用厚度仅为0.7mm。低温风洞排架使用厚度为16mm~40mm殷瓦钢，属于中厚板，殷瓦钢中厚板焊接工艺尚无可借鉴的经验，亟待发展一种在低温风洞排架焊接使用的殷瓦钢中厚板焊接工艺。
发明内容
本发明所要解决的技术问题是提供一种殷瓦钢中厚板焊接工艺。
本发明的殷瓦钢中厚板焊接工艺，包括以下步骤：
S10.焊前清洗，焊前用99.7%的无水酒精擦拭，去除殷瓦钢表面的油污、锈水、杂质，并进行殷瓦钢层间清渣；
S20.钨极惰性气体保护焊，钨极类型及直径WCe-20/Φ2.4mm，坡口形式X、V型，焊材型号Ni36LNG，填充金属尺寸Φ1.6mm；
S30.打底焊，极性DCEN，焊接电流130A~160A，电弧电压12V～16V，焊接速度8cm/min～12cm/min，线能量≤19.2kJ/cm；
S40.填充焊，极性DCEN，焊接电流160A~190A，电弧电压12V～16V，焊接速度8cm/min～12cm/min，线能量≤22.8kJ/cm；
S50.盖面焊，极性DCEN，焊接电流130A~160A，电弧电压12V～16V，焊接速度8cm/min～12cm/min，线能量≤19.2kJ/cm；
S60.背面清根，采用打磨方式，并用不锈钢丝刷见金属光泽；
施焊过程中，最小预热温度≥5℃，最大道间温度≤100℃。
进一步地，所述的殷瓦钢是厚度为16mm～40mm的4J36D殷瓦钢。
本发明的殷瓦钢中厚板焊接工艺，通过严格控制各阶段工艺参数，焊缝常温和低温力学性能得到显著提高，解决了厚度16mm~40mm殷瓦钢焊接问题。
附图说明
图1为本发明的殷瓦钢中厚板焊接工艺获得的V形焊接坡口示意图。
图中，16~40为16mm~40mm、3~4为3mm~4mm、0~1为0~1mm，单位均为mm。
表1为本发明的殷瓦钢中厚板焊接工艺获得的V形焊接坡口的焊后常温和低温拉伸强度；
表2为本发明的殷瓦钢中厚板焊接工艺获得的V形焊接坡口的焊后低温冲击功。
具体实施方式
下面结合附图和实施例详细说明本发明。
实施例1
本实施例的殷瓦钢厚度为16mm～40mm，材质为4J36D殷瓦钢。
本实施例的殷瓦钢中厚板焊接工艺，包括以下步骤：
S10.焊前清洗，焊前用99.7%的无水酒精擦拭，去除殷瓦钢表面的油污、锈水、杂质，并进行殷瓦钢层间清渣；
S20.钨极惰性气体保护焊，钨极类型及直径WCe-20/Φ2.4mm，坡口形式X、V型，焊材型号Ni36LNG，填充金属尺寸Φ1.6mm；
S30.打底焊，极性DCEN，焊接电流130A~160A，电弧电压12V～16V，焊接速度8cm/min～12cm/min，线能量≤19.2kJ/cm；
S40.填充焊，极性DCEN，焊接电流160A~190A，电弧电压12V～16V，焊接速度8cm/min～12cm/min，线能量≤22.8kJ/cm；
S50.盖面焊，极性DCEN，焊接电流130A~160A，电弧电压12V～16V，焊接速度8cm/min～12cm/min，线能量≤19.2kJ/cm；
S60.背面清根，采用打磨方式，并用不锈钢丝刷见金属光泽；
施焊过程中，最小预热温度≥5℃，最大道间温度≤100℃。
获得的V形焊接坡口见图1，焊后进行焊缝常温和77K低温拉伸强度、77K低温冲击功试验。试验结果分别见表1、表2，从表1、表2可知，殷瓦钢焊后的综合力学性能得到显著提高。
Figure DEST_PATH_IMAGE002
Figure DEST_PATH_IMAGE003
尽管本发明的实施方案已公开如上，但其并不仅限于说明书和实施方式中所列运用，它完全可以被适用于各种适合本发明的领域。对于熟悉本领域的人员而言，在不脱离本发明原理的前提下，可容易地实现另外的改进和润饰，本发明并不限于特定的细节和这里示出与描述的图例。

Claims (1)

1.一种殷瓦钢中厚板焊接工艺，其特征在于，殷瓦钢是厚度为16mm～40mm的4J36D殷瓦钢，包括以下步骤：
S10.焊前清洗，焊前用99.7%的无水酒精擦拭，去除殷瓦钢表面的油污、锈水、杂质，并进行殷瓦钢层间清渣；
S20.钨极惰性气体保护焊，钨极类型及直径WCe-20/Φ2.4mm，坡口形式X、V型，焊材型号Ni36LNG，填充金属尺寸Φ1.6mm；
S30.打底焊，极性DCEN，焊接电流130A~160A，电弧电压12V～16V，焊接速度8cm/min～12cm/min，线能量≤19.2kJ/cm；
S40.填充焊，极性DCEN，焊接电流160A~190A，电弧电压12V～16V，焊接速度8cm/min～12cm/min，线能量≤22.8kJ/cm；
S50.盖面焊，极性DCEN，焊接电流130A~160A，电弧电压12V～16V，焊接速度8cm/min～12cm/min，线能量≤19.2kJ/cm；
S60.背面清根，采用打磨方式，并用不锈钢丝刷见金属光泽；
施焊过程中，最小预热温度≥5℃，最大道间温度≤100℃；
焊缝在常温和77K低温拉伸强度、77K低温冲击功试验的结果是：常温拉伸强度达到491-492Mpa，77K低温拉伸强度最高800Mpa，77K低温冲击功最大63Akv（J）。
CN202210757147.XA 2022-06-30 2022-06-30 一种殷瓦钢中厚板焊接工艺 Active CN114799425B (zh)