CN114793922B - 一种含工业大麻纤维的猫砂 - Google Patents
一种含工业大麻纤维的猫砂 Download PDFInfo
- Publication number
- CN114793922B CN114793922B CN202210637391.2A CN202210637391A CN114793922B CN 114793922 B CN114793922 B CN 114793922B CN 202210637391 A CN202210637391 A CN 202210637391A CN 114793922 B CN114793922 B CN 114793922B
- Authority
- CN
- China
- Prior art keywords
- industrial hemp
- parts
- cat litter
- slurry
- industrial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种含工业大麻纤维的猫砂，涉及猫砂技术领域，由以下成分制成：改性工业大麻纤维、瓜尔胶、碳酸钙、硅藻土、椰壳活性炭、淀粉、纳米二氧化钛、海藻酸钠、薄荷汁液；本发明制备的猫砂不仅具有优异的吸附性能，能够更快的吸附刺激气味和水分，同时，具有优异的抑菌功能，能够避免细菌的滋生，从而延长了猫砂的使用时间，同时，由于避免细菌的滋生，对于猫的健康具有良好的保护作用。
Description
技术领域
本发明属于猫砂技术领域，具体涉及一种含工业大麻纤维的猫砂。
背景技术
猫砂是饲主为其饲养的猫用来掩埋粪便和尿液的物体，有较好的吸水性，一般会与猫砂盆一并使用，将适量的猫砂倒于猫砂盆内，受过训练的猫当需要排泄时便会走进猫砂盆内将猫屎排泄于其上面。
目前市面上的猫砂种类有很多，如水晶猫砂、膨润土猫砂、木屑猫砂、豆腐猫砂等，但普遍都对环保有着一定的影响。
现有技术CN 104351064 B，公开了一种碳纤维活性猫砂及其制备方法，“本发明公开了一种碳纤维活性猫砂及其制备方法，由以下重量份的原料制成：小麦秸秆30～45、甘蔗渣15～20、氯化钙10～14、氢氧化钠2～3、粉煤灰 15～25、纳米铁粉1～2、红土30～40、瓜尔豆胶2～4、粘结剂4～5和适量的水；具体是一种高活性炭纤维吸附猫砂，不同于以往炭化秸秆的秸秆类制成的活性炭吸附剂，它是由氢氧化钠加水煎煮浸泡过的甘蔗渣等富含高纤维的材质，之后去除多余的叶肉部分，留下纤维，纤维由碳结构更加稳定的形式存在，其团块更结实，尺寸也比较符合要求，使得成品猫砂的吸附能力更强，在快速吸水的同时能够吸附粪便异味，达到净化空气的目的。”然而其抑菌效果较差，长时间使用后，容易滋生细菌。
因此，需要对现有技术进行进一步的改善。
发明内容
本发明的目的是针对现有的问题，提供了一种含工业大麻纤维的猫砂。
本发明是通过以下技术方案实现的：
本发明采用的技术方案如下：
一种含工业大麻纤维的猫砂，按重量份计由以下成分制成：改性工业大麻纤维13-15份、瓜尔胶7-9份、碳酸钙5-10份、硅藻土22-25份、椰壳活性炭 4-6份、淀粉5-6份、纳米二氧化钛2.3-2.9份、海藻酸钠1-2份、薄荷汁液3-6 份。
作为进一步的技术方案：所述改性工业大麻纤维制备方法包括以下步骤：
(1)将工业大麻叶与水混合到一起，然后进行混合打浆，得到工业大麻浆液；
(2)向上述的工业大麻浆液中添加氢氧化钠，调节工业大麻浆液pH至 10.5，然后加热至80-90℃，保温搅拌2小时，得到工业大麻碱浆液；
(3)对得到的工业大麻碱浆液进行过滤，水洗至中性，然后进行粉碎，得到工业大麻纤维；
(4)将上述得到的工业大麻纤维添加到去离子水中，然后再依次添加马来酸酐、N-甲基-2-(2-羟乙基)吡咯烷、过硫酸铵，在惰性气氛保护下，调节温度至75℃，保温搅拌反应40min，然后进行过滤，得到反应物料；
(5)对上述得到的反应物料进行清洗至中性，再经过干燥，得到改性工业大麻纤维。
作为进一步的技术方案：所述工业大麻叶与水混合质量比为1:15；
所述打浆转速为3500r/min。
作为进一步的技术方案：所述工业大麻纤维、去离子水混合质量比为 1:10；
所述工业大麻纤维、马来酸酐、N-甲基-2-(2-羟乙基)吡咯烷、过硫酸铵混合质量比为10:2:1:0.3。
作为进一步的技术方案：所述惰性气氛为氖气气氛。
作为进一步的技术方案：所述薄荷汁液制备方法为：
将薄荷叶与水按1:1质量比例混合打浆后，得到薄荷浆液，然后进行过滤，去除残渣，得到滤液；
对滤液进行浓缩至原体积的五分之一，即可。
作为进一步的技术方案：所述椰壳活性炭为将椰壳进行碳化然后再经过粉碎所得到。
作为进一步的技术方案：所述淀粉为玉米淀粉；
所述玉米淀粉经过糊化处理：
将玉米淀粉与水按1:5质量比例混合后，加热至90℃，保温搅拌30min，然后再进行冷却，干燥，粉碎，即可。
作为进一步的技术方案：所述硅藻土平均粒度为300目。
本发明猫砂是以多种原料进行复合制备得到，现有的秸秆纤维中木质素与纤维素和半纤维素紧密结合，镶嵌形成酯键，质地坚硬，吸水性较差，因此，本发明通过引入经过改性处理的工业大麻纤维，从而使得制备的猫砂吸附能力大大增强，经过对工业大麻纤维的改性处理，使工业大麻纤维疏松，纤维比表面积增大，从而增强了其吸附性能，尤其是对气味和水分的吸收能力大幅度增强。
本发明制备的猫砂不同于以往秸秆类制成猫砂，对于气味和水分的吸附能力大幅度增加，通过采用改性工业大麻纤维，使得纤维结构更加稳定，能够结合其他组分共同作用，使得制备的猫砂吸附能力更强，在快速吸水的同时能够吸附粪便异味，达到净化空气的目的。
采用瓜尔豆胶和玉米淀粉作为粘接剂，能够将各组分牢固的结合到一起，避免使用化学粘结剂，本申请中采用的瓜尔胶和玉米淀粉成分安全无害，保障猫咪和主人的健康和安全。
通过引入一定量的薄荷汁，薄荷的香味具有浓浓的覆盖作用，能够将少量的未被吸附的刺激性气味遮盖住，从而给猫儿一个舒适的地方。
本发明相比现有技术具有以下优点：
本发明制备的猫砂不仅具有优异的吸附性能，能够更快的吸附刺激气味和水分，同时，具有优异的抑菌功能，能够避免细菌的滋生，从而延长了猫砂的使用时间，同时，由于避免细菌的滋生，对于猫的健康具有良好的保护作用。
本发明制备的猫砂脚感舒适，不易带出，受猫儿的喜爱。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种含工业大麻纤维的猫砂，按重量份计由以下成分制成：改性工业大麻纤维13份、瓜尔胶7份、碳酸钙5份、硅藻土22份、椰壳活性炭4份、淀粉 5份、纳米二氧化钛2.3份、海藻酸钠1份、薄荷汁液3份。
所述改性工业大麻纤维制备方法包括以下步骤：
(1)将工业大麻叶与水混合到一起，然后进行混合打浆，得到工业大麻浆液；
(2)向上述的工业大麻浆液中添加氢氧化钠，调节工业大麻浆液pH至 10.5，然后加热至80℃，保温搅拌2小时，得到工业大麻碱浆液；
(3)对得到的工业大麻碱浆液进行过滤，水洗至中性，然后进行粉碎，得到工业大麻纤维；
(4)将上述得到的工业大麻纤维添加到去离子水中，然后再依次添加马来酸酐、N-甲基-2-(2-羟乙基)吡咯烷、过硫酸铵，在惰性气氛保护下，调节温度至75℃，保温搅拌反应40min，然后进行过滤，得到反应物料；
(5)对上述得到的反应物料进行清洗至中性，再经过干燥，得到改性工业大麻纤维。
所述工业大麻叶与水混合质量比为1:15；
所述打浆转速为3500r/min。
所述工业大麻纤维、去离子水混合质量比为1:10；
所述工业大麻纤维、马来酸酐、N-甲基-2-(2-羟乙基)吡咯烷、过硫酸铵混合质量比为10:2:1:0.3。
所述惰性气氛为氖气气氛。
所述薄荷汁液制备方法为：
将薄荷叶与水按1:1质量比例混合打浆后，得到薄荷浆液，然后进行过滤，去除残渣，得到滤液；
对滤液进行浓缩至原体积的五分之一，即可。
所述椰壳活性炭为将椰壳进行碳化然后再经过粉碎所得到。
所述淀粉为玉米淀粉；
所述玉米淀粉经过糊化处理：
将玉米淀粉与水按1:5质量比例混合后，加热至90℃，保温搅拌30min，然后再进行冷却，干燥，粉碎，即可。
所述硅藻土平均粒度为300目。
实施例2
一种含工业大麻纤维的猫砂，按重量份计由以下成分制成：改性工业大麻纤维15份、瓜尔胶9份、碳酸钙10份、硅藻土25份、椰壳活性炭6份、淀粉6份、纳米二氧化钛2.9份、海藻酸钠2份、薄荷汁液6份。
所述改性工业大麻纤维制备方法包括以下步骤：
(1)将工业大麻叶与水混合到一起，然后进行混合打浆，得到工业大麻浆液；
(2)向上述的工业大麻浆液中添加氢氧化钠，调节工业大麻浆液pH至 10.5，然后加热至90℃，保温搅拌2小时，得到工业大麻碱浆液；
(3)对得到的工业大麻碱浆液进行过滤，水洗至中性，然后进行粉碎，得到工业大麻纤维；
(4)将上述得到的工业大麻纤维添加到去离子水中，然后再依次添加马来酸酐、N-甲基-2-(2-羟乙基)吡咯烷、过硫酸铵，在惰性气氛保护下，调节温度至75℃，保温搅拌反应40min，然后进行过滤，得到反应物料；
(5)对上述得到的反应物料进行清洗至中性，再经过干燥，得到改性工业大麻纤维。
所述工业大麻叶与水混合质量比为1:15；
所述打浆转速为3500r/min。
所述工业大麻纤维、去离子水混合质量比为1:10；
所述工业大麻纤维、马来酸酐、N-甲基-2-(2-羟乙基)吡咯烷、过硫酸铵混合质量比为10:2:1:0.3。
所述惰性气氛为氖气气氛。
所述薄荷汁液制备方法为：
将薄荷叶与水按1:1质量比例混合打浆后，得到薄荷浆液，然后进行过滤，去除残渣，得到滤液；
对滤液进行浓缩至原体积的五分之一，即可。
所述椰壳活性炭为将椰壳进行碳化然后再经过粉碎所得到。
所述淀粉为玉米淀粉；
所述玉米淀粉经过糊化处理：
将玉米淀粉与水按1:5质量比例混合后，加热至90℃，保温搅拌30min，然后再进行冷却，干燥，粉碎，即可。
所述硅藻土平均粒度为300目。
实施例3
一种含工业大麻纤维的猫砂，按重量份计由以下成分制成：改性工业大麻纤维14份、瓜尔胶8份、碳酸钙6份、硅藻土23份、椰壳活性炭5份、淀粉 5.2份、纳米二氧化钛2.6份、海藻酸钠1.5份、薄荷汁液5份。
所述改性工业大麻纤维制备方法包括以下步骤：
(1)将工业大麻叶与水混合到一起，然后进行混合打浆，得到工业大麻浆液；
(2)向上述的工业大麻浆液中添加氢氧化钠，调节工业大麻浆液pH至 10.5，然后加热至85℃，保温搅拌2小时，得到工业大麻碱浆液；
(3)对得到的工业大麻碱浆液进行过滤，水洗至中性，然后进行粉碎，得到工业大麻纤维；
(4)将上述得到的工业大麻纤维添加到去离子水中，然后再依次添加马来酸酐、N-甲基-2-(2-羟乙基)吡咯烷、过硫酸铵，在惰性气氛保护下，调节温度至75℃，保温搅拌反应40min，然后进行过滤，得到反应物料；
(5)对上述得到的反应物料进行清洗至中性，再经过干燥，得到改性工业大麻纤维。
所述工业大麻叶与水混合质量比为1:15；
所述打浆转速为3500r/min。
所述工业大麻纤维、去离子水混合质量比为1:10；
所述工业大麻纤维、马来酸酐、N-甲基-2-(2-羟乙基)吡咯烷、过硫酸铵混合质量比为10:2:1:0.3。
所述惰性气氛为氖气气氛。
所述薄荷汁液制备方法为：
将薄荷叶与水按1:1质量比例混合打浆后，得到薄荷浆液，然后进行过滤，去除残渣，得到滤液；
对滤液进行浓缩至原体积的五分之一，即可。
所述椰壳活性炭为将椰壳进行碳化然后再经过粉碎所得到。
所述淀粉为玉米淀粉；
所述玉米淀粉经过糊化处理：
将玉米淀粉与水按1:5质量比例混合后，加热至90℃，保温搅拌30min，然后再进行冷却，干燥，粉碎，即可。
所述硅藻土平均粒度为300目。
试验
对实施例与对比例猫砂吸水时间对比，试验蒸馏水50mL：
表1
| 吸水时间/s | |
| 实施例1 | 12 |
| 实施例2 | 10 |
| 实施例3 | 10 |
| 对比例1 | 25 |
| 对比例2 | 16 |
对比例1：与实施例1区别为将工业大麻纤维替换为玉米秸秆纤维；
对比例2：与实施例1区别为不对工业大麻纤维进行改性处理；
由表1可以看出，本发明制备的猫砂具有优异的吸水能力，吸水速度快。
除臭性：取250g猫砂普铺设在盒子内，均滴加30ml氨水，2min后，距离猫砂35cm，对猫砂异味进行评估，对比；
表2
| 除臭性 | |
| 实施例1 | 无明显刺激性气味 |
| 实施例2 | 无明显刺激性气味 |
| 实施例3 | 无明显刺激性气味 |
| 对比例1 | 有刺激性气味 |
| 对比例2 | 轻微刺激性气味 |
对比例1：与实施例1区别为将工业大麻纤维替换为玉米秸秆纤维；
对比例2：与实施例1区别为不对工业大麻纤维进行改性处理；
由表2可以看出，本发明制备的猫砂具有优异的除臭性能，能够锁定刺激性气味。
对实施例与对比例猫砂进行抑菌性能检测，试验对象为大肠杆菌；
表3
| 抑菌性能％ | |
| 实施例1 | 93.5 |
| 实施例2 | 92.8 |
| 实施例3 | 93.1 |
由表3可以看出，本发明制备的猫砂具有优异的抑菌性能。
以上所述仅为本发明的较佳实施例，但本发明不以所示限定实施范围，凡是依照本发明的构想所作的改变，或修改为等同变化的等效实施例，仍未超出说明书所涵盖的精神时，均应在本发明的保护范围内。
Claims (5)
1.一种含工业大麻纤维的猫砂，其特征在于：按重量份计由以下成分制成：改性工业大麻纤维13-15份、瓜尔胶7-9份、碳酸钙5-10份、硅藻土22-25份、椰壳活性炭4-6份、淀粉5-6份、纳米二氧化钛2.3-2.9份、海藻酸钠1-2份、薄荷汁液3-6份；
所述改性工业大麻纤维制备方法包括以下步骤：
(1)将工业大麻叶与水混合到一起，然后进行混合打浆，得到工业大麻浆液；
(2)向上述的工业大麻浆液中添加氢氧化钠，调节工业大麻浆液pH至10.5，然后加热至80-90℃，保温搅拌2小时，得到工业大麻碱浆液；
(3)对得到的工业大麻碱浆液进行过滤，水洗至中性，然后进行粉碎，得到工业大麻纤维；
(4)将上述得到的工业大麻纤维添加到去离子水中，然后再依次添加马来酸酐、N-甲基-2-(2-羟乙基)吡咯烷、过硫酸铵，在惰性气氛保护下，调节温度至75℃，保温搅拌反应40min，然后进行过滤，得到反应物料；
(5)对上述得到的反应物料进行清洗至中性，再经过干燥，得到改性工业大麻纤维；
所述工业大麻叶与水混合质量比为1:15；
所述打浆转速为3500r/min；
所述工业大麻纤维、去离子水混合质量比为1:10；
所述工业大麻纤维、马来酸酐、N-甲基-2-(2-羟乙基)吡咯烷、过硫酸铵混合质量比为10:2:1:0.3；
所述惰性气氛为氖气气氛。
2.根据权利要求1所述的一种含工业大麻纤维的猫砂，其特征在于：所述薄荷汁液制备方法为：
将薄荷叶与水按1:1质量比例混合打浆后，得到薄荷浆液，然后进行过滤，去除残渣，得到滤液；
对滤液进行浓缩至原体积的五分之一，即可。
3.根据权利要求1所述的一种含工业大麻纤维的猫砂，其特征在于：所述椰壳活性炭为将椰壳进行碳化然后再经过粉碎所得到。
4.根据权利要求1所述的一种含工业大麻纤维的猫砂，其特征在于：所述淀粉为玉米淀粉；
所述玉米淀粉经过糊化处理：
将玉米淀粉与水按1:5质量比例混合后，加热至90℃，保温搅拌30min，然后再进行冷却，干燥，粉碎，即可。
5.根据权利要求1所述的一种含工业大麻纤维的猫砂，其特征在于：所述硅藻土平均粒度为300目。