CN114464697A - 一种光伏软瓷饰面砖的制备方法 - Google Patents
一种光伏软瓷饰面砖的制备方法 Download PDFInfo
- Publication number
- CN114464697A CN114464697A CN202210144819.XA CN202210144819A CN114464697A CN 114464697 A CN114464697 A CN 114464697A CN 202210144819 A CN202210144819 A CN 202210144819A CN 114464697 A CN114464697 A CN 114464697A
- Authority
- CN
- China
- Prior art keywords
- soft porcelain
- photovoltaic
- layer
- base layer
- soft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本公开提供了一种光伏软瓷饰面砖及其制备方法，包括了步骤1：软瓷基层的制备步骤2：涂胶，在软瓷基层上进行涂胶，将粘连剂乙烯‑醋酸乙烯共聚物均匀涂覆在软瓷基层上；步骤3：安装光伏电池组件，将光伏电池组件贴服在软瓷基层上，并进行热压，热压完成后进行剪裁得到软瓷光伏饰面砖。本公开以软瓷作为基材用于光伏材料，制备得到了光伏建筑材料，扩宽了软瓷材料和光伏材料的应用；同时利用软瓷基材表面粗糙、材料自身富有柔性和可形变性能，能够与粘连剂充分结合，进而能够将光伏电池组层进行紧密固着；而无需对软瓷材料进行额外的加工处理，生产效率高，产品可靠性好。
Description
技术领域
本申请涉及一种建筑材料，具体的是一种绿色环保建筑材料，更具体的是一种光伏软瓷饰面砖的制备方法。
背景技术
现代建筑普遍追求绿色环保，包括对能源的充分利用是人们普遍追求的，目前我们看到许多建筑上再尝试使用太阳能电池板，为房屋进行供电，这种传统的能源利用都是基于目前的建筑上，重新安装太阳能电池板，并将太阳能转变为电能，但是这种传统方式存在安装成本高，并且会占据额外的面积，空间利用率低。
基于目前太阳能板的使用方式和成本问题，现有技术已有的提供了一些将光伏材料和建筑材料合二为一的材料，例如将光伏材料直接安装在瓦片上，该光伏瓦既能直接的利用太阳能，同时能够阻风挡雨，降低成本。
现有技术中，如授权公告号为CN214675054U的实用新型公开了一种平面屋顶光伏瓦片结构顶光伏瓦片结构，包括安装板，所述安装板的一侧固定连接有光伏电池，所述光伏电池的一侧设置有超白钢化玻璃，所述超白钢化玻璃的一侧设置有纳米涂层，所述安装板的一侧设置有连接块，所述连接块的一端设置有连接板，所述连接板的一侧设置有第一反光镜，所述连接板的另一侧设置有第二反光镜，所述安装板的一侧设置有第一凹型板，所述安装板的另一侧设置有第一凸型板，所述安装板的一端设置有第二凹型板，所述安装板的另一端设置有第二凸型板；该一种平面屋顶光伏瓦片结构通过设置有连接块、连接板、第一反光镜和第二反光镜，可以达到能够使光伏电池在阴雨天气下的产电效率提高。该方案所提到的光伏瓦其实质是光伏板，并没有能够与建筑材料结合，仅仅是将该材料作为建筑的瓦材。
公开号为CN113027042A的发明申请公开了一种本发明公开了一种光伏瓦制备方法，包括如下步骤：层叠：将基板、第一粘接层、第一抗冲击层、第二粘接层、电池层、第三粘接层、第二抗冲击层、第四粘接层、前膜依次铺设，准备层压；抽真空及去湿；层压；降温；切割；折边，得到光伏瓦，同时该方案还公开了将基板置于硝酸溶液中进行腐蚀处理，腐蚀后取出洗净；其中，所述硝酸溶液浓度为30-40％，温度为30-50℃，腐蚀时间30-60min。可以看出，其基板并非建筑材料，该光伏板仍然是一种太阳能板。
本发明针对于现有技术中光伏板仅仅是单独的作为太阳能的一种电组件，而并未与我们建筑材料相互结合，发挥我们建筑材料耐用、已成形的特点。
发明内容
本公开针对现有技术中光伏材料，尤其是建筑领域光伏材料的单一性问题，本公开提供了一种软瓷光伏饰面砖，该软瓷光伏饰面砖集合了建筑材料的易加工，安装方便的特点，同时具备光伏板的绿色能源利用功能。
本发明的构思之一在于提供一种软瓷光伏饰面砖，该饰面砖的基材为软瓷材料，软瓷材料的制备方法简单，并且存在一定幅度的柔软性，所指被的光伏饰面砖也存在一定的柔性，安装过程中更加方便。
本发明的另一构思还在于，提供了一种软瓷光伏饰面砖，使用软瓷材料替换了传统的玻璃材料，能够大幅度的降低成本。
本发明的另一构思还在于，提供了一种软瓷光伏饰面砖，该饰面砖与光伏电池组之间通过交联剂交联，并且经过压制，电池组与软瓷基材能够较好的接触。
本发明的另一构思还在于，提供了一种软瓷光伏饰面砖，利用软瓷材料的柔性，在高压的条件下软瓷饰面砖中高分子成分具有一定的形变，能够更好的贴合电池组以及交联组分，提高软瓷柔基材与电池组的结合，进而提高软瓷光伏饰面砖的使用寿命。
本发明的另一构思还在于，提供了一种软瓷光伏饰面砖，光伏饰面砖上具有电连接结构，而软瓷基材的加工型强，本发明软瓷光伏饰面砖的加工效率相较于传统光伏瓦的加工效率高。
具体的，本公开提供了一种光伏饰面砖，所述的光伏饰面砖包括软瓷基层和光伏电池组层和粘结层。
其中，所述的粘结层介于软瓷基层和光伏电池组层之间，用于固定软瓷基层和光伏电池组层。
进一步的，软瓷基层的原料包括硅丙乳液、水泥、石英砂、有机颜料、水。
其中按照重量份，硅丙乳液30-40份，水泥5-15份，石英砂15-20份，有机颜料1-3份，水5-10份。
相对于传统的软瓷饰面砖，本公开提高了硅丙乳液的含量比，将其含量比提高大于软瓷的总质量的50％。
在传统的光伏板制备过程中，为了提高光伏电池组件与基材的交联效果，往往需要对基材进行粗糙化处理，包括酸碱处理，增大基材表面的粗糙程度，提高光伏电池组件与基材的连接。本发明由于是建筑软瓷材料，表面粗糙程度自身较好，但是由于传统的软瓷材料，其硅丙乳液的含量相对较少，硅丙乳液起到粘连剂的作用，而石英砂起到骨料等作用，提高软瓷材料的强度。
本公开提高硅丙乳液的含量，目的之一在于提高软瓷材料的形变能力，基于目前软瓷材料表观的粗糙程度较好，但是在光伏瓦的制备过程中，光伏组件与软瓷基材之间还需要承压处理，用以提高软瓷材料、粘结层、光伏电池组层的连接性，而当软瓷基材具有一定的性变形时，在高压的作用下，粘结层能够快速的深入到软瓷的空隙中，并且基于形变能力，软瓷能够快速的与粘结层深入粘结，达到同时能够避免粘连层与软瓷基材之间产生气泡，提高材料使用寿命。
进一步的，所述的粘连剂为乙烯-醋酸乙烯共聚物。
所述的粘连剂原料中醋酸乙烯的含量为20-40％。
本公开选择的乙烯-醋酸乙烯共聚物中，醋酸乙烯的含量为20-40％，能够降低粘连剂结晶度，提高了韧性、抗冲击性、密封性能，能够配合软瓷材料的柔性，快速的将软瓷基层与光伏电池组粘连，并提高粘连效果。
进一步的，所述的光伏电池组层包括了抗冲击层、电池层和光伏电池底层。
所述的抗冲击层为透明光学玻璃。
抗冲击层，以损坏一方面，抗冲击层的高弹性能，使其能够吸收冲击能量，削减外物对光伏饰面砖力电池组件；另外，抗冲击层的耐冲击性能，使其能够承受较大的冲击力，光伏电池组破裂的几率。
进一步的，所述的抗冲击层和光伏电池底层对电池组进行封装，对光伏电池层进行保护。
在一些实施例中，所述的光伏电池组的光伏电池底层与软瓷基层通过连接基层连接。
在一些实施例中，本公开提供了一种光伏软瓷饰面砖的制备方法。
具体的，包括如下步骤：
1、软瓷基层的制备
将硅丙乳液和无机颜料进行搅拌，得到混合乳液；将得到的混合乳液加入到混合均匀的水泥和石英砂的粉料中，同时加入一定量的水，搅拌得到软瓷浆料；将软瓷浆料注入模具中进行固化成形，得到软瓷基层。
2、涂胶
在软瓷基层上进行涂胶，将粘连剂乙烯-醋酸乙烯共聚物均匀涂覆在软瓷基层上；
3、安装光伏电池组件
将光伏电池组件贴服在软瓷基层上，并进行热压，热压完成后进行剪裁得到软瓷光伏饰面砖。
进一步的，其中步骤3中的热压温度为70-90℃，优选的为80℃；
进一步的，其中步骤3中的热压时间为5-10min；
进一步的，其中步骤3中的热压压力为80-120Kg；
在另一实施例中，本公开提供了一种光伏软瓷饰面砖的制备方法。
包括如下步骤：
1、软瓷基层的制备
将硅丙乳液和无机颜料进行搅拌，得到混合乳液；将得到的混合乳液加入到混合均匀的水泥和石英砂的粉料中，同时加入一定量的水，搅拌得到软瓷浆料；将软瓷浆料注入模具中进行固化成形，得到软瓷基层。
其中硅丙乳液30-40份，水泥5-15份，石英砂15-20份，有机颜料1-3份，水5-10份。
2、涂胶
在软瓷基层上进行涂胶，将粘连剂乙烯-醋酸乙烯共聚物均匀涂覆在软瓷基层上；
其中，所述的粘连剂原料中醋酸乙烯的含量为20-40％。
3、安装光伏电池组件
将光伏电池组件贴服在软瓷基层上，并进行热压，热压完成后进行剪裁得到软瓷光伏饰面砖。
在另一实施例中，本公开提供了一种光伏软瓷饰面砖的制备方法，还包括步骤4，对步骤3得到的软瓷光伏饰面砖进行剪裁和安装电池连接组件。
与现有技术相比，本发明的有益效果在于：
1、以软瓷作为基材用于光伏材料，制备得到了光伏建筑材料，扩宽了软瓷材料和光伏材料的应用；
2、利用软瓷基材表面粗糙、材料自身富有柔性和可形变性能，能够与粘连剂充分结合，进而能够将光伏电池组层进行紧密固着；而无需对软瓷材料进行额外的加工处理；
3、软瓷基材的制备中，提高了软瓷材料中有机物硅丙乳液的含量，提高软瓷材料的柔性，有助于提高了软瓷组分与光伏电池组件的连接性能；
4、对热压参数进行调节，提高光伏电池组件与软瓷基层的连接，减小软瓷基层与光伏电池组件之间的气泡和空隙；
5、对粘连剂进行了特殊的调整，提高了粘连剂的流变性能，同时配合热压条件，提高连接效果。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本实施例中，具体提供了一种软瓷光伏饰面砖，该饰面砖包括软瓷基层、连接层和光伏电池组层。
本公开相对于现有的建筑材料而言，首次将光伏组件与软瓷材料进行结合，制备得到软瓷柔性光伏材料，软瓷光伏饰面砖具有加工简单，工艺环保等特点。
软瓷材料相对于传统光伏板基材而言，传统光伏板的基材一般TPT聚氟乙烯复合膜，该基板的制作成本较高，而本公开直接使用软瓷材料作为基层，其中软瓷材料首先具有表面粗糙的性能，能够高效的光伏电池组层进行连接，另外软瓷材料中的材料都是绝缘材料，具有良好的绝缘性能，同时有机-无机材料形成的软瓷材料还具有良好的耐候性，使用寿命长。
在另一实施例中，提供了一种柔性光伏饰面砖，其中连接层由粘连剂组成，其中粘连剂为乙烯-醋酸乙烯共聚物，粘连剂原料中醋酸乙烯的含量为20-40％。
连接层的由乙烯-醋酸乙烯共聚物构成，而针对于软瓷材料的多孔隙，粗糙表面的特性，本公开使用的粘连剂需要具有较好的流变性能，因此在原料中通过调整醋酸乙烯的含量而调节粘连剂的流变性能，使得粘连剂能够填充软瓷材料的粗糙表面，并结合软瓷材料的粗糙表面，产生更强的粘附效果。
在另一实施例中，光伏电池组层包括了抗冲击层、电池层和光伏电池底层，其中抗冲击层为光伏玻璃，能够对电池层进行保护，而光伏电池底层能够将光伏电池层进行固定，提高稳定性。
在另一实施例中，所述的光伏电池底层通过粘连剂与软瓷材料进行连接固定，光伏电池底层能够避免光伏电池组件中电池层直接与软瓷基层进行连接，造成光伏电池组件的损坏率提高。
在另一实施例中，所述的光伏电池组件与软瓷柔性基材进行粘连后，需要进行热压处理。
热压的目的，一方面能够提高粘连剂的流动性，粘连剂能够较好的填充到软瓷柔性饰面砖的空隙中，提高粘结性能；另一方面，热压能够使柔性软瓷中的高分子材料发生一定的形变，提高软瓷材料与链接剂的充分结合，提高粘连效果。
热压的条件中，需要根据软瓷的性变性能、粘连剂的流动性等确定热压条件，其中本公开针对于软瓷的性能，调整工艺，在热压温度为70-90℃，热压时间为5-10min；热压压力为80-120Kg是具有较好的粘结效果。
具体的，公开了实施例1，提供了一种光伏软瓷饰面砖，光伏软瓷饰面砖包括了软瓷基层、粘连层和光伏电池组层，其中粘连层由粘连剂乙烯-醋酸乙烯固化而成，电池组层包括了抗冲击层、电池层和光伏电池底层。
其中抗冲击层为光伏玻璃；
电池层为多晶硅电池，多晶硅电池上有导电铜带；
电池底层为绝缘塑料，用以固定电池层。
在另一实施例2中，提供了一种光伏软瓷饰面砖的制备方法，
1、软瓷基层的制备
将硅丙乳液和无机颜料进行搅拌，得到混合乳液；将得到的混合乳液加入到混合均匀的水泥和石英砂的粉料中，同时加入一定量的水，搅拌得到软瓷浆料；将软瓷浆料注入模具中进行固化成形，得到软瓷基层。
其中硅丙乳液25份，水泥20份，石英砂20份，有机颜料2份，水8份；
的固化条件为80-90℃，固化2-4h。
2、涂胶
在软瓷基层上进行涂胶，将粘连剂乙烯-醋酸乙烯共聚物均匀涂覆在软瓷基层上；
其中，所述的粘连剂原料中醋酸乙烯的含量为20％。
3、安装光伏电池组件
将光伏电池组件贴服在软瓷基层上，并进行热压，热压完成后进行剪裁得到软瓷光伏饰面砖。
其中热压温度为50℃、热压压力为50Kg，热压时间为10min。
在另一实施例3中，提供了一种光伏软瓷饰面砖的制备方法，
1、软瓷基层的制备
将硅丙乳液和无机颜料进行搅拌，得到混合乳液；将得到的混合乳液加入到混合均匀的水泥和石英砂的粉料中，同时加入一定量的水，搅拌得到软瓷浆料；将软瓷浆料注入模具中进行固化成形，得到软瓷基层。
其中硅丙乳液40份，水泥15份，石英砂15份，有机颜料2份，水5份。
2、涂胶
在软瓷基层上进行涂胶，将粘连剂乙烯-醋酸乙烯共聚物均匀涂覆在软瓷基层上；
其中，所述的粘连剂原料中醋酸乙烯的含量为20％。
3、安装光伏电池组件
将光伏电池组件贴服在软瓷基层上，并进行热压，热压完成后进行剪裁得到软瓷光伏饰面砖。
其中热压温度为50℃、热压压力为50Kg，热压时间为10min。
在另一实施例4中，提供了一种光伏软瓷饰面砖的制备方法，所述的方法与实施例3 相同，区别在于，1、软瓷的配方中，水泥的用量降低为10份；2、热压条件为热压温度为80℃、热压压力为90Kg，热压时间为8min。
在另一实施例5中，提供了一种光伏软瓷饰面砖的制备方法，所述的方法与实施例4 相同，其区别在于，1、使用的粘连剂为乙烯-醋酸乙烯，其中乙烯醋酸乙烯的含量为30％。
在另一实施例6中，提供了一种光伏软瓷饰面砖的制备方法，所述的方法与实施例4 相同，其区别在于，使用的粘连剂为乙烯-醋酸乙烯，其中乙烯醋酸乙烯的含量为10％。
在另一实施例7中，提供了一种光伏软瓷饰面砖的制备方法，所述的方法与实施例4 相同，还包括得对的的光伏软瓷饰面砖进行后续处理，包括对光伏软瓷饰面砖进行切割剪裁、安装接线盒和接头。
对上述实施例中得到的光伏软瓷饰面砖进行性能测试，测试电池组件与软瓷饰面砖之间的粘接强度。
具体的结果如下
从上述的表观和简单的剥离测试来看，首先软瓷和电池组可以进行复合，并且具有一定优异的力学性能，同时在具体的方案来看，如果要提高粘结强度，对于软瓷基材的配方以及粘合剂的配方有较高的要求。
以上所述，仅为本申请的具体实施方式，但本申请的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本申请揭露的技术范围内，可轻易想到变化或替换，都应涵盖在本申请的保护范围之内。因此，本申请的保护范围应以所述权利要求的保护范围为准。
Claims (9)
1.一种光伏软瓷饰面砖的制备方法，其特征在于，包括如下步骤：
步骤1：软瓷基层的制备
将硅丙乳液和无机颜料进行搅拌，得到混合乳液；将得到的混合乳液加入到混合均匀的水泥和石英砂的粉料中，同时加入一定量的水，搅拌得到软瓷浆料；将软瓷浆料注入模具中进行固化成形，得到软瓷基层；
步骤2：涂胶
在软瓷基层上进行涂胶，将粘连剂乙烯-醋酸乙烯共聚物均匀涂覆在软瓷基层上；
步骤3：安装光伏电池组件
将光伏电池组件贴服在软瓷基层上，并进行热压，热压完成后进行剪裁得到软瓷光伏饰面砖。
2.如权利要求1所述的一种光伏软瓷饰面砖的制备方法，其特征在于，
步骤3中的热压温度为70-90℃，热压时间为5-10min；热压压力为80-120Kg。
3.如权利要求1所述的一种光伏软瓷饰面砖的制备方法，其特征在于，
步骤1中原料按质量分，硅丙乳液30-40份，水泥5-15份，石英砂15-20份，有机颜料1-3份，水5-10份。
4.如权利要求1所述的一种光伏软瓷饰面砖的制备方法，其特征在于，
步骤1中的固化条件为80-90℃，固化2-4h。
5.如权利要求1所述的一种光伏软瓷饰面砖的制备方法，其特征在于，步骤2中，所述的粘连剂原料中醋酸乙烯的含量为20-40％。
6.如权利要求1所述的一种光伏软瓷饰面砖的制备方法，其特征在于，所述的制备方法还包括步骤4，对步骤3得到的光伏软瓷饰面砖进行切割剪裁、安装接线盒和接头。
7.一种光伏软瓷饰面砖，其特征在于使用如权利要求6所述的制备方法制备得到，所述光伏软瓷饰面砖包括软瓷基层、连接层和光伏电池组层。
8.如权利要求7所述的一种光伏软瓷饰面砖，其特征在于，所述的光伏电池组层包括了抗冲击层、电池组层和电池底层。
9.如权利要求7所述的一种光伏软瓷饰面砖，其特征在于，所述的连接层由粘连剂固化而成，所述的粘连剂为乙烯-醋酸乙烯，粘连剂原料中醋酸乙烯的含量为20-40％。