CN114426801B - Firm-bonding rubber tree cut surface cold-proof protective agent and preparation method thereof - Google Patents
Firm-bonding rubber tree cut surface cold-proof protective agent and preparation method thereof Download PDFInfo
- Publication number
- CN114426801B CN114426801B CN202111401185.3A CN202111401185A CN114426801B CN 114426801 B CN114426801 B CN 114426801B CN 202111401185 A CN202111401185 A CN 202111401185A CN 114426801 B CN114426801 B CN 114426801B
- Authority
- CN
- China
- Prior art keywords
- protective agent
- parts
- rubber tree
- heavy
- cut surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a rubber tree cut surface cold-proof protective agent with firm bonding and a preparation method thereof, belonging to the field of agricultural medicaments. The firmly-bonded rubber tree cutting surface cold-proof protective agent comprises the following components in parts by weight: 60-85 parts of heavy cerate, 10-30 parts of heavy furfural refined extract oil and 1-10 parts of ethylene propylene rubber. The main raw material heavy wax ointment of the rubber tree cut surface cold-proof protective agent with firm adhesion is a byproduct in the production process of an oil refinery, has the advantages of wide source and low cost, and the finally prepared rubber tree cut surface cold-proof protective agent has a firm and soft coating by screening the proportion of all the raw materials, so that the cut surface of a rubber tree can effectively resist cold damage by only one-time coating, the dry surface of the cut bark is smaller, the healing of the cut surface bark is good, and the rubber tapping operation in the next year is more convenient.
Description
Technical Field
The invention relates to a rubber tree cut surface cold-proof protective agent with firm bonding and a preparation method thereof, belonging to the field of agricultural medicaments.
Background
The safe winter protection and overwintering of the rubber tree cut surface is one of important measures for improving the yield and preventing diseases of the rubber tree. However, in winter when the rubber trees stop tapping, the rubber is blown off due to the invasion of cold current, so that the growth of the rubber trees and the amount and quantity of the gum produced in the next year are influenced, and in order to ensure that the rubber trees can safely live through the winter, the method of mixing the cattle manure with the yellow mud is used in folk, but the effect is poor. The cut surface is protected from wintering by using vaseline, diesel oil, or mixture of vaseline and rosin, or by coating the mixture of vaseline and diesel oil, palm oil, kerosene, etc. on the cut surface of rubber trees. A "rubber tree cutting surface protective agent" (patent No. 92111143.6) granted by Chinese patent office is prepared by using polyvinyl alcohol, downy blight, zinc sulfate, ammonium molybdate, growth regulator and additive to prepare paste, and coating the paste on the cutting surface in winter, so that the cutting surface can be protected from safe overwintering, the recovery rate of dead skin of the rubber tree is improved by 10-20%, the yield is increased by 7.8%, and the rubber tree can be prevented from strip ulcer. But the cost is relatively high due to more raw materials. And experiments in practice prove that the sealing is required to be carried out more than once every year in winter. The invention discloses a rubber tree cutting surface antifreezing protective agent (patent number: 01106038.7), which is prepared by using wax substances, an emulsifier, a plant growth regulator, a tackifier and water to prepare a medicament to coat and seal a cutting surface, wherein the wax substances are reduced second-line distillate oil, reduced third-line distillate oil, reduced fourth-line distillate oil or a mixture thereof, or No. 52-64 commercial paraffin, the emulsifier is a nonionic surfactant or a composite emulsifier consisting of the nonionic surfactant and an anionic surfactant or a cationic surfactant, the nonionic surfactant is a condensation product of fatty alcohol and ethylene oxide or a condensation product of fatty acid and ethylene oxide, the anionic surfactant is a saturated or unsaturated fatty acid salt, the cationic surfactant is triethanolamine fatty acid salt, the tackifier is natural resin rosin or synthetic resin polyisobutylene, petroleum resin or a mixture thereof, and the plant growth regulator is indolebutyric acid. The protective film formed by the agent has long retention time, can ensure that the rubber tree and the cut surface thereof can safely live through the winter when encountering severe winter with windy and overcast and rainy days, and has good healing of the bark of the cut surface, small dry surface of the bark of the cut opening and small internal shrinkage length of the cut line latex pipe. The disadvantages of the method are that the raw materials are various and complex, and the production cost is high. Another invention relates to a cold-proof coating agent for rubber tree cut surfaces and a production method thereof (patent number: CN 100394850C), which is prepared by adding vaseline into rubber seed oil, and the rubber tree cut surfaces are coated once to protect the cut surfaces from wintering safely. The disadvantages of the method are that the raw material source is narrow, and the production process is complex.
Disclosure of Invention
The invention aims to provide a rubber tree cutting surface cold-proof protective agent with firm bonding and a preparation method thereof.
In order to realize the purpose, the invention adopts the technical scheme that:
a rubber tree cutting surface cold-proof protective agent with firm bonding comprises the following components in parts by weight: 60-85 parts of heavy wax ointment, 10-30 parts of heavy furfural refined extract oil and 1-10 parts of ethylene propylene rubber.
The main raw material heavy wax ointment of the firmly-bonded rubber tree cutting surface cold-proof protective agent is a byproduct in the production process of an oil refinery, has the advantages of wide source and low cost, and has the main components of microcrystalline wax, good toughness and high melting point, so that a coating cannot be lost due to sunlight irradiation; the heavy furfural refined extract oil in the raw materials can be mutually dissolved with the rubber latex in the rubber tree secant latex pipe, so that the internal shrinkage length of the secant latex pipe is smaller, the withered surface of the cut bark is smaller, and the cut bark is well healed; the ethylene propylene rubber in the raw materials has excellent weather resistance, ozone resistance, heat resistance, acid and alkali resistance and steam resistance, and the adhesion and toughness of the coating can be improved by adding a certain amount of the ethylene propylene rubber, so that the coating is not easily washed away by rainwater and has high durability.
As a preferred embodiment of the firmly-bonded rubber tree cutting surface cold-proof protective agent, the protective agent comprises the following components in parts by weight: 70-80 parts of heavy cerate, 15-25 parts of heavy furfural refined extract oil and 3-8 parts of ethylene propylene rubber.
As a preferred embodiment of the firmly-bonded rubber tree cut surface cold-proof protective agent, the heavy wax ointment is wax ointment produced in a ketone-benzene dewaxing process by reducing four-line distillate oil or light deoiling.
In a preferred embodiment of the firmly-bonded rubber tree cut surface cold-proof protective agent of the present invention, the content of the microcrystalline wax in the heavy cerate is 80% to 90%. The microcrystalline wax is prepared by mainly taking residue after petroleum fractionation as a raw material, has good toughness and high melting point, and can be used as a main raw material of a coating, so that the coating cannot be lost due to sunlight irradiation and can be firmly adhered.
As a preferred embodiment of the firmly-bonded rubber tree cutting surface cold-proof protective agent, the heavy furfural refined extract oil is extract oil obtained by performing furfural refining extraction on reduced four-line distillate oil. The refined furfural extract oil can be mutually dissolved with the latex of the rubber tree in the secant latex pipe of the rubber tree, so that the internal shrinkage length of the secant latex pipe is smaller, the bark of a cut is smaller in dry surface, and the bark of the cut surface is well healed.
As a preferred embodiment of the firmly-bonded rubber tree cutting surface cold-proof protective agent, the content of high-boiling-point aromatic hydrocarbons in the heavy furfural refined extract oil is 75-95%; the boiling point of the high boiling point aromatic hydrocarbon is more than 450 ℃.
The invention also provides a preparation method of the rubber tree cut surface cold-proof protective agent with firm bonding, which comprises the following steps:
(1) Mixing and heating heavy cerate and heavy furfural refined extract oil, and uniformly stirring to obtain a mixture A;
(2) Mixing and heating ethylene propylene rubber and the mixture A, and stirring until the ethylene propylene rubber is completely dissolved to obtain a mixture B;
(3) And cooling the mixture B to room temperature to obtain the rubber tree cut surface cold-proof protective agent.
In a preferred embodiment of the method for preparing the firmly-bonded rubber tree cut surface cold protective agent of the present invention, the heating temperature in the step (1) is 90 ℃.
In a preferred embodiment of the method for preparing the firmly-bonded rubber tree cut surface cold protective agent of the present invention, the heating temperature in the step (2) is 130 to 180 ℃.
As a preferable embodiment of the method for preparing the firmly-bonded rubber tree cut surface cold-proof protective agent of the present invention, in the step (3), the mixture B is cooled to a temperature of 80 to 90 ℃ by cooling water before being placed in a container.
Compared with the prior art, the invention has the beneficial effects that:
the main raw materials of the rubber tree cutting surface cold-proof protective agent with firm bonding are byproducts of the production process of an oil refinery, and have wide sources and low cost; by screening the proportion of the raw materials, the finally prepared rubber tree cut surface cold-proof protective agent has a firmly-adhered and soft coating, so that the cut surface of the rubber tree can effectively resist cold damage only by coating once, the dry and dry surface of the bark of the cut is smaller, the bark of the cut surface is well healed, and the rubber tapping operation in the next year is more convenient.
Detailed Description
To better illustrate the objects, aspects and advantages of the present invention, the present invention will be further described with reference to specific examples.
Example 1
The rubber tree cutting surface cold-proof protective agent with firm bonding provided by the embodiment of the invention comprises the following raw materials in parts by weight: 80 parts of heavy cerate, 15 parts of heavy furfural refined extract oil and 5 parts of ethylene propylene rubber.
The preparation method of the rubber tree cut surface cold-proof protective agent with firm bonding comprises the following steps:
(1) Mixing heavy cerate and heavy furfural refined oil extract, heating to 90 deg.C, and stirring to obtain mixture A;
(2) Mixing ethylene propylene rubber with the mixture A, heating to 130-180 ℃, stopping heating, and stirring until the ethylene propylene rubber is completely dissolved to obtain a mixture B;
(3) And cooling the mixture B to 80 ℃ by cooling water, placing the mixture B in a container, and further cooling to room temperature to obtain the rubber tree cut surface cold-proof protective agent.
Example 2
The rubber tree cutting surface cold-proof protective agent with firm bonding provided by the embodiment of the invention comprises the following raw materials in parts by weight: 70 parts of heavy cerate, 25 parts of heavy furfural refined extract oil and 5 parts of ethylene propylene rubber.
The preparation method of the firmly-bonded rubber tree cut surface cold-proof protective agent is the same as that of the example 1.
Example 3
The rubber tree cutting surface cold-proof protective agent with firm bonding provided by the embodiment of the invention comprises the following raw materials in parts by weight: 75 parts of heavy cerate, 20 parts of heavy furfural refined extract oil and 5 parts of ethylene propylene rubber.
The preparation method of the firmly-bonded rubber tree cut surface cold-proof protective agent is the same as that of the example 1.
Example 4
The rubber tree cutting surface cold-proof protective agent with firm bonding provided by the embodiment of the invention comprises the following raw materials in parts by weight: 75 parts of heavy cerate, 15 parts of heavy furfural refined extract oil and 10 parts of ethylene propylene rubber.
The preparation method of the rubber tree cut surface cold-proof protective agent with firm bonding is the same as that of the example 1.
Example 5
The rubber tree cut surface cold-proof protective agent provided by the embodiment of the invention is composed of the following raw materials in parts by weight: 70 parts of heavy cerate, 20 parts of heavy furfural refined extract oil and 10 parts of ethylene propylene rubber.
The preparation method of the firmly-bonded rubber tree cut surface cold-proof protective agent is the same as that of the example 1.
Example 6
The rubber tree cut surface cold-proof protective agent provided by the embodiment of the invention is composed of the following raw materials in parts by weight: 60 parts of heavy cerate, 30 parts of heavy furfural refined extract oil and 10 parts of ethylene propylene rubber.
The preparation method of the firmly-bonded rubber tree cut surface cold-proof protective agent is the same as that of the example 1.
Example 7
The rubber tree cut surface cold-proof protective agent provided by the embodiment of the invention is composed of the following raw materials in parts by weight: 82 parts of heavy cerate, 10 parts of heavy furfural refined extract oil and 8 parts of ethylene propylene rubber.
The preparation method of the rubber tree cut surface cold-proof protective agent with firm bonding is the same as that of the example 1.
Example 8
The rubber tree cutting surface cold-proof protective agent with firm bonding provided by the embodiment of the invention comprises the following raw materials in parts by weight: 85 parts of heavy cerate, 14 parts of heavy furfural refined extract oil and 1 part of ethylene propylene rubber.
The preparation method of the firmly-bonded rubber tree cut surface cold-proof protective agent is the same as that of the example 1.
Example 9
The rubber tree cutting surface cold-proof protective agent with firm bonding provided by the embodiment of the invention comprises the following raw materials in parts by weight: 80 parts of heavy cerate, 17 parts of heavy furfural refined extract oil and 3 parts of ethylene propylene rubber.
The preparation method of the rubber tree cut surface cold-proof protective agent with firm bonding is the same as that of the example 1.
Comparative example 1
The difference between the comparative example and the example 3 is only that the proportions of the raw materials in the rubber tree cut cold-proof protective agent are different, and the rubber tree cut cold-proof protective agent which is firmly bonded consists of the following raw materials in parts by weight: 90 parts of heavy cerate, 20 parts of heavy furfural refined extract oil and 5 parts of ethylene propylene rubber.
Comparative example 2
The difference between the comparative example and the example 3 is only that the proportions of the raw materials in the rubber tree cut cold-proof protective agent are different, and the rubber tree cut cold-proof protective agent which is firmly bonded consists of the following raw materials in parts by weight: 75 parts of heavy cerate, 35 parts of heavy furfural refined extract oil and 5 parts of ethylene propylene rubber.
Comparative example 3
The difference between the comparative example and the example 3 is only that the proportions of the raw materials in the rubber tree cut cold-proof protective agent are different, and the rubber tree cut cold-proof protective agent which is firmly bonded consists of the following raw materials in parts by weight: 75 parts of heavy cerate, 20 parts of heavy furfural refined extract oil and 15 parts of ethylene propylene rubber.
Examples of effects
The rubber tree cut surface cold-proof protective agent prepared in the examples 1-9 and the comparative examples 1-3 is subjected to performance test.
The test method comprises the following steps: 5g of the rubber tree cut cold-proof protective agent prepared in each of examples 1 to 9 and comparative examples 1 to 3 was applied to rubber tree cut surfaces of the same size, and after 6 months, the coating defect rate of the rubber tree cut surfaces, the withering condition of the rubber tree cut surfaces, and the healing condition of the cut surfaces and barks were evaluated.
The results of performance tests of the rubber tree cut surface cold-proof protective agent are shown in table 1.
TABLE 1
Finally, it should be noted that the above embodiments are only used for illustrating the technical solutions of the present invention and not for limiting the protection scope of the present invention, and although the present invention is described in detail with reference to the preferred embodiments, it should be understood by those skilled in the art that modifications or equivalent substitutions can be made to the technical solutions of the present invention without departing from the spirit and scope of the technical solutions of the present invention.
Claims (7)
1. The rubber tree cut surface cold-proof protective agent with firm bonding is characterized by comprising the following components in parts by weight: 60-85 parts of heavy wax ointment, 10-30 parts of heavy furfural refined extract oil and 1-10 parts of ethylene propylene rubber; the heavy cerate is cerate generated in the process of ketone-benzene dewaxing by four-line-reduced distillate oil or light deoiling; the content of microcrystalline wax in the heavy wax ointment is 80-90%; the heavy furfural refined extract oil is the extract oil obtained by furfural refining extraction of the four-line distillate oil.
2. The firmly-bonded rubber tree cut surface cold-proof protective agent as claimed in claim 1, wherein the protective agent comprises the following components in parts by weight: 70-80 parts of heavy cerate, 15-25 parts of heavy furfural refined extract oil and 3-8 parts of ethylene propylene rubber.
3. The firmly-bonded rubber tree cut surface cold-proof protective agent as claimed in any one of claims 1-2, wherein the content of high-boiling-point aromatic hydrocarbons in the heavy furfural refined extract oil is 75-95%; the boiling point of the high boiling point aromatic hydrocarbon is more than 450 ℃.
4. The method for preparing the firmly-bonded rubber tree cut surface cold-proof protective agent as claimed in any one of claims 1 to 3, characterized by comprising the following steps:
(1) Mixing and heating heavy cerate and heavy furfural refined extract oil, and uniformly stirring to obtain a mixture A;
(2) Mixing and heating ethylene propylene rubber and the mixture A, and stirring until the ethylene propylene rubber is completely dissolved to obtain a mixture B;
(3) And cooling the mixture B to room temperature to obtain the rubber tree cut surface cold-proof protective agent.
5. The method for preparing a firmly-bonded rubber tree cut surface cold-proof protective agent as claimed in claim 4, wherein the heating temperature in the step (1) is 90 ℃.
6. The method for preparing a firmly-bonded rubber tree cut surface cold-proof protective agent as claimed in claim 4, wherein the heating temperature in the step (2) is 130-180 ℃.
7. The method for preparing a firm-adhered rubber tree cut surface cold-proof protective agent as claimed in claim 4, wherein in said step (3), mixture B is cooled to 80-90 ℃ by cooling water before being placed in a container.