CN114411338A - 一种大姜种植用防霜无纺布及其制备方法 - Google Patents
一种大姜种植用防霜无纺布及其制备方法 Download PDFInfo
- Publication number
- CN114411338A CN114411338A CN202210036650.6A CN202210036650A CN114411338A CN 114411338 A CN114411338 A CN 114411338A CN 202210036650 A CN202210036650 A CN 202210036650A CN 114411338 A CN114411338 A CN 114411338A
- Authority
- CN
- China
- Prior art keywords
- woven fabric
- frost
- parts
- antioxidant
- ginger
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种大姜种植用防霜无纺布及其制备方法，涉及农用无纺布技术领域，所述的大姜种植用防霜无纺布包括如下重量份数的原料组分：聚丙烯90‑100份、聚酯8‑10份、银离子抗菌剂0.5‑1.5份、甲壳素2‑3份、抗氧化剂2‑3份、热稳定剂0.1‑0.3份、光稳定剂0.2‑0.4份。使用本发明提供的大姜种植用防霜无纺布可以有效避免霜冻；使用本发明提供的大姜种植用防霜无纺布覆盖可以增加棚内温度5‑10℃，可延长大姜生长期20天左右，从而达到增产效果；使用本发明提供的大姜种植用防霜无纺布可错峰采收，可避开收姜用工高潮，掀开即可收取；使用本发明提供的大姜种植用防霜无纺布种植得到的大姜色泽老成，耐储存，掉秤少，售价高。
Description
技术领域
本发明涉及农用无纺布技术领域，具体涉及一种大姜种植用防霜无纺布及其制备方法。
背景技术
大姜具有特殊的香辣味，是人们普遍采用的香辛调味蔬菜。生姜供食用和药用的部分为其根茎。根茎内含多种营养成分，它除含有碳水化合物、蛋白质、多种维生素及矿物质外，还含有姜辣素、姜油酮、姜烯酚和姜醇等。
大姜的生长受气温的影响很大，气温在零上5℃以上,大姜可以无限生长。目前，种植大姜的农民使用PE膜对大姜进行保温，但使用透明PE膜覆盖，不透气不透水，PE膜内水蒸汽挥发不掉，会导致大姜叶子发黄腐烂，大姜停止生长。
发明内容
针对现有技术中的缺陷，本发明提供一种大姜种植用防霜无纺布及其制备方法，本发明提供的大姜种植用防霜无纺布具有显著的保温、防霜、透水、透光效果，在10月份霜冻来临之前，使用本发明提供的大姜种植用防霜无纺布，可有效预防冷空气带来的霜冻，保护大姜不被霜打；本发明提供的大姜种植用防霜无纺布覆盖可增加棚内温度5-10℃，大气温度在15℃时棚内温度可达25℃，大气温度在5℃时棚内温度可达10℃，可延长大姜生长期20天左右，从而达到增产效果。土壤保湿效果明显，使用本发明提供的大姜种植用防霜无纺布前，浇一遍地，采收时土壤依旧湿润松软，适宜采收。
本发明的一个目的在于保护所述的大姜种植用防霜无纺布，包括如下重量份数的原料组分：聚丙烯90-100份、聚酯8-10份、银离子抗菌剂0.5-1.5份、甲壳素2-3份、抗氧化剂2-3份、热稳定剂0.1-0.3份、光稳定剂0.2-0.4份。
优选地，所述的大姜种植用防霜无纺布包括如下重量份数的原料组分：聚丙烯95份、聚酯9份、银离子抗菌剂1份、甲壳素2.5份、抗氧化剂2.5份、热稳定剂0.2份、光稳定剂0.3份。
进一步优选地，所述的抗氧化剂为磷酸三丁酯、亚磷酸三苯酯、抗氧化剂1010和抗氧化剂1024；所述的抗氧化剂为磷酸三丁酯、亚磷酸三苯酯、抗氧化剂1010和抗氧化剂1024的重量份数比为1：1：1：2。
进一步优选地，所述的热稳定剂为硬脂酸钙。
进一步优选地，所述的光稳定剂为Tinuvin 329。
本发明的另一个目的在于保护上述的大姜种植用防霜无纺布的制备方法，步骤如下：在聚丙烯颗粒中加入聚酯颗粒、银离子抗菌剂、甲壳素、抗氧化剂、热稳定剂、光稳定剂，搅拌均匀，制得混合物，加入挤出机中进行加热熔融，经过喷丝板喷出丝束，将丝束经牵伸风机进行拉伸，拉伸后的丝束落到成网机网帘上铺成蓬松的网状，经热轧机进行热轧成型，制得热轧成型的无纺布，经卷绕机进行去边卷绕成卷后，经热粘合机进行粘合，制得所述的大姜种植用防霜无纺布。
优选地，所述的挤出机的七个区的温度设置分别为：一区225℃，二区215℃，三区215℃，四区220℃，五区220℃，六区223℃，七区225℃；所述的挤出机的压力控制在5兆帕。
优选地，所述的喷丝板的喷丝孔的尺寸为0.45mm。
优选地，所述的拉伸的倍数为4-6倍。
优选地，所述的热轧机的温度控制在132℃、压力控制在65兆帕；所述的热轧成型的无纺布的幅宽为2.9-3.2m，克重为20-21克/平方米。
本发明的有益效果体现在：
(1)本发明提供的大姜种植用防霜无纺布具有显著的保温、防霜、透水、透光效果。
(2)使用本发明提供的大姜种植用防霜无纺布可以有效避免霜冻；使用本发明提供的大姜种植用防霜无纺布覆盖可以增加棚内温度5-10℃，可延长大姜生长期20天左右，从而达到增产效果；使用本发明提供的大姜种植用防霜无纺布可错峰采收，可避开收姜用工高潮，掀开即可收取；使用本发明提供的大姜种植用防霜无纺布种植得到的大姜色泽老成，耐储存，掉秤少，售价高。
(3)本发明提供的大姜种植用防霜无纺布的制备方法，操作简单，技术稳定，原料易得，制得的产品效果优异，极具商业价值。
具体实施方式
下面将对本发明技术方案的实施例进行详细的描述。以下实施例仅用于更加清楚地说明本发明的技术方案，因此只作为示例，而不能以此来限制本发明的保护范围。
需要注意的是，除非另有说明，本申请使用的技术术语或者科学术语应当为本发明所属领域技术人员所理解的通常意义。
实施例1
本实施例提供了一种大姜种植用防霜无纺布，包括如下重量份数的原料组分：聚丙烯95份、聚酯9份、银离子抗菌剂1份、甲壳素2.5份、抗氧化剂2.5份、热稳定剂0.2份、光稳定剂0.3份。
抗氧化剂为磷酸三丁酯、亚磷酸三苯酯、抗氧化剂1010和抗氧化剂1024；
抗氧化剂为磷酸三丁酯、亚磷酸三苯酯、抗氧化剂1010和抗氧化剂1024的重量份数比为1：1：1：2。
热稳定剂为硬脂酸钙。
光稳定剂为Tinuvin 329。
上述的大姜种植用防霜无纺布的制备方法，步骤如下：
在聚丙烯颗粒中加入聚酯颗粒、银离子抗菌剂、甲壳素、抗氧化剂、热稳定剂、光稳定剂，搅拌均匀，制得混合物，加入挤出机中进行加热熔融，经过喷丝板喷出丝束，将丝束经牵伸风机进行拉伸，拉伸后的丝束落到成网机网帘上铺成蓬松的网状，经热轧机进行热轧成型，制得热轧成型的无纺布，经卷绕机进行去边卷绕成卷后，经热粘合机进行粘合，制得所述的大姜种植用防霜无纺布。
挤出机的七个区的温度设置分别为：一区225℃，二区215℃，三区215℃，四区220℃，五区220℃，六区223℃，七区225℃；挤出机的压力控制在5兆帕。
喷丝板的喷丝孔的尺寸为0.45mm。
拉伸的倍数为5倍。
热轧机的温度控制在132℃、压力控制在65兆帕。
热轧成型的无纺布的幅宽为2.9m，克重为20克/平方米。
实施例2
本实施例提供了一种大姜种植用防霜无纺布，包括如下重量份数的原料组分：聚丙烯90份、聚酯8份、银离子抗菌剂0.5份、甲壳素2份、抗氧化剂2份、热稳定剂0.1份、光稳定剂0.2份。
抗氧化剂为磷酸三丁酯、亚磷酸三苯酯、抗氧化剂1010和抗氧化剂1024；抗氧化剂为磷酸三丁酯、亚磷酸三苯酯、抗氧化剂1010和抗氧化剂1024的重量份数比为1：1：1：2。
热稳定剂为硬脂酸钙。
光稳定剂为Tinuvin 329。
上述的大姜种植用防霜无纺布的制备方法，步骤如下：
在聚丙烯颗粒中加入聚酯颗粒、银离子抗菌剂、甲壳素、抗氧化剂、热稳定剂、光稳定剂，搅拌均匀，制得混合物，加入挤出机中进行加热熔融，经过喷丝板喷出丝束，将丝束经牵伸风机进行拉伸，拉伸后的丝束落到成网机网帘上铺成蓬松的网状，经热轧机进行热轧成型，制得热轧成型的无纺布，经卷绕机进行去边卷绕成卷后，经热粘合机进行粘合，制得所述的大姜种植用防霜无纺布。
挤出机的七个区的温度设置分别为：一区225℃，二区215℃，三区215℃，四区220℃，五区220℃，六区223℃，七区225℃；挤出机的压力控制在5兆帕。
喷丝板的喷丝孔的尺寸为0.45mm。
拉伸的倍数为5倍。
热轧机的温度控制在132℃、压力控制在65兆帕。
热轧成型的无纺布的幅宽为2.9m，克重为20克/平方米。
实施例3
本实施例提供了一种大姜种植用防霜无纺布，包括如下重量份数的原料组分：聚丙烯100份、聚酯10份、银离子抗菌剂1.5份、甲壳素3份、抗氧化剂3份、热稳定剂0.3份、光稳定剂0.4份。
抗氧化剂为磷酸三丁酯、亚磷酸三苯酯、抗氧化剂1010和抗氧化剂1024；抗氧化剂为磷酸三丁酯、亚磷酸三苯酯、抗氧化剂1010和抗氧化剂1024的重量份数比为1：1：1：2。
热稳定剂为硬脂酸钙。
光稳定剂为Tinuvin 329。
上述的大姜种植用防霜无纺布的制备方法，步骤如下：
在聚丙烯颗粒中加入聚酯颗粒、银离子抗菌剂、甲壳素、抗氧化剂、热稳定剂、光稳定剂，搅拌均匀，制得混合物，加入挤出机中进行加热熔融，经过喷丝板喷出丝束，将丝束经牵伸风机进行拉伸，拉伸后的丝束落到成网机网帘上铺成蓬松的网状，经热轧机进行热轧成型，制得热轧成型的无纺布，经卷绕机进行去边卷绕成卷后，经热粘合机进行粘合，制得所述的大姜种植用防霜无纺布。
挤出机的七个区的温度设置分别为：一区225℃，二区215℃，三区215℃，四区220℃，五区220℃，六区223℃，七区225℃；挤出机的压力控制在5兆帕。
喷丝板的喷丝孔的尺寸为0.45mm。
拉伸的倍数为5倍。
热轧机的温度控制在132℃、压力控制在65兆帕。
热轧成型的无纺布的幅宽为2.9m，克重为20克/平方米。
试验例1
测试实施例1制得的大姜种植用防霜无纺布的力学性能和透光率
表1
| 性能指标 | 实施例1 |
| 纵向拉力(N) | 30 |
| 横向拉力(N) | 25 |
| 纵向断裂伸长率(％) | 100 |
| 纵向断裂伸长率(％) | 125 |
| 透光率(％) | 80 |
试验例2
种植大姜产量试验
试验地点：驿道镇周家涧、郭家店镇宋光村、平里店镇孟家和平里店镇龙冢庙四个试验地点中同一位置的四块相同面积的试验点，共16个试验点。
试验方法：采用本发明实施例1-3制得的大姜种植用防霜无纺布进行种植大姜；采用没有覆盖本发明提供的大姜种植用防霜无纺布作为对比例进行种植大姜；具体结果见表2。
表2
最后应说明的是：以上各实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述各实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分或者全部技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的范围，其均应涵盖在本发明的权利要求和说明书的范围当中。
Claims (10)
1.一种大姜种植用防霜无纺布，其特征在于：所述的大姜种植用防霜无纺布包括如下重量份数的原料组分：聚丙烯90-100份、聚酯8-10份、银离子抗菌剂0.5-1.5份、甲壳素2-3份、抗氧化剂2-3份、热稳定剂0.1-0.3份、光稳定剂0.2-0.4份。
2.根据权利要求1所述的大姜种植用防霜无纺布，其特征在于：所述的大姜种植用防霜无纺布包括如下重量份数的原料组分：聚丙烯95份、聚酯9份、银离子抗菌剂1份、甲壳素2.5份、抗氧化剂2.5份、热稳定剂0.2份、光稳定剂0.3份。
3.根据权利要求2所述的大姜种植用防霜无纺布，其特征在于：所述的抗氧化剂为磷酸三丁酯、亚磷酸三苯酯、抗氧化剂1010和抗氧化剂1024；所述的抗氧化剂为磷酸三丁酯、亚磷酸三苯酯、抗氧化剂1010和抗氧化剂1024的重量份数比为1：1：1：2。
4.根据权利要求2所述的大姜种植用防霜无纺布，其特征在于：所述的热稳定剂为硬脂酸钙。
5.根据权利要求2所述的大姜种植用防霜无纺布，其特征在于：所述的光稳定剂为Tinuvin 329。
6.权利要求1-5任一所述的大姜种植用防霜无纺布的制备方法，其特征在于：所述的制备方法，步骤如下：在聚丙烯中加入聚酯、银离子抗菌剂、甲壳素、抗氧化剂、热稳定剂、光稳定剂，搅拌均匀，制得混合物，加入挤出机中进行加热熔融，经过喷丝板喷出丝束，将丝束经牵伸风机进行拉伸，拉伸后的丝束落到成网机网帘上铺成蓬松的网状，经热轧机进行热轧成型，制得热轧成型的无纺布，经卷绕机进行去边卷绕成卷后，经热粘合机进行粘合，制得所述的大姜种植用防霜无纺布。
7.根据权利要求6所述的大姜种植用防霜无纺布的制备方法，其特征在于：所述的挤出机的七个区的温度设置分别为：一区225℃，二区215℃，三区215℃，四区220℃，五区220℃，六区223℃，七区225℃；所述的挤出机的压力控制在5兆帕。
8.根据权利要求6所述的大姜种植用防霜无纺布的制备方法，其特征在于：所述的喷丝板的喷丝孔的尺寸为0.45mm。
9.根据权利要求6所述的大姜种植用防霜无纺布的制备方法，其特征在于：所述的拉伸的倍数为4-6倍。
10.根据权利要求6所述的大姜种植用防霜无纺布的制备方法，其特征在于：所述的热轧机的温度控制在132℃、压力控制在65兆帕；所述的热轧成型的无纺布的幅宽为2.9-3.2m，克重为20-21克/平方米。