CN114368930A - 增强触变润滑剂及含有该增强触变润滑剂的石膏砂浆 - Google Patents
增强触变润滑剂及含有该增强触变润滑剂的石膏砂浆 Download PDFInfo
- Publication number
- CN114368930A CN114368930A CN202210094987.2A CN202210094987A CN114368930A CN 114368930 A CN114368930 A CN 114368930A CN 202210094987 A CN202210094987 A CN 202210094987A CN 114368930 A CN114368930 A CN 114368930A
- Authority
- CN
- China
- Prior art keywords
- gypsum
- thixotropic lubricant
- parts
- gypsum mortar
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了增强触变润滑剂及含有该增强触变润滑剂的石膏砂浆，所述增强触变润滑剂，包括如下重量份的组分：减水剂2‑4份，木质素纤维4‑6份，羟丙基淀粉醚2‑4份，瓜尔胶0.5‑1.5份，解决了现有技术存在的用水量大石膏砂浆强度低的问题。
Description
技术领域
本发明涉及建筑材料技术领域，具体涉及一种增强触变润滑剂及含有该增强触变润滑剂的石膏。
背景技术
随着国家双控政策的实施，石膏砂浆作为环保型建材逐步得到推广，但是石膏砂浆存在强度不高，不好分散，施工比较难的缺点，工人施工的时候不好批刮，在工地严重缺工人的情况下，石膏砂浆推广遇到一定难度。为了改善石膏砂浆的性能，常加入触变润滑剂。
目前的触变润滑剂是以淀粉醚，聚丙烯酰胺，膨润土为主，主要通过加大石膏砂浆的用水量在石膏砂浆表面形成水膜从而达到好用的目的，该类触变润滑剂存在的缺点是用水量大使得石膏砂浆强度变低，每增加5％的用水量砂浆强度损失15％。目前的石膏增强剂是一些石膏深加工产品，造纸废液等材料生产，添加量大，大概占砂浆的10％，这样石膏用量相对减少，达不到绿色产品的理念。
发明内容
本发明提供了一种增强触变润滑剂及含有该增强触变润滑剂的石膏砂浆，解决了现有技术存在的用水量大使得石膏砂浆强度变低的问题。
为了解决该技术问题，本发明提供了如下技术方案：
增强触变润滑剂，包括如下重量份的组分：
优选的，增强触变润滑剂包括如下重量份的组分：
优选的，所述减水剂为密胺系减水剂，减水剂能减少拌合用水量。
瓜尔胶胶凝材料粒子受诱导效应影响，表面极化，降低了空间位阻效应，防止石膏粒子团聚，提高了石膏粒子之间的均匀性，使得水分均匀分散在各粒子之间，使粒子之间结合更紧密，降低了空隙率，从而石膏砂浆干燥后整体强度均匀；木质素纤维在石膏砂浆里形成三维立体结构使得整体强度变高并抗裂，同时其导水功能使得砂浆整体干燥一致，也有了抗裂和提高强度的性能，强度提高；羟丙基淀粉醚和瓜尔胶协同作用可以提高石膏的抗垂性，提高增加砂浆的稠度，提高流动性能，使施工更顺畅，刮抹更平滑。
本发明还提供了上述的增强触变润滑剂的石膏砂浆，包括如下重量份的组分：
一种含有上述增强触变润滑剂的石膏砂浆，包括如下重量份的组分：
本发明可以有效改善石膏砂浆强度和施工难的情况，首先石膏强度不高是由于石膏本身较粘，搅拌不好分散，容易团聚水灰不均匀，干燥后强度不高，将各组分混合得到的石膏砂浆中，羟丙基甲基纤维素和羟丙基淀粉醚配合使用，具有较好的协同效果，不仅可以提高砂浆的抗垂性和抗滑移性，也可以大大提高增加砂浆的流动性能，刮抹更平滑；同时，增强触变润滑剂胶凝材料粒子受诱导效应影响，表面极化，降低了空间位阻效应，防止石膏粒子团聚，提高了石膏粒子之间的均匀性，使得水分均匀分散在各粒子之间，使粒子之间结合更紧密，降低了空隙率，从而石膏砂浆干燥后整体强度均匀；此外，木质素纤维在石膏砂浆里形成三维立体结构使得整体内聚力变高并抗裂，同时使得砂浆整体高燥一致，提高强度。
优选的，所述石膏砂浆的粒子为球状颗粒。
所述球状颗粒的粒径为1-5μm。
不使用本方案的增强触变润滑剂的石膏砂浆的粒子呈八面体或者十面体，表面棱角分明，粒子间间距大；加入本发明的增强触变润滑剂的石膏砂浆的粒子呈球状颗粒，粒子分布均匀，排列紧密，从而实现强度变高的目的。
本发明和现有技术相比，具有以下优点：
本发明添加量仅为砂浆量的0.2％，较小的添加量就可以达到要求。
本方案的增强触变润滑剂制备得到的石膏相比于现有技术，具有更好的抗折和抗压性能。
本产品具有润滑性和很大的触变性，灰刀披挂的时候灰变得活跃，粘度变低，灰刀停止的时候灰浆恢复粘度，使得工人用灰刀披挂的时候很轻松，并且灰浆不下垂，从而达到既好用又能达到很好的添灰找平的效果。
附图说明
此处所说明的附图用来提供对本发明实施例的进一步理解，构成本申请的一部分，并不构成对本发明实施例的限定。在附图中：
图1为对比例1未加石膏增强触变润滑剂的扫描电镜图；
图2为本发明实施例4添加了石膏增强触变润滑剂的扫描电镜图。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明白，下面结合实施例，对本发明作进一步的详细说明，本发明的示意性实施方式及其说明仅用于解释本发明，并不作为对本发明的限定。
实施例1
将3份三聚氰胺甲醛树脂磺酸钠、5份木质素纤维、3份羟丙基淀粉醚、1份瓜尔胶均匀搅拌得出石膏增强触变润滑剂成品。
实施例2
将2份三聚氰胺甲醛树脂磺酸钠、4份木质素纤维、2份羟丙基淀粉醚、0.5份瓜尔胶均匀搅拌得出石膏增强触变润滑剂成品。
实施例3
将4份三聚氰胺甲醛树脂磺酸钠、6份木质素纤维、4份羟丙基淀粉醚、1.5份瓜尔胶均匀搅拌得出石膏增强触变润滑剂成品。
实施例4
将实施例1制得的增强触变润滑剂制备得到的石膏砂浆，包括：脱硫石膏400克，羟丙基甲基纤维素2克，增强触变润滑剂2克，重钙粉596克，水420克，批刮使用后，该配方施工流畅，好批刮，易找平，可一次批刮2cm,该配方做成4mm*4mm*16mm试块，第二天脱模，烘箱到绝干，经测试力学强度为：抗折2.5兆帕，抗压5.3兆帕。所述石膏砂浆的扫描电镜图如图2所述。
实施例5
将实施例1制得的增强触变润滑剂制备得到的石膏砂浆，包括：脱硫石膏450克，羟丙基甲基纤维素3克，增强触变润滑剂3克，重钙粉650克，水450克，批刮使用后，该配方施工流畅，好批刮，易找平，可一次批刮2cm,该配方做成4mm*4mm*16mm试块，第二天脱模，烘箱到绝干，经测试力学强度为，抗折2.2兆帕，抗压5兆帕。
实施例6
将实施例1制得的增强触变润滑剂制备得到的石膏砂浆，包括：脱硫石膏350克，羟丙基甲基纤维素1克，增强触变润滑剂1克，重钙粉550克，水350克，批刮使用后，该配方施工流畅，好批刮，易找平，可一次批刮2cm,该配方做成4mm*4mm*16mm试块，第二天脱模，烘箱到绝干，经测试力学强度为，抗折2.2兆帕，抗压4.5兆帕。
对比例1
石膏砂浆，包括，脱硫石膏400克，羟丙基甲基纤维素2克，羟丙基淀粉醚2克，重钙粉596克，水420克，该配方比较粘，披挂起来表面有气泡，批刮2mm下垂明显，该配方做成4mm*4mm*16mm试块，第二天脱模，烘箱到绝干，经测试力学强度为，抗折2.0兆帕，抗压3.9兆帕；所述石膏砂浆的扫描电镜图如图1所述。
附图1是未加石膏增强触变润滑剂的扫描电镜效果图，可见粒子之间间隙较大，排列不均匀；附图2是加了石膏增强触变润滑剂的效果，可见粒子分布均匀，排列紧密，从而实现强度变高的目的；此外，从实施例4和对比例1的数据可知，本方案的增强触变润滑剂制备得到的石膏相比于现有技术，批刮使用后，该配方施工流畅，好批刮，易找平，同时具有更好的抗折和抗压性能，测试强度比不添加石膏增强触变润滑剂的强度提高15％以上。
以上所述的具体实施方式，对本发明的目的、技术方案和有益效果进行了进一步详细说明，所应理解的是，以上所述仅为本发明的具体实施方式而已，并不用于限定本发明的保护范围，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (7)
1.增强触变润滑剂，其特征在于，包括如下重量份的组分：
2.根据权利要求1所述的增强触变润滑剂，其特征在于，包括如下重量份的组分：
3.根据权利要求1或2所述的增强触变润滑剂，其特征在于，所述减水剂为密胺系减水剂。
4.含有权利要求1-3任一项所述的增强触变润滑剂的石膏砂浆，其特征在于，包括如下重量份的组分：
5.根据权利要求4所述的石膏砂浆，其特征在于，包括如下重量份的组分：
6.根据权利要求4或5所述的石膏砂浆，其特征在于，所述石膏砂浆的粒子为球状颗粒。
7.根据权利要求6所述的石膏砂浆，其特征在于，所述球状颗粒的粒径为1-5μm。