CN1142474A - Dolomite spray repleting material - Google Patents
Dolomite spray repleting material Download PDFInfo
- Publication number
- CN1142474A CN1142474A CN 96101728 CN96101728A CN1142474A CN 1142474 A CN1142474 A CN 1142474A CN 96101728 CN96101728 CN 96101728 CN 96101728 A CN96101728 A CN 96101728A CN 1142474 A CN1142474 A CN 1142474A
- Authority
- CN
- China
- Prior art keywords
- gunning refractory
- calcium oxide
- spray
- repleting
- dolomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A gunning refractory for alkaline smelting furnace contains magnesium oxide and calcium oxide. Its water-proof feature is obtained by mixing with coal tar, asphalt, etc. at 100-500 deg.C. Its advantages include long storage period (more than 3 months, low cost, rich raw materials and high calcium oxide content purifying molten steel.
Description
The present invention belongs to the furnace charge technical field, is a kind of novel spray repair furnace charge that contains magnesium oxide and calcium oxide.
At present, the Gunning refractory that China and even world's alkalescence steel melting furnace extensively adopt mainly is a magnesian gunning refractory, this Gunning refractory cost height, and resource is limited by the region.
Purpose of the present invention:
The one, adopt cheaply, resource is easily looked for, and the abundant raw material of reserves replaces.
The 2nd, adopt this material to make Gunning refractory, can not only prolongs life, can also purify hot metal.
The object of the present invention is achieved like this:
Rhombspar is after roasting, and processing is broken into release mesh, adds partially also mixing of coal tar, pitch, six more by a certain percentage, carries out preventing hydration and handle under 100-500 ℃.Preventing hydration can normally be preserved more than three months after handling.
The present invention has compared following advantage with former Gunning refractory:
1. cheap;
2. raw material resources are abundant, and are widely distributed;
3. the calcium oxide content height has cleaning action to molten steel.
The embodiment of the invention is described as follows:
With calcining in the stoving oven of high quality white marble about 1500 ℃ of buying, select, be broken into 0-5mm after the calcining, add partially also mixing of coal tar, pitch, six more by a certain percentage, under 100-500 ℃, carry out preventing hydration and handle.Pack after preventing hydration is handled and treat pin.
Claims (4)
1. the dolomite spray repleting material of an alkaline steel melting furnace, it mainly contains calcium oxide and magnesium oxide, it is characterized in that this Gunning refractory has carried out the preventing hydration processing.
2. Gunning refractory according to claim 1 is characterized in that it is to add coal tar, pitch, six by a certain percentage to carry out the preventing hydration processing partially.
3. Gunning refractory according to claim 1 is characterized in that it when preventing hydration is handled, and the Heating temperature scope is 100~500 ℃.
4. Gunning refractory according to claim 1 is characterized in that it contains calcium oxide is 35~60%.