CN101492277B - Waterproofing agent special for mending toilet and kitchen - Google Patents
Waterproofing agent special for mending toilet and kitchen Download PDFInfo
- Publication number
- CN101492277B CN101492277B CN2009101191734A CN200910119173A CN101492277B CN 101492277 B CN101492277 B CN 101492277B CN 2009101191734 A CN2009101191734 A CN 2009101191734A CN 200910119173 A CN200910119173 A CN 200910119173A CN 101492277 B CN101492277 B CN 101492277B
- Authority
- CN
- China
- Prior art keywords
- water
- cement
- proof material
- fast
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a waterproof material having obvious waterproof effects and safety use. The waterproof material permeates the inside of a cement structure by utilizing the prior water leakage channels, reacts with hydration products of cement to form water-insoluble crystals, colloid and combination substances, and blocks the water leakage channels or capillary pores under the condition of not damaging the optimum state of the prior building structure so as to achieve waterproof effects.
Description
Technical field:
The present invention relates to the liquid water-proof material that water penetration is repaired, especially at spreading the waterproof repairing water-proof material that defending of floor tile leaked between the kitchen.
Background technology:
At present, the water-proof material at water penetration has:
1, silicone based: the ventilation property hydrophobic film who forms few molecules thick after the film forming, have under the situation of ponding existence, hydraulic pressure during greater than the surface tension of water the hydrophobic film lose waterproof action, secondly artificial friction disappears waterproofing membrane fast, all can cause the waterproof failure.
2, acrylic acid class, SBS class, APP class, JS class, polyurethanes, polyethylene polypropylene class, their the waterproof principle is the waterproofing membrane that forms one deck flexible obturator at building surface, in use aging easily, embrittlement, artificial damage all can make the waterproof membrane breakage, causes losing waterproof effect.
3, silicates rapid hardening type rigid waterproofing dura mater is in artificial vibrations, and the splitting of buildings under the factor such as expand with heat and contract with cold due to the temperature difference, all can make the waterproof membrane cracking, causes secondary to leak.
4, high pressure pouring polyurathamc water-proof material class, the waterproof principle is: after this material was met water, foaming rapidly formed the spumescence adhesive bond that seals, and stops up leak paths or crackle, thereby reaches the waterproof purpose.The shortcoming of this material is: the pre-buried position of Water slop injector is not right, and water-proof material can not communicate with leak paths, causes control to leak to no effect.In addition, owing to be high pressure, changed the stress of primary structure, cracking leaks once more.
5, cementitious capillary waterproofing material: its depth of penetration is little has only several millimeters, the waterproof dense layer is thin, speed of response is slow, resultant is few, stop up the slit limited, can not well go to the crack of healing, and cost an arm and a leg.
In sum: the easy breakage of existing water-proof material flexibility on the market, inflexible ftractures easily, and this all is disadvantage of water-proof material.
Summary of the invention:
In order to overcome the deficiency of existing water-proof material, the water-proof material that the present invention is made up of infiltration component and crystallographic component.Its porous is to the cement structures inside of construction, and hydrated product reaction water-fast crystal of generation and colloid with cement form a closely knit more hard and soft bonded integral waterproofing layer.
One, technical formula
1, infiltration component: be by water glass, OP10, peregal, ethylene bottom oil is formed.
2, crystallographic component: by purified drinking water, sulfuric acid, vitriol is formed
Two, production technique:
1, earlier above material is taken by weighing by formula rate,, the tar after the emulsification is poured in the container that fills water glass slowly, stir while adding, be mixed to color even, the packing warehouse-in with peregal or OP10 breast tar.
2, pure water is poured in the acid proof container such as stainless steel, added vitriol then and stir, up to whole dissolvings, add an amount of vitriol oil more slowly, impurity is removed, the packing warehouse-in in static one hour of the back that stirs.
Specific implementation method:
This material after the dilute with water, can be penetrated into cement structures inside as water when construction, the hydrated product reaction with cement generates water-fast crystal and colloid, stops up leak paths, thereby reaches the waterproof purpose.
1. the function of infiltration component is: the leak paths of cleaning sand-cement slurry, the effect of softening water and diffusion.
2. the function of crystallographic component is: current smoothly in the leak paths that the infiltration component has been dredged, arrive the inner hydrated product reaction of cement structures and generate water-fast crystal, colloid and complex compound with cement, secondly, crystallographic component reacts with the infiltration component that is penetrated into inside configuration, generate water-fast material again, stopped up leak paths or pore again.Its chemical equation is as follows: [2 (Al are arranged in the hydrated product of cement
2O
3.3H
2O) (gel) CaO.SiO
2And Ca (OH)
2Deng]
3CaAl
2O
3CaSO
4?12H
2O+2Ca
2++2SO
2- 4+20H
2O＝3CaO.Al
2O
3.3CaSO
4.32H
2O
Al
2O
3.3H
2O+Ca(OH)
2+3Ca
2++3SO
2- 4+26H
2O＝3CaO.Al
2O
3.CaSO
4.32H
2O
Na
2SiO
3+Ca(OH)
2＝2NaOH+CaO.SiO
2
2Ca(OH)
2+SiO
2+nH
2O＝2CaO.SiO
2.mH
2O
Na
2SO
4+CaOH)
2＝2NaOH+CaSO
4
3Ca(OH)
2+Al
2(SO
4)
3＝3CaSO
4+2Al(OH)
3
From above reaction as can be seen, resultant has crystal, colloid and complex compound.They all are the active substances that stops up leak paths.In addition, be added with an amount of sulfuric acid in the prescription, above resultant is more water-fast after pickling, and unnecessary vitriol is isolated in outside the structure, is unlikely to expand once more and makes structure crack.So both play good waterproof action, do not damaged the optimum regime of original building structure again.
Claims (4)
1. one kind is utilized the infiltration component: water glass, OP-10 peregal, tar; Crystallographic component: pure water, the water-proof material that sulfuric acid, vitriol are formed, its feature is divided into two components, generates water-fast crystal with the hydrated product of cement, and colloid and complex compound stop up leak paths, thereby reach the waterproof purpose.
2. water-proof material according to claim 1 is characterized in that, this material use diffusion, dissemination are penetrated in the cement structures of buildings, generates water-fast material.
3. water-proof material according to claim 1 is characterized in that resultant is more water-fast after overpickling, and unnecessary vitriol is penetrated in the cement structures no longer unceasingly, can not expand the rimose situation.
4. water-proof material according to claim 1 is characterized in that, is used for spreading defending between the kitchen of floor tile, and this material can drain to cement structures inside by the floor brickwork joint, does not need to pound floor tile again.