CN114164954A - 一种带有气凝胶的防火阻燃岩棉保温材料 - Google Patents
一种带有气凝胶的防火阻燃岩棉保温材料 Download PDFInfo
- Publication number
- CN114164954A CN114164954A CN202111573685.5A CN202111573685A CN114164954A CN 114164954 A CN114164954 A CN 114164954A CN 202111573685 A CN202111573685 A CN 202111573685A CN 114164954 A CN114164954 A CN 114164954A
- Authority
- CN
- China
- Prior art keywords
- rock wool
- layer
- aerogel
- fireproof
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种带有气凝胶的防火阻燃岩棉保温材料，包括外壳面板，所述外壳面板的内壁固定连接有支撑杆，所述外壳面板内壁的一侧设置有防火层，所述防火层的一侧至少设置有第一岩棉层和第二岩棉层，所述第一岩棉层与第二岩棉层之间设置有气凝胶混合层，本发明涉及保温材料技术领域。该种带有气凝胶的防火阻燃岩棉保温材料，通过在岩棉板材中加入带有气凝胶的混合层，降低了导热系数，从而能够降低保温板的厚度；同时加入了防火层，在遇到火灾时能够有效的阻止火势的蔓延，整体结构便于组装，解决了现有的岩棉板保温性能较差的问题，提高了保温性。
Description
技术领域
本发明涉及保温材料技术领域，具体为一种带有气凝胶的防火阻燃岩棉保温材料。
背景技术
目前常用的墙体保温材料主要分为无机和有机两类，有机材料质量轻，保温、隔热效果好，但其最大的缺陷是防火安全性差，易燃烧，且燃烧时烟雾大、毒性大、使用安全性不如无机保温材料。无机保温材料防火性能好，且不具毒性，其应用范围越来越广泛。岩棉板作为无机保温材料的一种，广泛应用于建筑外墙，起到保温、隔热、吸音、降噪作用。但现有的岩棉板导热系数偏高，为了提高保温性能只能增加岩棉板的厚度，因此增加了成本。气凝胶是固体物质中导热系数最低的材料，仅仅略高于真空，大约为0.013W/m·K，因此气凝胶是世界上保温效果最好的保温材料。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种带有气凝胶的防火阻燃岩棉保温材料，解决了现有的岩棉板保温性能较差的问题，提高了保温性。
(二)技术方案
为实现以上目的，本发明通过以下技术方案予以实现：一种带有气凝胶的防火阻燃岩棉保温材料，包括外壳面板，所述外壳面板的内壁固定连接有支撑杆，所述外壳面板内壁的一侧设置有防火层，所述防火层的一侧至少设置有第一岩棉层和第二岩棉层，所述第一岩棉层与第二岩棉层之间设置有气凝胶混合层。
优选的，所述第一岩棉层、气凝胶混合层和第二岩棉层的表面设置有与支撑杆适配的孔，所述支撑杆的一端设置有盖板，所述盖板通过螺栓与支撑杆固定连接。
优选的，所述支撑杆的中部设置有固定孔，所述固定孔延伸至外壳面板的表面。
优选的，所述外壳面板采用防火板。
优选的，所述气凝胶混合层的原材料包括以下组分：二氧化硅气凝胶30-80份、岩棉纤维10-30份、珍珠岩粉末5-15份、石膏粉末3-9份、玻璃纤维6-13份、表面活性剂3-10份、去离子水20-50份、改性剂4-16份。
优选的，所述气凝胶混合层的制备包括以下步骤：
S1：将岩棉纤维、珍珠岩粉末、石膏粉末、玻璃纤维和去离子水按照组分量投入搅拌机中搅拌5-10分钟，搅拌过程中加入部分表面活性剂；
S2：将二氧化硅气凝胶投入到搅拌好的混合溶液中继续搅拌15-40分钟，搅拌过程中加入剩余的表面活性剂和改性剂；
S3：将搅拌所得的搅拌物放入板材模具中，在60-90℃下烘干15-40小时，随后脱模，即得到气凝胶混合层板；
S4：按照预设的尺寸进行切割钻孔。
优选的，所述第一岩棉层和第二岩棉层为岩棉板。
优选的，所述防火层包括玻璃纤维和阻燃剂，所述阻燃剂储藏于玻璃纤维间的缝隙里。
优选的，所述第一岩棉层和第二岩棉层与气凝胶混合层之间采用粘接剂固定，所述第一岩棉层、气凝胶混合层和第二岩棉层与支撑杆之间填充有发泡剂。
优选的，所述外壳面板的表面设置有防水层。
(三)有益效果
本发明提供了一种带有气凝胶的防火阻燃岩棉保温材料。具备以下有益效果：
该种带有气凝胶的防火阻燃岩棉保温材料，通过在岩棉板材中加入带有气凝胶的混合层，降低了导热系数，从而能够降低保温板的厚度；同时加入了防火层，在遇到火灾时能够有效的阻止火势的蔓延，整体结构便于组装。
附图说明
图1为本发明保温材料的截面图；
图2为本发明外壳面板与支撑杆的示意图。
图中：1-外壳面板、2-支撑杆、3-防火层、4-第一岩棉层、5-气凝胶混合层、6-第二岩棉层、7-盖板、8-防水层、9-螺栓、10-固定孔。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
请参阅图1-2，本发明提供以下技术方案：
实施例一：
一种带有气凝胶的防火阻燃岩棉保温材料，包括外壳面板1，外壳面板1采用防火板，外壳面板1的内壁固定连接有支撑杆2，支撑杆2可通过粘接剂与外壳面板1固定，也可采用螺栓固定的方式，外壳面板1的表面设置有防水层8，提高外壳面板1的防水性，外壳面板1内壁的一侧设置有防火层3，防火层3包括玻璃纤维和阻燃剂，阻燃剂储藏于玻璃纤维间的缝隙里，通过阻燃剂的设置，在外壳面板1发生燃烧后，阻燃剂能够迅速发挥作用，阻止火势的进一步蔓延；
防火层3的一侧至少设置有第一岩棉层4和第二岩棉层6，第一岩棉层4与第二岩棉层6之间设置有气凝胶混合层5，第一岩棉层4和第二岩棉层6为岩棉板。
第一岩棉层4和第二岩棉层6与气凝胶混合层5之间采用粘接剂固定，第一岩棉层4、气凝胶混合层5和第二岩棉层6与支撑杆2之间填充有发泡剂，第一岩棉层4、气凝胶混合层5和第二岩棉层6的表面设置有与支撑杆2适配的孔，支撑杆2的一端设置有盖板7，盖板7通过螺栓9与支撑杆2固定连接，在组装该保温材料时，首先在外壳面板1内壁铺上一层玻璃纤维，随后均匀撒上一层阻燃剂，压实后，依次放入第一岩棉层4、气凝胶混合层5和第二岩棉层6，并在气凝胶混合层5的两侧涂抹粘接剂，随后将盖板7对准支撑杆2并用螺栓9固定。
支撑杆2的中部设置有固定孔10，固定孔10延伸至外壳面板1的表面，便于通过固定孔10将保温材料固定在墙面。
气凝胶混合层5的原材料包括以下组分：二氧化硅气凝胶30份、岩棉纤维10份、珍珠岩粉末5份、石膏粉末3份、玻璃纤维6份、表面活性剂3份、去离子水20份、改性剂4份，改性剂采用硅烷偶联剂KH550，表面活性剂为吐温80。
所述气凝胶混合层5的制备包括以下步骤：
S1：将岩棉纤维、珍珠岩粉末、石膏粉末、玻璃纤维和去离子水按照组分量投入搅拌机中搅拌5分钟，搅拌过程中加入部分表面活性剂；
S2：将二氧化硅气凝胶投入到搅拌好的混合溶液中继续搅拌15分钟，搅拌过程中加入剩余的表面活性剂和改性剂；
S3：将搅拌所得的搅拌物放入板材模具中，在60℃下烘干15小时，随后脱模，即得到气凝胶混合层板；
S4：按照预设的尺寸进行切割钻孔。
实施例二：
与实施例一不同点在于：
所述气凝胶混合层5原材料包括以下组分：二氧化硅气凝胶80份、岩棉纤维30份、珍珠岩粉末15份、石膏粉末9份、玻璃纤维13份、表面活性剂10份、去离子水50份、改性剂16份。
气凝胶混合层5的制备包括以下步骤：
S1：将岩棉纤维、珍珠岩粉末、石膏粉末、玻璃纤维和去离子水按照组分量投入搅拌机中搅拌10分钟，搅拌过程中加入部分表面活性剂；
S2：将二氧化硅气凝胶投入到搅拌好的混合溶液中继续搅拌40分钟，搅拌过程中加入剩余的表面活性剂和改性剂；
S3：将搅拌所得的搅拌物放入板材模具中，在90℃下烘干40小时，随后脱模，即得到气凝胶混合层板；
S4：按照预设的尺寸进行切割钻孔。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。在没有更多限制的情况下，由语句“包括一个......”限定的要素，并不排除在包括所述要素的过程、方法、物品或者设备中还存在另外的相同要素。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (10)
1.一种带有气凝胶的防火阻燃岩棉保温材料，其特征在于：包括外壳面板(1)，所述外壳面板(1)的内壁固定连接有支撑杆(2)，所述外壳面板(1)内壁的一侧设置有防火层(3)，所述防火层(3)的一侧至少设置有第一岩棉层(4)和第二岩棉层(6)，所述第一岩棉层(4)与第二岩棉层(6)之间设置有气凝胶混合层(5)。
2.根据权利要求1所述的一种带有气凝胶的防火阻燃岩棉保温材料，其特征在于：所述第一岩棉层(4)、气凝胶混合层(5)和第二岩棉层(6)的表面设置有与支撑杆(2)适配的孔，所述支撑杆(2)的一端设置有盖板(7)，所述盖板(7)通过螺栓(9)与支撑杆(2)固定连接。
3.根据权利要求1所述的一种带有气凝胶的防火阻燃岩棉保温材料，其特征在于：所述支撑杆(2)的中部设置有固定孔(10)，所述固定孔(10)延伸至外壳面板(1)的表面。
4.根据权利要求1所述的一种带有气凝胶的防火阻燃岩棉保温材料，其特征在于：所述外壳面板(1)采用防火板。
5.根据权利要求1所述的一种带有气凝胶的防火阻燃岩棉保温材料，其特征在于：所述气凝胶混合层(5)的原材料包括以下组分：二氧化硅气凝胶30-80份、岩棉纤维10-30份、珍珠岩粉末5-15份、石膏粉末3-9份、玻璃纤维6-13份、表面活性剂3-10份、去离子水20-50份、改性剂4-16份。
6.根据权利要求5所述的一种带有气凝胶的防火阻燃岩棉保温材料，其特征在于：所述气凝胶混合层(5)的制备包括以下步骤：
S1：将岩棉纤维、珍珠岩粉末、石膏粉末、玻璃纤维和去离子水按照组分量投入搅拌机中搅拌5-10分钟，搅拌过程中加入部分表面活性剂；
S2：将二氧化硅气凝胶投入到搅拌好的混合溶液中继续搅拌15-40分钟，搅拌过程中加入剩余的表面活性剂和改性剂；
S3：将搅拌所得的搅拌物放入板材模具中，在60-90℃下烘干15-40小时，随后脱模，即得到气凝胶混合层板；
S4：按照预设的尺寸进行切割钻孔。
7.根据权利要求1所述的一种带有气凝胶的防火阻燃岩棉保温材料，其特征在于：所述第一岩棉层(4)和第二岩棉层(6)为岩棉板。
8.根据权利要求1所述的一种带有气凝胶的防火阻燃岩棉保温材料，其特征在于：所述防火层(3)包括玻璃纤维和阻燃剂，所述阻燃剂储藏于玻璃纤维间的缝隙里。
9.根据权利要求1所述的一种带有气凝胶的防火阻燃岩棉保温材料，其特征在于：所述第一岩棉层(4)和第二岩棉层(6)与气凝胶混合层(5)之间采用粘接剂固定，所述第一岩棉层(4)、气凝胶混合层(5)和第二岩棉层(6)与支撑杆(2)之间填充有发泡剂。
10.根据权利要求4所述的一种带有气凝胶的防火阻燃岩棉保温材料，其特征在于：所述外壳面板(1)的表面设置有防水层(8)。