CN114150892A - 一种利用抗冻融涂料修复古城墙的方法 - Google Patents
一种利用抗冻融涂料修复古城墙的方法 Download PDFInfo
- Publication number
- CN114150892A CN114150892A CN202210005626.6A CN202210005626A CN114150892A CN 114150892 A CN114150892 A CN 114150892A CN 202210005626 A CN202210005626 A CN 202210005626A CN 114150892 A CN114150892 A CN 114150892A
- Authority
- CN
- China
- Prior art keywords
- freeze
- coated
- resistant coating
- area
- reaction kettle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种利用抗冻融涂料修复古城墙的方法，包括如下步骤：首先准备异丁基三乙氧基硅烷、甲基三甲氧基硅烷、碳化硅、增稠剂、稳定剂以及交联剂；各类原料混合制出抗冻融涂料；确定涂料涂抹区域，擦拭待涂抹区域城墙砖、去除城墙砖孔隙内部杂物，随后等待待涂抹区域风干，确保其干燥；将制备完毕的抗冻融涂料均匀的涂抹在待涂抹区域，在基材表面形成憎水区域，如果砖体结构保持干燥就可以有效避免破坏；该一种利用抗冻融涂料修复古城墙的方法通过由异丁基三乙氧基硅烷、甲基三甲氧基硅烷、碳化硅、增稠剂、稳定剂以及交联剂制备而来的抗冻融涂料，能够对古城墙进行更加有效的修复操作。
Description
技术领域
本发明涉及城墙防护技术领域，具体为一种利用抗冻融涂料修复古城墙的方法。
背景技术
北方地区冬天的冰雪和夏天的雨水对城墙破坏很大，大部分城墙都没有好的办法解决城墙的抗冻融问题，随着城墙因为冻融而产生的破坏问题越来越多，提高城墙砖的抗冻融性能成为了城墙防护的重中之重，城砖的破坏总是与潮气和水有关，当城砖与水接触时，会有大量水进入砖体内，吸水量取决于其孔隙率，随着城砖吸水量的增加，会对城砖造成以下多种结构性的破坏。
现有技术存在以下缺陷或问题：
现有的古城墙易受到：氯化物、化学腐蚀、冻融、水化和结晶造成的盐析、泛碱、沾污、真菌、苔藓、地衣和藻类的孳生因素的破坏。
发明内容
本发明的目的在于针对现有技术的不足之处，提供一种利用抗冻融涂料修复古城墙的方法，以解决背景技术中所提出的问题。
为实现上述目的，本发明提供如下技术方案：一种利用抗冻融涂料修复古城墙的方法，包括以下步骤
步骤一：首先准备异丁基三乙氧基硅烷、甲基三甲氧基硅烷、碳化硅、增稠剂、稳定剂以及交联剂；
步骤二：向反应釜中加入稳定剂，使得其在1000-2000rpm的转速下进行均匀的搅拌；
步骤三：向反应釜中加入增稠剂，并将反应釜转速提示至2500rpm，然后再向反应釜内部加入甲基三甲氧基硅烷；
步骤四：向反应釜中加入碳化硅颗粒，高速分散20分钟；
步骤五：向反应釜中加入交联剂，分散均匀，即可得到抗冻融涂料；
步骤五：确定涂料涂抹区域，擦拭待涂抹区域城墙砖、去除城墙砖孔隙内部杂物，随后等待待涂抹区域风干，确保其干燥；
步骤六：将制备完毕的抗冻融涂料均匀的涂抹在待涂抹区域，在基材表面形成憎水区域，如果砖体结构保持干燥就可以有效避免破坏。
作为本发明的优选技术方案，包括以下重量份数配比的原料：异丁基三乙氧基硅烷40-50％，甲基三甲氧基硅烷30-35％，碳化硅4-5％，增稠剂0.2％，稳定剂10-15％，交联剂4-5％，碳化硅为洛克伍德1958，稳定剂为无水乙醇，交联剂为硅酸乙酯。
与现有技术相比，本发明提供了一种利用抗冻融涂料修复古城墙的方法，具备以下有益效果：
1、该一种利用抗冻融涂料修复古城墙的方法，通过由异丁基三乙氧基硅烷、甲基三甲氧基硅烷、碳化硅、增稠剂、稳定剂以及交联剂制备而来的抗冻融涂料，经过冻融试验，在-20摄氏度的环境下，可抗冻融3H，在20摄氏度的环境下，可在水中浸泡2h，具备良好的抗冻融效果的同时环境适应力更强，能够起到更好的防护作用，能够大幅降低城墙的氯离子吸收率和吸水量；保持城墙砖块的透气性；提供极佳的抗冻融循环保护；具备优异的耐碱性、良好的渗透性和附着力以及良好的抗紫外线性能；城墙表面不会发亮、回粘或黄变；该涂料使用安全、环保，不会对环境造成影响；
2、该一种利用抗冻融涂料修复古城墙的方法，修复过程中，对城墙砖砖缝处进行清理、风干，再进行涂匀工作，能够确保被修复古城墙能够更好的应对外界因素的影响。
具体实施方式
下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本实施方案中：其修复方法如下：步骤一：首先准备异丁基三乙氧基硅烷、甲基三甲氧基硅烷、碳化硅、增稠剂、稳定剂以及交联剂；
步骤二：向反应釜中加入稳定剂，使得其在1000-2000rpm的转速下进行均匀的搅拌；
步骤三：向反应釜中加入增稠剂，并将反应釜转速提示至2500rpm，然后再向反应釜内部加入甲基三甲氧基硅烷；
步骤四：向反应釜中加入碳化硅颗粒，高速分散20分钟；
步骤五：向反应釜中加入交联剂，分散均匀，即可得到抗冻融涂料；
步骤五：确定涂料涂抹区域，擦拭待涂抹区域城墙砖、去除城墙砖孔隙内部杂物，随后等待待涂抹区域风干，确保其干燥；
步骤六：将制备完毕的抗冻融涂料均匀的涂抹在待涂抹区域，在基材表面形成憎水区域，如果砖体结构保持干燥就可以有效避免破坏。
综上，抗冻融涂料，包括以下重量份数配比的原料：异丁基三乙氧基硅烷40-50％，甲基三甲氧基硅烷30-35％，碳化硅4-5％，增稠剂0.2％，稳定剂10-15％，交联剂4-5％，碳化硅为洛克伍德1958，稳定剂为无水乙醇，交联剂为硅酸乙酯。
本发明的工作原理及使用流程：首先准备异丁基三乙氧基硅烷、甲基三甲氧基硅烷、碳化硅、增稠剂、稳定剂以及交联剂；随后向反应釜中加入稳定剂，使得其在1000-2000rpm的转速下进行均匀的搅拌；搅拌完毕后向反应釜中加入增稠剂，并将反应釜转速提示至2500rpm，然后再向反应釜内部加入甲基三甲氧基硅烷；待反应釜内部原料充分混合后，向反应釜中加入碳化硅颗粒，高速分散20分钟；最后向反应釜中加入交联剂，分散均匀，即可得到抗冻融涂料；工作人员首先确定涂料涂抹区域，擦拭待涂抹区域城墙砖、去除城墙砖孔隙内部杂物，随后等待待涂抹区域风干，确保其干燥；之后将制备完毕的抗冻融涂料均匀的涂抹在待涂抹区域，在基材表面形成憎水区域，如果砖体结构保持干燥就可以有效避免破坏。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (2)
1.一种利用抗冻融涂料修复古城墙的方法，其特征在于：所述包括以下步骤
步骤一：首先准备异丁基三乙氧基硅烷、甲基三甲氧基硅烷、碳化硅、增稠剂、稳定剂以及交联剂；
步骤二：向反应釜中加入稳定剂，使得其在1000-2000rpm的转速下进行均匀的搅拌；
步骤三：向反应釜中加入增稠剂，并将反应釜转速提示至2500rpm，然后再向反应釜内部加入甲基三甲氧基硅烷；
步骤四：向反应釜中加入碳化硅颗粒，高速分散20分钟；
步骤五：向反应釜中加入交联剂，分散均匀，即可得到抗冻融涂料；
步骤五：确定涂料涂抹区域，擦拭待涂抹区域城墙砖、去除城墙砖孔隙内部杂物，随后等待待涂抹区域风干，确保其干燥；
步骤六：将制备完毕的抗冻融涂料均匀的涂抹在待涂抹区域，在基材表面形成憎水区域，如果砖体结构保持干燥就可以有效避免破坏。
2.根据权利要求1步骤一所述的一种利用抗冻融涂料修复古城墙的方法，其特征在于：包括以下重量份数配比的原料：异丁基三乙氧基硅烷40-50％，甲基三甲氧基硅烷30-35％，碳化硅4-5％，增稠剂0.2％，稳定剂10-15％，交联剂4-5％，碳化硅为洛克伍德1958，稳定剂为无水乙醇，交联剂为硅酸乙酯。