CN114132028A - Preparation method of plastic decorative sheet capable of purifying air for a long time - Google Patents
Preparation method of plastic decorative sheet capable of purifying air for a long time Download PDFInfo
- Publication number
- CN114132028A CN114132028A CN202111622726.5A CN202111622726A CN114132028A CN 114132028 A CN114132028 A CN 114132028A CN 202111622726 A CN202111622726 A CN 202111622726A CN 114132028 A CN114132028 A CN 114132028A
- Authority
- CN
- China
- Prior art keywords
- preparing
- decorative sheet
- plastic decorative
- purifying air
- sheet capable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a plastic decorative sheet capable of purifying air for a long time, which belongs to the technical field of plastic decorative sheet preparation and comprises the following steps: (1) preparing a base film, (2) preparing a functional coating, (3) preparing a functional patch, and (4) preparing a finished product. The invention provides a preparation method of a plastic decorative sheet capable of purifying air for a long time, the method has simple integral process and easy popularization and application, and the prepared plastic decorative sheet not only can play a traditional effect of beautifying and decorating, but also can continuously decompose various harmful substances such as formaldehyde, toluene, sulfur dioxide, TVOC and the like so as to achieve the purpose of purifying indoor air; meanwhile, the antibacterial and bacteriostatic agent can also inhibit the growth of various bacteria such as escherichia coli, staphylococcus aureus, candida albicans and the like, and has the effects of resisting and inhibiting bacteria and no mildew for a long time; provides a living environment with fresh and clean air for people.
Description
Technical Field
The invention belongs to the technical field of plastic decorative sheet preparation, and particularly relates to a preparation method of a plastic decorative sheet capable of purifying air for a long time.
Background
The plastic decorative sheet is widely applied to the field of home decoration such as wallpaper, wall panels, wardrobes and the like due to exquisite printing and rich patterns and colors, can play a role in beautifying the home, but cannot remove harmful substances such as formaldehyde, toluene, TVOC and the like continuously emitted by indoor decoration materials, and cannot meet the requirements of people on health.
Disclosure of Invention
The invention aims to provide a preparation method of a plastic decorative sheet capable of purifying air for a long time.
The technical purpose of the invention is realized by the following technical scheme:
a preparation method of plastic decorative sheet capable of purifying air for a long time comprises the following steps:
(1) preparing a base film:
printing patterns on the plastic base material film by using a printer to obtain a base film for later use;
(2) preparing a functional coating:
mixing rare earth, nano filler, polyurethane and water to prepare functional coating for later use;
(3) preparing functional dough sheets:
uniformly coating the functional coating prepared in the step (2) on a plastic dough sheet by using a coating machine, and obtaining a functional dough sheet for later use after finishing;
(4) and (3) preparing a finished product:
and (3) compounding and embossing the base film prepared in the step (1) and the functional patch prepared in the step (3) by using a compounding machine, and obtaining a finished product after finishing.
Further, the printing machine in the step (1) adopts a five-color gravure printing machine.
Further, the corresponding weight ratio of the rare earth, the nano filler, the polyurethane and the water in the step (2) is 2-4: 20-25: 10-15: 280 to 300.
Further, the rare earth in the step (2) is any one of lanthanum oxide, cerium oxide and yttrium nitrate.
Further, the nano filler in the step (2) is a mixture of nano titanium dioxide and nano silicon dioxide, and the weight ratio of the nano titanium dioxide to the nano silicon dioxide is 2-3: 1.
further, the speed of the control host machine of the coating machine in the step (3) is not less than 20m/min when the coating machine works; and the baking temperature is controlled to be 80 ℃.
Compared with the prior art, the invention has the following advantages:
the invention provides a preparation method of a plastic decorative sheet capable of purifying air for a long time, the method has simple integral process and easy popularization and application, and the prepared plastic decorative sheet not only can play a traditional effect of beautifying and decorating, but also can continuously decompose various harmful substances such as formaldehyde, toluene, sulfur dioxide, TVOC and the like so as to achieve the purpose of purifying indoor air; meanwhile, the antibacterial and bacteriostatic agent can also inhibit the growth of various bacteria such as escherichia coli, staphylococcus aureus, candida albicans and the like, and has the effects of resisting and inhibiting bacteria and no mildew for a long time; provides a living environment with fresh and clean air for people. Has high market competitiveness and production value.
Detailed Description
Example 1
A preparation method of plastic decorative sheet capable of purifying air for a long time comprises the following steps:
(1) preparing a base film:
printing patterns on the plastic base material film by using a printer to obtain a base film for later use;
(2) preparing a functional coating:
mixing rare earth, nano filler, polyurethane and water to prepare functional coating for later use;
(3) preparing functional dough sheets:
uniformly coating the functional coating prepared in the step (2) on a plastic dough sheet by using a coating machine, and obtaining a functional dough sheet for later use after finishing;
(4) and (3) preparing a finished product:
and (3) compounding and embossing the base film prepared in the step (1) and the functional patch prepared in the step (3) by using a compounding machine, and obtaining a finished product after finishing.
The printing machine in the step (1) adopts a five-color gravure printing machine.
The corresponding weight ratio of the rare earth, the nano filler, the polyurethane and the water in the step (2) is 2: 20: 10: 280.
the rare earth is lanthanum oxide.
The nano filler is a mixture of nano titanium dioxide and nano silicon dioxide, and the weight ratio of the nano titanium dioxide to the nano silicon dioxide is 2: 1.
when the coating machine in the step (3) works, controlling the speed of the host machine to be not less than 20 m/min; and the baking temperature is controlled to be 80 ℃.
Example 2
A preparation method of plastic decorative sheet capable of purifying air for a long time comprises the following steps:
(1) preparing a base film:
printing patterns on the plastic base material film by using a printer to obtain a base film for later use;
(2) preparing a functional coating:
mixing rare earth, nano filler, polyurethane and water to prepare functional coating for later use;
(3) preparing functional dough sheets:
uniformly coating the functional coating prepared in the step (2) on a plastic dough sheet by using a coating machine, and obtaining a functional dough sheet for later use after finishing;
(4) and (3) preparing a finished product:
and (3) compounding and embossing the base film prepared in the step (1) and the functional patch prepared in the step (3) by using a compounding machine, and obtaining a finished product after finishing.
The printing machine in the step (1) adopts a five-color gravure printing machine.
The corresponding weight ratio of the rare earth, the nano filler, the polyurethane and the water in the step (2) is 3: 23: 12: 290.
the rare earth is cerium oxide.
The nano filler is a mixture of nano titanium dioxide and nano silicon dioxide, and the weight ratio of the nano titanium dioxide to the nano silicon dioxide is 2.5: 1.
when the coating machine in the step (3) works, controlling the speed of the host machine to be not less than 20 m/min; and the baking temperature is controlled to be 80 ℃.
Example 3
A preparation method of plastic decorative sheet capable of purifying air for a long time comprises the following steps:
(1) preparing a base film:
printing patterns on the plastic base material film by using a printer to obtain a base film for later use;
(2) preparing a functional coating:
mixing rare earth, nano filler, polyurethane and water to prepare functional coating for later use;
(3) preparing functional dough sheets:
uniformly coating the functional coating prepared in the step (2) on a plastic dough sheet by using a coating machine, and obtaining a functional dough sheet for later use after finishing;
(4) and (3) preparing a finished product:
and (3) compounding and embossing the base film prepared in the step (1) and the functional patch prepared in the step (3) by using a compounding machine, and obtaining a finished product after finishing.
The printing machine in the step (1) adopts a five-color gravure printing machine.
The corresponding weight ratio of the rare earth, the nano filler, the polyurethane and the water in the step (2) is 4: 25: 15: 300.
the rare earth is yttrium nitrate.
The nano filler is a mixture of nano titanium dioxide and nano silicon dioxide, and the weight ratio of the nano titanium dioxide to the nano silicon dioxide is 3: 1.
when the coating machine in the step (3) works, controlling the speed of the host machine to be not less than 20 m/min; and the baking temperature is controlled to be 80 ℃.
The plastic decorative sheet provided by the invention is tested for antibacterial performance by adopting the GB/T31402-2015 standard, and the antibacterial rate of the plastic decorative sheet to escherichia coli is not lower than 99.9%, the antibacterial rate to staphylococcus aureus is not lower than 99.8%, and the antibacterial rate to candida albicans is not lower than 95.1%.
The plastic decorative sheet is subjected to toluene purification performance detection according to the standard of JC/T1074-2008, and the durability of the purification effect under the experimental condition is not lower than 63.0 percent; detecting the formaldehyde purification performance, and finding that the durability of the purification effect under the experimental condition is not lower than 86.3%; and detecting the purification performance of the sulfur dioxide, and finding that the durability of the purification effect under the experimental condition is not lower than 91.4%.
Therefore, the plastic decorative sheet prepared by the method has good use and popularization values.
The foregoing is only a preferred embodiment of the present invention, and it should be noted that modifications can be made by those skilled in the art without departing from the principle of the present invention, and these modifications should also be construed as the protection scope of the present invention.
Claims (6)
1. The preparation method of the plastic decorative sheet capable of purifying air for a long time is characterized by comprising the following steps:
(1) preparing a base film:
printing patterns on the plastic base material film by using a printer to obtain a base film for later use;
(2) preparing a functional coating:
mixing rare earth, nano filler, polyurethane and water to prepare functional coating for later use;
(3) preparing functional dough sheets:
uniformly coating the functional coating prepared in the step (2) on a plastic dough sheet by using a coating machine, and obtaining a functional dough sheet for later use after finishing;
(4) and (3) preparing a finished product:
and (3) compounding and embossing the base film prepared in the step (1) and the functional patch prepared in the step (3) by using a compounding machine, and obtaining a finished product after finishing.
2. The method for preparing plastic decorative sheet capable of permanently purifying air according to claim 1, wherein the printing machine in the step (1) is a five-color gravure printing machine.
3. The method for preparing plastic decorative sheet capable of purifying air permanently according to claim 1, wherein the weight ratio of the rare earth, the nano filler, the polyurethane and the water in the step (2) is 2-4: 20-25: 10-15: 280 to 300.
4. The method for preparing plastic decorative sheet capable of purifying air permanently as claimed in claim 1, wherein the rare earth in step (2) is any one of lanthanum oxide, cerium oxide and yttrium nitrate.
5. The method for preparing plastic decorative sheet capable of purifying air permanently as claimed in claim 1, wherein the nano filler in step (2) is a mixture of nano titanium dioxide and nano silica, and the weight ratio of the nano titanium dioxide to the nano silica is 2-3: 1.
6. the method for preparing plastic decorative sheet capable of permanently purifying air according to claim 1, wherein the speed of the main control machine in the operation of the coating machine in the step (3) is not less than 20 m/min; and the baking temperature is controlled to be 80 ℃.