CN114106598A - 一种抗菌抗病毒吸附二氧化碳特种涂料 - Google Patents
一种抗菌抗病毒吸附二氧化碳特种涂料 Download PDFInfo
- Publication number
- CN114106598A CN114106598A CN202111488395.0A CN202111488395A CN114106598A CN 114106598 A CN114106598 A CN 114106598A CN 202111488395 A CN202111488395 A CN 202111488395A CN 114106598 A CN114106598 A CN 114106598A
- Authority
- CN
- China
- Prior art keywords
- carbon dioxide
- particle size
- powder
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种抗菌抗病毒吸附二氧化碳特种涂料,属于涂料技术领域。解决了现有技术中内墙涂料的净化空气的效果有待进一步提高,且在湿度较高的情况下,密闭墙壁表面会发生结露,导致黑霉和细菌滋生的问题。本发明的涂料,组成为硅藻土、硅胶、氢氧化钙粉、石墨烯颗粒、二氧化钛粉、羟乙基纤维素粉、膨润土、纳米壳聚糖、可再分散性乳胶粉、介孔SiO2包覆的银纳米颗粒、消泡剂和去离子水。该涂料可以有效吸收二氧化碳,降低室内的二氧化碳浓度,吸附游离甲醛、苯、氨、氡、TVOC等有毒物质,适用于室内墙面的大面积涂装,改善居室环境,且杀菌,消毒,不易产生黑霉和细菌。
Description
技术领域
本发明属于涂料技术领域,具体涉及一种抗菌抗病毒吸附二氧化碳特种涂料。
背景技术
随着经济的发展和人民生活水平的提高,各种原料制成的建筑装饰材料已走入家庭。而建筑材料、家具、人造板材、各种黏合剂和合成纺织品等等建筑装饰材料皆会释放出甲醛。甲醛可与蛋白质反应生成氮次甲基化合物而使细胞中的蛋白质凝固变性,因而可抑制细胞机能。此外,甲醛还能和空气中的离子性氯化物反应生成二氯甲基醚,而后者是一种致癌物质。根据我国《室内空气质量标准》(GB/T 18883-2002)规定室内空气中甲醛的含量限值为0.10mg/m,其适用范围为住宅和办公建筑物,其他室内环境可参照该标准执行。室内甲醛污染物的含量标准对于弱势人群具有更为重要的意义。对于老人、儿童、孕妇、病人等弱势人群来说,受到甲醛危害远大于一般人群,所以有弱势群体居住时,室内甲醛含量的值最好控制为更低的范围内,因此室内甲醛含量至少保持在0.10mg/m以下才算是正常的。人体在不同浓度的甲醛环境中会有不良反应,当甲醛浓度在空气中达到0.06mg/m-0.07mg/m时,儿童就会发生轻微气喘;当室内空气中甲醛浓度达到0.1mg/m时,就会有异味和不适感;当室内空气中甲醛浓度达到0.5mg/m时,可刺激眼睛引起流泪;当室内空气中甲醛浓度达到0.6mg/m时,会引起咽喉不适或疼痛;当室内空气中甲醛浓度更高时,可引起恶心呕吐、咳嗽、胸闷、气喘甚至肺水肿;当室内空气中甲醛浓度达到30mg/m时,会立即致人死亡。此外,甲醛在室内的挥发期长达3-15年,甲醛可被室内的高比表面材料吸附富集,当室内温度升高时又重新释放出来,加剧污染效应。
此外,当人们长期吸入浓度过高的二氧化碳时,会造成人体生物钟紊乱,高浓度的二氧化碳会抑制呼吸中枢,浓度特别高会对呼吸中枢有麻痹作用,长期以往人们会有气血虚弱、低血脂等症状,而且大脑特别容易疲劳,严重影响生活和工作,如上班族会感觉工作力不从心,学生学习无法集中注意力。室内二氧化碳浓度在700ppm以下时属于清洁空气,人们会感觉舒适,当浓度在700ppm到1000ppm也还算正常,属于一般的空气质量,有些敏感人士会感觉不太好,当二氧化碳浓度超过1000ppm,但在1500ppm范围时空气属于临界阶段,大多数人都会有不舒适的感觉。
高效持久地净化室内有害气体,保持清新健康的生活、工作环境成了人们越来越迫切追求的目标。现有技术中,多采用带有吸附功能的内墙涂料解决这一问题,但是其净化空气的效果有待进一步提高。且在冬季,当房间内因暖气等原因湿度变高时,密闭房间的墙壁表面或墙壁背面会发生结露,导致黑霉和细菌滋生。
发明内容
本发明的目的是提供一种抗菌抗病毒吸附二氧化碳特种涂料,解决现有技术中内墙涂料的净化空气的效果有待进一步提高,且在湿度较高的情况下,密闭墙壁表面会发生结露,导致黑霉和细菌滋生的问题。
为实现上述目的,本发明采用以下技术方案。
本发明提供一种抗菌抗病毒吸附二氧化碳特种涂料,组成为:
优选的是,所述硅藻土的粒径为700-1000目。
优选的是,所述硅胶的粒径为60-100微米,孔径为4-6nm。
优选的是,所述氢氧化钙粉的粒径为600-800目。
优选的是,所述石墨烯颗粒的粒径为50-80纳米。
优选的是,所述二氧化钛粉的粒径为20-50纳米。
优选的是,所述膨润土的粒径为200-400目。
优选的是,所述纳米壳聚糖的粒径为20-80纳米。
优选的是,所述可再分散性乳胶粉的粒径为20-50微米。
优选的是,所述消泡剂为有机硅消泡剂。
与现有技术相比,本发明的有益效果为:
本发明的抗菌抗病毒吸附二氧化碳特种涂料可以有效吸收二氧化碳,降低室内的二氧化碳浓度,吸附游离甲醛、苯、氨、氡、TVOC等有毒重金属有害物质,适用于室内墙面的大面积涂装,改善居室环境,且杀菌,消毒,不易产生黑霉和细菌。
具体实施方式
为了进一步理解本发明,下面对本发明优选实施方案进行描述,但是应当理解,这些描述只是为进一步说明本发明的特征和优点,而不是对本发明权利要求的限制。
本发明的抗菌抗病毒吸附二氧化碳特种涂料,组成为50-60重量份硅藻土、5-10重量份硅胶、4-5重量份氢氧化钙粉、1-2重量份石墨烯颗粒、2-3重量份二氧化钛粉、10-15重量份羟乙基纤维素粉、0.5-1重量份膨润土、5-8重量份纳米壳聚糖、3-8重量份可再分散性乳胶粉、2-3重量份介孔SiO2包覆的银纳米颗粒、0.5-1重量份消泡剂和40-50重量份去离子水。
上述技术方案中,硅藻土的粒径为700-1000目,没有特殊限制可采用本领域技术人员熟知方案获得;硅胶的粒径为60-100微米,孔径为4-6nm,没有特殊限制可采用本领域技术人员熟知方案获得;氢氧化钙粉的粒径为600-800目,没有特殊限制可采用本领域技术人员熟知方案获得;石墨烯颗粒的粒径为50-80纳米,没有特殊限制可采用本领域技术人员熟知方案获得;二氧化钛粉的粒径为20-50纳米,没有特殊限制可采用本领域技术人员熟知方案获得;膨润土的粒径为200-400目,没有特殊限制可采用本领域技术人员熟知方案获得;纳米壳聚糖的粒径为20-80纳米,没有特殊限制可采用本领域技术人员熟知方案获得;可再分散性乳胶粉的粒径为20-50微米,没有特殊限制可采用本领域技术人员熟知方案获得;消泡剂为有机硅消泡剂,没有特殊限制可采用本领域技术人员熟知方案获得,如BYK-141;羟乙基纤维素粉没有特殊限制可采用本领域技术人员熟知方案获得;介孔SiO2包覆的银纳米颗粒没有特殊限制可采用本领域技术人员熟知方案获得,如北京化工大学学报(自然科学报,第37卷第4期)介孔二氧化硅包覆银纳米颗粒的制备及抗菌性能。
本发明的抗菌抗病毒吸附二氧化碳特种涂料没有特殊限制,按重量份称取各组分,搅拌混合均匀即可。
本发明所有原料,对其来源没有特别限制,在市场上购买的或按照本领域技术人员熟知的常规方法制备即可。本发明所有原料,对其纯度没有特别限制,本发明优先选用分析纯。
在本发明中所使用的术语,一般具有本领域普通技术人员通常理解的含义,除非另有说明。为了使本领域的技术人员更好地理解本发明的技术方案,下面将结合实施例对本发明作进一步的详细介绍。
在以下实施例中,未详细描述的各种过程和方法是本领域中公知的常规方法。下述实施例中所用的材料、试剂、装置、仪器、设备等,如无特殊说明,均可从商业途径获得。
实施例1
抗菌抗病毒吸附二氧化碳特种涂料,组成为50重量份硅藻土(700目)、6重量份硅胶(粒径为60微米,孔径为4nm)、4重量份氢氧化钙粉(600目)、1重量份石墨烯颗粒(粒径为50纳米)、2.5重量份二氧化钛粉(20纳米)、11重量份羟乙基纤维素粉、0.7重量份膨润土(粒径为200目)、7重量份纳米壳聚糖(20纳米)、4重量份可再分散性乳胶粉(20微米)、2重量份介孔SiO2包覆的银纳米颗粒、0.8重量份消泡剂(BYK-141)和40重量份去离子水。
实施例2
抗菌抗病毒吸附二氧化碳特种涂料,组成为55重量份硅藻土(800目)、8重量份硅胶(粒径为100微米,孔径为6nm)、4.5重量份氢氧化钙粉(700目)、1.5重量份石墨烯颗粒(粒径为60纳米)、2重量份二氧化钛粉(30纳米)、13重量份羟乙基纤维素粉、0.9重量份膨润土(粒径为300目)、7重量份纳米壳聚糖(40纳米)、5重量份可再分散性乳胶粉(40微米)、3重量份介孔SiO2包覆的银纳米颗粒、0.8重量份消泡剂(BYK-141)和40重量份去离子水。
实施例3
抗菌抗病毒吸附二氧化碳特种涂料,组成为60重量份硅藻土(900目)、5重量份硅胶(粒径为90微米,孔径为4.5nm)、4重量份氢氧化钙粉(800目)、1.5重量份石墨烯颗粒(粒径为60纳米)、2.5重量份二氧化钛粉(35纳米)、13重量份羟乙基纤维素粉、0.7重量份膨润土(粒径为400目)、7重量份纳米壳聚糖(60纳米)、8重量份可再分散性乳胶粉(45微米)、3重量份介孔SiO2包覆的银纳米颗粒、1量份消泡剂(BYK-141)和50重量份去离子水。
实施例4
抗菌抗病毒吸附二氧化碳特种涂料,组成为58重量份硅藻土(1000目)、8重量份硅胶(粒径为90微米,孔径为5.5nm)、5重量份氢氧化钙粉(600目)、2重量份石墨烯颗粒(粒径为55纳米)、2.5重量份二氧化钛粉(35纳米)、11重量份羟乙基纤维素粉、0.6重量份膨润土(粒径为350目)、5重量份纳米壳聚糖(35纳米)、6重量份可再分散性乳胶粉(40微米)、2重量份介孔SiO2包覆的银纳米颗粒、1重量份消泡剂(BYK-141)和40-50重量份去离子水。
对实施例1-4的涂料的性能进行检测。
1.1吸附二氧化碳性能测试
将实施例1-4的涂料涂在水泥板上,室温放置72h固化,称量水泥板的重量后,再放置24h、48h、72h分别称量重量。检测结果如表1所示。
表1实施例1-4的涂料的吸附效果
从表1可以看出,本发明的抗菌抗病毒吸附二氧化碳特种涂料能够很好的吸附二氧化碳。
1.2净化效果
依据标准JC/T 1074-2008《室内空气净化功能涂覆材料净化性能》检测涂料的甲醛、甲苯净化效果。
涂刷量0.5kg/m2,试验条件:温度(20±2)℃,相对湿度(50±10)%,开灯时间:48h,检测结果如表2所示。
表2实施例1-4的涂料抗菌性检测
从表2可以看出,本发明的抗菌抗病毒吸附二氧化碳特种涂料具有很好的净化效果。符合标准JC/T 1074-2008《室内空气净化功能涂覆材料净化性能》中“I类材料”的技术指标要求。
1.3抗菌性检测
依据标准HG/T 3950-2007《抗菌涂料》检测涂料的甲醛、甲苯净化效果。
将样品按照适当的粉水比混合搅拌均匀,涂刷在5cm*5cm金属基材上,干燥7天后进行实验。实验步骤:步骤一、菌种活化:将保藏菌接种在营养琼脂培养基斜面上,在37℃条件下培养24h;步骤二、对照样品和试验样品放置在超净工作台内,紫外消毒30min;步骤三、菌悬液制备、接种、培养:刮下菌种,稀释至合适的浓度,将菌液滴加到样品表面,薄膜覆盖,培养24h后,冲洗,接种,培养,菌落计数,计算样品的抗细菌率。相对湿度49%,温度23℃。结果如表3所示。
表3实施例1-4的涂料抗菌性检测
项目 | 金黄色葡萄球菌% | 大肠杆菌% |
标准 | ≥90 | ≥90 |
实施例1 | 99.99 | 99.99 |
实施例2 | 99.99 | 99.99 |
实施例3 | 99.99 | 99.99 |
实施例4 | 99.99 | 99.99 |
从表3可以看出,本发明的抗菌抗病毒吸附二氧化碳特种涂料具有很好的抗菌性。
1.4附着力测试
对实施例1-4的涂料的附着力进行检测,检测标准GB1720-79。经检测实施例1-4的涂料的附着力均为0级。
显然,上述实施方式仅仅是为清楚地说明所作的举例,而并非对实施例的限定。对于所属领域的普通技术人员来说,在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有实施例予以穷举。而由此所引申出的显而易见的变化或变动仍处于本发明创造的保护范围之中。
Claims (10)
2.根据权利要求1所述的一种抗菌抗病毒吸附二氧化碳特种涂料,其特征在于,所述硅藻土的粒径为700-1000目。
3.根据权利要求1所述的一种抗菌抗病毒吸附二氧化碳特种涂料,其特征在于,所述硅胶的粒径为60-100微米,孔径为4-6nm。
4.根据权利要求1所述的一种抗菌抗病毒吸附二氧化碳特种涂料,其特征在于,所述氢氧化钙粉的粒径为600-800目。
5.根据权利要求1所述的一种抗菌抗病毒吸附二氧化碳特种涂料,其特征在于,所述石墨烯颗粒的粒径为50-80纳米。
6.根据权利要求1所述的一种抗菌抗病毒吸附二氧化碳特种涂料,其特征在于,所述二氧化钛粉的粒径为20-50纳米。
7.根据权利要求1所述的一种抗菌抗病毒吸附二氧化碳特种涂料,其特征在于,所述膨润土的粒径为200-400目。
8.根据权利要求1所述的一种抗菌抗病毒吸附二氧化碳特种涂料,其特征在于,所述纳米壳聚糖的粒径为20-80纳米。
9.根据权利要求1所述的一种抗菌抗病毒吸附二氧化碳特种涂料,其特征在于,所述可再分散性乳胶粉的粒径为20-50微米。
10.根据权利要求1所述的一种抗菌抗病毒吸附二氧化碳特种涂料,其特征在于,所述消泡剂为有机硅消泡剂。