CN106833041A - 一种室内用除甲醛抗菌环保粉状涂料 - Google Patents

一种室内用除甲醛抗菌环保粉状涂料 Download PDF

Info

Publication number
CN106833041A
CN106833041A CN201710094372.9A CN201710094372A CN106833041A CN 106833041 A CN106833041 A CN 106833041A CN 201710094372 A CN201710094372 A CN 201710094372A CN 106833041 A CN106833041 A CN 106833041A
Authority
CN
China
Prior art keywords
friendlypowdery
indoor formaldehyde
powdery coating
removing antibiotic
environment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710094372.9A
Other languages
English (en)
Inventor
程艳青
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710094372.9A priority Critical patent/CN106833041A/zh
Publication of CN106833041A publication Critical patent/CN106833041A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种室内用除甲醛抗菌环保粉状涂料，以重量百分数计，包括如下原料组分：纳米银0.03～0.05％，壳聚糖0.3～1％，硅藻纯5～10％，锐钛钛白粉5～10％，重质碳酸钙30～45％，轻质碳酸氢钙25～35％，硫酸钡15～25％，余量为助剂。本发明所采用的原料均为环保无毒无污染材料，可有效抗菌且抗菌效力持久，能够自动吸附室内空气中的甲醛等有毒有害气体，净化效力持久且不会造成二次污染，其制备简单，包装、储存方便，适用于各种建筑室内装饰装修。

Description

一种室内用除甲醛抗菌环保粉状涂料
技术领域
本发明涉及涂料领域，具体地说，涉及一种室内用除甲醛抗菌环保粉状涂料。
背景技术
近年来，室内装修的安全性越来越受到人们的重视，尤其是环保型功能涂料的使用受到人们的追捧。目前市面上的除甲醛涂料主要添加活性炭成分，其吸附甲醛的持久性差，易达到吸附饱和，且吸附饱和后甲醛逸出会造成二次污染；现有的抗菌涂料中添加有机胺类、哌三嗪类、异噻唑啉酮类物质作为抗菌剂，其短期内抗菌效果明显，但耐久性差，耐温性差，紫外线下分解后还会产生有害物质。另外，液体涂料中添加的挥发性有机物挥发过程也会对室内空气造成污染。因此，亟需一种可持久净化空气且长效抗菌的环保涂料。
发明内容
基于现有技术的不足之处，本发明提供一种室内用除甲醛抗菌环保粉状涂料，可持久清除室内空气中的有害气体且长效抗菌。
本发明为了实现上述目的所采取的技术方案是：
一种室内用除甲醛抗菌环保粉状涂料，其特征在于：以重量百分数计，包括如下原料组分：纳米银0.03～0.05％，壳聚糖0.3～1％，硅藻纯5～10％，锐钛钛白粉5～10％，重质碳酸钙30～45％，轻质碳酸氢钙25～35％，硫酸钡15～25％，余量为助剂。
优选地，所述硅藻纯、锐钛钛白粉、重质碳酸钙、轻质碳酸氢钙、硫酸钡的细度为400～800目。
优选地，所述助剂包括：聚乙烯醇，羟乙基纤维素H250，润湿剂，分散剂，防霉剂，消泡剂，流平剂，抗磨剂。
优选地，如上所述的一种室内用除甲醛抗菌环保粉状涂料，以重量百分数计，包括如下原料组分：纳米银0.03～0.05％，壳聚糖0.3～1％，硅藻纯5～10％，锐钛钛白粉5～10％，重质碳酸钙30～45％，轻质碳酸氢钙25～35％，硫酸钡15～25％，聚乙烯醇0.3～0.6％，羟乙基纤维素H250 0.1～0.3％，润湿剂0.5～1％，分散剂0.3～1％，防霉剂0.3～1％，消泡剂0.1～0.3％，流平剂0.5～1.5％，抗磨剂0.3～1％。
优选地，所述润湿剂为聚乙二醇脂类非离子型润湿剂METOLAT P 588。
优选地，所述分散剂为六偏磷酸钠。
优选地，所述防霉剂为75号防霉剂。
本发明所用原料功效如下：
纳米银是粒径为纳米级的金属银单质，其抗菌谱广泛，低浓度下可触杀多种细菌、真菌、霉菌、孢子等微生物，且抗菌持久，无耐药性，无污染和毒副作用，是一种强效的天然抗菌剂。
壳聚糖是由自然界广泛存在的几丁质经过脱乙酰作用得到的一种高分子碱性多糖聚合物，具有较强的吸附性，可降低空气中的甲醛含量。此外，壳聚糖具有良好的抗菌活性和抗氧化性，与纳米银混合后一方面防止纳米银被氧化，另一方面与纳米银协同发挥抗菌作用。在本发明中，壳聚糖也作为增稠剂使用。
硅藻纯是以硅藻土、电气石及其它纯天然矿物土融合而成的一种空气过滤材料，多用于空气净化器滤芯的制造，其比表面积大、孔隙率高，内部的超细微孔比活性炭多5000到6000倍，难以吸附饱和；其天然分子筛结构保证被吸附的甲醛、苯、二甲苯、TVOC等有害气体不会重新溢出造成二次污染；另外，在本发明中硅藻纯还具有增容、增稠、提高附着力的作用。
锐钛钛白粉作为本发明颜料着色剂着色力高，遮盖力强，且耐候性好，在一定时间内不变色；另外作为成膜物质，对涂料的流变性、抗粉化性、防水性、耐腐蚀性具有一定增强作用。
重质碳酸钙作为本发明的主要填充料，稳定性高，强度高，亲水性好，增加容积并降低成本。
轻质碳酸氢钙白度高、遮盖力强，与重质碳酸钙混合使用增加填充料的均布性和综合机械能，防止发生团聚。
硫酸钡的稳定性佳，化学惰性强，防水耐腐蚀，可以避免涂料表面老化，具有很高的填充性，在本发明中作为增强剂，也作为一种廉价而有效的白色无机光稳定剂。
聚乙烯醇具有强力的粘接性、平滑性，是一种安全的成膜剂。
羟乙基纤维素无毒无味，具有良好的增稠性、分散性、粘合性、成膜性、保水性。
本发明所采用的原料均为环保无毒无污染材料，通过纳米银与壳聚糖联合使用，有效抗菌且抗菌效力持久；硅藻纯与壳聚糖相配合，自动吸附室内空气中的有毒有害气体，净化效力持久且不会造成二次污染；锐钛钛白粉着色力高，遮盖力强，耐候性好，与重质碳酸钙、轻质碳酸氢钙、硫酸钡配合使用，复合增强涂料的稳定性、耐候性、遮盖力，保证其使用时混合均匀防止其团聚结块。另外，本发明为粉状涂料，加水或乳胶搅拌后即可使用，其制备简单，包装、储存方便，适用于各种建筑室内装饰装修。
具体实施方式
下面结合实施例对本发明进行进一步详述：
实施例1
一种室内用除甲醛抗菌环保粉状涂料，按重量百分比计，包括：纳米银0.03％，壳聚糖0.3％，硅藻纯5.5％，锐钛钛白粉5.5％，重质碳酸钙45％，轻质碳酸氢钙25％，硫酸钡15％，聚乙烯醇0.3％，羟乙基纤维素H250 0.1％，聚乙二醇脂类非离子型润湿剂METOLAT P588 0.5％，六偏磷酸钠0.8％，75号防霉剂0.8％，消泡剂0.12％，流平剂0.5％，抗磨剂0.55％，以上原料成分均为粉状、颗粒状或块状物。
上述涂料的制备步骤为：将硅藻纯、锐钛钛白粉、重质碳酸钙、轻质碳酸氢钙、硫酸钡按比例混合均匀，置于研磨机内研磨，使得混合粉末细度为400～800目。将纳米银与壳聚糖按比例混合均匀，加入上述混合物中，并将其余物料按比例混入其中，放入混料搅拌机内，混合搅拌30～60分钟，静置2小时以上即可包装使用。
上述涂料使用时搅拌均匀，与水或乳胶溶液混合后使用。
实施例2
一种室内用除甲醛抗菌环保粉状涂料，按重量百分比计，包括：纳米银0.05％，壳聚糖1％，硅藻纯10％，锐钛钛白粉10％，重质碳酸钙30％，轻质碳酸氢钙25％，硫酸钡17.25％，聚乙烯醇0.6％，羟乙基纤维素H250 0.3％，聚乙二醇脂类非离子型润湿剂METOLAT P 588 1％，六偏磷酸钠1％，75号防霉剂1％，消泡剂0.3％，流平剂1.5％，抗磨剂1％，以上原料成分均为粉状、颗粒状或块状物。
实施例3
一种室内用除甲醛抗菌环保粉状涂料，按重量百分比计，包括：纳米银0.04％，壳聚糖1％，硅藻纯7％，锐钛钛白粉7.5％，重质碳酸钙30％，轻质碳酸氢钙30％，硫酸钡20％，聚乙烯醇0.5％，羟乙基纤维素H250 0.2％，聚乙二醇脂类非离子型润湿剂METOLAT P 5880.8％，六偏磷酸钠0.5％，75号防霉剂0.5％，消泡剂0.26％，流平剂1.2％，抗磨剂0.5％，以上原料成分均为粉状、颗粒状或块状物。
实施例4
一种室内用除甲醛抗菌环保粉状涂料，按重量百分比计，包括：纳米银0.05％，壳聚糖1％，硅藻纯5％，锐钛钛白粉5％，重质碳酸钙30％，轻质碳酸氢钙30％，硫酸钡25％，聚乙烯醇0.6％，羟乙基纤维素H250 0.1％，聚乙二醇脂类非离子型润湿剂METOLAT P 5881％，六偏磷酸钠0.3％，75号防霉剂0.3％，消泡剂0.1％，流平剂1.25％，抗磨剂0.3％，以上原料成分均为粉状、颗粒状或块状物。
实施例5
一种室内用除甲醛抗菌环保粉状涂料，按重量百分比计，包括：纳米银0.05％，壳聚糖0.7％，硅藻纯5％，锐钛钛白粉5％，重质碳酸钙30％，轻质碳酸氢钙35％，硫酸钡20％，聚乙烯醇0.3％，羟乙基纤维素H250 0.1％，聚乙二醇脂类非离子型润湿剂METOLAT P 5880.75％，六偏磷酸钠0.8％，75号防霉剂0.7％，消泡剂0.1％，流平剂0.7％，抗磨剂0.8％，以上原料成分均为粉状、颗粒状或块状物。
实施例6
一种室内用除甲醛抗菌环保粉状涂料，按重量百分比计，包括：纳米银0.05％，壳聚糖0.4％，硅藻纯7.5％，锐钛钛白粉7.5％，重质碳酸钙35％，轻质碳酸氢钙28％，硫酸钡18％，聚乙烯醇0.45％，羟乙基纤维素H250 0.2％，聚乙二醇脂类非离子型润湿剂METOLATP 588 0.5％，六偏磷酸钠0.4％，75号防霉剂0.4％，消泡剂0.2％，流平剂1％，抗磨剂0.4％，以上原料成分均为粉状、颗粒状或块状物。
根据JC/T1074-2008《室内空气净化功能涂覆材料净化性能》标准对实施例1-6中所述涂料进行48h甲醛净化测试，实验结果如表1所示：
表1
组别 甲醛净化效率(％)
实施例1 87.3
实施例2 93.7
实施例3 92.4
实施例4 88.4
实施例5 86.2
实施例6 90.9
由表1可知，本发明实施例1-6所述涂料甲醛净化效果良好。
对实施例1-6中所述涂料进行抗菌性能测试，检验菌种为大肠埃希氏菌ATCC 6538和金黄色葡萄球菌ATCC 25922。将5.0×105～10.0×105cfu/mL大肠埃希氏菌和金黄色葡萄球菌适量稀释，分别接种于待检涂料样品上并设置空白对照组。培养24h后洗涤样品，进行梯度稀释并涂布平板。平板培养24～48h后进行菌落总数计数并计算抗菌率。实验结果如表2所示：
表2
组别 大肠埃希氏菌抗菌率(％) 金黄色葡萄球菌抗菌率(％)
实施例1 99.98 99.95
实施例2 99.99 99.99
实施例3 99.99 99.99
实施例4 99.99 99.99
实施例5 99.99 99.99
实施例6 99.99 99.99
由表2可知，实施例1-6所述涂料抗菌效果良好。
以上仅是本发明的优选实施方式，本发明的保护范围并不仅限制于本文所示的实施例，凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理前提下对本发明各原料的等效替换及辅助成分的增减均落在本发明的保护范围和公开范围内。

Claims (7)

1.一种室内用除甲醛抗菌环保粉状涂料，其特征在于：以重量百分数计，包括如下原料组分：纳米银0.03～0.05％，壳聚糖0.3～1％，硅藻纯5～10％，锐钛钛白粉5～10％，重质碳酸钙30～45％，轻质碳酸氢钙25～35％，硫酸钡15～25％，余量为助剂。
2.根据权利要求1所述的一种室内用除甲醛抗菌环保粉状涂料，其特征在于：所述硅藻纯、锐钛钛白粉、重质碳酸钙、轻质碳酸氢钙、硫酸钡的细度为400～800目。
3.根据权利要求1所述的一种室内用除甲醛抗菌环保粉状涂料，其特征在于：所述助剂包括：聚乙烯醇，羟乙基纤维素H250，润湿剂，分散剂，防霉剂，消泡剂，流平剂，抗磨剂。
4.根据权利要求3所述的一种室内用除甲醛抗菌环保粉状涂料，其特征在于：以重量百分数计，包括如下原料组分：纳米银0.03～0.05％，壳聚糖0.3～1％，硅藻纯5～10％，锐钛钛白粉5～10％，重质碳酸钙30～45％，轻质碳酸氢钙25～35％，硫酸钡15～25％，聚乙烯醇0.3～0.6％，羟乙基纤维素H250 0.1～0.3％，润湿剂0.5～1％，分散剂0.3～1％，防霉剂0.3～1％，消泡剂0.1～0.3％，流平剂0.5～1.5％，抗磨剂0.3～1％。
5.根据权利要求4所述的一种室内用除甲醛抗菌环保粉状涂料，其特征在于：所述润湿剂为聚乙二醇脂类非离子型润湿剂METOLAT P 588。
6.根据权利要求4所述的一种室内用除甲醛抗菌环保粉状涂料，其特征在于：所述分散剂为六偏磷酸钠。
7.根据权利要求4所述的一种室内用除甲醛抗菌环保粉状涂料，其特征在于：所述防霉剂为75号防霉剂。
CN201710094372.9A 2017-02-21 2017-02-21 一种室内用除甲醛抗菌环保粉状涂料 Pending CN106833041A (zh)