CN113998973A - 一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆及其制备方法 - Google Patents
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆及其制备方法 Download PDFInfo
- Publication number
- CN113998973A CN113998973A CN202111316117.7A CN202111316117A CN113998973A CN 113998973 A CN113998973 A CN 113998973A CN 202111316117 A CN202111316117 A CN 202111316117A CN 113998973 A CN113998973 A CN 113998973A
- Authority
- CN
- China
- Prior art keywords
- waterproof
- foaming
- agent
- gypsum
- gypsum mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,由以下重量份的原料制成:石膏粉70~80份、水泥熟料10~20份、防水剂0.1~0.5份、减水剂0.1~0.5份、发泡剂1~5份、胶粉0.3~0.8份。本申请快速防水发泡石膏砂浆可替代市面上聚乙烯泡沫等进行封堵充填使用,增加快速防水发泡石膏砂浆自身的强度及防水性能,增加快速防水发泡石膏砂浆自身发泡体积。该快速防水发泡石膏砂浆可自身发泡并且较高防水性能,气自身与其他类型的磷石膏基材料具有强烈的衔接性能,不需要像加气砌块一样进行加热,也不需要使用特殊化学原料进行反应,可以在房屋外墙等特殊环境中使用。
Description
技术领域
本发明属于建筑材料技术领域,尤其涉及一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆及其制备方法。
背景技术
石膏砂浆较传统水泥砂浆具有施工迅速、不空鼓不开裂,且具有强度高、自重轻、防火隔热性能好等优点,近年来在建筑施工领域得到广泛应用,已具有全面替代传统水泥砂浆的趋势。砂浆是常用的建筑材料,一般用于砌筑和抹灰工程。砂浆是由胶凝材料(水泥、石灰、粘土等)和细骨料(砂)加水拌合而成。根据组成材料,可分为:①石膏砂浆:由石灰膏、砂和水按一定配比制成,一般用于强度要求不高、不受潮湿的砌体和抹灰层;②水泥砂浆:由水泥、砂和水按一定配比制成,一般用于潮湿环境或水中的砌体、墙面或地面等;③混合砂浆:在水泥或石灰砂浆中掺加适当掺合料如粉煤灰、硅藻土等制成,以节约硅酸盐水泥或石灰用量,并改善砂浆的和易性,常用的混合砂浆有水泥石灰砂浆、水泥粘土砂浆和石灰粘土砂浆等。按用途不同分为:砌筑砂浆、抹面砂浆(包括装饰砂浆、防水砂浆)、粘结砂浆等。目前,市售石膏砂浆在生产过程中,一般需要大量引入玻化微珠、膨胀珍珠岩、聚苯乙烯微球等价格高昂的保温材料,致使石膏砂浆价格居高不下;此外,现有石膏砂浆随时间推移会衰减,耐久性差,防水性差。
现有技术中,已经有不少关于石膏砂浆的文献公开,例如:1、专利申请201910557492.7,公开了一种防辐射石膏砂浆干混料及其制备方法,属于建筑材料技术领域,其包括原料处理、制备砂浆原料和制备防辐射石膏砂浆干混料三个步骤,以工业副产物绿矾为主要原料,通过与石灰浆及空气反应,制备得到砂浆原料,并与砂浆原料与外加剂、α石膏及砂等成分混合,制得防辐射石膏砂浆干混料。该方法具有工艺过程简单可控、实现了对绿矾的资源化利用、成本低廉、制得的砂浆干混料质量稳定的效果。2、专利申请202010297538.9,公开一种炉渣基防霉保温石膏砂浆及其制备方法,以燃煤电厂固体废弃物β石膏粉及轻骨料为主要原料,具体由以下质量百分数原料制成:β石膏粉18~25%、粒径为1.0~2.2mm的轻骨料30~35%、粒径为0.2~0.5mm的轻骨料35~49%、羟乙基纤维素1~1.5%、硅酸盐水泥0.5~1%、防霉剂0.5~1%、发泡剂1~1.5%;所述防霉剂由负载银离子/溴代水杨酰苯胺的磷酸锆和十三氟辛基三乙氧基硅烷1:(2~4)的质量比混合而成。该方法以燃煤电厂固体废弃物为主要原料,占石膏砂浆总质量的95%以上,实现废弃物的资源化利用,原料廉价易得,显著降低石膏砂浆生产成本,同时,较之传统石膏砂浆,本发明石膏砂浆更轻质,防水防潮、防霉抗菌、隔热保温、隔音减噪、减震性能均得到显著提升。
但是近年来,随着磷石膏产品推广使用要求的提高,目前市面上使用的部分针对孔洞或夹层进行安全封堵充填的产品多为聚乙烯泡沫等。聚乙烯泡沫等常见的充填体不防水也不防火,遇水见火后会发生一系列不良影响,安全方面有一定的不可控因素。
发明内容
本发明为解决上述技术问题,提供了一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆及其制备方法。本申请快速防水发泡石膏砂浆则可以有效的避免安全方面的不可控因素,因为本砂浆可以有效的防水防火,并发明了其在建筑美化及适用方面中的应用。
为了能够达到上述所述目的,本发明采用以下技术方案:
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,由以下重量份的原料制成:石膏粉70~80份、水泥熟料10~20份、防水剂0.1~0.5份、减水剂0.1~0.5份、发泡剂1~5份、胶粉0.3~0.8份。
进一步地,所述一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,由以下重量份的原料制成:石膏粉72~78份、水泥熟料12~18份、防水剂0.2~0.4份、减水剂0.2~0.4份、发泡剂2~4份、胶粉0.4~0.7份。
进一步地,所述一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,由以下重量份的原料制成:石膏粉75份、水泥熟料15份、防水剂0.3份、减水剂0.3份、发泡剂3份、胶粉0.6份。
进一步地,所述防水剂为干粉类的脂肪酸类防水剂或水剂类的有机硅防水剂;当防水剂为干粉类的脂肪酸类防水剂,使用时直接与石膏粉及其他原料混合搅拌;当防水剂为水剂类的有机硅防水剂,使用时先将其与水在转速为1200~1500r/min的搅拌机中高速搅拌乳化。
进一步地,所述减水剂是聚羧酸类减水剂。
进一步地,所述发泡剂是十二烷基硫酸钠或脂肪醇聚氧乙烯醚硫酸钠的阴离子表面活性剂。
进一步地,所述胶粉是塑胶粉末等常见高分子材料。
进一步地,所述石膏粉是磷石膏基石膏粉,是300~450℃高温煅烧的石膏粉,含有30%左右的无水二型β石膏。
进一步地,所述水泥熟料是常规的硅酸盐水泥熟料,28d强度>52.5MPa。
进一步地,所述的一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的制备方法,包括以下步骤:
(1)称料:按重量分数称取石膏粉、水泥熟料、防水剂、减水剂、发泡剂、胶粉,备用;
(2)混合:将步骤(1)的原料一起送入混料机中,打开混料机搅拌器充分搅拌,使各物料搅拌均匀,得所述用于厨卫间的高强防水抹灰石膏。
进一步地,在步骤(2),所述搅拌的转速为80~100r/min,时间为5~10min。
进一步地,一种如上述所述的用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的使用方法,先测算好需封堵或充填的空间体积,然后向快速防水发泡石膏砂浆中加入水,利用高速强制搅拌机进行搅拌,将搅拌后的快速防水发泡石膏砂浆浆体在90s~120s内快速直接灌入所需填充的房屋夹层或孔洞空间内;按照发泡后的快速防水发泡石膏砂浆体积为发泡前的3~6倍进行空间体积计算,搅拌时间为25s~35s,灌入房屋夹层或孔洞15~20min后发泡完成。
本发明采用石膏粉与发泡剂等原料产生反应,生成多气孔块状石膏,石膏粉本身有一定强度并且具有较好防火性能,可代替聚乙烯泡沫等进行房屋小范围孔洞进行安全封堵充填,制得的快速防水发泡石膏砂浆发泡后具有防水效果,可增加有效使用年限。
由于本发明采用了以上技术方案,具有以下有益效果:
(1)本申请快速防水发泡石膏砂浆可替代市面上聚乙烯泡沫等进行封堵充填使用,增加快速防水发泡石膏砂浆自身的强度及防水性能,增加快速防水发泡石膏砂浆自身发泡体积。该快速防水发泡石膏砂浆可自身发泡并且较高防水性能,气自身与其他类型的磷石膏基材料具有强烈的衔接性能,不需要像加气砌块一样进行加热,也不需要使用特殊化学原料进行反应,可以在房屋外墙等特殊环境中使用。
(2)本申请快速防水发泡石膏砂浆则可以有效的避免安全方面的不可控因素,因为该快速防水发泡石膏砂浆可以有效的防水防火,并发明了其在建筑美化及适用方面中的应用。
具体实施方式
下面对本发明的具体实施方式作进一步详细的说明,但本发明并不局限于这些实施方式,任何在本实施例基本精神上的改进或代替,仍属于本发明权利要求所要求保护的范围。
实施例1
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,由以下重量份的原料制成:石膏粉70份、水泥熟料10份、防水剂0.1份、减水剂0.1份、发泡剂1份、胶粉0.3份。
进一步地,所述防水剂为干粉类的脂肪酸类防水剂或水剂类的有机硅防水剂;当防水剂为干粉类的脂肪酸类防水剂,使用时直接与石膏粉及其他原料混合搅拌;当防水剂为水剂类的有机硅防水剂,使用时先将其与水在转速为1200r/min的搅拌机中高速搅拌乳化;所述减水剂是聚羧酸类减水剂;所述发泡剂是十二烷基硫酸钠或脂肪醇聚氧乙烯醚硫酸钠的阴离子表面活性剂;所述胶粉是塑胶粉末等常见高分子材料;所述石膏粉是磷石膏基石膏粉,是300℃高温煅烧的石膏粉,含有30%左右的无水二型β石膏;所述水泥熟料是常规的硅酸盐水泥熟料,28d强度>52.5MPa。
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的制备方法,包括以下步骤:
(1)称料:按重量分数称取石膏粉、水泥熟料、防水剂、减水剂、发泡剂、胶粉,备用;
(2)混合:将步骤(1)的原料一起送入混料机中,打开混料机搅拌器充分搅拌,使各物料搅拌均匀,得所述用于厨卫间的高强防水抹灰石膏;所述搅拌的转速为80r/min,时间为5min。
一种如上述所述的用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的使用方法,先测算好需封堵或充填的空间体积,然后向快速防水发泡石膏砂浆中加入水,利用高速强制搅拌机进行搅拌,将搅拌后的快速防水发泡石膏砂浆浆体在90s内快速直接灌入所需填充的房屋夹层或孔洞空间内;按照发泡后的快速防水发泡石膏砂浆体积为发泡前的3倍进行空间体积计算,搅拌时间为25s,灌入房屋夹层或孔洞15min后发泡完成。
实施例2
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,由以下重量份的原料制成:石膏粉80份、水泥熟料20份、防水剂0.5份、减水剂0.5份、发泡剂5份、胶粉0.8份。
进一步地,所述防水剂为干粉类的脂肪酸类防水剂或水剂类的有机硅防水剂;当防水剂为干粉类的脂肪酸类防水剂,使用时直接与石膏粉及其他原料混合搅拌;当防水剂为水剂类的有机硅防水剂,使用时先将其与水在转速为1500r/min的搅拌机中高速搅拌乳化;所述减水剂是聚羧酸类减水剂;所述发泡剂是十二烷基硫酸钠或脂肪醇聚氧乙烯醚硫酸钠的阴离子表面活性剂;所述胶粉是塑胶粉末等常见高分子材料;所述石膏粉是磷石膏基石膏粉,是450℃高温煅烧的石膏粉,含有30%左右的无水二型β石膏;所述水泥熟料是常规的硅酸盐水泥熟料,28d强度>52.5MPa。
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的制备方法,包括以下步骤:
(1)称料:按重量分数称取石膏粉、水泥熟料、防水剂、减水剂、发泡剂、胶粉,备用;
(2)混合:将步骤(1)的原料一起送入混料机中,打开混料机搅拌器充分搅拌,使各物料搅拌均匀,得所述用于厨卫间的高强防水抹灰石膏;所述搅拌的转速为100r/min,时间为10min。
一种如上述所述的用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的使用方法,先测算好需封堵或充填的空间体积,然后向快速防水发泡石膏砂浆中加入水,利用高速强制搅拌机进行搅拌,将搅拌后的快速防水发泡石膏砂浆浆体在120s内快速直接灌入所需填充的房屋夹层或孔洞空间内;按照发泡后的快速防水发泡石膏砂浆体积为发泡前的6倍进行空间体积计算,搅拌时间为35s,灌入房屋夹层或孔洞20min后发泡完成。
实施例3
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,由以下重量份的原料制成:石膏粉72份、水泥熟料12份、防水剂0.2份、减水剂0.2份、发泡剂2份、胶粉0.4份。
进一步地,所述防水剂为干粉类的脂肪酸类防水剂或水剂类的有机硅防水剂;当防水剂为干粉类的脂肪酸类防水剂,使用时直接与石膏粉及其他原料混合搅拌;当防水剂为水剂类的有机硅防水剂,使用时先将其与水在转速为1300r/min的搅拌机中高速搅拌乳化;所述减水剂是聚羧酸类减水剂;所述发泡剂是十二烷基硫酸钠或脂肪醇聚氧乙烯醚硫酸钠的阴离子表面活性剂;所述胶粉是塑胶粉末等常见高分子材料;所述石膏粉是磷石膏基石膏粉,是350℃高温煅烧的石膏粉,含有30%左右的无水二型β石膏;所述水泥熟料是常规的硅酸盐水泥熟料,28d强度>52.5MPa。
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的制备方法,包括以下步骤:
(1)称料:按重量分数称取石膏粉、水泥熟料、防水剂、减水剂、发泡剂、胶粉,备用;
(2)混合:将步骤(1)的原料一起送入混料机中,打开混料机搅拌器充分搅拌,使各物料搅拌均匀,得所述用于厨卫间的高强防水抹灰石膏;所述搅拌的转速为85r/min,时间为6min。
一种如上述所述的用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的使用方法,先测算好需封堵或充填的空间体积,然后向快速防水发泡石膏砂浆中加入水,利用高速强制搅拌机进行搅拌,将搅拌后的快速防水发泡石膏砂浆浆体在100s内快速直接灌入所需填充的房屋夹层或孔洞空间内;按照发泡后的快速防水发泡石膏砂浆体积为发泡前的4倍进行空间体积计算,搅拌时间为27s,灌入房屋夹层或孔洞16min后发泡完成。
实施例4
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,由以下重量份的原料制成:石膏粉78份、水泥熟料18份、防水剂0.4份、减水剂0.4份、发泡剂4份、胶粉0.7份。
进一步地,所述防水剂为干粉类的脂肪酸类防水剂或水剂类的有机硅防水剂;当防水剂为干粉类的脂肪酸类防水剂,使用时直接与石膏粉及其他原料混合搅拌;当防水剂为水剂类的有机硅防水剂,使用时先将其与水在转速为1400r/min的搅拌机中高速搅拌乳化;所述减水剂是聚羧酸类减水剂;所述发泡剂是十二烷基硫酸钠或脂肪醇聚氧乙烯醚硫酸钠的阴离子表面活性剂;所述胶粉是塑胶粉末等常见高分子材料;所述石膏粉是磷石膏基石膏粉,是400℃高温煅烧的石膏粉,含有30%左右的无水二型β石膏;所述水泥熟料是常规的硅酸盐水泥熟料,28d强度>52.5MPa。
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的制备方法,包括以下步骤:
(1)称料:按重量分数称取石膏粉、水泥熟料、防水剂、减水剂、发泡剂、胶粉,备用;
(2)混合:将步骤(1)的原料一起送入混料机中,打开混料机搅拌器充分搅拌,使各物料搅拌均匀,得所述用于厨卫间的高强防水抹灰石膏;所述搅拌的转速为95r/min,时间为9min。
一种如上述所述的用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的使用方法,先测算好需封堵或充填的空间体积,然后向快速防水发泡石膏砂浆中加入水,利用高速强制搅拌机进行搅拌,将搅拌后的快速防水发泡石膏砂浆浆体在110s内快速直接灌入所需填充的房屋夹层或孔洞空间内;按照发泡后的快速防水发泡石膏砂浆体积为发泡前的5倍进行空间体积计算,搅拌时间为33s,灌入房屋夹层或孔洞19min后发泡完成。
实施例5
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,由以下重量份的原料制成:石膏粉75份、水泥熟料15份、防水剂0.3份、减水剂0.3份、发泡剂3份、胶粉0.5份。
进一步地,所述防水剂为干粉类的脂肪酸类防水剂或水剂类的有机硅防水剂;当防水剂为干粉类的脂肪酸类防水剂,使用时直接与石膏粉及其他原料混合搅拌;当防水剂为水剂类的有机硅防水剂,使用时先将其与水在转速为1350r/min的搅拌机中高速搅拌乳化;所述减水剂是聚羧酸类减水剂;所述发泡剂是十二烷基硫酸钠或脂肪醇聚氧乙烯醚硫酸钠的阴离子表面活性剂;所述胶粉是塑胶粉末等常见高分子材料;所述石膏粉是磷石膏基石膏粉,是380℃高温煅烧的石膏粉,含有30%左右的无水二型β石膏;所述水泥熟料是常规的硅酸盐水泥熟料,28d强度>52.5MPa。
一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的制备方法,包括以下步骤:
(1)称料:按重量分数称取石膏粉、水泥熟料、防水剂、减水剂、发泡剂、胶粉,备用;
(2)混合:将步骤(1)的原料一起送入混料机中,打开混料机搅拌器充分搅拌,使各物料搅拌均匀,得所述用于厨卫间的高强防水抹灰石膏;所述搅拌的转速为90r/min,时间为8min。
一种如上述所述的用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的使用方法,先测算好需封堵或充填的空间体积,然后向快速防水发泡石膏砂浆中加入水,利用高速强制搅拌机进行搅拌,将搅拌后的快速防水发泡石膏砂浆浆体在105s内快速直接灌入所需填充的房屋夹层或孔洞空间内;按照发泡后的快速防水发泡石膏砂浆体积为发泡前的4.5倍进行空间体积计算,搅拌时间为30s,灌入房屋夹层或孔洞17min后发泡完成。
对比例1
按照专利申请201910557492.7(一种防辐射石膏砂浆干混料及其制备方法)中的实施例方法制备石膏砂浆。
对比例2
按照专利申请202010297538.9(一种炉渣基防霉保温石膏砂浆及其制备方法)中的实施例方法制备石膏砂浆。
为了进一步说明本发明能够达到所述技术效果,做以下实验:
将实施例1~5和对比例1~2制得的石膏砂浆用于房屋夹层或孔洞充填,结果发现,对比例1~2制得的石膏砂填补后,凝固比较慢,且存在漏水、渗水现象,而本申请快速防水发泡石膏砂浆则不没有以上问题,而且可以有效的防水防火,可以有效的避免安全方面的不可控因素。
综上所述,本申请快速防水发泡石膏砂浆可替代市面上聚乙烯泡沫等进行封堵充填使用,增加快速防水发泡石膏砂浆自身的强度及防水性能,增加快速防水发泡石膏砂浆自身发泡体积。该快速防水发泡石膏砂浆可自身发泡并且较高防水性能,气自身与其他类型的磷石膏基材料具有强烈的衔接性能,不需要像加气砌块一样进行加热,也不需要使用特殊化学原料进行反应,可以在房屋外墙等特殊环境中使用。
对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在没有背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同含义和范围内的所有变化囊括在本发明的保护范围之内。
Claims (10)
1.一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,其特征在于,由以下重量份的原料制成:石膏粉70~80份、水泥熟料10~20份、防水剂0.1~0.5份、减水剂0.1~0.5份、发泡剂1~5份、胶粉0.3~0.8份。
2.根据权利要求1所述的一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,其特征在于:所述防水剂为干粉类的脂肪酸类防水剂或水剂类的有机硅防水剂;当防水剂为干粉类的脂肪酸类防水剂,使用时直接与石膏粉及其他原料混合搅拌;当防水剂为水剂类的有机硅防水剂,使用时先将其与水在转速为1200~1500r/min的搅拌机中高速搅拌乳化。
3.根据权利要求1所述的一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,其特征在于:所述减水剂是聚羧酸类减水剂。
4.根据权利要求1所述的一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,其特征在于:所述发泡剂是十二烷基硫酸钠或脂肪醇聚氧乙烯醚硫酸钠的阴离子表面活性剂。
5.根据权利要求1所述的一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,其特征在于:所述胶粉是塑胶粉末等常见高分子材料。
6.根据权利要求1所述的一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,其特征在于:所述石膏粉是磷石膏基石膏粉,是300~450℃高温煅烧的石膏粉,含有30%左右的无水二型β石膏。
7.根据权利要求1所述的一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆,其特征在于:所述水泥熟料是常规的硅酸盐水泥熟料,28d强度>52.5MPa。
8.根据权利要求1~7任一项所述的一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的制备方法,其特征在于,包括以下步骤:
(1)称料:按重量分数称取石膏粉、水泥熟料、防水剂、减水剂、发泡剂、胶粉,备用;
(2)混合:将步骤(1)的原料一起送入混料机中,打开混料机搅拌器充分搅拌,使各物料搅拌均匀,得所述用于厨卫间的高强防水抹灰石膏。
9.根据权利要求8所述的一种用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的制备方法,其特征在于:在步骤(2),所述搅拌的转速为80~100r/min,时间为5~10min。
10.一种如权利要求1~9任一项所述的用于房屋夹层或孔洞充填的快速防水发泡石膏砂浆的使用方法,其特征在于:先测算好需封堵或充填的空间体积,然后向快速防水发泡石膏砂浆中加入水,利用高速强制搅拌机进行搅拌,将搅拌后的快速防水发泡石膏砂浆浆体在90s~120s内快速直接灌入所需填充的房屋夹层或孔洞空间内;按照发泡后的快速防水发泡石膏砂浆体积为发泡前的3~6倍进行空间体积计算,搅拌时间为25s~35s,灌入房屋夹层或孔洞15~20min后发泡完成。