CN113996796A - Preparation method of nickel-based as-cast brazing powder - Google Patents
Preparation method of nickel-based as-cast brazing powder Download PDFInfo
- Publication number
- CN113996796A CN113996796A CN202111299199.9A CN202111299199A CN113996796A CN 113996796 A CN113996796 A CN 113996796A CN 202111299199 A CN202111299199 A CN 202111299199A CN 113996796 A CN113996796 A CN 113996796A
- Authority
- CN
- China
- Prior art keywords
- nickel
- cast
- filler metal
- brazing filler
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the technical field of solder preparation, in particular to a preparation method of nickel-based as-cast brazing powder. The preparation method provided by the invention comprises the following steps: taking scraps of the nickel-based as-cast brazing filler metal, and performing ball milling to obtain the nickel-based as-cast brazing powder; the nickel-based as-cast brazing filler metal comprises B and/or Si and also comprises W and/or Mo. According to the invention, the nickel-based as-cast brazing powder is subjected to scrap taking, so that a part of enrichment phases in as-cast structures can be effectively crushed; and then, preparing powder by a ball milling mode, wherein in the ball milling process, the crushed metal chips and the grinding balls are violently collided and crushed for a long time, so that the powder particles are repeatedly subjected to cold welding and fracture, atoms in the powder particles are further diffused, and further the alloyed powder with uniform components is obtained. Meanwhile, the preparation method has low requirements on the size and defects of the nickel-based as-cast brazing filler metal, and the operation of the chip taking and ball milling processes is simple, so that the preparation method is suitable for quickly preparing the nickel-based brazing powder at low cost.
Description
Technical Field
The invention relates to the technical field of solder preparation, in particular to a preparation method of nickel-based as-cast brazing powder.
Background
In the current nickel-based high-temperature alloy brazing research, Ni-Cr-B or Ni-Cr-Si-B alloy brazing filler metal is generally adopted, the effect of lowering the melting point is achieved by adding B and/or Si and properly adjusting the addition amount of the B and/or Si, the high-temperature strength is improved by properly increasing W and/or Mo and other elements, but the addition of B, Si, W and Mo enables the brazing filler metal to easily form an enrichment phase in the smelting process, such as a hard and brittle Si-rich eutectic phase, and active B easily forms a boride phase at a grain boundary, so that the prepared cast-state brazing filler metal is hard and brittle due to uneven components in the smelting process of the brazing filler metal.
During powder preparation, the prior art generally adopts gas atomization powder preparation, rotary electrode powder preparation and other modes to have extremely high requirements on the dimensional precision, the surface state, the casting defects and the like of as-cast solder, in order to meet the corresponding requirements, strict control needs to be carried out on the aspects of smelting, machining and the like, the preparation cost is high, and in the powder preparation process, the enrichment phase existing in the as-cast solder is difficult to eliminate.
Disclosure of Invention
The invention aims to provide a preparation method of nickel-based as-cast brazing powder. The nickel-based as-cast brazing powder prepared by the preparation method is low in cost and can effectively eliminate an enrichment phase.
In order to achieve the above object, the present invention provides the following technical solutions:
the invention provides a preparation method of nickel-based as-cast brazing powder, which comprises the following steps:
taking scraps of the nickel-based as-cast brazing filler metal, and performing ball milling to obtain the nickel-based as-cast brazing powder;
the nickel-based as-cast brazing filler metal comprises B and/or Si and also comprises W and/or Mo.
Preferably, when the nickel-based as-cast brazing filler metal comprises B, the mass percentage of B in the nickel-based as-cast brazing filler metal is 1.0-4.0%;
when the nickel-based as-cast brazing filler metal comprises Si, the mass percentage of the Si in the nickel-based as-cast brazing filler metal is 0.5-4.0%;
when the nickel-based as-cast brazing filler metal comprises W, the mass percentage of the W in the nickel-based as-cast brazing filler metal is 3.5-6.5%;
when the nickel-based as-cast brazing filler metal comprises Mo, the mass percentage of the Mo in the nickel-based as-cast brazing filler metal is 3.0-7.0%.
Preferably, the nickel-based as-cast brazing filler metal comprises the following components in percentage by mass: 0.05-0.1% of C, 2.5-4.0% of Si, 3.0-4.0% of Mo, 7.0-8.0% of Ti, 2.5-6.5% of Al, 1.0-2.5% of B, 9.0-10.0% of Co, 0.05-0.20% of Fe, 0.1-1.5% of Hf0.02-0.2% of Re, 0.02-0.2% of Ta, 3.5-4.5% of W, 1.0-13.5% of Cr and the balance of Ni.
Preferably, the rotation speed of a lathe spindle used for taking chips is 40-60 r/min, the feeding amount is 0.008-0.012 mm/r, and the cutting amount is 0.4-0.5 mm.
Preferably, the rotation speed of the ball mill is 400-500 r/min, the time is 7-9 h, and the ball-to-material ratio is (10-12): 1.
preferably, the ball milling mode is wet ball milling.
Preferably, the materials of the ball milling pot and the ball milling beads adopted by the ball milling are tungsten carbide.
Preferably, drying is further included after the ball milling;
the drying temperature is 80 ℃, and the drying time is 8-10 h.
The invention provides a preparation method of nickel-based as-cast brazing powder, which comprises the following steps: taking scraps of the nickel-based as-cast brazing filler metal, and performing ball milling to obtain the nickel-based as-cast brazing powder; the nickel-based as-cast brazing filler metal comprises B and/or Si and also comprises W and/or Mo. According to the invention, the nickel-based as-cast brazing powder is subjected to scrap taking, so that part of enriched phases (such as Si-enriched eutectic phases) in the as-cast structure can be effectively crushed; and then, preparing powder by a ball milling mode, wherein in the ball milling process, the crushed metal chips and the grinding balls are violently collided and crushed for a long time, so that the powder particles are repeatedly subjected to cold welding and fracture, atoms in the powder particles are further diffused, and further the alloyed powder with uniform components is obtained. Meanwhile, the preparation method has low requirements on the size and defects of the nickel-based as-cast brazing filler metal, and the operation of the chip taking and ball milling processes is simple, so that the preparation method is suitable for quickly preparing the nickel-based brazing powder at low cost.
Drawings
FIG. 1 is a microstructure of the nickel-based as-cast braze described in example 1;
FIG. 2 is a back-scattered electron image of the nickel-based as-cast braze powder prepared in example 1;
FIG. 3 is a microstructure of the nickel-based as-cast braze described in example 2;
FIG. 4 is a back-scattered electron image of the nickel-based as-cast braze powder prepared in example 2;
FIG. 5 is a microstructure view of the nickel-based as-cast braze described in example 3;
FIG. 6 is a back-scattered electron image of the nickel-based as-cast braze powder prepared in example 3;
FIG. 7 is a microstructure photograph of a weld obtained in test example 1;
FIG. 8 is a fiber texture map of the nickel-based as-cast brazing powder prepared in comparative example 1;
FIG. 9 is a microstructure photograph of a weld obtained in test example 2.
Detailed Description
The invention provides a preparation method of nickel-based as-cast brazing powder, which comprises the following steps:
taking scraps of the nickel-based as-cast brazing filler metal, and performing ball milling to obtain the nickel-based as-cast brazing powder;
the nickel-based as-cast brazing filler metal comprises B and/or Si and also comprises W and/or Mo.
In the present invention, all the starting materials for the preparation are commercially available products known to those skilled in the art unless otherwise specified.
In the invention, when the nickel-based as-cast brazing filler metal comprises B, the mass percentage of B in the nickel-based as-cast brazing filler metal is preferably 1.0-4.0%, and more preferably 1.3-2.1%;
when the nickel-based as-cast brazing filler metal comprises Si, the mass percentage of the Si in the nickel-based as-cast brazing filler metal is preferably 0.5-4.0%, and more preferably 3.0-3.4%;
when the nickel-based as-cast brazing filler metal comprises W, the mass percentage of the W in the nickel-based as-cast brazing filler metal is preferably 3.5-6.5%, and more preferably 3.8-4.2%;
when the nickel-based as-cast brazing filler metal comprises Mo, the mass percentage of the Mo in the nickel-based as-cast brazing filler metal is preferably 3.0-7.0%, and more preferably 3.2-3.5%.
In the invention, the nickel-based as-cast brazing filler metal preferably comprises the following components in percentage by mass: 0.05-0.1% of C, 2.5-4.0% of Si, 3.0-4.0% of Mo, 7.0-8.0% of Ti, 2.5-6.5% of Al, 1.0-2.5% of B, 9.0-10.0% of Co, 0.05-0.20% of Fe, 0.1-1.5% of Hf0, 0.02-0.2% of Re, 0.02-0.2% of Ta0.02-0.2%, 3.5-4.5% of W, 1.0-13.0% of Cr and the balance of Ni; more preferably comprises the following components: 0.06-0.08% of C, 3.0-3.4% of Si, 3.2-3.5% of Mo, 7.3-7.6% of Ti, 2.8-6.2% of Al, 1.3-2.1% of B, 9.6-10.0% of Co, 0.13-0.18% of Fe, 0.6-1.2% of Hf0.07-0.16% of Re, 0.07-0.13% of Ta0.07, 3.8-4.2% of W, 1.1-12.0% of Cr and the balance of Ni.
The preparation process of the nickel-based as-cast brazing filler metal is not limited in any way, and the nickel-based as-cast brazing filler metal can be prepared conventionally by adopting a process well known to a person skilled in the art.
In the invention, the scrap taking is preferably carried out on the nickel-based as-cast brazing filler metal by adopting a lathe; the rotating speed of a lathe spindle for taking chips is preferably 40-60 r/min, more preferably 45-55 r/min, and most preferably 48-52 r/min; the feeding amount is preferably 0.008-0.012 mm/r, and more preferably 0.009-0.011 mm/r; the cutting depth is preferably 0.4 to 0.5mm, more preferably 0.43 to 0.45 mm.
In the invention, the rotation speed of the ball milling is preferably 400-500 r/min, more preferably 420-480 r/min, and most preferably 430-450 r/min; the time is preferably 7-9 h, more preferably 7.6-8.2 h; the ball-material ratio is preferably (10-12): 1, more preferably (10.8 to 11.5): 1. in the invention, the ball-to-material ratio is the mass ratio of the ball grinding beads to the nickel-based as-cast brazing filler metal. In the invention, the ball milling mode is preferably wet ball milling; the ball milling medium of the wet ball milling is preferably absolute ethyl alcohol; the amount of the absolute ethyl alcohol used in the present invention is not particularly limited, and may be those known to those skilled in the art. In the present invention, the anhydrous ethanol serves to prevent overheating during ball milling. In the present invention, the ball milling is preferably carried out in a planetary ball mill.
After ball milling, the method also preferably comprises drying, wherein the drying temperature is preferably 80 ℃, and the drying time is preferably 8-10 h. In the present invention, the drying is preferably performed in an oven.
After the drying is finished, the method also preferably comprises sieving, wherein the diameter of the sieved sieve is preferably 100-200 meshes, and more preferably 120-180 meshes.
The following examples are provided to illustrate the preparation of the nickel-based as-cast brazing powder according to the present invention, but they should not be construed as limiting the scope of the present invention.
Example 1
The nickel-based as-cast brazing filler metal comprises the following components: 0.1% of C, 3.5% of Si, 3.5% of Mo, 7.5% of Ti, 3.2% of Al, 1.8% of B, 9.5% of Co, 0.15% of Fe, 0.6% of Hf0.6%, 0.08% of Re, 0.09% of Ta, 4.0% of W, 11.5% of Cr and the balance of Ni, the microstructure being as shown in FIG. 1 (the nickel-based as-cast solder contains a large amount of a skeletal Si-rich eutectic phase, i.e., an enriched phase, formed by enrichment of Si, Mo, W and the like);
the nickel-based as-cast brazing filler metal is subjected to scrap taking by using a lathe, the rotating speed of a main shaft of the lathe is 50r/min, the feeding amount is 0.01mm/r, and the cutting amount is 0.5 mm; performing ball milling on a planet ball mill by using a tungsten carbide ball milling tank and ball milling beads, wherein the ball milling medium is absolute ethyl alcohol, the ball-material ratio is 10:1, the rotating speed is 400r/min, and the time is 8 hours; placing the ball-milled material in an oven, drying for 8 hours at 80 ℃, and sieving with a 160-mesh screen to obtain the nickel-based as-cast brazing powder;
fig. 2 is a back-scattered electron image of the nickel-based as-cast brazing powder, and as can be seen from fig. 2, the prepared nickel-based as-cast brazing powder has a uniform particle size, and compared with fig. 1, the bulk skeletal Si-rich eutectic phase ball-milled phase in the as-cast brazing filler metal is significantly reduced;
example 2
The nickel-based as-cast brazing filler metal comprises the following components: 0.1% of C, 2.5% of Si, 3.5% of Mo, 7.5% of Ti, 3.2% of Al, 1.5% of B, 9.5% of Co, 0.15% of Fe, 0.6% of Hf0.6%, 0.08% of Re, 0.09% of Ta, 4.0% of W, 13.5% of Cr and the balance of Ni, the microstructure being as shown in FIG. 3 (the nickel-based as-cast solder contains a large amount of a skeletal Si-rich eutectic phase, i.e., an enriched phase, formed by enrichment of Si, Mo, W and the like);
the nickel-based as-cast brazing filler metal is subjected to scrap taking by using a lathe, the rotating speed of a main shaft of the lathe is 50r/min, the feeding amount is 0.01mm/r, and the cutting amount is 0.5 mm; performing ball milling on a planet ball mill by using a tungsten carbide ball milling tank and ball milling beads, wherein the ball milling medium is absolute ethyl alcohol, the ball-material ratio is 10:1, the rotating speed is 400r/min, and the time is 8 hours; placing the ball-milled material in an oven, drying for 8 hours at 80 ℃, and sieving with a 160-mesh screen to obtain the nickel-based as-cast brazing powder;
fig. 4 is a back-scattered electron image of the nickel-based as-cast brazing powder, and as can be seen from fig. 4, the prepared nickel-based as-cast brazing powder has a uniform particle size, and compared with fig. 3, the bulk skeletal Si-rich eutectic phase ball-milled phase in the as-cast brazing filler metal is significantly reduced.
Example 3
The nickel-based as-cast brazing filler metal comprises the following components: 0.1% of C, 3.5% of Si, 3.5% of Mo, 7.5% of Ti, 3.2% of Al, 1.0% of B, 9.5% of Co, 0.15% of Fe, 0.6% of Hf0.6%, 0.08% of Re, 0.09% of Ta, 4.0% of W, 13.0% of Cr and the balance of Ni, the microstructure being as shown in FIG. 5 (the nickel-based as-cast solder contains a large amount of a skeletal Si-rich eutectic phase, i.e., an enriched phase, formed by enrichment of Si, Mo, W and the like);
the nickel-based as-cast brazing filler metal is subjected to chip removal by a lathe, the rotating speed of a main shaft of the lathe is 52r/min, the feeding amount is 0.011mm/r, and the cutting amount is 0.45 mm; performing ball milling on a planet ball mill by using a tungsten carbide ball milling tank and ball milling beads, wherein the ball milling medium is absolute ethyl alcohol, the ball-material ratio is 10:1, the rotating speed is 500r/min, and the time is 8.2 h; placing the ball-milled material in an oven for drying at 80 ℃ for 9h, and sieving the dried material with a 160-mesh screen to obtain the nickel-based as-cast brazing powder;
fig. 6 is a back-scattered electron image of the nickel-based as-cast brazing powder, and it can be seen from fig. 6 that the prepared nickel-based as-cast brazing powder has a uniform particle size, and compared with fig. 5, the bulk skeletal Si-rich eutectic phase ball-milled phase in the as-cast brazing filler metal is significantly reduced.
Test example 1
The nickel-based as-cast brazing powder prepared in the example 1 is used for brazing a nickel-based superalloy, wherein the nickel-based superalloy comprises 2.5% of Cr, 6.5% of Al, 8.0% of Mo, 0.9% of Re, 0.1% of Hf0, 1.0-4.5% of Ta, 0.1% of C and the balance of Ni; the brazing temperature is 1240 ℃, and the heat preservation time is 40 min;
FIG. 7 is a microstructure photograph of the obtained weld, and it can be seen from FIG. 7 that the brazed weld is full, the isothermal solidification region is wide, and the large block of skeleton-like Si-rich eutectic phases in the as-cast brazing filler metal are significantly reduced;
according to GB/T228.2-2015 part 2 of the tensile test for metallic materials: the tensile property of the brazed joint is tested by the high-temperature test method, and the tensile strength of the brazed joint at 760 ℃ is 737MPa and the tensile strength of the brazed joint at 980 ℃ is 387 MPa.
Comparative example 1
The nickel-based as-cast brazing filler metal comprises the following components: 0.05% of C, 2.9% of Si, 2.4% of Mo, 4.9% of Al, 1.2% of B, 1.42% of Hf, 4.2% of W, 1.2% of Cr and the balance of Ni; the contents of Mo, Si and B in the nickel-based as-cast brazing filler metal are obviously reduced compared with that in the embodiment 1;
adopting the mode of gas atomization powder process, right the nickel base as-cast brazing filler metal carries out the powder process, the condition of gas atomization powder process is: the atomizing medium is argon, the atomizing pressure is 1.8MPa, the nozzle structure is a circular seam type, the width of the circular seam is 0.8mm, the atomizing included angle is 39 degrees, the diameter of the leakage pipe is 8mm, and the nickel-based as-cast brazing powder is obtained;
fig. 8 is a microstructure photograph of the nickel-based as-cast brazing powder, and as can be seen from fig. 8, the nickel-based as-cast brazing powder has a distinct enrichment phase therein.
Test example 2
The nickel-based as-cast brazing powder prepared in comparative example 1 is used for brazing the nickel-based superalloy, and the nickel-based superalloy comprises the following components: 2.5% of Cr, 6.5% of Al, 8.0% of Mo, 0.9% of Re, 0.1% of Hf0, 1.0-4.5% of Ta, 0.1% of C and the balance of Ni; the brazing temperature is 1240 ℃, and the heat preservation time is 40 min;
FIG. 9 is a microstructure photograph of the obtained weld, and it can be seen from FIG. 9 that there exists a regular block-shaped enrichment phase in the weld, which has poor toughness and is not favorable for the mechanical properties of the joint;
according to GB/T228.2-2015 part 2 of the tensile test for metallic materials: the tensile strength of the brazed joint at 760 ℃ was 527MPa, which is a drop of 210MPa from the tensile strength of the brazed joint at 760 ℃ in test example 1.
The foregoing is only a preferred embodiment of the present invention, and it should be noted that, for those skilled in the art, various modifications and decorations can be made without departing from the principle of the present invention, and these modifications and decorations should also be regarded as the protection scope of the present invention.
Claims (8)
1. A preparation method of nickel-based as-cast brazing powder is characterized by comprising the following steps:
taking scraps of the nickel-based as-cast brazing filler metal, and performing ball milling to obtain the nickel-based as-cast brazing powder;
the nickel-based as-cast brazing filler metal comprises B and/or Si and also comprises W and/or Mo.
2. The preparation method according to claim 1, wherein when the nickel-based as-cast brazing filler metal comprises B, the mass percentage of B in the nickel-based as-cast brazing filler metal is 1.0-4.0%;
when the nickel-based as-cast brazing filler metal comprises Si, the mass percentage of the Si in the nickel-based as-cast brazing filler metal is 0.5-4.0%;
when the nickel-based as-cast brazing filler metal comprises W, the mass percentage of the W in the nickel-based as-cast brazing filler metal is 3.5-6.5%;
when the nickel-based as-cast brazing filler metal comprises Mo, the mass percentage of the Mo in the nickel-based as-cast brazing filler metal is 3.0-7.0%.
3. The preparation method according to claim 1 or 2, wherein the nickel-based as-cast brazing filler metal comprises the following components in percentage by mass: 0.05-0.1% of C, 2.5-4.0% of Si, 3.0-4.0% of Mo, 7.0-8.0% of Ti, 2.5-6.5% of Al, 1.0-2.5% of B, 9.0-10.0% of Co, 0.05-0.20% of Fe, 0.1-1.5% of Hf0.02-0.2% of Re, 0.02-0.2% of Ta, 3.5-4.5% of W, 1.0-13.5% of Cr and the balance of Ni.
4. The method according to claim 1, wherein the chips are taken by a lathe spindle with a rotation speed of 40 to 60r/min, a feed rate of 0.008 to 0.012mm/r, and a bite rate of 0.4 to 0.5 mm.
5. The preparation method of claim 1, wherein the rotation speed of the ball mill is 400-500 r/min, the time is 7-9 h, and the ball-to-material ratio is (10-12): 1.
6. the method of claim 5, wherein the ball milling is performed by wet ball milling.
7. The preparation method of claim 6, wherein the materials of the ball milling pot and the ball milling beads used for ball milling are tungsten carbide.
8. The method of claim 1, 5, 6 or 7, wherein the ball milling is followed by drying;
the drying temperature is 80 ℃, and the drying time is 8-10 h.