CN113912323A - 一种水泥石膏制品用助剂 - Google Patents
一种水泥石膏制品用助剂 Download PDFInfo
- Publication number
- CN113912323A CN113912323A CN202111320681.6A CN202111320681A CN113912323A CN 113912323 A CN113912323 A CN 113912323A CN 202111320681 A CN202111320681 A CN 202111320681A CN 113912323 A CN113912323 A CN 113912323A
- Authority
- CN
- China
- Prior art keywords
- eva
- weight
- agent
- cement
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种水泥石膏制品用助剂。所述助剂由100重量份的EVA乳液、0.01‑0.1重量份的苯丙三氮坐、0.01‑0.1重量份的分散剂、0.01‑0.1重量份的流平剂、0.01‑0.1重量份的成膜助剂组成，所述EVA乳液中EVA的质量含量为10‑50％，所述EVA的数均分子量为1000‑8000。现有技术普遍采用混凝土密封固化剂来对混凝土结构物进行处理，混凝土密封固化剂是一种多成分的化学试剂，粘度很小，涂装在混凝土结构物表面后，由于毛细作用可迅速渗入混凝土结构物内部并与其内部的游离钙反应生成不可溶解的非晶态水化硅酸钙，从而实现对混凝土结构物细孔的封堵，提高其硬度和防水性。
Description
技术领域
本发明涉及一种水泥石膏制品用助剂。
背景技术
由于混凝土硬化过程中，表层和内部结构含有大量相互贯穿的细孔，导致混凝土结构物在服役过程中，时常因为表面质量不良或密实度不够而难以抵挡环境中腐蚀物质的侵蚀，造成混凝土结构性能的加速劣化，降低混凝土结构物的耐久性和服役寿命，针对混凝土存在的缺陷。
现有技术普遍采用混凝土密封固化剂来对混凝土结构物进行处理，混凝土密封固化剂是一种多成分的化学试剂，粘度很小，涂装在混凝土结构物表面后，由于毛细作用可迅速渗入混凝土结构物内部并与其内部的游离钙反应生成不可溶解的非晶态水化硅酸钙，从而实现对混凝土结构物细孔的封堵，提高其硬度和防水性。
现有技术中，采用硅氧低聚物溶液渗透进入混凝土并与混凝土中的活性羟基发生反应形成一体化结构，从而达到对混凝土的加固密实的作用。
现有技术缺少一种具有高硬度、高耐磨的水泥石膏制品用助剂。
发明内容
本发明的目的是为解决现有技术的不足，提供了一种水泥石膏制品用助剂，所述助剂由100重量份的EVA乳液、0.01-0.1重量份的苯丙三氮坐、0.01-0.1重量份的分散剂、0.01-0.1重量份的流平剂、0.01-0.1重量份的成膜助剂组成，所述EVA乳液中EVA的质量含量为10-50％，所述EVA的数均分子量为1000-8000。
所述EVA为梳状有机硅改性接枝EVA。
所述成膜助剂为醇酯十二、乙二醇丁醚、丙二醇甲醚、丙二醇丁醚或丙二醇苯醚中的一种或几种。
述流平剂为有机硅类流平剂或丙烯酸类流平剂。
所述的分散剂为EVA蜡或脂肪醇聚氧乙烯醚。
一种水泥石膏制品的制作方法，包括以下步骤：
将水泥石膏制品助剂按照混凝土总质量1-3％的加入混凝土强度等级为C20自流平水泥中，流平固化后自然晾干8小时后，在自流平水泥表面按照100-300g/平方米喷涂本发明的助剂，自然晾干6小时后，用200～300目抛光片打磨地坪2次，后用500～600目抛光片打磨地坪1次，再用1000目抛光片打磨地坪1次，打磨过程中，保持打磨转速使得表面温度高于80摄氏度至少20分钟；
所述水泥石膏制品助剂由100重量份的EVA乳液、0.01-0.1重量份的苯丙三氮坐、0.01-0.1重量份的分散剂、0.01-0.1重量份的流平剂、0.01-0.1重量份的成膜助剂组成，所述EVA乳液中EVA的质量含量为10-50％，所述EVA的数均分子量为1000-8000。
所述EVA为梳状有机硅改性接枝EVA。
所述成膜助剂为醇酯十二、乙二醇丁醚、丙二醇甲醚、丙二醇丁醚或丙二醇苯醚中的一种或几种。
述流平剂为有机硅类流平剂或丙烯酸类流平剂。
所述的分散剂为EVA蜡或脂肪醇聚氧乙烯醚。
本发明的EVA乳液与水泥、石膏等固化混合，增加成品的硬度。此外，还提高了水泥、石膏制品的防水性，用于基材处理能有优异的湿粘性、初黏力以及抗剪切性能，对基材粘结适用性广、耐热性能好、具良好的防火性能。表涂或溶剂的情况下，能够材料产品表面形成柔韧且透明度较好的胶膜，增加亮度和耐度性能。
参考以下详细说明更易于理解本申请的上述以及其他特征、方面和优点。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将结合本发明实施例，对本发明实施例的技术方案进行清楚、完整地描述。显然，所描述的实施例是本发明的一部分实施例，而不是全部的实施例。基于所描述的本发明的实施例，本领域普通技术人员在无需创造性劳动的前提下所获得的所有其它实施例，都属于本发明保护的范围。
除非另作定义，此处使用的技术术语或者科学术语应当为本发明所属领域内具有一般技能的人士所理解的通常意义。本发明专利申请说明书以及权利要求书中使用的“第一”、“第二”以及类似的词语并不表示任何顺序、数量或者重要性，而只是用来区分不同的组成部分。同样，“一个”或者“一”等类似词语也不表示数量限制，而是表示存在至少一个。
一种水泥石膏制品用助剂，所述助剂由100重量份的EVA乳液、0.01-0.1重量份的苯丙三氮坐、0.01-0.1重量份的分散剂、0.01-0.1重量份的流平剂、0.01-0.1重量份的成膜助剂组成，所述EVA乳液中EVA的质量含量为10-50％，所述EVA的数均分子量为1000-8000。
所述EVA为梳状有机硅改性接枝EVA。
梳状有机硅改性接枝EVA改性方法采用离子型端-NCO的聚氨酯EVA共聚乳液进行接枝反应、冉然后加入硅烷偶联剂进行支链端基改性制备得到。
所述成膜助剂为醇酯十二、乙二醇丁醚、丙二醇甲醚、丙二醇丁醚或丙二醇苯醚中的一种或几种。
述流平剂为有机硅类流平剂或丙烯酸类流平剂。
所述的分散剂为EVA蜡或脂肪醇聚氧乙烯醚。
一种水泥石膏制品的制作方法，包括以下步骤：
将水泥石膏制品助剂按照混凝土总质量1-3％的加入混凝土强度等级为C20自流平水泥中，流平固化后自然晾干8小时后，在自流平水泥表面按照100-300g/平方米喷涂本发明的助剂，自然晾干6小时后，用200～300目抛光片打磨地坪2次，后用500～600目抛光片打磨地坪1次，再用1000目抛光片打磨地坪1次，打磨过程中，保持打磨转速使得表面温度高于80摄氏度至少20分钟；
本发明的EVA乳液与水泥、石膏等固化混合，增加成品的硬度。此外，还提高了水泥、石膏制品的防水性，用于基材处理能有优异的湿粘性、初黏力以及抗剪切性能，对基材粘结适用性广、耐热性能好、具良好的防火性能。表涂或溶剂的情况下，能够材料产品表面形成柔韧且透明度较好的胶膜，增加亮度和耐度性能。
本发明使用方法如下：
将本发明的助剂按照混凝土总质量1％的加入混凝土强度等级为C20自流平水泥中，流平固化后自然晾干8小时后，在自流平水泥表面按照100g/平方米喷涂本发明的助剂，自然晾干6小时后，用200～300目抛光片打磨地坪2次，后用500～600目抛光片打磨地坪1次，再用1000目抛光片打磨地坪1次，打磨过程中，保持打磨转速使得表面温度高于80摄氏度至少20分钟。测试混凝土的莫氏硬度。采用EVA(数均分子量为200，EVA乳液)制备得到的混凝土的莫氏硬度为7。采用改性EVA(梳状有机硅改性接枝EVA改性方法采用离子型端-NCO的聚氨酯EVA共聚乳液进行接枝反应、冉然后加入硅烷偶联剂进行支链端基改性制备得到。)制备得到的混凝土的莫氏硬度为8。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点,对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这中叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (10)
1.一种水泥石膏制品用助剂，其特征在于，所述助剂由100重量份的EVA乳液、0.01-0.1重量份的苯丙三氮坐、0.01-0.1重量份的分散剂、0.01-0.1重量份的流平剂、0.01-0.1重量份的成膜助剂组成，所述EVA乳液中EVA的质量含量为10-50％，所述EVA的数均分子量为1000-8000。
2.根据权利要求1所述的一种水泥石膏制品用助剂，其特征在于，所述EVA为梳状有机硅改性接枝EVA。
3.根据权利要求1所述的一种水泥石膏制品用助剂，其特征在于，所述成膜助剂为醇酯十二、乙二醇丁醚、丙二醇甲醚、丙二醇丁醚或丙二醇苯醚中的一种或几种。
4.根据权利要求1所述的一种水泥石膏制品用助剂，其特征在于，所述流平剂为有机硅类流平剂或丙烯酸类流平剂。
5.根据权利要求1所述的一种水泥石膏制品用助剂，其特征在于，所述的分散剂为EVA蜡或脂肪醇聚氧乙烯醚。
6.一种水泥石膏制品的制作方法，其特征在于，包括以下步骤：
将水泥石膏制品助剂按照混凝土总质量1-3％的加入混凝土强度等级为C20自流平水泥中，流平固化后自然晾干8小时后，在自流平水泥表面按照100-300g/平方米喷涂本发明的助剂，自然晾干6小时后，用200～300目抛光片打磨地坪2次，后用500～600目抛光片打磨地坪1次，再用1000目抛光片打磨地坪1次，打磨过程中，保持打磨转速使得表面温度高于80摄氏度至少20分钟；
所述水泥石膏制品助剂由100重量份的EVA乳液、0.01-0.1重量份的苯丙三氮坐、0.01-0.1重量份的分散剂、0.01-0.1重量份的流平剂、0.01-0.1重量份的成膜助剂组成，所述EVA乳液中EVA的质量含量为10-50％，所述EVA的数均分子量为1000-8000。
7.根据权利要求6所述的一种水泥石膏制品的制作方法，其特征在于，所述EVA为梳状有机硅改性接枝EVA。
8.根据权利要求6所述的一种水泥石膏制品的制作方法，其特征在于，所述成膜助剂为醇酯十二、乙二醇丁醚、丙二醇甲醚、丙二醇丁醚或丙二醇苯醚中的一种或几种。
9.根据权利要求6所述的一种水泥石膏制品的制作方法，其特征在于，述流平剂为有机硅类流平剂或丙烯酸类流平剂。
10.根据权利要求6所述的一种水泥石膏制品的制作方法，其特征在于，所述的分散剂为EVA蜡或脂肪醇聚氧乙烯醚。