CN113880554B - Method for preparing black ceramic material - Google Patents
Method for preparing black ceramic material Download PDFInfo
- Publication number
- CN113880554B CN113880554B CN202111217355.2A CN202111217355A CN113880554B CN 113880554 B CN113880554 B CN 113880554B CN 202111217355 A CN202111217355 A CN 202111217355A CN 113880554 B CN113880554 B CN 113880554B
- Authority
- CN
- China
- Prior art keywords
- ceramic
- iron
- raw material
- additive
- black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a method for preparing a black ceramic material, which comprises the following steps: adding an iron-containing material and an additive into a base material to form a ceramic raw material, and sintering the ceramic raw material to be black in an air atmosphere to obtain a black ceramic material; wherein, the additive contains one or more of Mn, Ni and Mg ions; based on the total weight of the ceramic raw material, the mixing amount of the iron-containing material is 30-70 wt%, and the mixing amount of the additive is 2-20 wt%. The method can directly utilize the 3-valent iron ions in the iron-containing material, does not need to reduce the 3-valent iron ions into 2-valent iron ions, and does not need non-oxidizing or reducing atmosphere, so that the 3-valent iron ions in the material can react with Mn, Ni and Mg ions of the additive to generate the required mineral phase, and the mineral phase directly acts on the ceramic material to blacken, thereby obviously reducing the preparation cost, having simple preparation process and good performance of the ceramic product. The invention is suitable for the fields of solid waste resource utilization and novel building material preparation.
Description
Technical Field
The invention belongs to the field of solid waste resource utilization and novel building material preparation, and particularly relates to a method for preparing a black ceramic material.
Background
Part of industrial solid wastes contain a large amount of iron oxide components, such as red mud, iron tailings, iron-containing dust and the like, and part of low-grade ores, inferior ores and muck contain a large amount of iron oxide components, so that the iron oxide components are difficult to be recycled at present. The common characteristics of the materials are that the mass percentage of the ferric oxide is more than 25 percent, and the main valence state of the iron ions is 3-valent iron.
The black ceramic material is a ceramic material with larger use amount in ceramic products and has high added value. If the iron-containing materials can be prepared into black ceramic raw materials, the added value and the market space of ceramic products can be improved. However, most of the iron ions and minerals with a valence of 3 are yellow, orange-yellow or brownish red, and ceramics fired in air, which contain a large amount of iron ions with a valence of 3, also appear yellow, orange-yellow or brownish red.
Since 2-valent iron is a black colorant, the industry typically reduces the 3-valent iron ions to 2-valent iron ions, which react with chromium, manganese, vanadium or other mineral ions to form black ceramics. However, these methods require non-oxidizing or reducing atmosphere, or add reducing agents such as coal dust, which results in higher cost; in addition, the prepared black ceramic has poor performance and is easy to foam, most of the 3-valent iron still forms brown or yellow mineral phases such as hematite and the like, and the black ceramic is difficult to convert into black.
Disclosure of Invention
The technical problem solved by the invention is to provide a method for preparing a black ceramic material, which does not need to reduce 3-valent iron ions into 2-valent iron ions and non-oxidizing or reducing atmosphere, obviously reduces the preparation cost, and has simple preparation process and good ceramic product performance.
In order to achieve the purpose, the invention provides the following technical scheme:
a method of making a black ceramic material, the method comprising:
adding an iron-containing material and an additive into a base material to form a ceramic raw material, and sintering the ceramic raw material to be black in an air atmosphere to obtain a black ceramic material;
wherein, the additive contains one or more of Mn, Ni and Mg ions; based on the total weight of the ceramic raw material, the mixing amount of the iron-containing material is 30-70 wt%, and the mixing amount of the additive is 2-20 wt%.
As an embodiment of the invention, the iron-bearing material is a solid waste or mineral containing ferric iron and having an iron oxide mass content of more than 25% by weight;
the mass content of ferric ions in the iron-containing material is higher than that of ferrous ions;
the iron-containing material is one or more of iron tailings, red mud, iron-containing dust, cheap iron-containing minerals and muck.
As an embodiment of the invention, the additive is selected from one or more of a magnesium oxide-containing material, a manganese oxide-containing material and a nickel oxide-containing material; preferably, the additive is selected from one or more of tailings, smelting slag, waste battery materials and waste electrode materials; the sum of the contents of Mn, Ni and Mg elements in the additive is 5-40 wt%;
optionally, the additive is selected from one or more of chemical magnesium oxide, carbonate, manganese ore or ferromanganese ore, manganese oxide, carbonate and nickel oxide and carbonate, and the sum of the contents of Mn, Ni and Mg in the additive is 40-79 wt%.
In one embodiment of the present invention, the base material is a ceramic mixed material composed of one or more of a quartz-based ceramic material, a feldspar-based ceramic material, and a clay-based ceramic material.
As an embodiment of the present invention, the sintering conditions are: the temperature is 1000 ℃ and 1200 ℃;
the black ceramic material comprises one or more of ceramic tiles, black bricks, rock plates, stone-like ceramic thick bricks, sintered bricks, archaized bricks, ancient bricks, sintered tiles and ceramic plates.
As an embodiment of the present invention, a spinel mineral in which ferric ions are present and one or more ions of manganese, magnesium and nickel are present together in the black ceramic material;
the spinel mineral comprises MnFe2O4,NiFe2O4,(Mg,Mn)(Fe,Al)2O4And MgFe2O4One or more of them.
As an embodiment of the present invention, the black ceramic material contains a pyroxene mineral or/and a calcium iron garnet mineral that contains two or more ions of solid-solution iron, manganese, magnesium and nickel;
the pyroxene mineral comprises (Mg, Mn, Fe, Ca, Ni) (Fe, Ni, Mg, Mn) Si2O6,Na(Al,Fe)Si2O6,Ca(Fe,Al)(Si,Al)2O6One or more of the above;
the calcium iron garnet mineral comprises Mn3Fe2[SiO4]3、Fe3Fe2[SiO4]3And (Ca, Mg)3Fe2[SiO4]3One or more of them.
The technical scheme provided by the invention at least brings the following beneficial effects:
the method can directly utilize the 3-valent iron ions in the iron-containing material, does not need to reduce the 3-valent iron ions into 2-valent iron ions, and does not need non-oxidizing or reducing atmosphere, so that the 3-valent iron ions in the material can react with Mn, Ni and Mg ions of the additive to generate the required mineral phase, and the mineral phase directly acts on the ceramic material to blacken, thereby obviously reducing the preparation cost, having simple preparation process and good performance of the ceramic product.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, embodiments of the present invention will be described in further detail below.
Example 1: the red mud ceramic added with the manganese ore with the mass purity of 64.7 percent, the red mud content in the ceramic raw material is 40 percent by weight, meanwhile, the manganese ore raw material which contains 64.7 percent by weight of manganese oxide is added into the ceramic raw material, and the content in the ceramic raw material is 5 percent by weight. The red mud ceramic is sintered in the air at the sintering temperature of 1130-1190 ℃ and is dark black. The mineral phase contains spinel minerals such as MnFe spinel2O4) And magnesium titanium ore (MgTi)2O5) Hematite, quartz, etc. The spinel minerals contain Mn2+、Fe3+And O2-And ions which have the function of making the red mud ceramic black after solid solution or reaction. Oxygen in red mud ceramicsThe iron oxide content was 14.9 wt%, the magnesium oxide content was 2.4 wt%, and the manganese oxide content was 8.7 wt%.
Example 2: red mud ceramic added with nickel oxide (chemical purity) with mass purity of 98%
The red mud content in the ceramic raw material is 40 wt%, and the chemically pure nickel oxide raw material containing 98 wt% manganese oxide is added into the ceramic raw material, and the content in the ceramic raw material is 10 wt%. The red mud ceramic is sintered in the air at the sintering temperature of 1130-1190 ℃ and is black in color. The mineral phase contains spinel minerals such as nickel magnetite (NiFe)2O4) And calspodumene (CaFeSi)2O6) Hematite, quartz, nickel titanium ore (NiTiO)3) And the like. These minerals contain Ca2+、、Fe3+、Ni2+And O2-And plasma, wherein the ions have the function of making the red mud ceramic black after solid solution or reaction. The red mud ceramic has an iron oxide content of about 14.9 wt.% and a nickel oxide content of about 9.8 wt.%.
Example 3: red mud ceramic added with talc
The red mud content in the ceramic raw material is 40 wt%, and the talc raw material containing 16 wt% of magnesium oxide is added into the ceramic raw material, and the red mud content in the ceramic raw material is 10 wt%. The red mud ceramic is sintered in a roller kiln at the sintering temperature of 1160-1180 ℃ and is brownish black in color. The ore phase contains spinel (Mg (Al, Fe) with magnesium, aluminum and iron solid solution2O4Forsterite (Mg)2SiO4) And hematite and anorthite. These minerals contain Mg2+、Fe3+、Al3+And O2-And plasma, wherein the ions have the function of making the red mud ceramic black after solid solution or reaction. However, the spinel formed was in the form of a solid solution, which reduced the blackness of the sample, and the color was slightly shifted to brown, but the whole was still pale black. The red mud ceramic contains about 15.3 wt% iron oxide, about 4.5 wt% magnesium oxide, and about 19.4 wt% aluminum oxide.
Example 4: red mud ceramic added with manganese-containing tailings
The red mud content in the ceramic raw material is 40 wt%, and meanwhile, the manganese-containing tailing raw material which contains 16.9 wt% of manganese oxide is added into the ceramic raw material, and the content in the ceramic raw material is 10 wt%. The red mud ceramic is sintered in air at the sintering temperature of 1130-1190 ℃ and is black in color. The mineral phase contains spinel minerals such as MnFe spinel2O4) Calcium iron garnet mineral (Ca)3Fe2(SiO4)3) And so on. The spinel minerals and calcium iron garnet minerals contain Mn2+、Fe3+、Ca2+And O2-And plasma, wherein the ions have the function of making the red mud ceramic black after solid solution or reaction. The red mud ceramic contains about 16.9 wt% of iron oxide, about 1.9 wt% of manganese oxide and about 5.7 wt% of calcium oxide.
Example 5: red mud ceramic added with manganese-containing tailings
The red mud content in the ceramic raw material is 40 wt%, and meanwhile, the manganese-containing tailing raw material which contains 16.9 wt% of manganese oxide is added into the ceramic raw material, and the content of the manganese-containing tailing raw material in the ceramic raw material is 20 wt%. The red mud ceramic is sintered in air at the sintering temperature of 1130-1190 ℃ and is dark black. The mineral phase contains spinel minerals such as MnFe spinel2O4) And manganese spinel (MnAl)2O4) Calcium iron garnet mineral (Ca)3Fe2(SiO4)3) And hematite, quartz, anorthite, etc. The spinel minerals and calcium iron garnet minerals contain Mn2+、Fe3+、Ca2+And O2-And plasma, wherein the ions have the function of making the red mud ceramic black after solid solution or reaction. The red mud ceramic contains about 19.5 wt% of iron oxide, about 3.8 wt% of manganese oxide and about 6.2 wt% of calcium oxide.
Example 6: red mud ceramic added with silicomanganese smelting slag
The red mud content in the ceramic raw material is 40 wt%, and meanwhile, the silicomanganese smelting slag (abbreviated as silicomanganese slag) raw material which contains 9.4 wt% of manganese oxide is added into the ceramic raw material, and the content of the red mud in the ceramic raw material is 10 wt%. The red mud ceramic is sintered in the air,the sintering temperature is 1130-1180 ℃, and the color is brownish black. The mineral phase contains spinel minerals such as MgFe2O4) Manganese-iron spinel (MnFe)2O4) And hematite, quartz, anorthite, and the like. The spinel mineral contains Mn2+、Mg2+、Fe3+And O2-And ions which have the function of making the red mud ceramic black after solid solution or reaction. The red mud ceramic contains about 14.4 wt% of iron oxide, about 1.2 wt% of manganese oxide, and about 4.7 wt% of magnesium oxide.
Example 7: red mud ceramic added with ferronickel smelting slag
The red mud content in the ceramic raw material is 40 wt%, meanwhile, ferronickel smelting slag (nickel-iron slag for short) raw material which contains 2.6 wt% of nickel oxide and 16.4 wt% of magnesium oxide is added into the ceramic raw material, and the red mud content in the ceramic raw material is 10 wt%. The red mud ceramic is sintered in air at the sintering temperature of 1130-1180 ℃ and is light black in color. The mineral phase contains spinel minerals such as MgFe2O4) Nickel-iron spinel (NiFe)2O4) And hematite, quartz, anorthite, and the like. The generated spinel mineral contains Mg2+、Ni2+、Fe3+And O2-And ions which have the function of making the red mud ceramic black after solid solution or reaction. The red mud ceramic contains about 15.2 wt% of iron oxide, about 0.3 wt% of nickel oxide and about 2.4 wt% of magnesium oxide.
Example 8: adding iron tailing ceramics containing manganese oxide
The tailing content in the ceramic raw material is 30 wt%, and meanwhile, a manganese oxide chemical pure raw material which contains 98 wt% of manganese oxide is added into the ceramic raw material, and the content in the ceramic raw material is 10 wt%. The tailing ceramics is sintered in the air at the sintering temperature of 1130-1190 ℃ and is black in color. The mineral phase contains spinel minerals such as MnFe spinel2O4) And manganese spinel (MnAl)2O4) And hematite, quartz, and the like. These minerals contain Mn2+、Fe3+、Ca3+、Si4+And O2-And plasma, wherein the ions have the function of making the tailing ceramic black after solid solution or reaction. The tailings ceramic had an iron oxide content of about 11.4 wt%, a manganese oxide content of about 8.7 wt%, and an alumina content of about 21.5 wt%.
Example 9: red mud ceramic added with black slag
The red mud content in the ceramic raw material was 40 wt%, and the black slag raw material, which contains 4.08 wt% of manganese oxide and 2.66 wt% of magnesium oxide, was added to the ceramic raw material, and the content in the ceramic raw material was 17 wt%. The red mud ceramic is sintered in air at 1150-1170 ℃ and is black in color. The mineral phase contains spinel minerals such as magnesium ferrite (MgFe)2O4) Manganese-iron spinel (MnFe)2O4) And hematite, quartz, anorthite, and the like. The spinel minerals contain Mn2+、Mg2+、Fe3+And O2-And ions which have the function of making the red mud ceramic black after solid solution or reaction. The red mud ceramic contains about 23.6 wt% of iron oxide, about 0.9 wt% of manganese oxide and about 4.2 wt% of magnesium oxide.
Comparative example: mineral or solid waste without addition of one or more of manganese oxide, magnesium oxide, zinc oxide and nickel oxide
The red mud contains 34.1 wt% of Fe2O3The main mineral phases are hematite, quartz, calcium iron garnet, calcium magnesium garnet and perovskite, the iron ions mainly comprise ferric iron ions, and the color is orange red. The red mud content in the red mud ceramic is 40 wt%. The red mud ceramic is sintered in the air, the sintering temperature is 1130-1190 ℃, the color is brownish red, the ore phase contains quartz, hematite, calcium iron ore, rutile and albite, and the minerals mainly contain Fe3+、Si4+、Ca2+、Na+、O2-And (3) plasma. The red mud ceramic contains about 15.7 wt% of iron oxide, about 1.2 wt% of magnesium oxide, and about 4.4 wt% of sodium oxide.
The invention researches and analyzes the manganese-containing tailings, the nickel-iron slag and the likeThe manganese, nickel and magnesium raw materials can be mixed with Fe in red mud or tailings3+The reaction is combined to generate spinel minerals, or one of garnet group minerals and pyroxene minerals, such as ferromanganese spinel, nickel magnetite, pleonaste, calcium iron garnet and the like, can be generated to make the red mud ceramic show black under the reflection of visible light. And the degree of black color varies depending on the content of the substances. The invention provides a research idea for converting ferric ion-rich substances such as red mud into spinel substances, improves the additional value and market competition space of red mud or iron tailing ceramics and the like, and has the advantages of low production cost, simple process, remarkable effect and the like.
The above description is only for the purpose of illustrating the preferred embodiments of the present invention and should not be taken as limiting the scope of the present invention, which is intended to cover any modifications, equivalents, improvements, etc. within the spirit and scope of the present invention.
Claims (8)
1. A method of making a black ceramic material, the method comprising:
adding an iron-containing material and an additive into a base material to form a ceramic raw material, and sintering the ceramic raw material to be black in an air atmosphere to obtain a black ceramic material;
wherein the additive contains one or two of Mn and Ni ions; based on the total weight of the ceramic raw material, the mixing amount of the iron-containing material is 30-70 wt%, and the mixing amount of the additive is 2-20 wt%;
the iron-containing material is solid waste or mineral containing ferric iron and the mass content of ferric oxide exceeds 25 weight percent; the mass content of ferric ions in the iron-containing material is higher than that of ferrous ions; the iron-containing material is one or more of iron tailings, red mud, iron-containing dust, cheap iron-containing minerals and muck;
the sintering conditions are as follows: temperature 1130-1200 ℃.
2. The method of claim 1, wherein the additive is selected from one or both of a manganese oxide containing material and a nickel oxide containing material.
3. The method of claim 2, wherein the additive is selected from one or more of tailings, smelting slag, waste battery material and waste electrode material; the sum of the contents of Mn and Ni elements in the additive is 5-40 wt%.
4. The method according to claim 3, wherein the additive is one or more selected from manganese ore, ferromanganese ore, manganese oxide, manganese carbonate, nickel oxide and nickel carbonate, and the sum of the contents of Mn and Ni elements in the additive is 40-79 wt%.
5. The method according to claim 1, wherein the base material is a ceramic mixed raw material composed of one or more of a quartz-based ceramic raw material, a feldspar-based ceramic raw material, and a clay-based ceramic raw material.
6. The method of claim 1, wherein the black ceramic material comprises one or more of a rock plate, a stone-like ceramic tile, an antique brick, a sintered tile, and a ceramic plate.
7. The method according to claim 1, characterized in that a spinel mineral of ferric ions and one or both of manganese and nickel ions is present in the black ceramic material;
the spinel mineral comprises MnFe2O4、NiFe2O4One or two of them.
8. The method according to claim 1, characterized in that pyroxene minerals or/and calcium iron garnet minerals in which ferric ions are present and one or more of manganese and nickel are present simultaneously in the black ceramic material;
the pyroxene mineral comprises Na (Al, Fe)Si2O6、Ca(Fe,Al)(Si,Al)2O6One or two of (a) and (b);
the calcium iron garnet mineral comprises Mn3Fe2[SiO4]3、Fe3Fe2[SiO4]3One or two of them.