CN113717624A - 一种环保水性聚氨酯防水涂料及制作方法 - Google Patents
一种环保水性聚氨酯防水涂料及制作方法 Download PDFInfo
- Publication number
- CN113717624A CN113717624A CN202110961451.1A CN202110961451A CN113717624A CN 113717624 A CN113717624 A CN 113717624A CN 202110961451 A CN202110961451 A CN 202110961451A CN 113717624 A CN113717624 A CN 113717624A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof coating
- environment
- polyurethane waterproof
- mixed solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及防水涂料技术领域，名称是一种环保水性聚氨酯防水涂料及制作方法，由下述重量份的原材料制备而成：水性聚氨酯分散体乳液200—400份，填料130—360份，成膜助剂5—10份，防腐防霉剂2—8份，分散剂5—10份，pH调节剂，消泡剂5—10份，去离子水50—80份，润湿剂2—5份。本发明的水性聚氨酯防水涂料通过水分挥发固化成膜，不含有机溶剂，无刺激性气味，具有聚氨酯的优异韧性、弹性以及粘结力，可对多种基材提供持久保护，能有效抵抗基层的收缩以及变形开裂；其卓越的低温性能，可适用于温差较大的地域及场所；吸水率低，长期浸水不会发生溶胀。
Description
技术领域
本发明涉及防水技术领域，具体的是涉及防水涂料及制作方法。
背景技术
中国防水材料市场年需求量超过20亿平方米，其中防水涂料约占27%，产量达到45万吨。聚氨酯防水市场占防水涂料市场的重要部分，约30%。防水涂料向无溶剂水性化方向发展，聚氨酯防水市场正处于“油转水”的阶段。目前，高性能环保型水性防水涂料是我国防水市场上的重点。在防水市场上，虽然一直有水性聚氨酯防水涂料的存在，但是这些水性聚氨酯防水涂料与真正的水性聚氨酯类相比，其性能指标及防水效果均比较差，例如产品的化学性质稳定不佳，耐候性较差，不能长期经受日光的照射，拉伸强度低，延伸率小，弹性差，防水效果差等。
其次是传统聚氨酯防水涂料属于反应型防水涂料，目前国内聚氨酯防水涂料主要由预聚体、增塑剂、无机填料、颜料、交联剂、溶剂和助剂组成。首先是主要的生产原料甲苯二异氰酸酯(TDI)挥发性强，具有强烈的刺激气味，有毒，对人体粘膜有刺激性，其次是有机溶剂，在使用过程中会产生挥发，对人体和环境有害且不环保，所以制备一种高性能耐水环保的防水涂料迫在眉睫。
发明内容
本发明的目的就是针对上述缺点，提供一种环保水性聚氨酯防水涂料产品及制作方法。
本发明环保水性聚氨酯防水涂料的制作方法的技术方案这样实现：
a、将重量是100—200份的水性聚氨酯分散体乳液、5—10份的阴离子表面活性剂、3—6份的消泡剂放置在反应釜中搅拌均匀，加入pH调节剂调至初步混合液呈现弱碱性，得到初步混合液；
b、向具有初步混合液的反应釜中加入沉淀硫酸钡和/或钛白粉（填料）130—360份，充分搅拌，得到二级混合液；
c、向具有二级混合液的反应釜中加入100—200份的水性聚氨酯分散体乳液、重量是50—80份去离子水、5—9份的消泡剂搅拌均匀，得到三级混合液；
d、将上述三级混合液里面加入重量是5—10份的邻苯二甲酸二甲酯（成膜助剂），润湿剂2—5份、得到四级混合液；
e、将上述四级混合液上面的气泡破碎，用滤网过滤即得到所述的水性聚氨酯防水涂料。
较好的，所述的阴离子表面活性剂是分散剂5040。
较好的，所述的在步骤a中得到的初步混合液还用PH调节剂将初步混合液调制成弱碱性。
较好的，所述的PH调节剂是AMP-95。
较好的，所述的步骤a中水性聚氨酯分散体乳液是150份、阴离子表面活性剂7.5份、消泡剂是4份；
较好的，所述的步骤b中的沉淀硫酸钡和钛白粉（填料）是130—360份。
较好的，所述的步骤 c的水性聚氨酯分散体乳液是150份、去离子水的重量是65份、消泡剂是7份。
较好的，所述的步骤 d中还加入2—8份重量的防腐防霉剂。
本发明的环保水性聚氨酯防水涂料的技术方案是：环保水性聚氨酯防水涂料，由上述方法制得的防水涂料。
本发明的有益效果是：
（1）本发明所述的聚氨酯防水涂料是一种以水性聚氨酯分散体为主要成膜物质，加入填料及其他助剂配制而成，通过水分挥发固化成膜的单组分防水材料。
（2）本发明所述的水性聚氨酯防水涂料不含有机溶剂，无刺激性气味，环保性能优异，超低的VOC，无毒无害，绿色健康安全。
（3）本发明所述的水性聚氨酯防水涂料具有聚氨酯的优异韧性、弹性以及粘结力，可对多种基材提供持久保护，能有效抵抗基层的收缩以及变形开裂。
（4）本发明所述的水性聚氨酯防水涂料具有卓越的低温性能，可适用于温差较大的地域及场所。
（5）本发明所述的水性聚氨酯防水涂料吸水率低，耐水性强，长期浸水不会发生溶胀。施工便捷，施工效率高、多样化，可在无明水基面施工。
（6）本发明所述的水性聚氨酯防水涂料适用性广，广泛适用于建筑室内、屋面、地下、新建及维修金属屋面以及密闭半密闭、受限空间的防水工程。
具体实施方式
下面结合实施例对本发明作进一步的描述。
首先，对部分原料做如下介绍：
水性聚氨酯分散体乳液：万华化学生产的Archsol-8355阴离子型脂肪族水性聚氨酯分散体；
沉淀硫酸钡：本发明要求为800目，它的主要作用是填料。阴离子表面活性剂：是一类物质，包括羧酸盐、磺酸盐、硫酸酯盐和磷酸酯盐等，在下面的实施例中具体使用分散剂5040，它的主要作用是分散剂；
钛白粉：四川龙蟒集团生产的R996金红石型钛白粉，它的主要作用是填料；
消泡剂：矿物油基消泡剂210、矿物油基消泡剂3858中的一种或两种，它的主要作用是消泡；
邻苯二甲酸二甲酯：这里用作成膜助剂；
阴离子表面活性剂：这里用作分散剂；
聚醚改性聚二甲基硅氧烷：这里用作润湿剂。
将上述材料按照下面的步骤生产：
a、将上述步骤a中所用的水性聚氨酯分散体乳液、步骤 a中所用的阴离子表面活性剂、步骤 a中所用的消泡剂放置在反应釜中搅拌均匀，加入pH调节剂调至初步混合液呈现弱碱性，得到初步混合液；
b、向具有初步混合液的反应釜中加入上述步骤 b中所用的沉淀硫酸钡和钛白粉，充分搅拌，得到二级混合液；
c、向具有二级混合液的反应釜中加入步骤 c中所用的去离子水、步骤 c中所用的水性聚氨酯分散体乳液、步骤 c中所用的消泡剂搅拌均匀，得到三级混合液；
d、将上述三级混合液里面加入步骤 d中所用的邻苯二甲酸二甲酯，润湿剂，得到四级混合液；
e、将上述四级混合液上面的气泡破碎，用滤网过滤即得到所述的水性聚氨酯防水涂料。
分别制成制成1-1、1-2、1-3产品。
根据标准GB/T 19250-2013Ⅰ型测试产品的性能，结果如表2所示：
表11-1、1-2、1-3水性聚氨酯防水涂料产品性能检测结果
以上事实证明：本发明环保水性聚氨酯防水涂料各项指标均符合国家标准，且具有良好的粘结和不透水性，产品的化学性质稳定，耐候性优异，能长期经受日光的照射，拉伸强度高，延伸率大，弹性好，防水效果好。
事实上，发明人做过许多类似的实验，得出相同的结论，本领域的技术技术人员，按照此方法还可以做出许多实验和推理，不再赘述。
将上述实施例中的沉淀硫酸钡换成钛白粉或沉淀硫酸钡和钛白粉的混合物，得到同样的效果。
将上述实施例中的矿物油基消泡剂210换成矿物油基消泡剂3858，得到同样的效果。
在上述实施例中，在任一步骤中加入防腐防霉剂2—8份，最好是5份，所得到的环保水性聚氨酯防水涂料还具有较好的防腐防霉的效果。
较好的，步骤b中所述的加入pH调节剂调至初步混合液呈现弱碱性，是pH=10～12。
较好的，在上述步骤c中，将二级混合液、将去离子水、消泡剂都加热至60～70℃的情况下，配置成三级混合液，其他工艺不变，所得到的防水涂料在低温弯折性上更加提升，实践证明，可以达到-40—-45℃，无裂纹。
较好的，在上述步骤d中、将加入的邻苯二甲酸二甲酯、润湿剂都加热至50—50℃的情况下，配置四级混合液；其他工艺不变，所得到的防水涂料在拉伸强度上有更加显著提升，实践证明，可以达到拉伸强度≥4.2～5.5 /Mpa。
以上实施例仅为本发明的部分实施例，但本发明的宗旨并不限于此，任何本领域的技术人员在本发明的领域内，所作的变化或修饰皆涵盖在本发明的专利范围内。
Claims (10)
1.一种环保水性聚氨酯防水涂料的制作方法，其特征是，包括如下步骤：
a、将重量是100—200份的水性聚氨酯分散体乳液、5—10份的阴离子表面活性剂、3—6份的消泡剂放置在反应釜中搅拌均匀，加入pH调节剂调至初步混合液呈现弱碱性，得到初步混合液；
b、向具有初步混合液的反应釜中加入沉淀硫酸钡和/或钛白粉130—360份，充分搅拌，得到二级混合液；
c、向具有二级混合液的反应釜中加入100—200份的水性聚氨酯分散体乳液、重量是50—80份去离子水、5—9份的消泡剂搅拌均匀，得到三级混合液；
d、将上述三级混合液里面加入重量是加入5—10份的邻苯二甲酸二甲酯，润湿剂2—5份、得到四级混合液；
e、将上述四级混合液上面的气泡破碎，用滤网过滤即得到所述的水性聚氨酯防水涂料。
2.根据权利要求1所述的环保水性聚氨酯防水涂料的制作方法，其特征是：所述的阴离子表面活性剂是分散剂5040。
3.根据权利要求1或2所述的环保水性聚氨酯防水涂料的制作方法，其特征是：所述的PH调节剂是AMP-95，pH调节剂加入1—3份。
4.根据权利要求1或2所述的环保水性聚氨酯防水涂料的制作方法，其特征是：所述的步骤a中水性聚氨酯分散体乳液是150份的、阴离子表面活性剂7.5份、消泡剂是4份。
5.根据权利要求4所述的环保水性聚氨酯防水涂料的制作方法，其特征是：所述的步骤b中的沉淀硫酸钡是100—300份，钛白粉是30—60份。
6.根据权利要求5所述的环保水性聚氨酯防水涂料的制作方法，其特征是：所述的步骤b中的沉淀硫酸钡是200份，钛白粉是45份。
7.根据权利要求4、5或6所述的环保水性聚氨酯防水涂料的制作方法，其特征是：所述的步骤 c的水性聚氨酯分散体乳液150份、去离子水的重量是65份、消泡剂是7份。
8.根据权利要求7所述的环保水性聚氨酯防水涂料的制作方法，其特征是：所述的步骤d中还加入2—8份重量的防腐防霉剂。
9.根据权利要求8所述的环保水性聚氨酯防水涂料的制作方法，其特征是：所述防腐防霉剂份数是5份。
10.一种环保水性聚氨酯防水涂料，其特征是:它是由上述方法制得的防水涂料。