CN113652024A - 一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料及其制备方法 - Google Patents
一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料及其制备方法 Download PDFInfo
- Publication number
- CN113652024A CN113652024A CN202111096721.3A CN202111096721A CN113652024A CN 113652024 A CN113652024 A CN 113652024A CN 202111096721 A CN202111096721 A CN 202111096721A CN 113652024 A CN113652024 A CN 113652024A
- Authority
- CN
- China
- Prior art keywords
- sheath material
- preparation
- retardant
- micro
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料及其制备方法，所述护套料包含以下材料：聚烯烃树脂、弹性体、相容剂、抗氧剂、引发剂、润滑剂、阻燃剂和阻燃协效剂，所述制备方法包含以下步骤：步骤一：将聚烯烃树脂、弹性体、相容剂、抗氧剂、引发剂和润滑剂在密炼机中搅拌均匀；步骤二：在密炼机中加入阻燃剂及阻燃协效剂，继续密炼；步骤三：密炼完成后经双螺杆、单螺杆风冷造粒。该电伴热带用微交联低烟无卤阻燃聚烯烃护套料及其制备方法，护套料挤出稳定，加工性好，护套料有优异的耐热性能、阻燃性能及机械性能。
Description
技术领域
本发明涉及电缆料制备技术领域，具体为一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料及其制备方法。
背景技术
电伴热带是由导电聚合物和两根平行金属导线及绝缘护套层构成，在日常使用时因为电伴热带长期置于空气中，很容易产生潮湿和积水的现象，所以其护套要求有较高的耐老化性能、耐紫外光性能、抗撕裂性能，电伴热带在使用过程中会根据使用场所的不同，会有不同的加热温度设定，且有的加热时间会很长，这对其长期的耐热变形性能又提出了较高的要求，因此现有的护套料制备方法依旧存在以下缺陷：
目前，电伴热带护套料主要存在的问题是加工性能和耐热性能的兼容上，一方面，交联后的聚烯烃的阻燃性能、耐磨性能、机械性能、耐热性能都有不同程度的提高，另一方面，添加相对分子量高的树脂材料可以提高材料的耐热性能，但分子量高的树脂材料的加工性能较差，针对上述问题，急需在原有电缆护套料制备方法的基础上进行创新设计。
发明内容
本发明的目的在于提供一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料及其制备方法，以解决上述背景技术提出电伴热带护套料主要存在的问题是加工性能和耐热性能的兼容上，一方面，交联后的聚烯烃的阻燃性能、耐磨性能、机械性能、耐热性能都有不同程度的提高，另一方面，添加相对分子量高的树脂材料可以提高材料的耐热性能，但分子量高的树脂材料的加工性能较差的问题。
为实现上述目的，本发明提供如下技术方案，一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料，所述护套料包含以下材料：聚烯烃树脂、弹性体、相容剂、抗氧剂、引发剂、润滑剂、阻燃剂和阻燃协效剂。
优选的，所述制备方法包含以下步骤：
步骤一：将聚烯烃树脂、弹性体、相容剂、抗氧剂、引发剂和润滑剂在密炼机中搅拌均匀；
步骤二：在密炼机中加入阻燃剂及阻燃协效剂，继续密炼；
步骤三：密炼完成后经双螺杆、单螺杆风冷造粒。
优选的，所述步骤一中的各个组分的重量份数为：聚烯烃树脂40～60份，弹性体15～35份，相容剂15～35份，抗氧剂0.2～0.4份，引发剂0.1～0.2份，润滑剂0.5～2份，且聚烯烃树脂为聚乙烯醋酸乙烯酯、中密度聚乙烯、高密度聚乙烯、聚丙烯中的至少一种，并且聚烯烃树脂的密度为0.8～1.1g/cm3，熔融指数为1～4g/10min。
优选的，所述步骤一中的弹性体为乙烯辛烯共聚物、丁二烯共聚物、乙烯丁烯共聚物或乙丙橡胶中的至少一种。
优选的，所述步骤一中的相容剂为乙烯-辛烯共聚物接枝马来酸酐、乙烯-醋酸乙烯共聚物接枝马来酸酐或聚乙烯接枝马来酸酐中的至少一种。
优选的，所述步骤一中的抗氧剂为2，6-三级丁基-4-甲基苯酚、双(3，5-三级丁基-4-羟基苯基)硫醚、四〔β-(3，5-三级丁基-4-羟基苯基)丙酸〕季戊四醇、4，4’-硫代双(6-叔丁基-3-甲基苯酚)中的至少一种。
优选的，所述步骤一中的引发剂为过氧化二异丙苯、过氧化二苯甲酰中的至少一种。
优选的，所述步骤一中的润滑剂为聚乙烯蜡、硅酮母粒、有机硅中的至少一种。
优选的，所述步骤二中的阻燃剂150～200份，且阻燃协效剂10～30份，并且阻燃剂为硅烷处理后的氢氧化铝、氢氧化镁中的至少一种。
优选的，所述步骤二中的阻燃协效剂为二氧化二锑、硼酸锌、氰尿酸三聚氰胺中的至少一种。
与现有技术相比，本发明的有益效果是：该电伴热带用微交联低烟无卤阻燃聚烯烃护套料及其制备方法，护套料挤出稳定，加工性好，护套料有优异的耐热性能、阻燃性能及机械性能；
1.在配方中添加少量的引发剂，在不影响材料加工性能的同时使聚烯烃微交联，从而提高材料的性能；
2.在配方中添加阻燃协效剂，在提高材料阻燃性能的同时还能适当的减少阻燃剂的填充量，从而提高材料的加工性能；
3.选择硅烷处理后的阻燃剂，未经表面处理的阻燃剂在体系中流动性较差，而硅烷处理后的阻燃剂的加工性能会有较大的提升。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供一种技术方案：
实施例1
将50份聚乙烯-醋酸乙烯酯、5份高密度聚乙烯、10份聚丙烯、20份乙烯辛烯共聚物、15份乙烯-辛烯共聚物接枝马来酸酐、0.3份双(3，5-三级丁基-4-羟基苯基)硫醚、0.1份过氧化二异丙苯和2份有机硅在密炼机中搅拌均匀，再在密炼机中加入160份硅烷处理后的氢氧化铝及15份三氧化二锑继续密炼至物料全部熔融，密炼完成后经双螺杆、单螺杆风冷造粒。
实施例1性能如下：
| 项目 | 单位 | 测试方法 | 结果 | |
| 1 | 密度 | g/cm<sup>3</sup> | GB/T1033.1 | 1.51 |
| 2 | 拉伸强度 | MPa | GB/T1040 | 12.45 |
| 3 | 断裂伸长率 | ％ | GB/T1040 | 185 |
| 4 | 氧指数 | ％ | GB/T2406 | 32 |
| 5 | 20℃体积电阻率 | Ω·m | GB/T1410 | 3.46×10<sup>12</sup> |
| 6 | 热变形(90℃×4h) | ％ | GB/T8815 | 10 |
实施例2
将50份聚乙烯-醋酸乙烯酯、10份中密度聚乙烯、5份聚丙烯、15份丁二烯共聚物、20份乙烯-辛烯共聚物接枝马来酸酐、0.4份四〔β-(3，5-三级丁基-4-羟基苯基)丙酸〕季戊四醇、0.15份过氧化二苯甲酰和2份聚乙烯蜡在密炼机中搅拌均匀，再在密炼机中加入150份硅烷处理后的氢氧化镁及15份硼酸锌继续密炼至物料全部熔融，密炼完成后经双螺杆、单螺杆风冷造粒。
实施例2性能如下：
| 项目 | 单位 | 测试方法 | 结果 | |
| 1 | 密度 | g/cm<sup>3</sup> | GB/T1033.1 | 1.50 |
| 2 | 拉伸强度 | MPa | GB/T1040 | 13.16 |
| 3 | 断裂伸长率 | ％ | GB/T1040 | 180 |
| 4 | 氧指数 | ％ | GB/T2406 | 34 |
| 5 | 20℃体积电阻率 | Ω·m | GB/T1410 | 6.54×10<sup>12</sup> |
| 6 | 热变形(90℃×4h) | ％ | GB/T8815 | 12 |
实施例3
将45份聚乙烯-醋酸乙烯酯、10份中密度聚乙烯、10份聚丙烯、20份乙烯丁烯共聚物、20份聚乙烯接枝马来酸酐、0.3份双(3，5-三级丁基-4-羟基苯基)硫醚、0.15份过氧化二异丙苯和2份有机硅在密炼机中搅拌均匀，再在密炼机中加入100份硅烷处理后的氢氧化铝、50份硅烷处理后的氢氧化镁及15份三氧化二锑继续密炼至物料全部熔融，密炼完成后经双螺杆、单螺杆风冷造粒。
实施例3性能如下：
| 项目 | 单位 | 测试方法 | 结果 | |
| 1 | 密度 | g/cm<sup>3</sup> | GB/T1033.1 | 1.50 |
| 2 | 拉伸强度 | MPa | GB/T1040 | 13.18 |
| 3 | 断裂伸长率 | ％ | GB/T1040 | 190 |
| 4 | 氧指数 | ％ | GB/T2406 | 35 |
| 5 | 20℃体积电阻率 | Ω·m | GB/T1410 | 5.13×10<sup>12</sup> |
| 6 | 热变形(90℃×4h) | ％ | GB/T8815 | 9 |
尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料，其特征在于：所述护套料包含以下材料：聚烯烃树脂、弹性体、相容剂、抗氧剂、引发剂、润滑剂、阻燃剂和阻燃协效剂。
2.根据权利要求1所述的一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料的制备方法，其特征在于：所述制备方法包含以下步骤：
步骤一：将聚烯烃树脂、弹性体、相容剂、抗氧剂、引发剂和润滑剂在密炼机中搅拌均匀；
步骤二：在密炼机中加入阻燃剂及阻燃协效剂，继续密炼；
步骤三：密炼完成后经双螺杆、单螺杆风冷造粒。
3.根据权利要求2所述的一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料的制备方法，其特征在于：所述步骤一中的各个组分的重量份数为：聚烯烃树脂40～60份，弹性体15～35份，相容剂15～35份，抗氧剂0.2～0.4份，引发剂0.1～0.2份，润滑剂0.5～2份，且聚烯烃树脂为聚乙烯醋酸乙烯酯、中密度聚乙烯、高密度聚乙烯、聚丙烯中的至少一种，并且聚烯烃树脂的密度为0.8～1.1g/cm3，熔融指数为1～4g/10min。
4.根据权利要求2所述的一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料的制备方法，其特征在于：所述步骤一中的弹性体为乙烯辛烯共聚物、丁二烯共聚物、乙烯丁烯共聚物或乙丙橡胶中的至少一种。
5.根据权利要求2所述的一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料的制备方法，其特征在于：所述步骤一中的相容剂为乙烯-辛烯共聚物接枝马来酸酐、乙烯-醋酸乙烯共聚物接枝马来酸酐或聚乙烯接枝马来酸酐中的至少一种。
6.根据权利要求2所述的一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料的制备方法，其特征在于：所述步骤一中的抗氧剂为2，6-三级丁基-4-甲基苯酚、双(3，5-三级丁基-4-羟基苯基)硫醚、四〔β-(3，5-三级丁基-4-羟基苯基)丙酸〕季戊四醇、4，4’-硫代双(6-叔丁基-3-甲基苯酚)中的至少一种。
7.根据权利要求2所述的一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料的制备方法，其特征在于：所述步骤一中的引发剂为过氧化二异丙苯、过氧化二苯甲酰中的至少一种。
8.根据权利要求2所述的一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料的制备方法，其特征在于：所述步骤一中的润滑剂为聚乙烯蜡、硅酮母粒、有机硅中的至少一种。
9.根据权利要求2所述的一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料的制备方法，其特征在于：所述步骤二中的阻燃剂150～200份，且阻燃协效剂10～30份，并且阻燃剂为硅烷处理后的氢氧化铝、氢氧化镁中的至少一种。
10.根据权利要求2所述的一种电伴热带用微交联低烟无卤阻燃聚烯烃护套料的制备方法，其特征在于：所述步骤二中的阻燃协效剂为二氧化二锑、硼酸锌、氰尿酸三聚氰胺中的至少一种。