CN113603446A - 一种厨卫专用厚层抗裂砂浆及其制备方法 - Google Patents
一种厨卫专用厚层抗裂砂浆及其制备方法 Download PDFInfo
- Publication number
- CN113603446A CN113603446A CN202111090508.1A CN202111090508A CN113603446A CN 113603446 A CN113603446 A CN 113603446A CN 202111090508 A CN202111090508 A CN 202111090508A CN 113603446 A CN113603446 A CN 113603446A
- Authority
- CN
- China
- Prior art keywords
- kitchens
- bathrooms
- thick
- layer anti
- cellulose ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种厨卫专用厚层抗裂砂浆，其原材料包括以下重量百分比的材料：普通水泥10‑30％；高强石膏粉10‑30％，轻钙粉1‑5％，重钙粉1‑50％，玻化微珠1‑20％，石英砂20‑50％；木质纤维素1‑3％，纤维素醚0.1‑3％，粉状胶粘剂0.1‑10％，缓凝剂1‑5％，具有极佳的抗开裂性、高粘结强度，防止收缩、空鼓开裂的优点。本发明还公开了一种厨卫专用厚层抗裂砂浆的制备方法，制备工艺简单可靠、操作方便。
Description
技术领域
本发明涉及建筑砂浆领域，具体是指一种厨卫专用厚层抗裂砂浆及其制备方法。
背景技术
近代以来，水泥材料在建筑装修过程中大范围得到应用，其水化产物具有很高抗压强度和抗折强度，是一种良好的装饰、装修材料。但是其也存在水泥材料粘结性差、易收缩、空鼓开裂等诸多弊端。
公开号为CN109180133B的中国发明中公开了一种聚合物抗裂干粉抹灰砂浆，它以质量份数计的原料包括硅酸盐水泥55-65份、高铝水泥25-35份、石膏13-17份、粉煤灰110-120份、砂720-750份、增稠剂0.1-0.15份、纤维0.7-1.3份、聚合物乳胶粉23-27份、触变剂0.1-0.2份、触变润滑剂23-27份、减水剂0.7-1.3份。然而该发明中高铝水泥的主要矿物组成为铝酸一钙CA、铝酸二钙CA2，其遇水后的水化反应首先生成CAH10、C2AH8这二种不稳定晶体，之后会转变为稳定的C3AH6晶体，晶型转变会导致孔隙率增大、强度降低，亦即高铝水泥水化产物的耐久性很差；在硅酸盐水泥、高铝水泥、石膏三元系统中，虽然高铝水泥的主要水化产物是钙矾石AFt，但其系统的稳定性(尤其是在高碱环境下)依然很差，由其配成的砂浆的稳定性、抗裂性也很差。
发明内容
本发明的目的是克服现有技术中的不足之处，提供一种厨卫专用厚层抗裂砂浆，具有高粘结强度，防止收缩、空鼓开裂的优点。
本发明的目的之二在于提供一种厨卫专用厚层抗裂砂浆的制备方法，具有制备工艺简单可靠、操作方便的特点。
本发明的目的是通过以下技术方案来实现的：
一种厨卫专用厚层抗裂砂浆，其原材料包括以下重量百分比的材料：普通水泥10-30％；高强石膏粉10-30％，轻钙粉1-5％，重钙粉1-50％，玻化微珠1-20％，石英砂20-50％；木质纤维素1-3％，纤维素醚0.1-3％，粉状胶粘剂0.1-10％，缓凝剂1-5％。
进一步的，所述普通水泥为通用硅酸盐水泥，所述通用硅酸盐水泥的强度等级为32.5、42.5、52.5中的一种。
进一步的，所述缓凝剂为酒石酸或柠檬酸或其盐类。
进一步的，所述粉状胶粘剂为聚乙烯醇。
进一步的，所述纤维素醚为羟丙基甲基纤维素醚、羟乙基甲基纤维素醚、羟乙基纤维素醚中的一种或两种的混合。
一种厨卫专用厚层抗裂砂浆的制备方法，包括：
步骤一、将普通水泥、高强石膏粉、轻钙粉、重钙粉、玻化微珠、石英砂依次加入到无重力粉体搅拌机中，搅拌10分钟；
步骤二、再将木质纤维素、纤维素醚、粉状胶粘剂、缓凝剂依次加入到步骤一所述无重力粉体搅拌机中，继续搅拌30分钟；直至搅拌均匀，得到该厨卫专用厚层抗裂砂浆。
本发明相比现有技术具有以下优点及有益效果：
1、本发明的厨卫专用厚层抗裂砂浆利用聚乙烯醇的水溶性，使其随水迁移至砂浆界面或表面处，在界面处聚集、成膜，连接、填充界面过渡区的空隙与孔隙，以大幅提高粘结强度；利用纤维素醚在砂浆中的保水、增稠、引气作用，使砂浆具有良好的施工性，并可降低抹灰砂浆上墙后的粉化、开裂现象。聚乙烯醇中的羟基与亲水性的纤维素醚复合后，聚乙烯醇中的羟基与纤维素醚中的醚键上的氧原子缔合成氢键，因而具有超叠加效应。所以，极少量的聚乙烯醇复合少量的纤维素醚，就有很好的抗裂增强作用，使砂浆具有较好的抗裂性(无裂纹)和较高的粘结强度，成本很低、性价比很高，还可防止收缩、空鼓开裂。
2、本发明提供的厨卫专用厚层抗裂砂浆，添加了木质纤维素，木质纤维素用作增稠剂和粘结剂，添加进砂浆后，可锁住砂浆中的水分，使其不被加气砌块快速吸收，木质纤维素的加入量，可保证抹灰时的保水速度，使砂浆中的胶凝材料可在预定的时间内慢慢凝固，在抹灰时不会存在因水分被吸收而出现粉化、开裂的问题；在砂浆抹面时，砂浆受到剪切力的作用，砂浆稠度降低，而将低稠度的砂浆进行抹灰，不会出现抹灰刀被砂浆粘住而造成抹灰表面被拖挂的不平整的现象，施工方便、简单。因此，木质纤维素加入，保证抹灰时砂浆中的水分不被快速吸收，提高了抹灰墙面的质量，且降低了施工难度，使抹灰表面平整。
具体实施方式
为了使本领域技术人员更好地理解本发明，下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一
一种厨卫专用厚层抗裂砂浆，其原材料包括以下重量百分比的材料：普通水泥10％；高强石膏粉10％，轻钙粉1％，重钙粉1％，玻化微珠1％，石英砂20％；木质纤维素1％，纤维素醚0.1％，粉状胶粘剂0.1％，缓凝剂1％。
一种厨卫专用厚层抗裂砂浆的制备方法，包括：
步骤一、将普通水泥、高强石膏粉、轻钙粉、重钙粉、玻化微珠、石英砂依次加入到无重力粉体搅拌机中，搅拌10分钟；
步骤二、再将木质纤维素、纤维素醚、粉状胶粘剂、缓凝剂依次加入到步骤一所述无重力粉体搅拌机中，继续搅拌30分钟；直至搅拌均匀，得到该厨卫专用厚层抗裂砂浆。
本实施例1得到厨卫专用厚层抗裂砂浆的抗裂性能好、抗压强度、拉伸粘结强度均优于现有技术的砂浆，收缩率小，可以达到防止收缩、空鼓开裂的效果。
实施例二
一种厨卫专用厚层抗裂砂浆，其原材料包括以下重量百分比的材料：普通水泥20％；高强石膏粉20％，轻钙粉2.5％，重钙粉25％，玻化微珠10％，石英砂35％；木质纤维素1.5％，纤维素醚1.5％，粉状胶粘剂5％，缓凝剂2.5％。
一种厨卫专用厚层抗裂砂浆的制备方法，包括：
步骤一、将普通水泥、高强石膏粉、轻钙粉、重钙粉、玻化微珠、石英砂依次加入到无重力粉体搅拌机中，搅拌10分钟；
步骤二、再将木质纤维素、纤维素醚、粉状胶粘剂、缓凝剂依次加入到步骤一所述无重力粉体搅拌机中，继续搅拌30分钟；直至搅拌均匀，得到该厨卫专用厚层抗裂砂浆。
本实施例2得到厨卫专用厚层抗裂砂浆的抗裂性能好、抗压强度、拉伸粘结强度均优于现有技术的砂浆，收缩率小，可以达到防止收缩、空鼓开裂的效果。
实施例三
一种厨卫专用厚层抗裂砂浆，其原材料包括以下重量百分比的材料：普通水泥30％；高强石膏粉30％，轻钙粉5％，重钙粉50％，玻化微珠20％，石英砂50％；木质纤维素3％，纤维素醚3％，粉状胶粘剂10％，缓凝剂5％。
一种厨卫专用厚层抗裂砂浆的制备方法，包括：
步骤一、将普通水泥、高强石膏粉、轻钙粉、重钙粉、玻化微珠、石英砂依次加入到无重力粉体搅拌机中，搅拌10分钟；
步骤二、再将木质纤维素、纤维素醚、粉状胶粘剂、缓凝剂依次加入到步骤一所述无重力粉体搅拌机中，继续搅拌30分钟；直至搅拌均匀，得到该厨卫专用厚层抗裂砂浆。
本实施例3得到厨卫专用厚层抗裂砂浆的抗裂性能好、抗压强度、拉伸粘结强度均优于现有技术的砂浆，收缩率小，可以达到防止收缩、空鼓开裂的效果。
本发明实施例1-3进行性能检测，所得厨卫专用厚层抗裂砂浆的物理力学性能见表1和表2，适合于一般厨卫施工基层找平砂浆层施工厚度大于5mm的抹灰施工，且可于-10℃环境下施工。
表1厨卫专用厚层抗裂砂浆的技术要求
表2厨卫专用厚层抗裂砂浆的性能结果
如表1和表2所示，我们可以得知实施例二的拉伸粘结强度最优，在实施例二中的粉状胶黏剂配比较实施例一和实施例三相比为最佳，本发明中粉状胶黏剂为聚乙烯醇，利用聚乙烯醇的水溶性，使其随水迁移至砂浆界面或表面处，在界面处聚集、成膜，连接、填充界面过渡区的空隙与孔隙，以大幅提高粘结强度；利用纤维素醚在砂浆中的保水、增稠、引气作用，使砂浆具有良好的施工性，并可降低抹灰砂浆上墙后的粉化、开裂现象。聚乙烯醇中的羟基与亲水性的纤维素醚复合后，聚乙烯醇中的羟基与纤维素醚中的醚键上的氧原子缔合成氢键，因而具有超叠加效应。所以，极少量的聚乙烯醇复合少量的纤维素醚，就有很好的抗裂增强作用，使砂浆具有较好的抗裂性(无裂纹)和较高的粘结强度，成本很低、性价比很高，还可防止收缩、空鼓开裂。
采用本厨卫专用厚层抗裂砂浆的制备方法，具有制备工艺简单可靠、操作方便的特点。
所述普通水泥为通用硅酸盐水泥，所述通用硅酸盐水泥的强度等级为32.5、42.5、52.5中的一种。
所述缓凝剂为酒石酸或柠檬酸或其盐类，缓凝剂的作用是为了延长水泥的水化硬化时间,使新拌混凝土能在较长时间内保持塑性,从而调节新拌混凝土的凝结时间。
所述粉状胶粘剂为聚乙烯醇，利用聚乙烯醇的水溶性，使其随水迁移至砂浆界面或表面处，在界面处聚集、成膜，连接、填充界面过渡区的空隙与孔隙，以大幅提高粘结强度。
所述纤维素醚为羟丙基甲基纤维素醚、羟乙基甲基纤维素醚、羟乙基纤维素醚中的一种或两种的混合，利用纤维素醚在砂浆中的保水、增稠、引气作用，使砂浆具有良好的施工性，并可降低抹灰砂浆上墙后的粉化、开裂现象。
需要说明的是，上述具体实施方式仅仅为本发明的较佳实施例及所运用技术原理，在本发明所公开的技术范围内，任何熟悉本技术领域的技术人员在未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都应涵盖在本发明的保护范围内。
Claims (6)
1.一种厨卫专用厚层抗裂砂浆，其特征在于，其原材料包括以下重量百分比的材料：普通水泥10-30％；高强石膏粉10-30％，轻钙粉1-5％，重钙粉1-50％，玻化微珠1-20％，石英砂20-50％；木质纤维素1-3％，纤维素醚0.1-3％，粉状胶粘剂0.1-10％，缓凝剂1-5％。
2.根据权利要求1所述的一种厨卫专用厚层抗裂砂浆，其特征在于：所述普通水泥为通用硅酸盐水泥，所述通用硅酸盐水泥的强度等级为32.5、42.5、52.5中的一种。
3.根据权利要求1所述的一种厨卫专用厚层抗裂砂浆，其特征在于：所述缓凝剂为酒石酸或柠檬酸或其盐类。
4.根据权利要求1所述的一种厨卫专用厚层抗裂砂浆，其特征在于：所述粉状胶粘剂为聚乙烯醇。
5.根据权利要求1所述的一种厨卫专用厚层抗裂砂浆，其特征在于：所述纤维素醚为羟丙基甲基纤维素醚、羟乙基甲基纤维素醚、羟乙基纤维素醚中的一种或两种的混合。
6.一种如权利要求1-5任意一项所述的厨卫专用厚层抗裂砂浆的制备方法，其特征在于，包括：
步骤一、将普通水泥、高强石膏粉、轻钙粉、重钙粉、玻化微珠、石英砂依次加入到无重力粉体搅拌机中，搅拌10分钟；
步骤二、再将木质纤维素、纤维素醚、粉状胶粘剂、缓凝剂依次加入到步骤一所述无重力粉体搅拌机中，继续搅拌30分钟；直至搅拌均匀，得到该厨卫专用厚层抗裂砂浆。