CN113576129A - Jewelry and surface treatment method thereof - Google Patents
Jewelry and surface treatment method thereof Download PDFInfo
- Publication number
- CN113576129A CN113576129A CN202110932242.4A CN202110932242A CN113576129A CN 113576129 A CN113576129 A CN 113576129A CN 202110932242 A CN202110932242 A CN 202110932242A CN 113576129 A CN113576129 A CN 113576129A
- Authority
- CN
- China
- Prior art keywords
- jewelry
- glaze
- surface treatment
- drying
- target
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a jewelry and a surface treatment method thereof, wherein the surface treatment method of the jewelry comprises the following steps: mixing a transparent low-temperature enamel glaze with a curing agent, and then carrying out first heating and drying treatment to obtain an initial glaze; carrying out vacuum treatment on the initial glaze to obtain a target glaze; coating the target glaze on the surface of the jewelry; and carrying out second heating and drying treatment or air drying treatment on the coated jewelry. The jewelry is obtained by adopting the surface treatment method. The invention can clearly show the surface effect or texture of the jewelry under the enamel, not only can keep the unique effect of the jewelry surface, but also adds clear and colorful colors.
Description
Technical Field
The invention belongs to the technical field of jewelry processing, and particularly relates to a jewelry and a surface treatment method thereof.
Background
The color of the enamel of the existing jewelry goods is generally flat and solid, and the metal surface effect or texture under the enamel cannot be clearly shown. Further, if enamel is fired at a high temperature on the surface of the existing jewelry goods, the processing temperature is usually about 1000 ℃ (centigrade), thereby increasing the complexity of surface treatment of the jewelry goods.
Disclosure of Invention
The invention aims to overcome the defects of the prior art and provides an ornament and a surface treatment method thereof, which can clearly show the surface effect or texture of the ornament under the enamel, not only can keep the unique effect of the surface of the ornament, but also add clear and colorful colors.
In order to solve the technical problems, the invention adopts the following technical scheme: a surface treatment method of jewelry comprises the following steps: mixing a transparent low-temperature enamel glaze with a curing agent, and then carrying out first heating and drying treatment to obtain an initial glaze; carrying out vacuum treatment on the initial glaze to obtain a target glaze; coating the target glaze on the surface of the jewelry; and carrying out second heating and drying treatment or air drying treatment on the coated jewelry.
In a particular embodiment, the low temperature enamel frit comprises polyepichlorohydrin.
In one particular embodiment, the curing agent comprises: a mixture of dimethyl, nonylphenol, aminomethyl, methylenediyl and benzyl alcohol.
In one embodiment, the low temperature enamel frit and the curing agent are mixed in a ratio of 5: 2-4: 1.5 weight ratio for uniform mixing.
In one embodiment, the step of mixing the low-temperature enamel glaze with the curing agent and then subjecting the mixture to a first heating and drying treatment to obtain the initial glaze comprises: and uniformly mixing the low-temperature enamel glaze with the curing agent, and then putting the mixture into an oven for baking for a certain time to obtain the initial glaze.
In a specific embodiment, the baking temperature of the oven is 70-100 ℃, and the baking time of the oven is 3-5 minutes.
In one embodiment, the step of subjecting the initial glaze to vacuum treatment to obtain the target glaze comprises: and discharging bubbles in the initial glaze material in a negative pressure vacuumizing mode to obtain the target glaze material.
In one embodiment, the vacuumizing time is 5-10 minutes, and the vacuum degree is minus 0.1 MPa.
In one particular embodiment, the step of applying the target glaze to the surface of the jewelry comprises: glazing is carried out by adopting a special tool according to a mode of a small number of times and the same direction.
In one embodiment, the step of subjecting the coated jewelry to the second heating and drying process comprises: placing the coated jewelry into a first drying oven to be baked for a certain time; or, the coated jewelry is put into a second drying oven to be baked for a certain time, and is taken out and placed in a room temperature environment to be naturally cooled.
In a specific embodiment, the baking temperature of the first drying oven is 70-100 ℃, and the baking time of the first drying oven is 40-60 minutes.
In a specific embodiment, the baking temperature of the second drying oven is 70-100 ℃, the baking time of the second drying oven is 5-10 minutes, and the natural cooling time is 10-20 minutes.
In a specific embodiment, the step of air-drying the coated jewelry comprises: and naturally drying the coated jewelry at room temperature.
In a specific embodiment, the natural air drying time is 10-12 hours.
The jewelry is obtained by adopting the surface treatment method.
Compared with the prior art, the invention has the beneficial effects that:
the surface treatment method of the jewelry can simply and efficiently glaze the surface of the jewelry, and the glazed jewelry can clearly show the surface effect or texture of the jewelry under the enamel, thereby not only keeping the unique effect of the surface of the jewelry, but also adding clear and colorful colors.
Drawings
Fig. 1 shows a flow diagram of the surface treatment method of jewelry of the present invention.
Detailed Description
The invention will be further described with reference to examples of embodiments shown in the drawings.
As shown in figure 1, the surface treatment method of the jewelry provided by the invention comprises the following steps:
(1) mixing the transparent low-temperature enamel glaze with a curing agent, and then carrying out first heating and drying treatment to obtain an initial glaze. Wherein the curing agent functions to promote the solidification and hardening of the target glaze in the subsequent steps. If the curing agent is lacked, the target glaze cannot be solidified and hardened after being coated on the surface of the jewelry. The first heating and drying process functions to increase the fluidity of the target glaze, thereby facilitating glazing in a subsequent step.
(2) And carrying out vacuum treatment on the initial glaze to obtain the target glaze. Wherein, through carrying out vacuum treatment to the initial glaze, can discharge the bubble in the glaze to obtain the required target glaze of coating.
(3) And coating the target glaze on the surface of the jewelry. The target glaze is coated on the surface of the jewelry in a specific mode by adopting a special tool, so that the surface of the jewelry is full and smooth and is free of bubbles.
(4) And carrying out second heating and drying treatment or air drying treatment on the coated jewelry. And the second heating and drying are carried out on the coated jewelry, so that the solidification and hardening speed of the target glaze can be increased.
When in use, the surface treatment method of the jewelry can simply, rapidly and efficiently carry out glazing treatment on the surface of the jewelry, and the treated jewelry can clearly show the surface effect or texture (such as metal surface effect or texture) of the jewelry under the enamel, thereby not only keeping the unique effect of the surface of the jewelry, but also adding clear and colorful colors, being simple, rapidly and efficiently and having good safety.
In a particular embodiment, the low-temperature enamel glaze comprises polyepichlorohydrin, which is preferably used for the surface treatment of jewelry and is safe since polyepichlorohydrin does not contain harmful elements which have an effect on the human body.
In a particular embodiment, the curing agent comprises: the mixture of dimethyl, nonyl phenol, aminomethyl, methylene-bis-group and benzyl alcohol, the curing agent and the low-temperature enamel glaze have good uniform mixing effect, and can prevent the target glaze from accelerating solidification and drying or from being incapable of solidifying and hardening. The mixture of dimethyl, nonyl phenol, aminomethyl, methylene biradical and benzyl alcohol does not contain harmful elements which have influence on human body, so that the safety is good.
In one particular embodiment, the low temperature enamel frit is mixed with a curing agent according to a ratio of 5: 2-4: 1.5 weight ratio for uniform mixing. For example, by stirring to mix the two uniformly. If the mixing of the low-temperature enamel glaze and the curing agent is not uniform, the target glaze is agglomerated and heated unevenly. The proportion of the low-temperature enamel glaze and the curing agent can be set according to actual needs. If the content of the low-temperature enamel glaze is too large, the target glaze obtained by mixing is too viscous, and the distribution of the low-temperature enamel glaze in the target glaze is not uniform. If the content of the curing agent is too large, the target glaze material is accelerated to solidify and dry, and the target glaze material cannot be used. Preferably, the low-temperature enamel glaze and the curing agent are mixed according to a ratio of 5: 2, the low-temperature enamel glaze has good distribution uniformity in the target glaze and good solidification effect of the target glaze.
In a particular embodiment, the step of mixing the low-temperature enamel glaze with the curing agent followed by a first heating and drying treatment to obtain an initial glaze comprises: and uniformly mixing the low-temperature enamel glaze with a curing agent, and putting the mixture into an oven for baking for a certain time to obtain the initial glaze.
In a specific embodiment, the baking temperature of the oven is 70-100 ℃. The baking time of the oven is 3-5 minutes. Specifically, if the process temperature is too low, the initial glaze surface is not glossy and does not flow. If the temperature is too high in the process, the initial glaze is directly solidified and cannot be used. If the process time is too short, the initial glaze surface is not glossy and the fluidity is poor. If the process is too long, the initial glaze is solidified and hardened, and cannot be used. Preferably, the baking temperature of the oven is 85 ℃, the baking time of the oven is 4 minutes, and the surface gloss of the initial glaze is good and the fluidity is good.
In a particular embodiment, the step of subjecting the initial glaze to vacuum treatment to obtain the target glaze comprises: and discharging bubbles in the initial glaze material in a negative pressure vacuumizing mode to obtain the target glaze material. Through the evacuation, can effectively eliminate the bubble that produces in low temperature enamel frit and the curing agent stirring process, improve the quality of target glaze to can reduce the bubble on the surface of ornament when using, easily glazing.
In a specific embodiment, the vacuum pumping time is 5 to 10 minutes, and the vacuum degree is minus 0.1 mpa, so that bubbles generated during the stirring process of the low-temperature enamel glaze and the curing agent can be effectively eliminated. Specifically, at normal temperature (20-25 ℃), the low-temperature enamel glaze and the curing agent are uniformly mixed and then are placed into a vacuum extractor for vacuum-pumping for 5-10 minutes, the vacuum degree is minus 0.1 MPa, bubbles in the initial glaze can be effectively discharged, and the target glaze after the bubbles are discharged can be simply and efficiently obtained. Preferably, the vacuumizing time is 7.5 minutes, the vacuum degree is minus 0.1 MPa, bubbles generated in the stirring process of the low-temperature enamel glaze and the curing agent can be effectively eliminated, and the stability is good.
In one particular embodiment, the step of applying the target glaze to the surface of the jewelry comprises: glazing is carried out by adopting a special tool according to a mode of a small number of times and the same direction. Specifically, the toothpick or the embroidery needle is adopted for glazing in a mode of a small amount of times and the same direction, so that the surface of the jewelry can be full and smooth and is free of bubbles. For example, the target glaze is uniformly coated on the surface of the jewelry in the same direction (for example, all directions of upward, downward, leftward or rightward) by using toothpicks or embroidery needles for more than three times, and the workpiece is ensured not to have large vibration during operation. Wherein the glazing amount is 0.005-0.01 g each time.
In a preferred embodiment, the jewelry is made of a metal material. When in use, the target glaze is uniformly coated along the metal surface of the jewelry, so that the metal surface effect or texture under the enamel can be clearly shown, the unique effect of the jewelry surface can be kept, and the clear and colorful colors are added.
In one embodiment, the step of subjecting the coated jewelry piece to the second heating and drying process comprises: and placing the coated jewelry into a first drying oven to be baked for a certain time.
In a specific embodiment, the jewelry with the target glaze is fixed on a clamp and placed into a first drying oven at the temperature of 70-100 ℃ for baking for 40-60 minutes. Specifically, if the temperature in the process is too low, the surface of the treated target glaze is not smooth enough and is not flat. If the temperature in the process is too high, the color of the treated target glaze is changed and is not bright enough. If the process time is too short, the treated target glaze surface is not glossy. If the process time is too long, the color of the treated target glaze material has color difference and is easy to crack. Preferably, the baking temperature of the first drying oven is 85 ℃, the baking time of the first drying oven is 50 minutes, so that the surface of the treated target glaze is smoother, smoother and glossy, and the stability is good.
In a specific embodiment, the coated jewelry is put into a second drying oven to be baked for a certain time, and is taken out and placed in a room temperature environment to be naturally cooled.
In a specific embodiment, the jewelry with the target glaze is fixed on a fixture, placed in a second drying oven with the temperature of 70-100 ℃ for baking for 5-10 minutes, taken out and placed in a room temperature environment for naturally cooling for 10-20 minutes, so that the surface of the treated target glaze is smoother, smoother and glossy, the controllability and stability of the solidification and hardening speed of the target glaze can be improved, and the economical efficiency is good. Preferably, the baking temperature of the second drying oven is 85 ℃, the baking time of the second drying oven is 7.5 minutes, the natural cooling time is 15 minutes, the surface of the treated target glaze is smoother, smoother and more glossy, and the controllability of the solidification and hardening speed of the target glaze is good, and the stability is good.
In a specific embodiment, the step of air-drying the coated jewelry comprises: and (4) placing the coated jewelry in a room temperature environment for natural air drying.
In a specific embodiment, the jewelry covered with the target glaze is placed in a room temperature environment for 10-12 hours to be naturally dried. Wherein, the natural air drying time can be determined according to actual needs. Preferably, the jewelry covered with the target glaze is placed in a room temperature environment for natural air drying for 11 hours, and the air drying effect is good.
The surface treatment method of the jewelry can simply, rapidly and efficiently glaze the surface part of the jewelry, and the glazed jewelry can clearly show the metal surface effect or texture under the enamel, so that the unique effect of the metal surface can be maintained, and the transparent colorful color is added, thereby being simple, rapidly and efficiently and having good safety.
On the basis of the above embodiments, the invention provides a jewelry obtained by processing with the above surface treatment method.
The above embodiments are all described in a progressive manner, and the same and similar parts among the embodiments can be referred to each other, and each embodiment focuses on the differences from the other embodiments.
The protective scope of the present invention is not limited to the above-described embodiments, and it is apparent that various modifications and variations can be made to the present invention by those skilled in the art without departing from the scope and spirit of the present invention. It is intended that the present invention cover the modifications and variations of this invention provided they come within the scope of the appended claims and their equivalents.
Claims (15)
1. A surface treatment method of jewelry is characterized by comprising the following steps:
mixing a transparent low-temperature enamel glaze with a curing agent, and then carrying out first heating and drying treatment to obtain an initial glaze;
carrying out vacuum treatment on the initial glaze to obtain a target glaze;
coating the target glaze on the surface of the jewelry;
and carrying out second heating and drying treatment or air drying treatment on the coated jewelry.
2. The method for the surface treatment of jewelry according to claim 1, wherein said low temperature enamel frit comprises polyepichlorohydrin.
3. The method for surface treatment of jewelry according to claim 1, wherein the curing agent comprises: a mixture of dimethyl, nonylphenol, aminomethyl, methylenediyl and benzyl alcohol.
4. The method for surface treatment of jewelry according to claim 1, wherein the ratio of said low-temperature enamel frit to said curing agent is 5: 2-4: 1.5 weight ratio for uniform mixing.
5. The method for surface treatment of jewelry as claimed in claim 1, wherein the step of mixing said low temperature enamel frit with said curing agent and then subjecting to a first heating and drying treatment to obtain said initial frit comprises: and uniformly mixing the low-temperature enamel glaze with the curing agent, and then putting the mixture into an oven for baking for a certain time to obtain the initial glaze.
6. The jewelry surface treatment method according to claim 5, wherein the baking temperature of the oven is 70-100 ℃, and the baking time of the oven is 3-5 minutes.
7. The method for surface treatment of jewelry of claim 1, wherein the step of subjecting the initial glaze to vacuum treatment to obtain the target glaze comprises: and discharging bubbles in the initial glaze material in a negative pressure vacuumizing mode to obtain the target glaze material.
8. The surface treatment method of jewelry as claimed in claim 7, wherein the time of evacuation is 5 to 10 minutes, and the degree of vacuum is minus 0.1 mpa.
9. The method of surface treatment of jewelry of claim 1, wherein the step of applying the target glaze to the surface of the jewelry comprises: glazing is carried out by adopting a special tool according to a mode of a small number of times and the same direction.
10. The method of surface treatment of jewelry as claimed in claim 1, wherein the step of second heating and drying the coated jewelry comprises: placing the coated jewelry into a first drying oven to be baked for a certain time; or, the coated jewelry is put into a second drying oven to be baked for a certain time, and is taken out and placed in a room temperature environment to be naturally cooled.
11. The surface treatment method of jewelry according to claim 10, wherein the baking temperature of the first drying oven is 70 to 100 ℃, and the baking time of the first drying oven is 40 to 60 minutes.
12. The surface treatment method of jewelry, according to claim 10, wherein the baking temperature of the second drying oven is 70 to 100 ℃, the baking time of the second drying oven is 5 to 10 minutes, and the natural cooling time is 10 to 20 minutes.
13. The method of surface treatment of jewelry as claimed in claim 1, wherein the step of air drying the coated jewelry comprises: and naturally drying the coated jewelry at room temperature.
14. The surface treatment method of jewelry as claimed in claim 13, wherein the natural air drying time is 10 to 12 hours.
15. An ornament, characterized in that the ornament is obtained by adopting the surface treatment method of any one of claims 1 to 14.