CN113456515A - 一种有机硅组合物及其制备方法和应用 - Google Patents
一种有机硅组合物及其制备方法和应用 Download PDFInfo
- Publication number
- CN113456515A CN113456515A CN202110781206.2A CN202110781206A CN113456515A CN 113456515 A CN113456515 A CN 113456515A CN 202110781206 A CN202110781206 A CN 202110781206A CN 113456515 A CN113456515 A CN 113456515A
- Authority
- CN
- China
- Prior art keywords
- parts
- organic silicon
- fluorophlogopite
- mixing
- treated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于日用化学品技术领域。本发明提供了一种有机硅组合物，包括如下质量份的组分：乙烯基聚二甲基硅氧烷/聚甲基硅氧烷倍半硅氧烷交联聚合物30～90份；聚甲基倍半硅氧烷20～60份；三乙氧基辛基硅烷处理氟金云母5～30份；淀粉辛烯基琥珀酸铝5～20份；肉豆蔻酸镁5～20份。本发明还提供了一种有机硅组合物的制备方法和应用。本发明的有机硅化合物组分安全性高，对人体健康和生态环境无不良影响；有机硅组合物的顺滑感、通透性、柔焦和细腻度显著提高，具有优异的定妆效果。
Description
技术领域
本发明涉及日用化学品技术领域，尤其涉及一种有机硅组合物及其制备方法和应用。
背景技术
受益于颜值经济的发展，彩妆消费群体不断扩大，彩妆产品销售量不断攀升，特别是散(蜜)粉近两年增长速度极快。但因受限于成本的控制，大多数产品在用料上还是选择低价格的滑石粉、云母、淀粉类、塑料微球等原料进行简单的混合，以往的定妆散(蜜)粉产品更注重使用效果，在产品的用料上关注的较少。然而，随着经济的发展和生活水平的提高，人们对于生活品质的要求越来越高，对彩妆产品的安全性也提出了更高的要求。产品成分的安全性已经成为消费者的一种共识和市场发展趋势，安全无争议的成分逐渐开始替代现有产品中的不友好成分。并且，现有技术中的散(蜜)粉由于原料成分自身特性和生产工艺的简单化，容易出现卡粉，假滑，柔焦和通透性差，不细腻，定妆效果差等问题。
因此，研究开发一种原料成分安全性好，并且提高顺滑感、通透性、柔焦、细腻度和定妆效果的组合物，具有非常重要的价值和意义。
发明内容
本发明的目的是针对现有技术的不足提供一种有机硅组合物及其制备方法。本发明的有机硅组合物的顺滑感、通透性、柔焦和细腻度显著提高，具有优异的定妆效果。
为了实现上述发明目的，本发明提供以下技术方案：
本发明提供了一种有机硅组合物，包括如下质量份的组分：乙烯基聚二甲基硅氧烷/聚甲基硅氧烷倍半硅氧烷交联聚合物30～90份；聚甲基倍半硅氧烷20～60份；三乙氧基辛基硅烷处理氟金云母5～30份；淀粉辛烯基琥珀酸铝5～20份；肉豆蔻酸镁5～20份。
作为优选，所述有机硅组合物还包括防腐剂、着色剂和活性物，所述防腐剂、着色剂、活性物和肉豆蔻酸镁的质量比为0.1～2：0.01～1:0.01～1:5～20。
作为优选，所述活性物包含茉莉花提取物、山茶花提取物、细叶益母草提取物、白芨根提取物、白术根提取物、白蔹根提取物、珍珠粉和桃花提取物中的一种或几种。
作为优选，所述防腐剂包含苯氧乙醇、辛甘醇、羟苯甲酯和羟苯丙酯；所述苯氧乙醇、辛甘醇、羟苯甲酯和羟苯丙酯的质量比为5～7:3～5:1～3:0.5～2。
作为优选，所述防腐剂包含乙基己基甘油、辛甘醇、羟苯甲酯和羟苯丙酯；所述乙基己基甘油、辛甘醇、羟苯甲酯和羟苯丙酯的质量比为5～7:3～5:1～3:0.5～2。
本发明还提供了一种所述的有机硅组合物的制备方法，包含如下步骤：
1)将三乙氧基辛基硅烷处理氟金云母和肉豆蔻酸镁混合后进行细化处理，得到细化产物；
2)将细化产物和剩余组分混合后进行细化处理，得到有机硅组合物。
作为优选，步骤1)所述混合的时间为30～90s，所述混合在1000～3000r/min的转速下进行；所述细化产物的粒径≤20μm。
作为优选，步骤2)所述混合的时间为40～150s，所述混合在1000～3000r/min的转速下进行；所述有机硅组合物的粒径≤100μm。
作为优选，当有机硅组合物包含着色剂时，将部分三乙氧基辛基硅烷处理氟金云母和着色剂进行第一次混合后再与剩余三乙氧基辛基硅烷处理氟金云母、肉豆蔻酸镁、防腐剂进行第二次混合；
所述部分三乙氧基辛基硅烷处理氟金云母与剩余三乙氧基辛基硅烷处理氟金云母的质量比为35～45:55～65；
所述第一次混合的时间为20～40s，第二次混合的时间为20～40s。
本发明还提供了一种所述的有机硅组合物在日用化学品中的应用。
本发明的有益效果包括以下几点：
1)本发明的有机硅化合物组分安全性高，对人体健康和生态环境无不良影响。
2)本发明的有机硅组合物的顺滑感、通透性、柔焦和细腻度显著提高，具有优异的定妆效果，其中，顺滑感、通透性来自于组合物中高含量的球形粉末。
具体实施方式
本发明提供了一种有机硅组合物，包括如下质量份的组分：乙烯基聚二甲基硅氧烷/聚甲基硅氧烷倍半硅氧烷交联聚合物30～90份；聚甲基倍半硅氧烷20～60份；三乙氧基辛基硅烷处理氟金云母5～30份；淀粉辛烯基琥珀酸铝5～20份；肉豆蔻酸镁5～20份。
本发明的有机硅组合物包含30～90份乙烯基聚二甲基硅氧烷/聚甲基硅氧烷倍半硅氧烷交联聚合物，优选为40～80份，进一步优选为50～70份，更优选为55～65份，还优选为60份。
本发明的有机硅组合物包含20～60份聚甲基倍半硅氧烷，优选为30～50份，进一步优选为35～45份，更优选为40份。
本发明的有机硅组合物包含5～30份三乙氧基辛基硅烷处理氟金云母，优选为10～25份，进一步优选为15～20份，更优选为16～18份；所述三乙氧基辛基硅烷处理氟金云母优选由合成氟金云母和三乙氧基辛基硅烷制备得到。
本发明的有机硅组合物包含5～20份淀粉辛烯基琥珀酸铝，优选为8～18份，进一步优选为10～15份，更优选为12～14份。
本发明的有机硅组合物包含5～20份肉豆蔻酸镁，优选为8～18份，进一步优选为10～15份，更优选为12～14份。
本发明所述有机硅组合物优选还包括防腐剂、着色剂和活性物，所述防腐剂、着色剂、活性物和肉豆蔻酸镁的质量比优选为0.1～2：0.01～1:0.01～1:5～20，进一步优选为0.5～1.5:0.1～0.8:0.1～0.8:8～18，更优选为1：0.3～0.5:0.3～0.5:10～15。
本发明所述活性物优选包含茉莉花提取物、山茶花提取物、细叶益母草提取物、白芨根提取物、白术根提取物、白蔹根提取物、珍珠粉和桃花提取物中的一种或几种；当活性物同时包含几种组分时，各组分优选以等质量比进行混合。
本发明所述防腐剂优选包含苯氧乙醇、辛甘醇、羟苯甲酯和羟苯丙酯；所述苯氧乙醇、辛甘醇、羟苯甲酯和羟苯丙酯的质量比优选为5～7:3～5:1～3:0.5～2，进一步优选为5.5～6.5:3.5～4.5:1.5～2.5:1～1.5，更优选为6:4:2:1.2。
本发明所述防腐剂还优选为包含乙基己基甘油、辛甘醇、羟苯甲酯和羟苯丙酯；所述乙基己基甘油、辛甘醇、羟苯甲酯和羟苯丙酯的质量比优选为5～7:3～5:1～3:0.5～2，进一步优选为5.5～6.5:3.5～4.5:1.5～2.5:1～1.5，更优选为6:4:2:1.2。
本发明所述着色剂根据实际需要进行添加，所述着色剂优选为CI 77891、CI77491、CI 77492、CI 77499、CI 15850、CI 15985、CI 19140或CI 42090。
本发明还提供了一种所述的有机硅组合物的制备方法，包含如下步骤：
1)将三乙氧基辛基硅烷处理氟金云母和肉豆蔻酸镁混合后进行细化处理，得到细化产物；
2)将细化产物和剩余组分混合后进行细化处理，得到有机硅组合物。
本发明步骤1)所述混合的时间优选为30～90s，进一步优选为40～80s，更优选为50～70s；所述混合优选在1000～3000r/min的转速下进行，进一步优选2000r/min；所述细化产物的粒径优选≤20μm。
本发明步骤2)所述混合的时间优选为40～150s，进一步优选为60～120s，更优选为70～100s，还优选为80～90s；所述混合优选在1000～3000r/min的转速下进行，进一步优选2000r/min；所述有机硅组合物的粒径优选≤100μm。
本发明的有机硅组合物包含防腐剂时，所述防腐剂优选和三乙氧基辛基硅烷处理氟金云母、肉豆蔻酸镁同时进行混合，所述混合的时间、转速与步骤1)相同。
本发明的有机硅组合物包含着色剂时，优选将部分三乙氧基辛基硅烷处理氟金云母和着色剂进行第一次混合后再与剩余三乙氧基辛基硅烷处理氟金云母、肉豆蔻酸镁、防腐剂进行第二次混合；
所述部分三乙氧基辛基硅烷处理氟金云母与剩余三乙氧基辛基硅烷处理氟金云母的质量比优选为35～45:55～65，进一步优选为40:60；
所述第一次混合的时间优选为20～40s，进一步优选为30s；第二次混合的时间优选为20～40s，进一步优选为30s；所述第一次混合和第二次混合优选在1000～3000r/min的转速下进行，进一步优选2000r/min。
本发明的有机硅组合物包含活性物时，优选将细化产物和活性物以外的剩余组分混合后再与活性物进行混合；所述活性物优选以喷洒的方式加入；所述细化产物和活性物以外的剩余组分混合的时间优选为60～90s，进一步优选为70～80s；所述与活性物进行混合的时间优选为25～40s，进一步优选为30～35s。
本发明还提供了一种所述的有机硅组合物在日用化学品中的应用。
下面结合实施例对本发明提供的技术方案进行详细的说明，但是不能把它们理解为对本发明保护范围的限定。
实施例1
将8g三乙氧基辛基硅烷处理氟金云母、5g肉豆蔻酸镁和0.5g防腐剂在1200r/min的转速下混合80s，防腐剂中包含质量比为5:3:2:1的苯氧乙醇、辛甘醇、羟苯甲酯和羟苯丙酯，混合完成后得到的均匀混合物在气流粉碎机中进行粉碎处理，得到粒径为20μm的细化产物。
将细化产物、35g乙烯基聚二甲基硅氧烷/聚甲基硅氧烷倍半硅氧烷交联聚合物、25g聚甲基倍半硅氧烷和5g淀粉辛烯基琥珀酸铝在1200r/min的转速下混合90s，得到的均匀混合物进行过筛处理，得到粒径为100μm的有机硅组合物。
实施例2
将28g三乙氧基辛基硅烷处理氟金云母、20g肉豆蔻酸镁和2g防腐剂在2800r/min的转速下混合30s，防腐剂中包含质量比为7:5:3:2的乙基己基甘油、辛甘醇、羟苯甲酯和羟苯丙酯，混合完成后得到的均匀混合物在气流粉碎机中进行粉碎处理，得到粒径为19μm的细化产物。
将细化产物、85g乙烯基聚二甲基硅氧烷/聚甲基硅氧烷倍半硅氧烷交联聚合物、55g聚甲基倍半硅氧烷和20g淀粉辛烯基琥珀酸铝在2800r/min的转速下混合60s，将0.4g茉莉花提取物和0.4g珍珠粉喷洒到混合物中，以2800r/min的转速混合25s，得到的均匀混合物进行过筛处理，得到粒径为95μm的有机硅组合物。
实施例3
将8g三乙氧基辛基硅烷处理氟金云母和0.6g着色剂CI 77891在2000r/min的转速下混合30s，然后在气流粉碎机中进行粉碎处理，得到粒径为18μm的细化产物1。将12g三乙氧基辛基硅烷处理氟金云母、15g肉豆蔻酸镁和1g防腐剂在2000r/min的转速下混合30s，防腐剂中包含质量比为6:4:2:1的乙基己基甘油、辛甘醇、羟苯甲酯和羟苯丙酯，混合完成后得到的均匀混合物在气流粉碎机中进行粉碎处理，得到粒径为18μm的细化产物2。
将细化产物1、细化产物2、60g乙烯基聚二甲基硅氧烷/聚甲基硅氧烷倍半硅氧烷交联聚合物、40g聚甲基倍半硅氧烷和15g淀粉辛烯基琥珀酸铝在2000r/min的转速下混合80s，得到的均匀混合物进行过筛处理，得到粒径为92μm的有机硅组合物。
实施例4
将7g三乙氧基辛基硅烷处理氟金云母和0.4g着色剂CI 15850在2200r/min的转速下混合25s，然后与11g三乙氧基辛基硅烷处理氟金云母、12g肉豆蔻酸镁和1.2g防腐剂在2200r/min的转速下混合35s，防腐剂中包含质量比为6:4:2:1的苯氧乙醇、辛甘醇、羟苯甲酯和羟苯丙酯，混合完成后得到的均匀混合物在气流粉碎机中进行粉碎处理，得到粒径为18μm的细化产物。
将细化产物、50g乙烯基聚二甲基硅氧烷/聚甲基硅氧烷倍半硅氧烷交联聚合物、30g聚甲基倍半硅氧烷和15g淀粉辛烯基琥珀酸铝在2200r/min的转速下混合90s，将0.5g白术根提取物喷洒到混合物中，以2200r/min的转速混合30s，得到的均匀混合物进行过筛处理，得到粒径为90μm的有机硅组合物。
不同年龄、不同皮肤性质的人对实施例1～3的有机硅组合物和市售品的顺滑感、通透性、柔焦感、定妆时间进行评测，结果如表1所示。
表1实施例1～3的有机硅组合物和市售品的性能比较
备注：1.皮肤性质填写个人面部肌肤状况，如：油性、中性、干性、混合性。
2.顺滑感、通透性、柔焦感打分机制为：0～10分，分值越高代表效果越好。
3.定妆时间为当天使用产品后，实际定妆时间。
由表1可知，实施例1～3的有机硅组合物的顺滑感、通透性和柔焦感显著提高，具有优异的定妆效果。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (10)
1.一种有机硅组合物，其特征在于，包括如下质量份的组分：乙烯基聚二甲基硅氧烷/聚甲基硅氧烷倍半硅氧烷交联聚合物30～90份；聚甲基倍半硅氧烷20～60份；三乙氧基辛基硅烷处理氟金云母5～30份；淀粉辛烯基琥珀酸铝5～20份；肉豆蔻酸镁5～20份。
2.根据权利要求1所述的有机硅组合物，其特征在于，所述有机硅组合物还包括防腐剂、着色剂和活性物，所述防腐剂、着色剂、活性物和肉豆蔻酸镁的质量比为0.1～2：0.01～1:0.01～1:5～20。
3.根据权利要求2所述的有机硅组合物，其特征在于，所述活性物包含茉莉花提取物、山茶花提取物、细叶益母草提取物、白芨根提取物、白术根提取物、白蔹根提取物、珍珠粉和桃花提取物中的一种或几种。
4.根据权利要求2或3所述的有机硅组合物，其特征在于，所述防腐剂包含苯氧乙醇、辛甘醇、羟苯甲酯和羟苯丙酯；所述苯氧乙醇、辛甘醇、羟苯甲酯和羟苯丙酯的质量比为5～7:3～5:1～3:0.5～2。
5.根据权利要求2或3所述的有机硅组合物，其特征在于，所述防腐剂包含乙基己基甘油、辛甘醇、羟苯甲酯和羟苯丙酯；所述乙基己基甘油、辛甘醇、羟苯甲酯和羟苯丙酯的质量比为5～7:3～5:1～3:0.5～2。
6.权利要求1～5任意一项所述的有机硅组合物的制备方法，其特征在于，包含如下步骤：
1)将三乙氧基辛基硅烷处理氟金云母和肉豆蔻酸镁混合后进行细化处理，得到细化产物；
2)将细化产物和剩余组分混合后进行细化处理，得到有机硅组合物。
7.根据权利要求6所述的制备方法，其特征在于，步骤1)所述混合的时间为30～90s，所述混合在1000～3000r/min的转速下进行；所述细化产物的粒径≤20μm。
8.根据权利要求6或7所述的制备方法，其特征在于，步骤2)所述混合的时间为40～150s，所述混合在1000～3000r/min的转速下进行；所述有机硅组合物的粒径≤100μm。
9.根据权利要求8所述的制备方法，其特征在于，当有机硅组合物包含着色剂时，将部分三乙氧基辛基硅烷处理氟金云母和着色剂进行第一次混合后再与剩余三乙氧基辛基硅烷处理氟金云母、肉豆蔻酸镁、防腐剂进行第二次混合；
所述部分三乙氧基辛基硅烷处理氟金云母与剩余三乙氧基辛基硅烷处理氟金云母的质量比为35～45:55～65；
所述第一次混合的时间为20～40s，第二次混合的时间为20～40s。
10.权利要求1～5任意一项所述的有机硅组合物在日用化学品中的应用。